Thermodynamic Constraints of Slag Formation
Thermodynamic Constraints of Slag Formation
Thermodynamic Constraints of Slag Formation
A classical way to illustrate the slag formation event is to draw a “slag path” in the ternary slag
diagram CaO-SiO2-“FeO”. In Figure 1, the left arrow represents a “hard” blow with low “FeO”
content in the slag. It passes the first CaSiO3 “nose” but meets the second Ca2SiO4 “nose” at 1500-
1700 ⁰C, which then inhibits lime dissolution. On the other hand, along the “FeO”-rich path (right)
slag formation can proceed freely as the Ca2SiO4 “ridge” comes up only to 1600 ⁰C which
Figure 1. Typical slag paths during BOF blow presented in ternary diagram of main slag
constituents. During the oxygen blow the slag temperature rises from 1300 ⁰C to 1700 ⁰C [9].
Principally, another way to promote slag formation is to add compounds, which “flux” the silicate
nose by shifting the Ca2SiO4 isotherms towards the CaO-SiO2 axis. In the next figure the influenceof
selected compounds on the liquidus line in the Ca2SiO4 - Mx(O,F)y systems can be seen. The
calculations were done by using the FactSage 7.0 Package with FToxide database.
Figure 2. Influence of different additions on liquidus line in Ca2SiO4 - Mx(O,F)y –system.
Iron oxides (Fe0.945O, Fe2O3) can be used as references to describe the fluxing effect. Ti-oxide is
in the same category, Al2O3 little stronger, CaF2 much stronger and boron oxide the strongest. Of
these fluorspar CaF2 is commonly used. B2O3, as colemanite (calcium borate hydroxide) mineral
was already tested in 1970s [7, 8]. It was an efficient flux but had one significant drawback: even
a small amount of B2O3-bearing converter slag carried over into the ladle can result in little boron
pick-up into steel as [B]. Boron has an extremely strong hardening effect in steel. That might be
very dangerous in many steel grades. Hence, colemanite did not become any common flux in BOF.
In addition to the liquidus temperature the width of the solid-liquid region and the position of
solidus line in relation to the pure phase is essential. They were not drawn in the figure. For oxide
additions the solidus is close to the y-axis, whereas for CaF2 the solid-liquid region is narrower
Steel Scrap
Steel scrap is a major source of metallic iron for steelmaking. About half of the 700 million tones
of crude steel now produced annually in the world will be recycled as scrap to the steelmaking
furnaces sooner or later. (Every tonne of scrap consumed in steelmaking is estimated to conserve
• purchased scrap.
Home scrap (also known as circulating scrap) is the residue left from the steelmaking, rolling
and finishing operations and includes croppings, offcuts and material rejected by quality
inspection procedures. The home scrap usually accounts for about 10% of total crude steel
production in an integrated steelworks. In other words, from each 100 tonnes of crude steel produced in
the steelmaking furnaces, 90
tonnes will be shipped from the plant as finished product; the remainder will be returned to the
Purchased scrap returns to the industry from various sources, partly as manufacturers' offcuts
and defectives, and partly as obsolete and worn-out goods discarded at the end of their useful
lives. Ship-breakers, for example, recover large tonnages. Increasing tonnages of steel cans are
There is a considerable international trade in scrap and prices are sensitive to the variable supply
The basic oxygen steelmaking process can consume up to 20% scrap in its metallic charge. As
well as supplying ferrous feed units the scrap is used to control the temperature generated by the
chemical reactions. The percentage of scrap used in the BOS can be influenced by such factors as
blast furnace metal chemistry, use of cold iron and iron ore in the charge. Special pre-heating
techniques can increase the scrap charged to the BOS to 30% of the charge but heat processing
times are then normally extended. The BOS process depends on the oxidation of C, Si, P and
other impurities (also some Fe to form the correct slag) to supply the heat needed to reach the
final temperature (about 1650°C).
The electric arc furnace process is often based entirely on scrap because the furnace is suited for
heating, rather than extensive chemical reaction. In mini-mills, purchased scrap is generally used
and this often has 'tramp' elements of Cu, Ni and Sn associated with it. These sometimes need to
be lowered to meet the steel specification, so often a pure source of iron units such as HBI (Hot
Briquetted direct reduced Iron) is added to the charge to dilute the residual tramp elements.
In 'special' or alloy steel plants (i.e. stainless steel), the scrap is a useful source of expensive
alloying components containing Ni, Mo and Cr, so it must be carefully sorted and used according