WATER-BASED SYSTEMS
REALIZABLE TO IMPROVE
1st 2nd
FILM THICKNESS SALT SPRAY ADHESION
RECOMMENDATION RECOMMENDATION
HOURS (SYNERGY)
HALOX® SZP-391 JM 3-5% HALOX® 430 JM 3-5%
<15 microns 100 hours ® ®
__
& HALOX 550 1-3% & HALOX 550 1-3%
ACRYLIC
HALOX® 570 LS or
EMULSION 25-50 microns 336 hours ®
HALOX SZP-391 3-5% HALOX® 750 3-5%
PRIMER HALOX® 515 1-3%
HALOX® 570 LS or
>50 microns 500 hours HALOX® SZP-391 5% HALOX® 750 5%
HALOX® 515 1-3%
ACRYLIC ELASTOMERIC ®
HALOX 570 LS or
COATINGS (ERC) - 300-500 microns 336 hours HALOX® CW-314 5-8% HALOX® SZP-391 5-8% ®
WHITE HALOX 515 1-3%
ACRYLIC ELASTOMERIC ®
HALOX 570 LS or
COATINGS (ERC) - 300-500 microns 336 hours HALOX® CW-314 5-8% HALOX® SZP-391 5-8% ®
PIGMENTED HALOX 515 1-3%
HALOX® 570 LS or
DIRECT-TO-METAL <25 microns 100 hours HALOX® SZP-391 JM 1-3% HALOX® 430 JM 1-3%
HALOX® 515 1-3%
HIGH GLOSS
ACRYLIC ENAMEL HALOX® 570 LS or
>25 microns 336-500 hours HALOX® SZP-391 3-5% HALOX® 430 3-5% ®
HALOX 515 1-3%
DIRECT-TO-METAL
®
HIGH GLOSS HALOX 570 LS 1-3%
ACRYLIC ENAMEL
80-90 microns 336 hours HALOX® CW-314 3-5% HALOX® 430 JM 3-5% ® ®
or HALOX FLASH-X 150 1%
(Zinc free)
® ®
HALOX SZP-391 JM 3% HALOX 550 WF or
<25 microns 100-200 hours HALOX® 430 JM
ALKYD EMULSIONS & & HALOX® 570 LS 1-3% HALOX® 515 1-3%
DISPERSIONS ®
HALOX SZP-391 1-3%
®
HALOX 570 LS or
25-50 microns 336 hours HALOX® 750 3-5%
& HALOX® 550 WF 1-3% HALOX® 515 1-3%
ALKYD EMULSIONS & ®
HALOX 570 LS or
DISPERSIONS >50 microns 500 hours HALOX® CW-314 2-3% ®
HALOX 430 JM 2-3% ®
(Zinc free) HALOX 550 1-3%
<25 microns 100-200 hours HALOX® 430 JM 1-3% HALOX® SZP-391 JM 5% HALOX® 570 LS 1-3%
2K
POLYURETHANE
®
HALOX® SW-111 3-5%
®
>25 microns 336-500 hours HALOX 430 3-5% HALOX 570 LS 1-3%
® ® ®
<25 microns 336 hours HALOX 430 JM 1-3% HALOX SZP-391 JM 1-3% HALOX 550 WF 1-3%
2K EPOXY
® ® ®
>25 microns 500+ hours HALOX SW-111 3-5% HALOX 430 3-5% HALOX 550 WF 1-3%
2K EPOXY 1000 ®
45-50 microns HALOX CW-314 5-8% HALOX® SW-111 5-8% HALOX® 550 WF 1-3%
(Zinc free) (CRS / Bonderite® 952)
HALOX® 750 5% ®
1K EPOXY 25+ microns 68-336 hours ® HALOX SW-111 5% HALOX® 550 WF 1-3%
or HALOX 550 2%
® HALOX® 570 LS or
<25 microns 336 hours HALOX 430 JM 1-3% HALOX® SZP-391 JM 1-3% ®
EPOXY HALOX 515 1-3%
DISPERSION HALOX® 570 LS or
>25 microns 500+ hours HALOX® SW-111 5-7% HALOX® 750 5% ®
HALOX 515 1-3%
POLYVINYLIDENE
CHLORIDE <25 microns 200 hours HALOX® SZP-391 JM 1-3% HALOX® 430 JM 1-3% HALOX® 550 / 550 WF 1-3%
PVDC
PVDC
<25 microns 48-168 hours HALOX® RC-980 HALOX® 550 WF 3-5% __
(Rust Converter Primer)
Revised 9/14/2018
PRODUCT RECOMMENDATION GUIDE
HALOX® Corrosion Inhibitors
WATER-BASED SYSTEMS
REALIZABLE TO IMPROVE
1st 2nd
FILM THICKNESS SALT SPRAY ADHESION
RECOMMENDATION RECOMMENDATION
HOURS (SYNERGY)
CATIONIC ALKYD >50 microns 200 hours HALOX® 550 / 550 WF 1-3% __ __
CATIONIC
HALOX® FLASH-X® 330 4-5% __
POLYURETHANE <50 microns >200 hours HALOX® 550 1-3%
DISPERSIONS Pre-mix (1:1) with Water
ANIONIC
POLYURETHANE >50 microns <200 hours HALOX® 430 3-5% ®
HALOX 570 LS 1-3%
®
HALOX 550 1-3%
DISPERSIONS
1K CATIONIC EPOXY
