Endorsed by

Designation: A 105/A 105M – 05 Manufacturers Standardization Society

of the Valve and Fittings Industry
Used in USDOE-NE Standards

Standard Specification for

Carbon Steel Forgings for Piping Applications1
This standard is issued under the fixed designation A 105/A 105M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.

1. Scope* NOTE 1—The dimensionless designator NPS (nominal pipe size) has
been substituted in this standard for such traditional terms as “nominal
1.1 This specification2 covers forged carbon steel piping diameter,” “size,” and “nominal size.”
components for ambient- and higher-temperature service in
pressure systems. Included are flanges, fittings, valves, and 2. Referenced Documents
similar parts ordered either to dimensions specified by the 2.1 In addition to those reference documents listed in
purchaser or to dimensional standards such as the MSS, Specification A 961, the following list of standards apply to
ASME, and API specifications referenced in Section 2. Forg- this specification:
ings made to this specification are limited to a maximum 2.2 ASTM Standards: 3
weight of 10 000 lb [4540 kg]. Larger forgings may be ordered A 266/A 266M Specification for Carbon Steel Forgings for
to Specification A 266/A 266M. Tubesheets and hollow cylin- Pressure Vessel Components
drical forgings for pressure vessel shells are not included A 370 Test Methods and Definitions for Mechanical Testing
within the scope of this specification. Although this specifica- of Steel Products
tion covers some piping components machined from rolled bar A 675/A 675M Specification for Steel Bars, Carbon, Hot-
and seamless tubular products (see 4.2), it does not cover raw Wrought, Special Quality, Mechanical Properties
material produced in these product forms. A 696 Specification for Steel Bars, Carbon, Hot-Wrought or
1.2 Supplementary requirements are provided for use when Cold-Finished, Special Quality, for Pressure Piping Com-
additional testing or inspection is desired. These shall apply ponents
only when specified individually by the purchaser in the order. A 788 Specification for Steel Forgings, General Require-
1.3 Specification A 266/A 266M covers other steel forgings ments
and Specifications A 675/A 675M and A 696 cover other steel A 961 Specification for Common Requirements for Steel
bars. Flanges, Forged Fittings, Valves, and Parts for Piping
1.4 This specification is expressed in both inch-pound units Applications
and SI units. However, unless the order specifies the applicable 2.3 MSS Standards:
“M” specification designation (SI units), the material shall be SP 44 Standard for Steel Pipe Line Flanges4
furnished to inch-pound units. 2.4 ASME Standards:
1.5 The values stated in either inch-pound units or SI are to B16.5 Dimensional Standards for Steel Pipe Flanges and
be regarded separately as standard. Within the text, the SI units Flanged Fittings5
are shown in brackets. The values stated in each system are not B16.9 Wrought Steel Buttwelding Fittings5
exact equivalents; therefore, each system must be used inde- B16.10 Face-to-Face and End-to-End Dimensions of Fer-
pendently of the other. Combining values from the two systems rous Valves5
may result in nonconformance with the specification. B16.11 Forged Steel Fittings, Socket Weld, and Threaded5

1 3
This specification is under the jurisdiction of ASTM Committee A01 on Steel, For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee contact ASTM Customer Service at [email protected]. For Annual Book of ASTM
A01.22 on Steel Forgings and Wrought Fittings for Piping Applications and Bolting Standards volume information, refer to the standard’s Document Summary page on
Materials for Piping and Special Purpose Applications. the ASTM website.
4
Current edition approved June 1, 2005. Published June 2005. Originally Available from Manufacturers Standardization Society of the Valve and Fittings
approved in 1926. Last previous edition approved in 2003 as A 105/A 105M – 03. Industry (MSS), 127 Park St., NE, Vienna, VA 22180-4602.
2 5
For ASME Boiler and Pressure Vessel Code applications see related Specifi- Available from American Society of Mechanical Engineers (ASME), ASME
cation SA-105 in Section II of that Code. International Headquarters, Three Park Ave., New York, NY 10016-5990.

*A Summary of Changes section appears at the end of this standard.

Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
--`,,```,,,,,````,,,,,````,,`-`-`,,`,,`,`,,`---

Copyright ASTM International 1

Copyright by ASTM Int'l (all rights reserved);
Reproduced by IHS under license with ASTM Licensee=Loc 25-27Venezuela/Parlaguan,Puerto la Cr,San Die/5919206111, User=hern
No reproduction or networking permitted without license from IHS Not for Resale, 09/01/2005 14:12:02 MDT
Reproduction authorized per License Agreement with Kathe Hooper (ASTMIHS Account); Wed Jun 22 10:41:58 EDT 2005
 A 105/A 105M – 05
B16.34 Valves-Flanged, Threaded and Welding End5 TABLE 1 Chemical Requirements
B16.47 Large Diameter Steel Flanges5 NOTE—For each reduction of 0.01 % below the specified carbon
2.5 ASME Boiler and Pressure Vessel Code: maximum (0.35 %), an increase of 0.06 % manganese above the specified
Section IX Welding Qualifications5 maximum (1.05 %) will be permitted up to a maximum of 1.35 %.
2.6 API Standards: Element Composition, %
API-600 Flanged and Butt-Welding-End Steel Gate Valves6 Carbon 0.35 max
API-602 Compact Design Carbon Steel Gate Valves for Manganese 0.60–1.05
Refinery Use6 Phosphorus 0.035 max
Sulfur 0.040 max
Silicon 0.10–0.35
3. Ordering Information Copper 0.40 maxA
3.1 See Specification A 961. Nickel 0.40 maxA
Chromium 0.30 maxA,B
3.1.1 Additional requirements (see 12.2). Molybdenum 0.12 maxA,B
Vanadium 0.08 max
4. General Requirements A
The sum of copper, nickel, chromium, molybdenum and vanadium shall not
4.1 Product furnished to this specification shall conform to exceed 1.00 %.
B
The sum of chromium and molybdenum shall not exceed 0.32 %.
the requirements of Specification A 961, including any supple-
mentary requirements that are indicated in the purchase order.
Failure to comply with the requirements of Specification A 961 TABLE 2 Mechanical RequirementsA
constitutes nonconformance with this specification. In case of Tensile strength, min, psi [MPa] 70 000 [485]
Yield strength, min, psi [MPa]B 36 000 [250]
a conflict between the requirements of this specification and Elongation in 2 in. or 50 mm, min, %:
Specification A 961, this specification shall prevail. Basic minimum elongation for walls 5⁄16 in. [7.9 mm] 30
4.2 Except as permitted by Section 6 in Specification A 961, and over in thickness, strip tests.
When standard round 2-in. or 50-mm gage length or 22
the finished product shall be a forging as defined in the smaller proportionally sized specimen with the gage
Terminology Section of Specification A 788. length equal to 4D is used
For strip tests, a deduction for each 1⁄32-in. [0.8-mm] 1.50C
5. Heat Treatment decrease in wall thickness below 5⁄16 in. [7.9 mm]
from the basic minimum elongation
5.1 Heat treatment is not a mandatory requirement of this of the percentage points of Table 3
specification except for the following piping components: Reduction of area, min, %D 30
Hardness, HB, max 187
5.1.1 Flanges above Class 300,7 A
For small forgings, see 7.3.4.
5.1.2 Flanges of special design where the design pressure at B
Determined by either the 0.2 % offset method or the 0.5 % extension-under-
the design temperature exceeds the pressure-temperature rat- load method.
C
ings of Class 300, Group 1.1, D
See Table 3 for computed minimum values.
For round specimens only.
5.1.3 Flanges of special design where the design pressure or
design temperature are not known,
--`,,```,,,,,````,,,,,````,,`-`-`,,`,,`,`,,`---

