InnoPlus LLDPE is produced by low pressure polymerization, using

LLDPE
Linear Low Density
Linear Low Density Polyethylene (LLDPE) under
the brand of InnoPlus, is produced by PTT Global
Gas Phase of Unipol process under the license of Univation
Technology. This technology can provide the wide range of LLDPE
Polyethylene Chemical Public Company Limited (PTTGC). products. The variety of catalysts and comonomers could be used
The capacity for LLDPE production is at 400,000 MTA. in order to produce products for the various applications covering
film, rotational molding, injection and wire & cable.
Test Film Metallocene Film
Properties Method Unit (1) (1) (1) (1)
LL7410D2(1) (1) (1) (1) (1) (2) (2)
(ASTM) LL7410A LL7410D LL7410D1 LL7410G1 LL7420A LL7420D LL7420D1 LL7428A LL7810A LL7810D LL7820A(2) LL7820D(2) LL7835A(2) LL7910A(2)
Melt Index D1238 g/10 min 1 1 1 1 1 2 2 2 2.8 1 1 2 2 3.5 1
Density D792 g/cm3 0.918 0.921 0.920 0.920 0.921 0.918 0.921 0.920 0.918 0.918 0.920 0.918 0.920 0.920 0.918
Film Properties
Tensile Strength at Break (MD) D882 Mpa 34 34 34 34 34 31 31 31 30 50 54 45 43 45 60

LLDPE
Tensile Strength at Break (TD) D882 Mpa 26 26 26 26 26 23 23 23 23 50 54 50 45 40 53
Elongation at break (MD) D882 % 600 600 600 600 600 600 600 600 600 700 600 675 650 850 490
Elongation at break (TD) D882 % 800 800 800 800 800 800 800 800 800 800 710 700 670 900 675
1% Secant Modulus (MD) D882 Mpa 190 190 190 190 190 195 195 195 200 200 230 230 265 230 191
1% Secant Modulus (TD) D882 Mpa 230 230 230 230 230 220 230 250 200 230 290 290 295 250 224
Dart Impact Strength D1709 g 100 100 90 90 90 85 85 85 90 >423 >423 >423 >423 140 206
Tear Strength (MD) D1922 g 100 100 100 100 100 100 100 100 100 300 300 300 300 300 250
Tear Strength (TD) D1922 g 300 300 300 300 300 300 300 300 300 400 400 450 450 400 450
Vicat Softening Point D1525 ํC 100 100 101 101 100 97 97 97 95 106 107 105 105 105 106
Gloss (45 ํ) D2457 - 55 50 50 50 50 50 50 50 45 35 49 45 50 27 62
Haze D1003 % 10 17 13 11 20 10 20 16 15 13 15 13 15 19 8
Special Feature - High Slip & Low Slip & Low Slip & Very high Slip & - High Slip & Low Slip & - - Meduim Slip & - Medium Slip & - -
Antiblock Antiblock Antiblock Antiblock Antiblock Antiblock Antiblock Antiblock
Heavy duty films, Heavy duty films,
Cast stretch films, Stretch films, Shrink
Heavy duty films, Liners, Heavy duty films, Cast stretch films, Lamination films, film, Liners, Food
General Purpose films, Liners, Food packaging, Lamination films, Food packaging, Liners, Lamination films, packaging,
Application Heavy duty and Agricultural films Stretch films, Liners, Industrial bags, Refuse sacks and Garbage bag Muti-layer packaging films and freezer Blown films,
Food packaging, Muti-layer packaging Food packaging Muti-layer
packaging films films and freezer packaging films packaging films,
and Muti-layer and freezer
packaging films packaging films

Test Rotational Molding Injection Wire and Cable Test Extrusion

Properties Method Unit LL9640U/ LL9641U/ LL9450U/ Properties Method Unit
(ASTM) LL9630A LL9630U LL9640UP LL8420A LL6420A (ASTM) LL70600
LL9641UP LL9450UP
Melt Index D1238 g/10 min 3.2 3.2 4 4 5 20 2 Physical Properties
Density D792 g/cm3 0.938 0.938 0.932 0.938 0.936 0.924 0.918
Molded Plague Properties Melt Flow Rate (190 ํC, 2.16 kg) D1238 g/10 min 0.6
3
Tensile Strength at Yield D638 Mpa 20 20 15 20 17 15 10 Density D792 g/cm 0.923
Tensile Strength at Break D638 Mpa 30 30 25 25 24 10 25 Melting Point D3418 ํC 113
Elongation at Break D638 % 1000 1000 1000 950 1000 700 900
Secant Modulus D638 Mpa - - - - - 310 200 Mechanical Properties
Brittleness Temperature D746 ํC <-70 <-70 <-70 <-70 <-70 - - Tensile Modulus D638 kg/cm2 4400
Vicat Softening Point D1525 ํC 118 118 110 118 114 92 97
The above information is based on the data of which Flexural Modulus D790 g 750 750 550 750 600 - - Tensile Strength @ Yield D638 kg/cm2 130
we are aware and is believed to be correct as of Durometer Hardness D2240 Shore D 60 60 56 57 56 53 47 Tensile Strength @ Break D638 kg/cm2 300
the date hereof. Since this information may be Notch Izod Impact Strength D256 kg.cm/cm 30(NB)* 30(NB)* 240(P)* 50(P)* 50(P)* - -
ESCR, 100% Igepal, F50 D1693 Hours >1000 >1000 >1000 >500 - - - Elongation @ Yield D638 % 17
applied under conditions beyond our control and with
which we may be unfamillar and since data made Volume Resistivity (500V) D257 ohm.cm - - - - - - 8.00E+16 Elongation @ Break D638 % 620
available subsequent to the date hereof may suggest Dielectric Strength (500V/sec) D149 kV/mm - - - - - - >50 Flexural Modulus D790 kg/cm2 3600
modifications of the information, we do not assume Dielectric Constant (60 Hz) D150 - - - - - - - 2.2
Dissipation Factor (60 Hz) D150 - - - - - - - 0.001 ESCR F50
any responsibility for the results of its use. D1693 hrs >1000
Special Feature - UV8 Resistance UV8 Resistance UV8 Resistance UV8 Resistance - - (Conditoin B, 100% lgepal)
This information is furnished upon condition that the General purpose Low voltage silane
Plastic tube
person receiving it shall make his own determination applications; Lids, cross-linkable power extrusion for
of the suitability of the material for his particular Application Outdoor storage container, Water & Chemical tanks, Toy & Playgrond equipments Housewares, insulation cable, Low voltage Application cosmetic and
Trash bins, thermoplastic jacketing and personal care
purpose. Masterbatch carrier. telecommunication jacketing products
Remark: *NB = Non Break *P = Partial Break
Note: (1) Film properties obtained from 25 microns film which was blown film extruded at blow up ratio 2.0 (2) Film properties obtained from 25 microns film which was blown film extruded at blow up ratio 2.5