Fosroc Nitobond EP constructive solutions

Epoxy resin concrete bonding agent

Uses Specification

For bonding fresh wet cementitious materials to existing Epoxy bonding agent
cementitious surfaces. For use on horizontal surfaces or on
The bonding agent shall be Nitobond EP, a two-component
vertical surfaces where mortar or concrete can be supported
solvent-free epoxy resin. The two components shall be
by formwork. The long ‘open’ life makes it suitable for use
differentially pigmented in order to ensure visually that correct
with formwork or where additional steel reinforcement has to
mixing has taken place prior to the application.
be fitted. The product is ideal for roads, bridges, pavements,
loading bays and factories, and for bonded or granolithic floor
Properties
toppings. Nitobond EP is equally suited to internal and external
Test method Typical result
applications.
Compressive strength : 70 N/mm2
Advantages (ASTM D695)
Tensile strength : 30 N/mm2
Nitobond EP may also be used as part of a repair system (ASTM D638)
where a substrate/repair barrier is required or where the Slant Shear Strength : 36 N/mm²
substrate is likely to remain permanently damp or wet. (BS 6319, Part 4)
„ Can be applied on to dry or damp substrates Water Absorption : 0.05%
(ASTM D570)
„ Exhibits high mechanical strength

„ Positive adhesion - exceeds that of the tensile strength Design criteria

of the host concrete
Nitobond EP is designed with an overlay time of 12 hours at
„ Slow cure allows time to erect steel reinforcement and 35ºC and 5 hours at 45ºC, making it more suitable for use
formwork where additional steel reinforcement and formwork has to be
„ Solvent-free - can be used in enclosed locations fitted or where temperatures are high. The minimum
application temperature for Nitobond EP is 5ºC. Consult the
Description local Fosroc office for further information.

Nitobond EP is based on solvent-free epoxy resins containing Application Aspects

pigments and fine fillers. It is supplied as a two-component Working Life (4ltr pack)
material in pre-weighed quantities ready for on-site mixing @ 25°C : 160mins
and use. The ‘base’ component is white and the ‘hardener’ @ 30°C : 90 mins
component is green, providing visual evidence that adequate @ 35°C : 80 mins
mixing has been achieved. Full cure : 5 days @ 35ºC
(Nitobond EPFS, suitable for cold weather working, can be 4 days @ 45ºC
made available when specifically requested.) Maximum Overlay time : 16 hours @ 25°C
12 hours @ 35ºC
Standards compliance 5 hours @ 45ºC
Minimum overlay time : Overlay when tacky but
ASTM C881: Type II, grade 2 class E & F. not wet.
Nitobond EP
Fosroc Nitobond EP

Instructions for use Cleaning

Preparation Nitobond EP should be removed from tools, equipment and

mixers with Fosroc Solvent 102 immediately after use.
Clean all surfaces and remove any dust, unsound material,
Hardened material can only be removed mechanically.
plaster, oil, paint, grease, corrosion deposits or algae.
Roughen the surfaces, remove any laitance and expose the High temperature working
aggregate by light scrabbling or grit-blasting.
Whilst the performance properties of Nitobond EP at elevated
Oil and grease deposits should be removed by steam cleaning, temperatures are assured, application under such conditions
detergent scrubbing or the use of a proprietary degreaser. The can sometimes be difficult. It is therefore suggested that, for
effectiveness of decontamination and soundness of the temperatures above 35ºC, the following guidelines are
substrate should then be assessed by a pull-off test. adopted as a prudent working regime:

Mixing (i) Store unmixed materials in a cool (preferably temperature

controlled) environment, avoiding exposure to direct
Any steel reinforcement and formwork should be prepared,
sunlight.
cut to size and shape, and made ready for assembly before
mixing commences. (ii) Keep mixing and placing equipment cool, arranging shade
protection if necessary. It is especially important to keep
Care should be taken to ensure that Nitobond EP is thoroughly
cool those surfaces of the equipment which will come into
mixed. The ‘hardener’ and ‘base’ components should be
direct contact with the material itself.
stirred separately before mixing to disperse any settlement.
(iii) Try to eliminate application in the middle of the day, and
The entire contents of the ‘hardener’ tin should then be poured
certainly avoid application in direct sunlight.
into the ‘base’ tin and the two materials thoroughly mixed using
a suitable slow-speed drill and mixing paddle for 2 minutes (iv) Have a ready supply of Fosroc Solvent 102 available for
until a fully uniform colour is obtained. The sides of the tin immediate cleaning of tools after use.
should then be scraped and mixing should continue for a
further 2 minutes. Technical support

Application Fosroc offers a comprehensive technical support service to

specifiers, end users and contractors. It is also able to offer
Nitobond EP should be applied as soon as the mixing process
on-site technical assistance, an AutoCAD facility and dedicated
has been completed. It should be brush or roller applied to the
specification assistance in locations all over the world.
prepared surfaces, being sure to achieve an unbroken coating
across the entire substrate.