TABLE 3 Computed Minimum Values

5.1.4 Piping components other than flanges which meet
both of the following criteria: (1) over NPS 4 and (2) above Wall Thickness Elongation in 2 in. or 50
mm, min, %
Class 300, and in. mm
5.1.5 Piping components of Special Class8 other than ⁄
5 16 (0.312) 7.9 30.00
flanges which meet both of the following criteria: (1) over NPS ⁄
9 32 (0.281) 7.1 28.50
1⁄4 (0.250) 6.4 27.00
4 and (2) when the working pressure at the operating tempera- 7⁄32 (0.219) 5.6 25.50
ture exceeds the tabulated values for Special Class 300, Group 3⁄16 (0.188) 4.8 24.00
5⁄32 (0.156) 4.0 22.50
1.1. 1⁄8 (0.125) 3.2 21.00
5.2 Heat treatment, when required by 5.1 shall be annealing, 3⁄32 (0.094) 2.4 19.50
normalizing, or normalizing and tempering or quenching and 1⁄16 (0.062) 1.6 18.00
tempering in accordance with Specification A 961. Note—The above table gives the computed minimum elongation values for
each 1⁄32-in. [0.8-mm] decrease in wall thickness. Where the wall thickness lies
6. Chemical Composition between two values shown above, the minimum elongation value is determined by
the following equation:
6.1 The steel shall conform to the chemical requirements
specified in Table 1. E 5 48T 1 15.00
6.2 Steels to which lead has been added shall not be used. where:
7. Mechanical Properties E = elongation in 2 in. or 50 mm, %, and
T = actual thickness of specimen, in. [mm].
7.1 The material shall conform to the mechanical property
requirements prescribed in Table 2 and Table 3.

6
7.2 For normalized, normalized and tempered, or quenched
Available from The American Petroleum Institute (API), 1220 L. St., NW,
Washington, DC 20005.
and tempered forgings, the central axis of the test specimen
7
For definition of Class 300, see ASME B16.5. shall correspond to the 1⁄4 T plane or deeper position, where T
8
For definition of special class, see ASME B16.34. is the maximum heat-treated thickness of the represented

Copyright ASTM International 2

Reproduced by IHS under license with ASTMCopyright by ASTM Int'l (all rights reserved); Licensee=Loc 25-27Venezuela/Parlaguan,Puerto la Cr,San Die/5919206111, User=hern
No reproduction or networking permitted without license from IHS Not for Resale, 09/01/2005 14:12:02 MDT
Reproduction authorized per License Agreement with Kathe Hooper (ASTMIHS Account); Wed Jun 22 10:41:58 EDT 2005
 A 105/A 105M – 05
forging. In addition, for quenched and tempered forgings, the 8. Hydrostatic Tests
midlength of the test specimen shall be at least T from any 8.1 Such tests shall be conducted by the forging manufac-
second heat-treated surface. When section thickness does not turer only when Supplementary Requirement S8 in Specifica-
permit this positioning, the test specimen shall be positioned as tion A 961 is specified.
near as possible to the prescribed location.
7.3 Tension Tests: 9. Retreatment
7.3.1 One tension test shall be made for each heat of 9.1 If the results of the mechanical tests do not conform to
as-forged components. the requirement specified, the manufacturer may heat treat or
7.3.2 One tension test shall be made from each heat-treating reheat treat the forgings as applicable and repeat the test
charge. If more than one heat is included in such a charge, each specified in Section 7.
heat shall be tested.
7.3.2.1 When the heat-treating temperatures are the same 10. Repair by Welding
and the furnaces (either batch or continuous type), are con- 10.1 Repair of defects by the manufacturer is permissible
trolled within 625 °F [614 °C] and equipped with recording for forgings made to dimensional standards such as those of
pyrometers so that complete records of heat treatment are ASME or for other parts made for stock by the manufacturer.
available, then one tension test from each heat is required Prior approval of the purchaser is required to repair-weld
instead of one test from each heat in each heat-treatment special forgings made to the purchaser’s requirements.
charge. The test specimen material shall be included with a 10.2 Weld repairs shall be made by a process that does not
furnace charge. produce undesirably high levels of hydrogen in the welded
7.3.3 Testing shall be performed in accordance with Test areas.
Methods and Definitions A 370. The largest feasible round 10.3 All forgings repaired by welding shall be post-weld
specimen as described in Test Methods and Definitions A 370 heat treated between 1100 °F [593 °C] and the lower transfor-
shall be used except when hollow cylindrically shaped parts are mation temperature for a minimum of 1⁄2 h/in. [1⁄2 h/25.4 mm]
machined from seamless tubulars. The gage length for mea- of maximum section thickness, or alternatively annealed,
suring elongation shall be four times the diameter of the test normalized and tempered, or quenched and tempered. If the
section. When hollow cylindrically shaped parts are machined forging was not previously heat treated, the original tempering
from seamless tubular materials, strip tests may be used. temperature was exceeded, or the forging was fully heat treated
in the post weld cycle, then the forging shall be tested in
7.3.4 Forgings too small to permit obtaining a subsize
accordance with Section 7 on completion of the cycle.
specimen of 0.250 in. [6.35 mm] diameter or larger (see Test
10.4 The mechanical properties of the procedure-
Methods and Definitions A 370) parallel to the dimension of
qualification weldment shall, when tested in accordance with
maximum working, and produced in equipment unsuitable for
Section IX of the ASME Boiler and Pressure Vessel Code,
the production of a separately forged test bar such as an
conform with the requirements listed in Table 2 for the thermal
automatic or semi-automatic press, may be accepted on the
--`,,```,,,,,````,,,,,````,,`-`-`,,`,,`,`,,`---

