GENERAL INFORMATION

9.6 PP 100 / 20 PP 1.2

1 2 3 4 5 6

1 CORE DIAMETER 9.6mm

2 CORE TYPE PP
3 CORE DENSITY 100kg/m3
4 TOTAL THICKNESS 20mm
5 LAMINATION PP
6 LAMINATION THICKNESS 1.2mm

CORE
Dimensions

Thicknesses (mm) : 19
Density (gr/m2 ): 1900
Rheological properties

Melt Flow Index 230°C/2.16 kg ISO 1133 g/10 min 1.3

Mechanical properties

Tensile Strength at Yield ISO 527-3 MPa 29

Elongation at Yield ISO 527-3 % 6
Tensile Modulus ISO 527-3 MPa 1500
Flexural Modulus ISO 178 MPa 1400
Izod Impact Strength (notched) ISO 180 kJ/m2 at 23°C >50
at -20°C 9
Charpy Impact Strength (notched) IS0 179 kJ/m2 at 23°C >50
at -20°C 10
Hardness Rockwell - R-scale ISO 2039-2 82
Thermal properties

Melting Point ISO 3146 °C 165

Vicat Softening Point ISO 306 °C 50N-50°C per hour 75
10N-50°C per hour 151
Heat Deflection Temperature ISO 752 °C 1.80 Mpa - 120°C per hour 54
0.45 Mpa - 120°C per hour 92

IMPACT RESILIENT
The special honeycomb core made of
polypropylene is an additional flexible area,
whereby high-energy absorption, without core
deformation, can be achieved.
Özer Toprak, Gıda, Plastik, Enerji, İnşaat, Turizm Sanayi ve Ticaret A.Ş.
Organize Sanayi Bölgesi 3. Cad. No:1 Eskişehir Tel: +90(222)236 22 22 Fax: +90(222)236 25 12
[email protected] www.roplast.com.tr

HEXAPAN
LAMINATION TOTAL THICKNESS (mm) TOTAL DENSITY (g/m2)
Material Composition Thickness (mm)
PP 1.2 20 4500

Mechanical Properties L T

BENDING PROPERTIES ASTM C393

kg 75,15 150,75
Maximum Force

Flexural Bending at Maximum

mm 4,50 2,10
Force

Elongation % 5,45 2,45

Core Shear Stress at Maximum

MPa 0,40 0,65
Force

Support Span Range :100 mm

Load span Range:50 mm Surface Tension MPa 8,55 13,40

LOAD PROPERTIES ASTM C365

Maximum Force kg 438,80

Compression at Maximum
mm 1,10
Force

Compression Ratio % 5,40

Permanent Compression Ratio % 0,50

Compression Strength MPa 1,70

LOAD DEFLECTION (mm)

SPAN
10kg 20kg 30kg 40kg 50kg
(mm)

200 0,40 0,60 0,80 0,90 1,00

300 0,70 1,05 1,35 1,60 1,85

600 2,40 3,60 5,25 6,80 8,35

1000 7,35 15,20 22,50 30,20 38,95

Özer Toprak, Gıda, Plastik, Enerji, İnşaat, Turizm Sanayi ve Ticaret A.Ş.
Organize Sanayi Bölgesi 3. Cad. No:1 Eskişehir Tel: +90(222)236 22 22 Fax: +90(222)236 25 12
[email protected] www.roplast.com.tr

MAXIMUM LOAD (kg)

129,71 133,58
150,00 120,73
Maximum Load (kg)

99,42
79,03 75,19 85,15
100,00

50,00 26,56

0,00

1m2 PANEL WEIGHT (kg) 6,1

6
4,5
5 4,1 3,9
4
Density (kg/m2)

3,3 2,9
3 1,9 1,8
2
1
0

DEFLECTION UNDER THE 10kg

2,99
1,00
0,76
0,80
Deflection (mm)

0,53 0,56
0,60 0,36 0,41
0,40 0,24 0,22
0,20
0,00

STRENGTH COMPARISON

100,00 86,27
69,85
Strength (kg/mm)

80,00
60,00 41,91
40,00 21,62 26,66
15,30 18,40
20,00 3,41
0,00