Design Considerations for the Cosmetics

of Injection-Molded Plastic Parts

Compiled by the Customer Engineering Staff of Proto Labs, Inc.

Many factors affect the cosmetic appearance of injection-molded plastic

parts. Some of these are within the control of the part designer, and some
are not. In this white paper we describe several of the factors affecting
cosmetic appearance, the interactions between those factors, and steps
the designer can take to improve final appearance.

Optimized for on-screen viewing.

www.protomold.com 877.479.3680
Table of Contents

Page Contents

3 Introduction; The Design Challenge

4 Factors: Geometry, Choice of Material, Mold Design

5 Cross-coupled Variables; Issues, Causes, and Solutions Table

7 Knit lines

9 Sink

11 Highlighted materials samples: Black ABS and Light Gray ABS

12 Highlighted materials samples: Black Nylon 66

13 Highlighted materials samples: Black Santoprene TPE and Black Delrin 500

14 Changing Part Geometry

15 Summary; Footnotes

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

2
Design Considerations for the Cosmetics
of Injection-Molded Plastic Parts
The success of the products we design can often be affected by their visual appearance. In addition to the visual
appearance, the cosmetics of a plastic part impacts the tactile feel. Quality judgments are often by how a product
feels when we hold it or touch it.

In product design, cosmetics must be traded off against other factors like strength, durability, function and cost.
For internal parts, cosmetics should be weighed less than other, more operational characteristics. For external
components cosmetics may be a primary consideration.

The cosmetics of a part can contribute to both function and esthetics. For example, the color of a part might be
chosen for safety reasons as well as for its attractiveness. The texture on a handle might be chosen both for its looks
as well as how it improves the feel and the grip.

There are four major drivers to the cosmetic appearance of your part: the part’s geometry, the choice of material, the
design of the mold (or tool), and processing parameters during the injection process. These drivers are cross-coupled
with each other and additional design factors such as strength and durability. While the part designer has complete
control over geometry and resin selection, they typically have only a small input into the design of the mold.

Generally, processing parameters are best left to the mold process technician. Injection molding machines have
many process parameters that can be dialed-in to affect the molding process and hence the resulting parts. You can
assume the process tech has applied his or her entire skill set to finding the best process for your part before you see
samples. On occasion, however, the tech may have focused on optimizing one aspect at the expense of another that
might not reflect your priorities (for example, the tech may have designed the process to minimize sink while your
concern is minimizing flash, or vice versa). If you have cosmetic issues with a sample part it’s worthwhile having a
discussion with your Customer Service Engineer about possible alternative tradeoffs in processing.

The Design Challenge

The first step toward achieving your cosmetic goal is to determine the relative importance of cosmetic appearance
compared to other factors such as strength, function, or cost. Are cosmetics primary or secondary? Generally, better
appearance is correlated with higher mold cost, and sometimes higher part cost. Don’t put money into cosmetics
if cosmetics don’t make a different in the end product.

Second, understand the method of manufacture. There are different tradeoffs for the different types of mold
material (aluminum or the several mold steels in common usage) and the mold production technique (milling,
EDM,1 etc.). Your Customer Service Engineer will be able to help you understand how the method of manufacture
affects your project.

Third, recognize that some cosmetic problems may not manifest themselves until you actually mold a part, which is
one of the reasons people make prototypes using the actual production process before committing to
full-scale production.

Fourth, recognize that cosmetic problems can be the result of multiple factors. We’ll discuss three of the major
factors on the next page; bear in mind there are other factors as well.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

3
Factor: Part Geometry
Part geometry can affect many aspects of cosmetics. There are so many possible geometries it’s impossible
to provide a comprehensive recipe for good cosmetic results. Following the usual rules2 for good injection-molded
part design will usually improve the cosmetics of the part, and violating those rules often leads to cosmetic issues. It’s
simple physics: there are basic physical laws to the melting, flow, filling of the mold cavity,
and solidification of resin; the geometry of the part governs how those physical laws are manifested in your
part’s appearance.

Factor: Choice of Material

The resin you choose will have a dramatic effect on appearance. The most obvious effect is color, but beyond color
there are many aspects affected by the material selection. Material selection includes the base resin (the choice of
which is often constrained by the part’s functions), colorant (the choice of which is constrained by the base resin
and the desired appearance), and the filler, if any (the choice of which is constrained by the base resin and the
part’s function).