Nitobond EP should be tacky before the new concrete, screed

or mortar is placed.

The maximum overlay times (see Properties) should also be

carefully observed. Failure to apply the new concrete, screed
or mortar within the maximum overcoating time will result in
Nitobond EP becoming ‘hard’, thus creating a slip plane rather
than a bonding action.

If the maximum overlay time is missed, then the Nitobond EP

must be mechanically removed and a fresh application made.
The concrete, screed or mortar should then be applied in
accordance with the overcoating minimum and maximum
stated above.

As soon as the Nitobond EP has been applied, any required

steel reinforcement and/or formwork should be erected and
fixed securely in place.

Nitobond EP - Page 2 of 4
Fosroc Nitobond EP

Estimating Precautions

Supply Health and safety

Nitobond EP : 1 and 4 litre packs
Nitobond EP and Fosroc Solvent 102 should not come in
Fosroc Solvent 102 : 5 litre cans
contact with skin or eyes, or be swallowed. Ensure adequate
Coverage ventilation and avoid inhalation of vapours. Some people are
Nitobond EP : 3.5 - 4.0 m2/litre sensitive to resins, hardeners and solvents. Wear suitable
protective clothing, gloves and eye protection. If working in
Note: The coverage figures for Nitobond EP products are confined areas, suitable respiratory protective equipment must
theoretical - due to wastage factors and the variety and be used. The use of barrier creams provide additional skin
nature of possible substrates, practical coverage figures protection. In case of contact with skin, remove immediately
will be reduced. with resin removing cream followed by washing with soap
and water.

Do not use solvent. In case of contact with eyes, rinse

Storage immediately with plenty of clean water and seek medical
Shelf life advice. If swallowed, seek medical attention immediately - do
not induce vomiting.
Nitobond EP has a shelf life of 12 months. Fosroc Solvent 102
has a shelf life of 24 months if kept in a dry store in the original Fire
unopened packs. Nitobond EP is non-flammable.
Storage conditions Fosroc Solvent 102 is flammable. Keep away from sources of
Store in dry conditions in the original unopened packs. If stored ignition. No smoking. In the event of fire, extinguish with CO2
at high temperatures, the shelf life may be reduced. or foam. Do not use a water jet.

Flash points
Limitations Fosroc Solvent 102 : 33ºC
- Nitobond EP should not be applied when the temperature For further information, refer to the Product Material Safety
is below 5ºC or is 5ºC and falling. If any doubts arise Data Sheet.
concerning temperature or substrate conditions, consult
the local Fosroc office.

Nitobond EP - Page 3 of 4
Fosroc Nitobond EP

Additional Information

Fosroc manufactures a wide range of complementary

products which include :

„ waterproofing membranes & waterstops

„ joint sealants & filler boards

„ cementitious & epoxy grouts

„ specialised flooring materials

Fosroc additionally offers a comprehensive package of

products specifically designed for the repair and
refurbishment of damaged concrete. Fosroc’s ‘Systematic
Approach’ to concrete repair features the following :

„ hand-placed repair mortars

„ spray grade repair mortars

„ fluid micro-concretes

„ chemically resistant epoxy mortars

„ anti-carbonation/anti-chloride protective coatings

„ chemical and abrasion resistant coatings

For further information on any of the above, please consult

your local Fosroc office - as below.

* Denotes the trademark of Fosroc International Limited

†
See separate data sheet

Important note
Fosroc products are guaranteed against defective materials and manufacture and are sold subject to its standard Conditions for
the Supply of Goods and Service. All Fosroc datasheets are updated on a regular basis. It is the user’s responsibility to
obtain the latest version.

Head Office
telephone: +254 709 106 000 email: [email protected]
Fosroc Kenya Ltd
Po Box 78527-00507,
Mombasa rd near Syokimau
Railway Station, Nairobi
www.fosroc.com