Bredent GB

breCAM
consumables
03/2015
Image of Lab. Od. Lazetera Antonio - Savona (IT)
2 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

breCAM
consumables
breCAM consumables - development leads to plastic
Our research and development already led to these Our materials show that there is no longer any reason
materials years ago, completely in line with our mis- to merely resort to the traditional materials such as
sion statement, which incorporates the values “capa- metal, ceramic or zircon for the indications cited.
ble, spirit of partnership and innovative”. With these These plastics offer significant benefits in the fields of
high-performance plastics, we have found the innova- aesthetics, processing, cost-efficiency, durability and
tive way of providing patients with the best possible patient acceptance. They offer a win-win situation
treatment from the very beginning, whilst simultane- for both parties in a relationship based on partnership
ously offering them success-oriented, efficient and between patients and their care team.
capable solutions from a team consisting of a dentist Take advantage of our competence in the field of plas-
and prosthetist. tics and in digital processing:
STABLE - With breCAM.cast make dimensionally DEFINITIVE – With breCAM.HIPC you have a uni-
stable and low-stress plastic frames for implementa- versal genius at your disposal. Whether used as milled
tion in the metal framework casting technique. veneering or as a monolithic abutment, this material
offers you the most elegant solution for a number of
EFFICIENT - With breCAM.model you complete the indications and for all framework materials (including
digital manufacturing process of making the model to BioHPP).
completing the final denture. PHYSIOLOGICAL – With breCAM.BioHPP you find
yourself in the bionic age. The physiological properties
SMART – Take advantage of the benefits of the digi- of this framework material are only surpassed by na-
tal world in traditional technology with breCAM.wax. ture itself. BioHPP allows patients to forget that they
are wearing an abutment as it is just as elastic, light
and has the same thermal conductivity as bone.
CLEAN – breCAM.resin enables you to produce safe,
biocompatible, aesthetic temporary prostheses that are
stable in terms of colour and shape. EFFICIENT - With breCAM.model you complete the
digital manufacturing process of making the model to
completing the final denture.
UNIVERSAL – With breCAM.multicom you increase
the wearing time of the temporary prosthesis to two
years and offer even more polished aesthetics.
3
E F F I Z EFFIZiENT
I STABLE
EiNT
breCAM.cast
is made of PMMA (100% polymethylmethacrylate) Due to the relative sensitivity of wax to temperature
which burns out without residue. changes and UV radiation, this material is very stable
The material is ideal for the production of CAD/CAM and leads to low-stress, precise castings.
dental structures for implementation in the metal
casting technique.
Machined plastic frames have no Dimensions and thermally stable material

thermal stresses within the structure. »» milled plastic frameworks can be tried onto
»» More accurate metal castings compared to different models due to its form stability for
waxed frame works control purposes, implemented and processed
breCAM.cast may be processed using CAD/CAM

Systems problem free
»» wet/dry with fast milling templates
Framework design
According to DIN EN ISO 10477
Shore Flexural strength Density
> 2800 MPa ≥ 60 MPa > 1.1g/cm2

breCAM.cast
Processing
Metal cutting using mills can be carried out in dry conditions. In the case of HSC mills,
single or double-edged tools with large air gaps should be used.
Dry machining Wet machining Dry machining

PMMA/composite PMMA/composite Thermoplastic/cutter
Order information
These milling blanks are a standard size at Ø 98.5 mm with 10 mm fold.
Set Colour 18 mm
breCAM.cast blue REF 540 0220 0
W

EFFICiENT
breCAM.model
is a high-density plastic model for fast cutting produc- Due to the high stability of the material , the models
tion of master models . The material is very homoge- produced in this way are also suitable for long-term
neous and behaves very dimensionally stable. archiving , as they keep their stable form as opposed
Here, the breCAM.model is very durable and has high to light-curing resins .
edge strength.
breCAM.model is easy to mill wet or dry and can be
modified as necessary with a carbide bur.
High-performance model plastic CAD/CAM processing

»» Very fast processing parameters »» Always consistent quality, by loss or damage
always reproducible from the digital archives
Rigid material
»» Perfect for long-term archiving
Processing
Metal cutting using mills can be carried out in dry conditions. In the case of HSC mills,
single or double-edged tools with large air gaps should be used.

Order information
Set Colour 28 mm
breCAM.model
breCAM.model beige REF 540 0204 0
W
5
SMART
breCAM.wax
breCAM.wax is extremely well-suited to the digital addition to its homogeneous and virtually tension-free
production of fully anatomical or reduced frameworks, structure: No further thermal treatments by means of
inlays, onlays, implant work including large span bridges fusion or applications, mixing of different wax qualities,
for cast metal and ceramic press technology. no damage due to overheating or impurities.
The cutting preparation of wax cutting blanks in a den-

tal laboratory has the following benefits in comparison
with conventional wax dipping and modelling, in
mechanical production of crowns and frameworks for wide range and reproducibility of desired morphologies
gold casting and ceramic pressing technology and tooth shapes
»» Cost and time saving »» the same quality and flexibility of work
better fit of the gold casting due to tension-free pro- One-pass processing of wax: impurities and loss of wax
cessing properties do not apply
»» less reworking, less material loss (gold alloys) »» no material contamination as a result of re-used,
impure wax
uniform framework designs/connector strengths due to
the CAD construction flexible production
»» more stable frameworks and the same qualities, less »» existing CNC capacities can be exhausted in terms of
reworking and time saving time
breCAM.wax
Images: Lab. Od. Lazetera Antonio - Savona (IT)