Among resins, the most cosmetic-friendly entrants include ABS, polycarbonate, and ABS/polycarbonate blends.
Some less-friendly resins include acetal (e.g., Delrin®) and PBT. Highly-cosmetically-challenging resins include any
glass-filled resin and TPE (thermoplastic elastomer, e.g., Santoprene™). Depending on which aspects of cosmetics are
important to you (e.g., sink, uniform texture, flash), you may be able to find a substitute for your first choice of resin
that also satisfies your other design constraints. Ask your plastics supplier for advice, or use a resin guide.3 Since you
are the only person who knows enough about your requirements to make the decision, most advisors will help with
general advice and resin parameters but leave the final choice up to you.

If the resin choice is constrained, you may have to compromise on cosmetics. For example, if you must use a glass-
filled resin, don’t design a part to have a highly-polished surface. A filled resin will never achieve a highly-polished
look, and the money you spend having the mold polished will be wasted. If you use a TPE such as Santoprene, you’ll
be disappointed if you spend money on class A or textured finishes since TPEs generally are insensitive to nuanced
mold finishes.

Bear in mind that mold polish levels (e.g., SPI-C1, SPI-B1, SPI-A2, bead-blast texture) are specified and standardized
for the surface of the mold and not the surface of the resin. The appearance of a part made in a mold with an A2
finish may be quite different for different resins. If you’re thinking of trying a new resin, ask your molder for a sample
plaque made from your resin or a similar resin (be sure to specify fillers if you’re thinking of using them). The plaque
should display different mold finishes so you can judge what cosmetic level your part might be able to achieve.

Factor: Mold Design (Gating, Venting, and Flow)

Many cosmetic problems arise from the design of the mold. Some of these, such as parting lines4 and ejector pin
marks result from the practical requirement that the part has to somehow get out of the mold.

Most mold-related cosmetic problems have to do with resin entry and flow. The path or paths resin takes in filling the
mold, from entering at the gate to flowing to the farthest ends of the cavity (as well as letting trapped air out ahead
of the resin through mold vents), greatly affect the cosmetics of the resulting part.

In most cases, the mold designer proposes gate and vent locations and, thereby, resin flow. The goal is to choose
gate and vent locations that will produce the best part, but like other aspects of part design, gating can entail
compromises. The mold designer cannot know your goals without your input, which is why you will be asked to
approve a gate and ejector layout prior to manufacturing a mold. If necessary, the mold designer may simulate
the flow of solidification of resin using an injection-molding simulation program.5

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

4
The mold material6 can have several effects on cosmetics. Aluminum molds cannot be polished as highly as steel
molds (SPI-A2 is about the highest achievable polish in aluminum, although this is sufficient for most purposes).
Aluminum molds can’t withstand as high of injection pressure as a steel mold, so some processing options aren’t
available for extreme part geometries. Aluminum molds are more easily damaged than steel molds, so specialized
finishes such as Mold-Tech®7 finishes aren’t advised for aluminum molds due to the turn-around time
and expense of repair in case of accidental damage or wear by abrasive resins.

Cross-Coupled Variables
Fixing potential cosmetic problems involve choices, and problems often result from trade-offs between two or more
factors. Table 1 shows some common cosmetic problems and their causes, and some ways to address them.
Sometimes addressing one problem will exacerbate another.

Table 1: Common Cosmetic Issues, Causes, and Potential Solutions

Cosmetic Issue Common Causes Potential Solutions
Gate Vestiges Resin needs to be injected into your part Change type of gate or gate location.
somewhere. The place where that occurs Note that changing gate placement or
will have a gate vestige or blemish. type to a sub-optimal configuration can
often cause other issues.
Sink All resins shrink as they cool. Thick 1. Core out thicker areas.
areas tend to shrink more than thin 2. Keep wall thicknesses uniform.
areas around them causing noticeable
3. Changing base resin can sometimes
dips in surfaces.8
improve sink if the geometry
can’t change.
Ejector Pin Blemishes9 Ejector pins always mar the surface of 1. Place the pins on a non-cosmetic
the part. The mold designer will usually area of the part (not always possible
try to orient the part in the mold to allow given the total design constraints of
the ejector pins to interact with a non- the part).
cosmetic surface of the part. 2. When the entire part is cosmetic
(e.g., a plastic lens), special features
need to be designed into (or added to)
the part to aid in ejection.
3. More complex molds may use methods
such as stripper plates10 to eject parts.
These are much more expensive than
ejector pins and will still leave
a blemish.
Drag Marks Usually caused by insufficient draft. 1. Add draft.
The part drags along the mold wall 2. Change the finish on the affected areas
during mold ejection, marring the to show the marks less.
surface of the part.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

