    This document provides information on the CHF101/CHW-S12 flux/wire combination for submerged arc welding. The combination has good arc stability and slag detachability. The deposited weld metal has a fine appearance and good low temperature impact toughness. It is suitable for welding mild steels and equivalent tensile strength low alloy steels used in structures like boilers, pressure vessels and LPG cylinders. The flux is a fluoride-basic type sintered flux with a basicity of around 1.8. It has received approvals from several classification societies for grade 3YM/IIIYM/KAW53M welding.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    CHF101 CHW S12

    Uploaded by

    Immalatulhusna
    152 views1 page
    This document provides information on the CHF101/CHW-S12 flux/wire combination for submerged arc welding. The combination has good arc stability and slag detachability. The deposited weld metal has a fine appearance and good low temperature impact toughness. It is suitable for welding mild steels and equivalent tensile strength low alloy steels used in structures like boilers, pressure vessels and LPG cylinders. The flux is a fluoride-basic type sintered flux with a basicity of around 1.8. It has received approvals from several classification societies for grade 3YM/IIIYM/KAW53M welding.

    Original Title

    CHF101-CHW-S12

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on the CHF101/CHW-S12 flux/wire combination for submerged arc welding. The combination has good arc stability and slag detachability. The deposited weld metal has a fine appearance and good low temperature impact toughness. It is suitable for welding mild steels and equivalent tensile strength low alloy steels used in structures like boilers, pressure vessels and LPG cylinders. The flux is a fluoride-basic type sintered flux with a basicity of around 1.8. It has received approvals from several classification societies for grade 3YM/IIIYM/KAW53M welding.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    152 views1 page

    CHF101 CHW S12

    Uploaded by

    Immalatulhusna
    This document provides information on the CHF101/CHW-S12 flux/wire combination for submerged arc welding. The combination has good arc stability and slag detachability. The deposited weld metal has a fine appearance and good low temperature impact toughness. It is suitable for welding mild steels and equivalent tensile strength low alloy steels used in structures like boilers, pressure vessels and LPG cylinders. The flux is a fluoride-basic type sintered flux with a basicity of around 1.8. It has received approvals from several classification societies for grade 3YM/IIIYM/KAW53M welding.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    CHF101/CHW-S12

    Flux/Wire Combination for Submerged Arc Welding


    AWS A5.17M F48A4-EM12K

    ISO 14171-A-S 38 4 FB S2Si

    ISO 14171-B-S 49A 4 FB SU21

    BS EN 756-S 38 4 FB S2Si

    Type of Flux: Agglomerated (sintered)


    Type of Current: DCEP or AC

    Features & Applications


    CHF101 is a fluoride-basic type sintered flux and its basicity is about 1.8. The welding
    performance of this combination is good arc stability and good slag detachability and the
    weld metal has fine appearance and good performance of low temperature impact
    toughness. It is suitable to weld structures made by mild steels or equivalent tensile
    strength low alloy steels, such as boilers, pressure vessels, LPG cylinders and so on.

    Chemical Composition (%)


    C Mn Si S P Cr Ni
    CHW-S12 Standard 0.05-0.15 0.80-1.25 0.10-0.35 ≤0.030 ≤0.030 — —
    (EM12K) Typical 0.08 1.06 0.22 0.014 0.016 0.025 0.026
    Deposited Metal Typical 0.056 1.30 0.30 0.011 0.020 0.02 0.01

    Mechanical Properties of Deposited Metal (AW)


    Tensile Strength Yield Strength Elongation Impact Value (J)
    Rm (MPa) ReL (MPa) A4 (%) -40℃
    Standard 480-660 ≥400 ≥22 ≥27
    Typical 510 420 30 110
    X-ray radiographic inspection: Grade Ⅰ

    Quality Guarantee of Flux


    Moisture Solid Impurities S P Mesh
    ≤0.10% ≤0.30% ≤0.060% ≤0.080% 10-60

    Approvals
    Institute LR ABS GL BV DNV NK
    Grade 3YM 3YM 3YM A3YM ⅢYM KAW53M

    Notice: 1) To avoid rust the wire must be kept in dry condition and keep the package in
    good condition also before welding.
    2) The flux should be re-baked at 300℃-350℃ for 1-2 hours before use.
    3) The surfaces to be welded must be cleaned away impurities of oil
    contamination, rust, moisture and so on.
    4) The welding conditions mentioned above for reference only and it is better to
    do a welding procedure qualification according to project before put it into
    formal welding.