N52M Grade Neodymium Magnets Data

Download as pdf or txt
Download as pdf or txt
You are on page 1of 1

N52M

N52M Grade Sintered Neodymium-Iron-Boron Magnets

These are also referred to as "Neo" or NdFeB magnets. They offer a


combination of high magnetic output at moderate cost. Please contact ALB Characteristic Units C // C
for additional grade information and recommendations for protective coating.
Reversible Temperature Coefficients (1)
Assemblies using these magnets can also be provided.

Thermal Properties
of Induction, α(Br) %/ºC -0.120
of Coercivity, α(Hcj) %/ºC -0.675
Coefficient of Thermal Expansion (2)
-6
Characteristic Units min. nominal max. ∆L/L per ºCx10 7.5 -0.1
Gauss 14,200 14,450 14,700 Thermal Conductivity W / (m • K) 7.6
Br, Residual Induction
mT 1420 1445 1470 Specific Heat (3) J / (kg • K) 460
Magnetic Properties

Oersteds 12,500 13,250 14,000 Curie Temperature, Tc ºC 310


HcB, Coercivity
kA/m 995 1054 1114 psi 41,300
Flexural Strength

Properties
Oersteds 13,000 MPa 285
HcJ, Intrinsic Coercivity

Other
kA/m 1,035 Density g/cm3 7.5
MGOe 49 51 53 Hardness, Vickers Hv 620
BHmax, Maximum Energy Product
kJ/m3 390 406 422 Electrical Resistivity,   • cm 180
Notes: (1) Coefficients measured between 20 and 100 ºC
(2) Between 20 and 200 ºC (3) Between 20 and 140 ºC
Demagnetisation Curves
kG Tesla
Pc = B H
0.5
Grade: N52M 0.75 1
-40°C
1.5 2 3 5
15

14 1.4
20°C

13

12 1.2

11

Flux Density, B
10 1.0

0.3 9
60°C

8 0.8

80°C 7

Polarization, J
6 0.6
100°C
5
120°C
4 0.4

150°C
0.1 3

2 0.2

0 0
30
kOe 28 26 24 22 20 18 16 14 12 10 8 6 4 2 0

kA/m 2230 2070 1910 1750 1590 1430 1275 1115 955 795 640 475 320 160 0
Demagnetizing Field, H
1 kA/m = 12.566 Oe 1 kOe = 79.577 kA/m

Notes: The material data and demagnetization curves shown above represent typical properties that may vary due to product shape and size.
Magnets can be supplied thermally stabilized or magnetically calibrated to customer specifications.
Additional grades are available. Please contact the factory for information.

ALB Materials Inc E-mail: [email protected] https://www.albmagnets.com/


Page 1 of 1