Designation: A 36/A 36M – 01

Standard Specification for

Carbon Structural Steel1
This standard is issued under the fixed designation A 36/A 36M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.

This standard has been approved for use by agencies of the Department of Defense.

1. Scope Rolled Structural Steel Bars, Plates, Shapes, and Sheet

1.1 This specification2 covers carbon steel shapes, plates, Piling3
and bars of structural quality for use in riveted, bolted, or A 27/A 27M Specification for Steel Castings, Carbon, for
welded construction of bridges and buildings, and for general General Application4
structural purposes. A 307 Specification for Carbon Steel Bolts and Studs,
1.2 Supplementary requirements are provided for use where 60 000 psi Tensile Strength5
additional testing or additional restrictions are required by the A 325 Specification for High-Strength Bolts for Structural
purchaser. Such requirements apply only when specified in the Steel Joints5
purchase order. A 325M Specification for High-Strength Bolts for Struc-
1.3 When the steel is to be welded, a welding procedure tural Steel Joints [Metric]5
suitable for the grade of steel and intended use or service is to A 500 Specification for Cold-Formed Welded and Seamless
be utilized. See Appendix X3 of Specification A 6/A 6M for Carbon Steel Structural Tubing in Rounds and Shapes6
information on weldability. A 501 Specification for Hot-Formed Welded and Seamless
1.4 For Group 4 and 5 wide flange shapes for use in tension, Carbon Steel Structural Tubing6
it is recommended that the purchaser consider specifying A 502 Specification for Steel Structural Rivets5
supplementary requirements, such as fine austenitic grain size A 563 Specification for Carbon and Alloy Steel Nuts5
and Charpy V-notch impact testing. A 563M Specification for Carbon and Alloy Steel Nuts
1.5 The values stated in either inch-pound units or SI units [Metric]5
are to be regarded separately as standard. Within the text, the A 570/A 570M Specification for Steel, Sheet and Strip,
SI units are shown in brackets. The values stated in each Carbon, Hot-Rolled, Structural Quality7
system are not exact equivalents; therefore, each system is to A 668/A 668M Specification for Steel Forgings, Carbon
be used independently of the other, without combining values and Alloy, for General Industrial Use8
in any way. F 568M Specification for Carbon and Alloy Steel Externally
1.6 The text of this specification contains notes or footnotes, Threaded Metric Fasteners5
or both, that provide explanatory material. Such notes and 3. Appurtenant Materials
footnotes, excluding those in tables and figures, do not contain
any mandatory requirements. 3.1 When components of a steel structure are identified with
1.7 For structural products cut from coiled product, the this ASTM designation but the product form is not listed in the
additional requirements, including additional testing require- scope of this specification, the material shall conform to one of
ments and the reporting of additional test results, of A 6/A 6M the standards listed in Table 1 unless otherwise specified by the
apply. purchaser.

2. Referenced Documents 4. General Requirements for Delivery

2.1 ASTM Standards: 4.1 Material furnished under this specification shall con-
A 6/A 6M Specification for General Requirements for form to the requirements of the current edition of Specification
A 6/A 6M, for the ordered material, unless a conflict exists in
which case this specification shall prevail.
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
3
Stainless Steel, and Related Alloys, and is the direct responsibility of Subcommittee Annual Book of ASTM Standards, Vol 01.04.
4
A01.02 on Structural Steel for Bridges, Buildings, Rolling Stock, and Ships. Annual Book of ASTM Standards, Vol 01.02.
5
Current edition approved Sept. 10, 2001. Published September 2001. Originally Annual Book of ASTM Standards, Vol 15.08.
6
published as A 36 – 60 T. Last previous edition A 36/A 36M – 00a. Annual Book of ASTM Standards, Vol 01.01.
2 7
For ASME Boiler and Pressure Vessel Code Applications, see related Specifi- Annual Book of ASTM Standards, Vol 01.03.
8
cations SA-36 in Section II of that Code. Annual Book of ASTM Standards, Vol 01.05.

Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.

1
Copyright by ASTM Int'l (all rights reserved);
Reproduction authorized per License Agreement with LUIS MORENO (); Tue Mar 15 18:19:49 EST 2005
 NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.

A 36/A 36M – 01
TABLE 1 Appurtenant Material Specifications 5.2 Unless otherwise specified, mechanical tests shall not be
NOTE 1—The specifier should be satisfied of the suitability of these required for plates over 11⁄2 in. [40 mm] in thickness used as
materials for the intended application. Chemical composition and/or bearing plates in structures other than bridges, subject to the
mechanical properties may be different than specified in A 36/A 36M. requirement that they shall contain 0.20 to 0.33 % carbon by
heat analysis, that the chemical composition shall conform to
Material ASTM Designation
the requirements of Table 2 in phosphorus and sulfur content,
Steel rivets A 502, Grade 1
Bolts A 307, Grade A or F 568M, Class 4.6 and that a sufficient discard shall be made to secure sound
High-strength bolts A 325 or A 325M plates.
Steel nuts A 563 or A 563M
Cast steel A 27/A 27M, Grade 65–35 [450–240]
Forgings (carbon steel) A 668, Class D 6. Materials and Manufacture
Hot-rolled sheets and strip A 570/A 570M, Grade 36
Cold-formed tubing A 500, Grade B 6.1 The steel for plates and bars over 1⁄2 in. [12.5 mm] in
Hot-formed tubing A 501 thickness and shapes other than Group 1 shall be semi-killed or
Anchor bolts F 1554
killed.

