    This document provides information on the HI100H injection molding grade of polypropylene, including its applications, properties, and processing guide. It has very high impact strength at room and cold temperatures. Its properties include a tensile strength of 39 MPa, tensile elongation of 5% minimum, and Izod impact strength of 460 J/m at 23°C. The processing guide recommends drying at 80-80°C for 2-4 hours and melting at 210-240°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    LG Abs - Hi100h

    Uploaded by

    qshakim
    92 views2 pages
    This document provides information on the HI100H injection molding grade of polypropylene, including its applications, properties, and processing guide. It has very high impact strength at room and cold temperatures. Its properties include a tensile strength of 39 MPa, tensile elongation of 5% minimum, and Izod impact strength of 460 J/m at 23°C. The processing guide recommends drying at 80-80°C for 2-4 hours and melting at 210-240°C.

    Original Description:

    LG ABS datasheet

    Original Title

    Lg Abs - Hi100h

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on the HI100H injection molding grade of polypropylene, including its applications, properties, and processing guide. It has very high impact strength at room and cold temperatures. Its properties include a tensile strength of 39 MPa, tensile elongation of 5% minimum, and Izod impact strength of 460 J/m at 23°C. The processing guide recommends drying at 80-80°C for 2-4 hours and melting at 210-240°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    92 views2 pages

    LG Abs - Hi100h

    Uploaded by

    qshakim
    This document provides information on the HI100H injection molding grade of polypropylene, including its applications, properties, and processing guide. It has very high impact strength at room and cold temperatures. Its properties include a tensile strength of 39 MPa, tensile elongation of 5% minimum, and Izod impact strength of 460 J/m at 23°C. The processing guide recommends drying at 80-80°C for 2-4 hours and melting at 210-240°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    HI100H

    Injection Molding Grade

    Description Applications
    - Very High Impact Strength at Room & Cold Temperature - Helmet, Pipe & Fittings, Miscellaneous Goods

    Properties Method Unit HI100H


    Physical  
    Specific Gravity , 23℃ ASTM D792 1.02
    Mold Shrinkage , 23℃, 3.2mm , 23℃ ASTM D955 % 0.4 ~ 0.7
    Melt Flow Rate , 220℃, 10kg ASTM D1238 g/10min 10
    Mechanical  
    Tensile Strength at Yield , 23℃, 50mm/min, 3.2mm ASTM D638 Mpa 39
    Tensile Elongation at Yield , 23℃, 50mm/min, 3.2mm ASTM D638 %, (Min) 5
    Tensile Elongation at Break , 23℃, 50mm/min, 3.2mm ASTM D638 %, (Min) 10
    Tensile Modulus , 23℃, 50mm/min, 3.2mm ASTM D638 MPa 1660
    Flexural Strength , 23℃, 15mm/min, 3.2mm ASTM D790 Mpa 62
    Flexural Modulus , 23℃, 15mm/min, 3.2mm ASTM D790 MPa 2000
    Izod Impact Strength , Notched, 3.2mm, 23℃ ASTM D256 J/m 460
    Izod Impact Strength , Notched, 3.2mm, -30℃ ASTM D256 J/m 245
    Izod Impact Strength , Notched, 6.4mm, 23℃ ASTM D256 J/m 440
    Izod Impact Strength , Notched, 6.4mm, -30℃ ASTM D256 J/m 245
    Rockwell Hardness , R-Scale ASTM D785 94
    Thermal  
    HDT , Edgewise, 1.82MPa, 6.4mm, Unannealed ASTM D648 ℃ 84
    VICAT , 50N, 50℃/h ASTM D1525 ℃ 92
    RTI Electrical UL 746B ℃ 60
    RTI Mechanical with Impact UL 746B ℃ 60
    RTI Mechanical without Impact UL 746B ℃ 60
    Flammability, 1.5mm UL 94 HB
    Flammability, 3.0mm UL 94 HB

    Note
    Typical values can be used only for the purpose of selecting material, and there can be variation within normal tolerances for various colors.Values given should not be
    interpreted as specification and not be used for designing part or tool.All properties, except melt flow rate are measured by injection molded specimens after 48 hours
    storage at 23℃, 50% relative humidity.

    Updated Date : 17-Nov-17 Issued Date : 6-Mar-18

    The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that the result described herein will be
    obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or advice. Further, any information contained herein shall not be construed as a part
    of legally binding offer. Especially, the typical values should be regarded as reference values only and not as binding minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's
    materials, products, recommendations, or advice for its own particular use. Each user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe
    and suitable for use under end - use conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.

    page 1 /2
    HI100H
    Injection Molding Grade

    Description Applications
    - Very High Impact Strength at Room & Cold Temperature - Helmet, Pipe & Fittings, Miscellaneous Goods

    Processing Guide (Injection Molding)
    Processing Parameters Unit Value
    Drying Temperature ℃ 80 ~ 80
    Drying Time hrs 2~4
    Minimum Moisture Content % 0.01 ~ 0.01
    Melt Temperature ℃ 210 ~ 240
    Cylinder Temperature , Rear ℃ 180 ~ 200
    Cylinder Temperature, Middle ℃ 190 ~ 210
    Cylinder Temperature , Front ℃ 200 ~ 220
    Nozzle Temperature ℃ 200 ~ 230
    Mold Temperature ℃ 40 ~ 70
    Back Pressure, Hydraulic Type kg/㎠ 300 ~ 600
    Screw Speed rpm 30 ~ 60

    Note
    Back Pressure & Measuring Speed are only mentioned as general guidelines.These may not apply or need adjustment in specific situations such as low shot sizes, thin
    wall molding and gas-assist molding.

    Updated Date : 17-Nov-17 Issued Date : 6-Mar-18

    The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that the result described herein will be
    obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or advice. Further, any information contained herein shall not be construed as a part
    of legally binding offer. Especially, the typical values should be regarded as reference values only and not as binding minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's
    materials, products, recommendations, or advice for its own particular use. Each user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe
    and suitable for use under end - use conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.

    page 2 /2