condition of repair-welded forgings.

basis of hardness only. One percent of the forgings per lot (see
Note 2), or ten forgings, whichever is the lesser number, shall
11. Rejection and Rehearing
be selected at random, prepared, and tested using the standard
Brinell test in Test Methods and Definitions A 370. The 11.1 Each forging that develops injurious defects during
locations of the indentations shall be at the option of the shop working or application shall be rejected and the manu-
manufacturer but shall be selected to be representative of the facturer notified.
forging as a whole. One indentation per forging shall be
required but additional indentations may be made to establish 12. Certification
the representative hardness. The hardness of all forgings so 12.1 Identification Marking—For forgings made to speci-
tested shall be 137 to 187 HB inclusive. fied dimensions, when agreed upon by the purchaser, and for
forgings made to dimensional standards, application of identi-
NOTE 2—A lot is defined as the product from a mill heat or if heat fication marks as required in Specification A 961 shall be the
treated, the product of a mill heat per furnace charge.
certification that the forgings have been furnished in accor-
7.4 Hardness Tests—Except when only one forging is dance with the requirements of this specification. The specifi-
produced, a minimum of two forgings shall be hardness tested cation designation included on test reports shall include year
per batch or continuous run as defined in 7.3.2.1 to ensure that date and revision letter, if any.
forgings are within the hardness limits given in Table 2. When 12.2 Test Reports—When test reports are required, the
only one forging is produced, it shall be hardness tested as manufacturer shall also provide the following, where appli-
defined in 7.3.2.1 to ensure it is within the hardness limits cable:
given in Table 2. Testing shall be in accordance with Test 12.2.1 Type heat treatment, Section 5,
Methods and Definitions A 370. The purchaser may verify that 12.2.2 Tensile property results, Section 7 (Table 2), report
the requirement has been met by testing at any location on the the yield strength and ultimate strength, in ksi [MPa], elonga-
forging, provided such testing does not render the forging tion and reduction in area, in percent; and, if longitudinal strip
useless. tension specimens are used, report the width of the gage length,

Copyright ASTM International 3

Reproduced by IHS under license with ASTM Copyright by ASTM Int'l (all rights reserved); Licensee=Loc 25-27Venezuela/Parlaguan,Puerto la Cr,San Die/5919206111, User=hern
No reproduction or networking permitted without license from IHS Not for Resale, 09/01/2005 14:12:02 MDT
Reproduction authorized per License Agreement with Kathe Hooper (ASTMIHS Account); Wed Jun 22 10:41:58 EDT 2005
 A 105/A 105M – 05
12.2.3 Chemical analysis results, Section 6 (Table 1). When apply). The specification number marked on the forgings need
the amount of an unspecified element is less than 0.02 %, then not include specification year date and revision letter.
the analysis for that element may be reported as “< 0.02 %,” 13.4 Bar Coding—In addition to the requirements in
12.2.4 Hardness results, Section 7 (Table 2), and Specification A 961 and 13.3, bar coding is acceptable as a
12.2.5 Any supplementary testing required by the purchase supplemental identification method. The purchaser may
order. specify in the order a specific bar coding system to be used.
The bar coding system, if applied at the discretion of the
13. Product Marking supplier, should be consistent with one of the published
13.1 If the forgings have been quenched and tempered, the industry standards for bar coding. If used on small parts, the
letters “QT” shall be stamped on the forgings following this bar code may be applied to the box or a substantially applied
specification number. tag.
13.2 Forgings repaired by welding shall be marked with the
letter “W” following this specification number. 14. Keywords
13.3 When test reports are required for larger products, the 14.1 pipe fittings, steel; piping applications; pressure con-
markings shall consist of the manufacturer’s symbol or name, taining parts; steel flanges; steel forgings, carbon; steel valves;
this specification number, and such other markings as neces- temperature service applications, elevated; temperature service
sary to identify the part with the test report (13.1 and 13.2 shall applications, high

SUPPLEMENTARY REQUIREMENTS

The following supplementary requirements shall apply only when specified by the purchaser in the
inquiry, contract, and order.

