Pressure Vessel Plates, Carbon Steel, For Intermediate-And Higher-Temperature Service

Designation: A 515/A 515M – 01
Standard Specification for

Pressure Vessel Plates, Carbon Steel, for Intermediate- and
Higher-Temperature Service1
This standard is issued under the fixed designation A 515/A 515M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope Steel Plates for Pressure Vessels3

1.1 This specification2 covers carbon-silicon steel plates 3. General Requirements and Ordering Information
primarily for intermediate- and higher-temperature service in
welded boilers and other pressure vessels. 3.1 Material supplied to this material specification shall
1.2 Material under this specification is available in three conform to Specification A 20/A 20M. These requirements
grades having different strength levels as follows: outline the testing and retesting methods and procedures,
Tensile Strength,
permissible variations in dimensions, and mass, quality and
Grade U.S. [SI] ksi [MPa] repair of defects, marking, loading, etc.
60 [415] 60–80 [415–550] 3.2 Specification A 20/A 20M also establishes the rules for
65 [450] 65–85 [450–585]
70 [485] 70–90 [485–620]
the ordering information that should be complied with when
purchasing material to this specification.
1.3 The maximum thickness of plates is limited only by the 3.3 In addition to the basic requirements of this specifica-
capacity of the composition to meet the specified mechanical tion, certain supplementary requirements are available when
property requirements; however, current practice normally additional control, testing, or examination is required to meet
limits the maximum thickness of plates furnished under this end use requirements. These include:
specification as follows: 3.3.1 Vacuum treatment,
Maximum Thickness, 3.3.2 Additional or special tension testing,
Grade U.S. [SI] in. [mm]
60 [415] 8 [200]
3.3.3 Impact testing, and
65 [450] 8 [200] 3.3.4 Nondestructive examination.
70 [485] 8 [200] 3.4 The purchaser is referred to the listed supplementary
1.4 For plates produced from coil, the additional require- requirements in this specification and to the detailed require-
ments, including additional testing requirements and the re- ments in Specification A 20/A 20M.
porting of additional test results, of Specification A 20/A 20M 3.5 Coiled product is excluded from qualification to this
apply. specification until it is decoiled, leveled, and cut to length.
1.5 The values stated in either inch-pound units or SI units Plate produced from coil means plate that has been cut to
are to be regarded separately as standard. Within the text, the individual lengths from a coiled product and is furnished
SI units are shown in brackets. The values stated in each without heat treatment. The processor decoils, levels, cuts to
system are not exact equivalents; therefore, each system must length, and marks the product. Except as allowed by Section 6
be used independently of the other. Combining values from the in Specification A 20/A 20M, the processor is responsible for
two systems may result in nonconformance with the specifi- performing and certifying all tests, examinations, repairs,
cation. inspections, and operations not intended to affect the properties
of the material. For plate produced from coils, the results of the
2. Referenced Documents tests performed shall be reported for each qualifying coil. See
2.1 ASTM Standards: Note 1.
A 20/A 20M Specification for General Requirements for NOTE 1—Additional requirements regarding plate produced from coil
are described in Specification A 20/A 20M.
3.6 If the requirements of this specification are in conflict
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel, with the requirements of Specification A 20/A 20M, the re-
Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee quirements of this specification shall prevail.
A01.11 on Steel Plates for Boilers and Pressure Vessels.
Current edition approved Sept. 10, 2001. Published September 2001. Originally
published as A515 – 64. Last previous edition A 515/A 515M – 92(1997).
2
For ASME Boiler and Pressure Vessel Code applications, see related Specifi-
3
cation SA-515/SA-515M in Section II of that Code. Annual Book of ASTM Standards, Vol 01.04.
Copyright © ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959, United States.
1
A 515/A 515M
4. Manufacture 6. Chemical Requirements
4.1 Steelmaking Practice—The steel shall be killed and 6.1 The steel shall conform to the chemical requirements
made to a coarse austenitic grain size practice. shown in Table 1 unless otherwise modified in accordance with
Supplementary Requirement S17, Vacuum Carbon-Deoxidized
5. Heat Treatment Steel, in Specification A 20/A 20M.
5.1 Plates 2 in. [50 mm] and under in thickness are normally
supplied in the as-rolled condition. The plates may be ordered 7. Mechanical Requirements
normalized or stress relieved, or both. 7.1 Tension Test Requirements—The material as represented
5.2 Plates over 2 in. [50 mm] in thickness shall be normal- by the tension-test specimens shall conform to the require-
ized. ments shown in Table 2.
TABLE 1 Chemical Requirements
Composition, %
Elements
Grade 60[Grade 415] Grade 65[Grade 450] Grade 70[Grade 485]
Carbon, maxA:
1 in. [25 mm] and under 0.24 0.28 0.31
Over 1 to 2 in. [25 to 50 mm], incl 0.27 0.31 0.33
Over 8 in. [200 mm] 0.31 0.33 0.35
Manganese, max:
Heat analysis 0.90 0.90 1.20
Product analysis 0.98 0.98 1.30
Phosphorus, maxA 0.035 0.035 0.035
Sulfur, maxA 0.035 0.035 0.035
Silicon:
Heat analysis 0.15–0.40 0.15–0.40 0.15–0.40
Product analysis 0.13–0.45 0.13–0.45 0.13–0.45
A
Applies to both heat and product analyses.
TABLE 2 Tensile Requirements
Grade
60 [415] 65 [450] 70 [485]
Tensile strength, ksi [MPa] 60–80 [415–550] 65–85 [450–585] 70–90 [485–620]
Yield strength, min, ksi [MPa] 32 [220] 35 [240] 38 [260]
Elongation in 8 in. [200 mm], min, %A 21 19 17
Elongation in 2 in. [50 mm], min, %A 25 23 21
A
See Specification A 20/A20M for elongation adjustment.
SUPPLEMENTARY REQUIREMENTS
Supplementary requirements shall not apply unless specified in the order.