5
Table 1 continued
Cosmetic Issue Common Causes Potential Solutions
Texture Shadowing Any blemish (e.g., mild sink) will be 1. Change to a lighter color resin
accentuated by a textured surface if possible.
because raised features of the texture 2. Correct the underlying blemish issue.
casts shadows when light strikes the
3. Remove the texture.
surface at an angle.
4. Add features (e.g., text, decorative
ribs) to break up the surface to
hide the blemish.
5. Eliminate thick and thin wall section
transitions under the textured area.
Knit Lines11 1. Holes in the part will always cause 1. Remove holes if possible.
knit lines. 2. Change gate locations.
2. Multiple gates will always cause 3. Use the fewest number of
knit lines. gates possible.
3. Extreme geometries can cause 4. Correct geometry issues that cause
knit lines. pathological flows or require multiple
4. Incorrectly placed single gates may gates or sub-optimal gate locations.
cause knit lines.
Flash12 1. Excessive pressure is required to 1. Correct any underlying issue requiring
fully fill the mold due to thin walls or excessive injection pressure.
sections, long thin parts, sub-optimal 2. Change the resin to one less
gate location, correcting sink in thick susceptible to flashing.
sections, etc.
3. Simplify the design to allow
2. Some materials flash more easily simplifying the parting line.
than others.
3. Very complex parting lines may not be
able to shut off properly.
Burns Air trapped in dead-ended sections 1. Allow the mold designer to add vents
of the mold can rapidly increase in as needed to relieve trapped gas. This
temperature as it is compressed by the may leave blemishes similar to ejector
high-pressure incoming resin. This can pin marks.
cause unsightly scorching of the resin. 2. Change the material to one less
Some resins (e.g., nylon) burn more susceptible to burning.
easily than others.
3. Change the design to remove dead
ends that trap gas.
Inconsistent Color 1. Custom colors created by 1. Arrange for pre-compounded resins.13
mix-in colorants 2. Correct any design issues driving
2. Much less often, processing issues processing issues.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

6
The cross-coupled nature of solving cosmetic issues is best
shown by example.
Example: Knit lines
Refer to the photograph in Figure 1. This shows a section of a cover for a consumer device. The external side of the
cover is textured with a medium bead blast. The mold designer chose to use two edge gates (located on the opposite
non-cosmetic side of the part, not visible). The reasoning was the part would be hard to fill since it is fairly large and
quite thin with a few thicker sections. Gate location was chosen to hide the gate vestiges.

Figure 1: Knit line blemish in textured area. The lighter vertical elliptical area in the center is textured visually
differently than the surrounding area.

The photo shows a knit line on the textured area. It has been lighted to accentuate the issue. The knit line itself (the
vertical line in the middle) is visible in this lighting, but the biggest issue is with the texture. The cooler flow fronts of
the resin aren’t forced into the mold surface texture as well as the hotter resin behind the flow front. Since the part is
thin and cools quickly, the mold process tech can’t fill the part to achieve uniform texture appearance. This leaves a
noticeable change in the appearance of the texture near the knit line.

There were several possibilities to mitigate the problem. A single edge gate would eliminate the knit line in this area,
but the part would likely have had problems filling. The part could have been made thicker to make a single edge
gate practical, though this adds weight and cost as well as the additional re-designing time and possible issues with
mating parts. The gates could have been moved closer to the affected area so the cold area of the joining flow fronts
might have been pushed away by the flow front, but this would have put edge gate vestiges in cosmetic areas.

In this case, working with the Customer Service Engineer, the customer chose to use a hot tip gate in the center of the
part. A hot tip gate injects resin through the A-side of the mold directly into the part (i.e., without sprue or runners),
leaving a small vestige (see Figure 2 for a close-up of the gate vestige). In addition, there is a slight blushing around
the hot tip (barely visible in Figure 2, an area about twice the diameter of the dime, and Figure 3). Moving the gate
was a tradeoff between having a hot-tip vestige (which was why a hot tip wasn’t tried first) and eliminating the
knit line.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

7
Figure 2: Hot Tip Gate Vestige. The vestige is the small bump on the top edge of the part where Teddy is
looking. Normally the bump is trimmed as flush as possible after molding, but a vestige always remains.