S1. Hardness S3. Marking Small Forgings

S1.1 The purchaser may check the hardness of any or all S3.1 For small products where the space for marking is less
forgings supplied at any location on the forging and the than 1 in. [25 mm] in any direction, test reports are mandatory
hardness shall be 137 to 187 HB. All forgings not within the and marking may be restricted to only such symbols or codes
specified hardness range shall be rejected. as are necessary to identify the parts with test reports.
S2. Heat Treatment S3.2 When the configuration or size does not permit mark-
S2.1 All forgings shall be heat treated as specified by the ing directly on the forging, the marking method shall be a
purchaser. matter of agreement between the manufacturer and the pur-
S2.2 When forgings not requiring heat treatment by 5.1 are chaser.
supplied heat treated by purchaser request, the basis for
determining conformance with Table 2 and Table 3 shall be S4. Carbon Equivalent
hardness testing per 7.4 and either (1) tensile testing of heat S4.1 The maximum carbon equivalent, based on heat analy-
treated forgings per 7.2, or (2) tensile tests from as-forged sis, shall be 0.47 for forgings with a maximum section
forgings or separately forged test blanks, as agreed upon thickness of 2 in. or less, and 0.48 for forgings with a
between the supplier and purchaser. maximum section thickness of greater than 2 in.
S2.3 When test reports are required, and tensile test results
were obtained from as-forged forgings or as-forged test blanks, S4.2 Determine the carbon equivalent (CE) as follows:
it shall be so indicated on the test report. CE 5 C 1 Mn/6 1 ~Cr 1 Mo 1 V!/5 1 ~Ni 1 Cu!/15
S2.4 In addition to the marking required by Section 13, this
specification shall be followed by the letter: A for annealed, N S4.3 A lower maximum carbon equivalent may be agreed
for normalized, NT for normalized and tempered, or QT for upon between the supplier and the purchaser.
quenched and tempered, as appropriate.

--`,,```,,,,,````,,,,,````,,`-`-`,,`,,`,`,,`---

Copyright ASTM International 4

Copyright by ASTM Int'l (all rights reserved);
Reproduced by IHS under license with ASTM Licensee=Loc 25-27Venezuela/Parlaguan,Puerto la Cr,San Die/5919206111, User=hern
No reproduction or networking permitted without license from IHS Not for Resale, 09/01/2005 14:12:02 MDT
Reproduction authorized per License Agreement with Kathe Hooper (ASTMIHS Account); Wed Jun 22 10:41:58 EDT 2005
 A 105/A 105M – 05
SUMMARY OF CHANGES

Committee A01 has identified the location of selected changes to this specification since the last issue,
A 105/A 105M - 03, that may impact the use of this specification. (Approved June 1, 2005)

(1) Revised 12.2.2 to require reporting the width of the gage

length of longitudinal strip tensile specimens, if they are used.

Committee A01 has identified the location of selected changes to this specification since the last issue,
A 105/A 105M - 02, that may impact the use of this specification. (Approved October 1, 2003)

(1) Deleted Columbium from Table 1.

Committee A01 has identified the location of selected changes to this specification since the last issue,
A 105/A 105M - 01, that may impact the use of this specification. (Approved November 10, 2002)

(1) Deleted reference to Specification A 695 in 1.3 and 2.2.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website
(www.astm.org).

--`,,```,,,,,````,,,,,````,,`-`-`,,`,,`,`,,`---

Copyright ASTM International 5

Copyright by ASTM Int'l (all rights reserved);
Reproduced by IHS under license with ASTM Licensee=Loc 25-27Venezuela/Parlaguan,Puerto la Cr,San Die/5919206111, User=hern
No reproduction or networking permitted without license from IHS Not for Resale, 09/01/2005 14:12:02 MDT
Reproduction authorized per License Agreement with Kathe Hooper (ASTMIHS Account); Wed Jun 22 10:41:58 EDT 2005