API 571 Coloured Key

The document lists 64 damage mechanisms and categorizes them based on the materials they typically affect. Common damage mechanisms include sulfidation, hydrogen sulfide damage, creep, high temperature corrosion, oxidation, thermal fatigue, sour water corrosion, and stress corrosion cracking. The mechanisms can impact carbon steels, low alloy steels, stainless steels, and non-ferrous alloys. The document provides an overview of typical corrosion and degradation failures that may occur in industrial processes.

Uploaded by

muhammad faisal
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
971 views1 page

API 571 Coloured Key

The document lists 64 damage mechanisms and categorizes them based on the materials they typically affect. Common damage mechanisms include sulfidation, hydrogen sulfide damage, creep, high temperature corrosion, oxidation, thermal fatigue, sour water corrosion, and stress corrosion cracking. The mechanisms can impact carbon steels, low alloy steels, stainless steels, and non-ferrous alloys. The document provides an overview of typical corrosion and degradation failures that may occur in industrial processes.

Uploaded by

muhammad faisal
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

API 571‐ Damage Mechanisms key based on Affected Materials

DM# Damage Mechanism DM# Damage Mechanism


1 Sulfidation 34 Softening (Spheroidization)

2 Wet H2S Damage (Blistering/HIC/SOHIC/SSC) 35 Reheat Cracking

3 Creep / Stress Rupture 36 Sulfuric Acid Corrosion


4 High temp H2/H2S Corrosion 37 Hydrofluoric Acid Corrosion
5 Polythionic Acid Cracking 38 Flue Gas Dew Point Corrosion
6 Naphthenic Acid Corrosion 39 Dissimilar Metal Weld (DMW) Cracking
7 Ammonium Bisulfide Corrosion 40 Hydrogen Stress Cracking in HF
8 Ammonium Chloride Corrosion 41 Dealloying (Dezincification/ Denickelification)
9 HCI Corrosion 42 CO2 Corrosion
10 High Temperature Hydrogen Attack 43 Corrosion Fatigue
11 Oxidation 44 Fuel Ash Corrosion
12 Thermal Fatigue 45 Amine Corrosion
13 Sour Water Corrosion (acidic) 46 Corrosion Under Insulation (CUI)
14 Refractory Degradation 47 Atmospheric Corrosion
15 Graphitization 48 Ammonia Stress Corrosion Cracking
16 Temper Embrittlement 49 Cooling Water Corrosion
17 Decarburization 50 Boiler Water / Condensate Corrosion
18 Caustic Cracking 51 Microbiologically Induced Corrosion (MIC)
19 Caustic Corrosion 52 Liquid Metal Embrittlement
20 Erosion / Erosion‐Corrosion 53 Galvanic Corrosion
21 Carbonate SCC 54 Mechanical Fatigue
22 Amine Cracking 55 Nitriding
23 Chloride Stress Corrosion Cracking 56 Vibration‐Induced Fatigue
24 Carburization 57 Titanium Hydriding
25 Hydrogen Embrittlement 58 Soil Corrosion
26 Steam Blanketing 59 Metal Dusting
27 Thermal Shock 60 Strain Aging
28 Cavitation 61 Sulfate Stress Corrosion Cracking
29 Graphitic Corrosion (see Dealloying) 62 Phosphoric Acid Corrosion
30 Short term Overheating ‐ Stress Rupture 63 Phenol (carbolic acid) Corrosion
31 Brittle Fracture 64 Ethanol Stress Corrosion Cracking
32 Sigma Phase/ Chi Embrittlement 65 Oxygen‐Enhanced Ignition and Combustion
Organic Acid Corrosion Of Distillation Tower
33 885°F (475°C) Embrittlement 66
Overhead Systems

Carbon Steel Carbon Steel & Low Alloy Steel& Stainless Steel
Carbon Steel & Low Alloy Steel Carbon Steel+ Mo Steel
Low Alloy Steel Low Alloy Steel& Stainless Steel
All Materials Heaters& Furnances
Stainless Steel Non Ferrous Alloys