>50 microns 100-500 hours HALOX® 391 5% HALOX® 430 JM 5% HALOX® 550 / 550 WF 1-3%
(pH<7)
HYBRID
>50 microns <200 hours HALOX® 515 1-3% HALOX® 570 LS 1-3%
®
HALOX 550 / 550 WF 1-3%
ACRYLIC ALKYD
SILICONE
>50 microns 200 hours HALOX® SZP-391 6-8% ®
HALOX 570 LS 1-3% HALOX® 550 WF 1-3%
EMULSION
®
SILICONE HALOX 570 LS or
300-500 microns 336-500 hours HALOX® CW-314 5-8% HALOX® SZP-391 5-8%
ROOF COATINGS ®
HALOX 515 1-3%
RUST PREVENTATIVE
<5 microns 1-24 hours ®
HALOX 550 / 550 WF __ SEE TDS
COATING (Temporary)
Revised 9/14/2018
PRODUCT RECOMMENDATION GUIDE
HALOX® Corrosion Inhibitors
®
MOISTURE CURE HALOX 550 WF
POLYURETHANE
>25 microns 336 hours HALOX® CW-2230 3-5% ®
HALOX 430 JM 3-5% ®
or HALOX 630 1-3%
®
WASH (Etch) HALOX SZP-391 JM 3-5% & HALOX® 430 JM 3-5%
<25 microns 336 hours __
PRIMERS ®
HALOX 550 WF 1-3%
®
& HALOX 550 WF 1-3%
®
COIL COATING HALOX 430JM 5-8% HALOX® SZP-391 JM 5%
<25 microns 500+ hours __
EPOXY POLYESTER ®
& HALOX 650 0.5%
®
& HALOX 650 0.5%
®
HALOX SZP-391 6% & ®
PHENOLIC ALKYD 25-50 microns 336 hours ® HALOX SZP-391 6% HALOX® 630 1%
HALOX 550 WF 1%
®
ACRYLIC TOPCOAT 25-50 microns 200 hours HALOX 550 WF 1-3% HALOX® 630 1-3% __
SILOXANE (Epoxy)
75-175 microns 2000 hours HALOX® 550 / 550 WF 1-3% __ __
ACRYLIC
UV CURE URETHANE
25-50 microns 500 hours HALOX® SZP-391 JM 3-5% HALOX® 570 0.5-2% HALOX® 550 WF 1-2%
OR EPOXY ACRYLATE
POWDER COATING
>25 microns 500 hours HALOX® 430 JM 5% HALOX® CW-314 HALOX® 650 1-2%
POLYESTER/TGIC
POWDER COATING
>25 microns 500+ hours HALOX® 550 WF 1-3% HALOX® 430 5-7% __
GMA ACRYLIC
Revised 9/14/2018
PRODUCT RECOMMENDATION GUIDE
HALOX® Corrosion Inhibitors
E-COAT
<25 microns __ HALOX® 550 WF 1-3% __ __
CATHODIC
E-COAT
<25 microns __ HALOX® 550 1-3% __ __
ANODIC
SILICONE
30-50 microns <200 hours HALOX® SZP-391 5-7% __ HALOX® 550 WF 1-2%
(Heat Resistant Coating)
®
ZINC RICH PRIMERS 20-40 microns __ HALOX 550 / 550 WF 2-3% HALOX® SZP-391 JM 2-6% __
Although the information and recommendations set forth herein (hereinafter “Information”) are presented in good faith and believed to be correct as of the date hereof, ICL Phosphate Specialty, a division of ICL Specialty Products Inc. (“ICL”) makes no representations or warranties as to the completeness or accuracy thereof.
Information is supplied upon the condition that the persons receiving same will make their own determination as to its suitability for their purposes prior to use. In no event will ICL be responsible for damages of any nature whatsoever resulting from the use or reliance upon Information or the product to which Information refers.
Nothing contained herein is to be construed as a recommendation to use any product, process, equipment or formulation in conflict with any patent, and ICL makes no representation or warranty, express or implied, that the use thereof will not infringe any patent. NO REPRESENTATIONS OR WARRANTIES, EITHER
EXPRESSED OR IMPLIED, OF MERCHANTABILITY, FITNESS FOR A PARTICULAR PURPOSE OR OF ANY OTHER NATURE ARE MADE HEREUNDER WITH RESPECT TO INFORMATION OR THE PRODUCT TO WHICH INFORMATION REFERS.
Revised 5/15/2019