    Strenx 700 MC: Advanced High Strength Steel

    Uploaded by

    dba
    Strenx 700 MC is a hot-rolled structural steel with a minimum yield strength of 700 MPa, intended for stronger and lighter load-bearing structures. It is available as coils, slit coils, or cut sheets between 2-10 mm thick and up to 1600 mm wide. The steel has a minimum yield strength of 700 MPa, tensile strength between 750-950 MPa, and elongation of 10% at sheet thickness under 3mm. It can be cold formed and has good welding properties but is not suited for heat treatments over 580°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Strenx 700 MC: Advanced High Strength Steel

    Uploaded by

    dba
    216 views2 pages
    Strenx 700 MC is a hot-rolled structural steel with a minimum yield strength of 700 MPa, intended for stronger and lighter load-bearing structures. It is available as coils, slit coils, or cut sheets between 2-10 mm thick and up to 1600 mm wide. The steel has a minimum yield strength of 700 MPa, tensile strength between 750-950 MPa, and elongation of 10% at sheet thickness under 3mm. It can be cold formed and has good welding properties but is not suited for heat treatments over 580°C.

    Original Description:

    materijal

    Original Title

    Strenx 700 MC

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Strenx 700 MC is a hot-rolled structural steel with a minimum yield strength of 700 MPa, intended for stronger and lighter load-bearing structures. It is available as coils, slit coils, or cut sheets between 2-10 mm thick and up to 1600 mm wide. The steel has a minimum yield strength of 700 MPa, tensile strength between 750-950 MPa, and elongation of 10% at sheet thickness under 3mm. It can be cold formed and has good welding properties but is not suited for heat treatments over 580°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    216 views2 pages

    Strenx 700 MC: Advanced High Strength Steel

    Uploaded by

    dba
    Strenx 700 MC is a hot-rolled structural steel with a minimum yield strength of 700 MPa, intended for stronger and lighter load-bearing structures. It is available as coils, slit coils, or cut sheets between 2-10 mm thick and up to 1600 mm wide. The steel has a minimum yield strength of 700 MPa, tensile strength between 750-950 MPa, and elongation of 10% at sheet thickness under 3mm. It can be cold formed and has good welding properties but is not suited for heat treatments over 580°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    1(2)

    Data Sheet 2008en Strenx 700 MC 2015-04-08

    Strenx 700 MC
    Advanced High Strength steel

    General Product Description

    Strenx 700 MC is a hot-rolled structural cold-forming steel with a minimum yield strength of 700 MPa intended to give stronger
    and lighter structures. Strenx 700 MC meet or exceed the requirements of S700MC in EN 10149-2.
    Typical applications are a wide range of components and parts for example demanding load bearing structures.

    Available dimensions
    Strenx 700 MC is available in thicknesses of 2.00-10.00 mm and widths up to 1600 mm as coils, slit coils or
    cut to length sheets in lengths up to 16 meters.

    Mechanical Properties
    Yield strength Tensile strength Elongation Elongation
    ReH1) Min MPa Rm MPa A80 Min % A5 Min %
    Sheet shickness t ˂ 3mm Sheet thickness t ≥ 3mm
    7002) 750 - 950 10 12
    The mechanical properties are tested in the longitudinal direction.
    1)
    If ReH is not applicable then Rp 0,2 is used.
    2)
    On thicknesses >8 mm the minimum yield strength may be 20MPa lower.

    Impact properties 700 MC D - 20 °C 700 MC E - 40 °C


    Minimum energy for test on longitudinal Charpy V
    40 27
    10x10 mm test specimens (J)
    Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 6mm. The specified minimum value corresponds to a full-size specimen.

    Bending properties t ≤ 3 mm 3 mm < t ≤ 6 mm t > 6 mm


    Min. inner bending radius for a 90 ° bend 0.8xt 1.2xt 1.6xt
    For both longitudinal and transverse direction.

    Chemical Composition (ladle analysis)


    C% Si % Mn % P% S% Al tot % Nb % V% Ti %
    Max Max Max Max Max Min Max Max Max
    0.12 0.211) 2.10 0.020 0.010 0.015 0.092) 0.202) 0.152)
    1) If the material is to be hot-dip galvanized according to category A or category B in EN 10149-2 this must be specified at the time of order.
    2) Sum of Nb, V and Ti = max 0.22%
    The steel is grain refined.

    Carbon equivalent
    2 mm ≤ t ≤ 10 mm
    CET / CEV Typical 0.25 / 0.39
    CET = C + Mn + Mo + Cr + Cu + Ni CEV = C + Mn + Cr + Mo + V + Ni + Cu
    10 20 40 6 5 15

    www.ssab.com
    2(2)
    Data Sheet 2008en Strenx 700 MC 2015-04-08

    Tolerances
    More details are given on www.ssab.com.

    Thickness
    Tolerances according to Strenx Thickness Guarantees.
    Strenx Guarantees offer considerably narrower thickness tolerances compared to EN 10 051.

    Length and width


    Width and length tolerances according to SSAB standard.
    The SSAB standard offer narrower width and length tolerances compared to EN 10 051.
    Length tolerances only apply for cut to length sheets.

    Shape
    Tolerances according to EN 10 051.
    Narrower tolerances according to the SSAB standard are available on request.

    Flatness
    Tolerances according to Strenx Flatness Guarantees Class A.

    Strenx is a registered trademark of SSAB Technology AB, Sweden.


    Strenx Flatness Guarantees offer narrower tolerances compared to EN 10 051.
    Flatness guarantees only apply for cut to length sheets.

    Surface Properties
    According to EN 10 163-2 Class A, Subclass 3.

    Delivery Conditions
    Thermomechanically Rolled. Strenx 700 MC is available in as rolled or pickled surface condition with mill or cut edge.

    Fabrication and Other Recommendations


    Welding, bending and machining
    Strenx 700 MC has good welding, cold forming and cutting performance.

    Strenx 700 MC is a cold forming steel not suited for heat treatments at temperatures above 580°C since the material then may
    lose its guaranteed properties.

    For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support,
    [email protected].

    Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the
    product.

    Contact and Information


    For information, see SSAB’s brochures on www.ssab.com or consult Tech Support, [email protected].