4.1.1 Coiled product is excluded from qualification to this 7. Chemical Composition

specification until decoiled, leveled, and cut to length. Struc- 7.1 The heat analysis shall conform to the requirements
tural products produced from coil means structural products prescribed in Table 2, except as specified in 5.2.
that have been cut to individual lengths from a coiled product 7.2 The steel shall conform on product analysis to the
and are furnished without heat treatment. The processor
requirements prescribed in Table 2, subject to the product
decoils, levels, cuts to length, and marks the product. The
analysis tolerances in Specification A 6/A 6M.
processor is responsible for performing and certifying all tests,
examinations, repairs, inspections, or operations not intended
to affect the properties of the material. For structural products 8. Tension Test
produced from coils, two test results shall be reported for each 8.1 The material as represented by the test specimen, except
qualifying coil. See Note 1. as specified in 5.2 and 8.2, shall conform to the requirements as
NOTE 1—Additional requirements regarding structural products from to the tensile properties prescribed in Table 3.
coil are described in Specification A 6/A 6M. 8.2 Shapes less than 1 in.2[645 mm 2] in cross section and
bars, other than flats, less than 1⁄2 in. [12.5 mm] in thickness or
5. Bearing Plates
diameter need not be subjected to tension tests by the manu-
5.1 Unless otherwise specified, plates used as bearing plates facturer, provided that the chemical composition used is
for bridges shall be subjected to mechanical tests and shall appropriate for obtaining the tensile properties in Table 3.
conform to the tensile requirements of Section 8.

TABLE 2 Chemical Requirements

NOTE 1— Where “. . .’’ appears in this table, there is no requirement. The heat analysis for manganese shall be determined and reported as described
in the heat analysis section of Specification A 6/A 6M.
Product ShapesA PlatesB Bars
Over 3⁄4 Over 11⁄2 Over 21⁄2 Over 3⁄4 Over 11⁄2
To 3⁄4 To 3⁄4
to 11⁄2 to 21⁄2 to 4 Over 4 to 11⁄2 to 4 Over 4
Thickness, in. [mm] All [20], [20],
[20 to 40], [40 to 65], [65 to 100], [100] [20 to 40], [100], [100]
incl incl
incl incl incl incl incl
Carbon, max, % 0.26 0.25 0.25 0.26 0.27 0.29 0.26 0.27 0.28 0.29
Manganese, % ... ... 0.80–1.20 0.80–1.20 0.85–1.20 0.85–1.20 ... 0.60–0.90 0.60–0.90 0.60–0.90
Phosphorus, max, % 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04
Sulfur, max, % 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05
Silicon, % 0.40 max 0.40 max 0.40 max 0.15–0.40 0.15–0.40 0.15–0.40 0.40 max 0.40 max 0.40 max 0.40 max
Copper, min, % when cop- 0.20 0.20 0.20 0.20 0.20 0.20 0.20 0.20 0.20 0.20
per steel is specified
A
Manganese content of 0.85–1.35 % and silicon content of 0.15–0.40 % is required for shapes over 426 lb/ft [634 kg/m].
B
For each reduction of 0.01 percentage point below the specified carbon maximum, an increase of 0.06 percentage point manganese above the specified maximum
will be permitted, up to the maximum of 1.35 %.

2
Copyright by ASTM Int'l (all rights reserved);
Reproduction authorized per License Agreement with LUIS MORENO (); Tue Mar 15 18:19:49 EST 2005
 NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.

A 36/A 36M – 01
TABLE 3 Tensile RequirementsA 9. Keywords
Plates, Shapes,B and Bars: 9.1 bars; bolted construction; bridges; buildings; carbon;
Tensile strength, ksi [MPa] 58–80 [400–550] plates; riveted construction; shapes; steel; structural steel;
Yield point, min, ksi [MPa] 36 [250]C
Plates and BarsD,E: welded construction
Elongation in 8 in. [200 mm], min, % 20
Elongation in 2 in. [50 mm], min, % 23
Shapes:
Elongation in 8 in. [200 mm], min, % 20
Elongation in 2 in. [50 mm], min, % 21B
A
See the Orientation subsection inthe Tension Tests section of Specification
A 6/A 6M.
B
For wide flange shapes over 426 lb/ft [634 kg/m], the 80 ksi [550 MPa]
maximum tensile strength does not apply and a minimum elongation in 2 in. [50
mm] of 19 % applies.
C
Yield point 32 ksi [220 MPa] for plates over 8 in. [200 mm] in thickness.
D
Elongation not required to be determined for floor plate.
E
For plates wider than 24 in. [600 mm], the elongation requirement is reduced
two percentage points. See the Elongation Requirement Adjustments subsection
under the Tension Tests section of Specification A 6/A 6M.

SUPPLEMENTARY REQUIREMENTS

These requirements shall not apply unless specified in the order.

Standardized supplementary requirements for use at the option of the purchaser are listed in
Specification A 6/A 6M. Those that are considered suitable for use with this specification are listed by
title:

S5. Charpy V-Notch Impact Test.

S30. Charpy V-Notch Impact Test for Structural Shapes:
Alternate Core Location
In addition, the following optional supplementary
requirement is also suitable for use with this specification:
S97. Limitation on Rimmed or Capped Steel
S97.1 The steel shall be other than rimmed or capped.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website
(www.astm.org).

3
Copyright by ASTM Int'l (all rights reserved);
Reproduction authorized per License Agreement with LUIS MORENO (); Tue Mar 15 18:19:49 EST 2005