Figure 3: Same area as is shown in Figure 1 after changing to one hot tip gate. The gate is on the top edge in
the center of this photo.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

8
Example: Sink
Another example of a problem with several potential solutions is shown in Figure 4. This shows a bad sink mark on
a cosmetic part. Flipping the part over, we find the reason for the sink: a thin-walled part with a large solid boss
(Figure 5). As the resin in the boss froze from the outside in, the core contracted and pulled from both ends of
the boss. This left a significant cosmetic blemish that was not able to be processed out by the mold process tech.
The material exacerbated the problem; the customer needed polycarbonate, which is extremely stiff (among the
stiffest of all engineering resins), and is very prone to sink. The design guidelines for polycarbonate14 call for wall
thickness of at least 0.040" (1mm) in small parts (and this is not a small part) and no more than 0.150" (3.8mm) in
larger parts. The base of the boss exceeds the maximum thickness recommended for polycarbonate by quite a bit.

Figure 4: Sink. The center of this sink mark is about 0.040" (1mm) below the design surface profile of the part.

Figure 5: The culprit. This 3" (76mm) tall boss has a base diameter of about 0.375” (9.5mm). Because of
internal and external draft requirements, the center hole reaches less than halfway down the boss.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

9
The ideal solution to this issue would be to core out the boss to its bottom, with a hole large enough to leave only
a thin tube standing on the back side of the cosmetic surface (ideally the tube wall thickness would be 40–60% of
the shell’s thickness15). This was not possible in this case due to the draft requirements on the inside and outside of
the tube. Without draft on the outside, the boss would stick in the mold, typically breaking off in the mold during
ejection. Without draft on the inside, the boss grabs onto the core pin, either breaking off the pin during ejection or
distorting the part as it is pushed off the undrafted pin.

Substituting a different material (polycarbonate/ABS blend) helped quite a bit (see Figure 6). The sink issues were
almost completely eliminated. Material selection can have a huge effect on cosmetic appearance, and not just for sink.

Figure 6: No more sink using PC/ABS. This photo shows the same area shown in Figure 4.

Figures 7 through 10 show several different materials shot in exactly the same mold (a material sample plaque) and
photographed under lighting designed to bring out surface contrasts. The different finishes on the plaque include
SPI-A2 (buffed with grade 6 diamond), SPI-B1 (polished with 600 grit paper), SPI-C1 (polished with 600 stone), PM-
F0 (as-machined), PM-F1 (most milling marks removed), PM-T1 (light bead-blast texture) and PM-T2 (medium bead
blast texture).

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

10
Figure 7: Black ABS. This resin faithfully reproduces the finishes in the mold.

Figure 8: Light Gray ABS. A lighter-colored resin can often be used to cover surface defects such as uneven
texture or sink.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

11
Figure 9: Black Nylon 66. Like ABS, unfilled nylon makes good-looking parts.

Figure 10: Black Nylon 66, 33% Glass Filled. Compare this to the unfilled nylon 66 in Figure 9. The difference
between texture (T1 and T2), stone (C1), and paper (B1) finishes is much less apparent. The SPI-A2 area
shows a slightly textured appearance.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

12
Figure 11: Black Santoprene TPE (55 durometer). Note almost no difference in appearance between a highly-
polished mold surface (SPI-A2) and as-machined (PM-F0).

Figure 12: Black Delrin 500 (Acetal). Note the flow lines and the uneven sink in the SPI-A2 area. It is possible
to make a good-looking acetal part, but the design rules for acetal must be followed carefully.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

13
Example: Changing Part Geometry
Occasionally, the best solution to a cosmetic problem is to modify the geometry of the part. Figure 13 shows a part
intended to illustrate the cross-coupled nature of all aspects of the design, from geometry to material to processing
parameters. This part is made from acetal, which is considered to be difficult to process for highly cosmetic results.