A list of standardized supplementary requirements for use at the option of the purchaser are included
in Specification A 20/A 20M. Those which are considered suitable for use with this specification are
listed below by title.
S1. Vacuum Treatment, S9. Magnetic Particle Examination,

S2. Product Analysis, S11. Ultrasonic Examination in accordance with Specifica-
S3. Simulated Post-Weld Heat Treatment of Mechanical tion A 577/A 577M,
Test Coupons,
S12. Ultrasonic Examination in accordance with Specifica-
S4.1 Additional Tension Test,
tion A 578/A 578M,
S5. Charpy V-Notch Impact Test,
S6. Drop-Weight Test, S14. Bend Test, and
S7. High-Temperature Tension Test, S17. Vacuum Carbon-Deoxidized Steel.
S8. Ultrasonic Examination in accordance with Specifica-
tion A 435/A 435M,
2
A 515/A 515M
ADDITIONAL SUPPLEMENTARY REQUIREMENTS
Also listed below is an additional optional supplementary requirement suitable for this specification:
S61. Austenitic Grain Size

S61.1 The material shall have a carburized austenitic grain
size of 1 to 5.
The American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connection
with any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any such
patent rights, and the risk of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM Headquarters. Your comments will receive careful consideration at a meeting of the responsible
technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your
views known to the ASTM Committee on Standards, at the address shown below.
This standard is copyrighted by ASTM, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above address or at
610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website (www.astm.org).

Pressure Vessel Plates, Carbon Steel, For Intermediate-And Higher-Temperature Service

Uploaded by

Copyright:

Available Formats

Pressure Vessel Plates, Carbon Steel, For Intermediate-And Higher-Temperature Service

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Pressure Vessel Plates, Carbon Steel, For Intermediate-And Higher-Temperature Service

Uploaded by

Copyright:

Available Formats

What are the different grades and their tensile strength ranges specified in the document?

What is the heat treatment requirement for plates of different thicknesses?

Designation: A 515/A 515M – 01

Standard Specification for

1. Scope Steel Plates for Pressure Vessels3

TABLE 1 Chemical Requirements

TABLE 2 Tensile Requirements

Supplementary requirements shall not apply unless specified in the order.

S1. Vacuum Treatment, S9. Magnetic Particle Examination,

S61. Austenitic Grain Size

You might also like