The original part shown in Figure 13 has thick sections in violation of good plastic design practices. The mold process
tech varied one aspect of the process (injection speed) to find the best compromise. Extremes are shown in (A) and (B).
In (A) the injection speed was slowed to minimize gate blush, which produced an orange peel effect. In (B) the injection
speed was set higher to eliminate orange peel, which results in gate blush and exacerbates sink in the thick areas.
Gates and runners are shown for illustrative purposes. After optimizing the process for the best cosmetics without
compromising material properties (not shown), the appearance of this part was still substandard, with noticeable sink
marks and some gate blush.

To improve cosmetics, this part was redesigned following basic plastics design rules. In this case, the walls were
designed with uniform thickness in the dimensional range recommended for acetal. The result is shown in Figure 13 (C).
The resolution of the photograph isn’t fine enough to make a detailed comparison, but the end result is definitely better.

A B C
Figure 13: Acetal Part. (A) Optimized for minimum gate blush. (B) Optimized for minimum orange peel. (C) Redesigned to remove thick sections.

© Proto Labs 2010 Proto Labs, Inc., 5540 Pioneer Creek Dr., Maple Plain, MN 55359 USA | 877.479.3680

14
In Summary
Appearance is one of many issues that must be addressed in designing a plastic part. It is, however, a particularly
complex issue comprising color, form, and finish and is affected by design, material, and the molding process. It is
subjective as well, which complicates the issue greatly. Because so many factors are involved, final appearance can be
difficult to predict.

In working with Protomold, the injection molding service offered by Proto Labs, you provide the initial design and
own the final product. Between beginning and end, however, Protomold offers input that can be used to fine-tune
what will become the end result. You can use the information Protomold provides during the quoting and molding
processes to modify your part, refining the design to achieve the best possible cosmetic outcome. The final test,
of course, is prototyping, which sends the product either on to production or back to the drawing board for
further refinement.

1 
EDM: Electo-Discharge Machining. In mold construction, this usually implies a graphite electrode being burned into a mold using a spark
erosion process, and is used to create features that can’t otherwise be formed using traditional machining processes.
2 
General design guidelines for injection molding. (www.protomold.com/DesignGuidelines.aspx)
3 
A resin guide can be found here which rates various generic engineering resins on various aspects, some of which are important
to appearance. (www.protomold.com/DesignGuidelines_ResinGuide.aspx)
4 
The location where the pieces of a mold come together. Typically, a thin line is created on the part at this line.
5 
See, for example, ProtoFlow. (www.protomold.com/DesignGuidelines_FillAnalysis.aspx)
6 
Other materials are sometimes used for molds, such as RTV, but they are not capable of injection pressures and the appearance of the parts
is quite different that for an injection process part.
7 
Mold-Tech: see www.mold-tech.com.
8 
Sink: As plastic solidifies in a mold it freezes from the outside in. In thick sections this results in inward pulling stresses (due to contraction)
that can cause depressions (sink marks) in the outer surfaces of the part. Avoiding sink: see guidelines. (http://www.protomold.com/
DesignGuidelines_UniformWallThickness.aspx)
9 
Ejector pin: A round pin usually mounted in the B-side of an injection mold used to push the part out of the cavity after molding. Typically
these will leave a round blemish on the part.
Stripper plate: Defined here. Stripper plates are generally not available in rapid injection tooling. (www.ides.com/glossary/s/stripper-plate.asp)
10 

Knit lines: visible mark in the finished part where two or more resin flow fronts come together. In addition to being unsightly, knit lines are
11 

potentially weaker than the base material since the flow fronts are cooling and total melding may not occur.
Flash: resin forced into the parting line between faces of the mold halves, or around shut-offs forming holes in the part, or around or side-action
12 

faces. This resin hardens to form thin sheets of excess/unwanted plastic, which must be removed from the finished part in a secondary (usually
hand) operation.
Example compounder: PolyOne (www.polyone.com)
13 

Recommended minimum and maximum wall thicknesses for common resins can be found here.
14 

(www.protomold.com/DesignGuidelines_RecommendedWallThickness.aspx)
Recommended uniform wall guidelines can be found here. (www.protomold.com/DesignGuidelines_UniformWallThickness.aspx)
15 

Protomold is a service of Proto Labs, the world’s fastest source for custom CNC machined and injection molded parts.
Protomold offers interactive and highly-illustrated ProtoQuote® online quotations backed up by a streamlined manufacturing
system that can ship real injection molded parts in as fast as the next business day.