The breCAM.wax blanks are made from a special milling industrial processes and subsequently cooled in a
wax (micro-crystalline hydrocarbon wax with hard defined temperature ramp. This results in an extremely
paraffin and polyethylene parts), which is very easy to homogeneous and tension-free wax, which ultimately
process. The wax has a drying point of 120 °C, possesses leads to reproducible and equal fits in the practice of
slight elasticity, strong edge stability for fast milling metal casting technology.
speeds and burns without residues. The raw material in
the wax blanks is fused in a controlled manner in
Indication
Metal casting Press ceramics Wax-up

BioHPP for2press
Order information
These milling blanks are a standard size at 98 x 20 mm
Item 20 mm
breCAM.wax 2 REF 510 0092 1
W
breCAM.wax
7
CLEAN
breCAM.resin
The basis of this thermoplastic production process is to the powder-form PMMA and therefore trigger the
an industrial polymerisation process for producing a formation of long-chain polymers. Unfortunately,
high-purity PMMA. Only this production process can unbound radicals (residual monomers MMA) remain
convert all MMA into PMMA with a theoretic level of in the chemoplast during chemical polymerisation.
purity of up to 99.9%. Residual by-products of this These and the polymerisation initiators, inhibitors
reaction (<0.1%) are not cell-toxic and are therefore and benzoyl peroxides are substances that trigger al-
harmless. The PMMA acquired from this procedure is lergies, which are responsible for triggering material
subsequently fused directly using heat with no ad- intolerances.
ditional MMA and injected as a blank.
The disadvantage of the otherwise frequent chemo-

plastic procedure: If both PMMA and MMA (powder/
liquid) components are mixed, a chain reaction is
triggered by the initiator, which generates free radi-
cals. These radicals allow the MMA to be bonded
The beneficial material properties of a thermoplas-

tic PMMA are:
a higher homogeneity of the thermoplastic PMMA causes fewer allergies, high-purity PMMA
»» lower susceptibility to plaque »» high biocompatibility
»» the restoration is more durable »» Customers with requirements for increased bio-
»» fewer patient recalls compatibility can be treated more safely.
longer molecular chains, higher levels of stability

breCAM.resin
»» Better long-term stability and resistance leads

to fewer repairs and a higher level of customer
acceptance.

breCAM.resin
Indication Therapy Processing Securing
Permanent dental Braces Framework Temporary cement

prosthesis
Crowns & Bridges Table tops Can be veneered
Try-ins Monolithic
Metal-free
Framework design
breCAM.resin
Minimum wall strength Pontics Front teeth Side teeth
(unveneered) Ø Connector Ø Connector
> 1,00 occlusal max. 1 > 10 mm2 > 15 mm2

0.6 mm cervical
Material properties
E-modulus Flexural strength Water solubility Water absorption Residual monomer Wearing time
≥ 2800 MPa ≥ 100 MPa ≤ 0.6μg/mm³ ≤ 24 μg/mm³ ≤ 0.24 % up to 6 months
9
CLEAN
Processing
Thermoplastic materials generally place high demands used here. No special adjustments or processing prop-
on expert metal cutting in dry machining due to their erties need to be observed in favoured wet machining
sensitivity to heat and therefore the associated risk of with standard milling templates and PMMA mills.
deformities. Special cutters and adapted milling tem-
plates with a reduced cutting speed must definitely be
Rough machining (Ø 2 mm) Smooth machining (Ø 1 mm)

19,000 U/min - Feed of 15 mm/s – Delivery 0.5 mm 25,000 U/min – Feed 25 mm/s

Order information
16 mm 20 mm 24 mm
breCAM.resin A REF 540 0201 0 REF 540 0201 1 REF 540 0201 2
breCAM.resin
breCAM.resin B REF 540 0201 3 REF 540 0201 4 REF 540 0201 5 W
breCAM.resin C REF 540 0201 6 REF 540 0201 7 REF 540 0201 8
breCAM.resin transparent REF 540 0201 9 REF 540 0202 0 REF 540 0202 1

UNIVERSAL
breCAM.multiCOM
The polychrome composite is suitable for a dental optimised material properties in the field of strength,
prosthesis with a wearing time of up to two years. It abrasion properties and for dry or wet metal cutting.
is manufactured based on polymethylmethacrylate The multichromatic layering of breCAM.multiCOM
and has been offset with >20% ceramic fillers in or- gives the dental prosthesis a natural colour gradient.
der to increase the strength. Here, the inorganic filler
(ceramic particle) has been integrated in the plastic
matrix of the organic PMMA. This results in
A 2-year wearing time is optimal for the temporary »» considerable savings of various veneer materials
abutment within the scope of surgical procedures and additional work stages
and longer regeneration phases.
»» The restoration does not need to be exchanged can be used universally
after 6 months, which leads to optimum healing »» monolithic or as a polychromatic temporary
results. veneer plastic
»» Cost and time saving for both the patient and the »» A number of different indications can be covered
dentist with a single material.
breCAM.multiCOM
polychromatic colouration ceramic filler
»» highly aesthetic temporary dental prosthesis with »» By its chemical definition, breCAM.multiCOM is a
low material costs composite.
»» high level of customer acceptance, especially in »» It possesses improved milling properties and opti-
the field of front tooth restoration mum abrasion properties.
monolithic abutment
»» polychromatic colouration in only one manufac-
turing process
11
UNIVERSAL
Permanent dental Braces Can be veneered Temporary cement

prosthesis
Crowns & Bridges Table tops Monolithic

breCAM.multiCOM
Implant-supported Metal-free
Framework design
> 1.00 occlusal max. 1 > 10 mm2 > 15 mm2

0.6 mm cervical
Material properties
≥ 2200 MPa ≥ 100 MPa ≥ 8 μg/mm³ ≤ 20 μg/mm³ ≤ 0.7 % up to 2 years

Processing
breCAM.multiCOM is generally suitable for both dry This should be taken into consideration/adjusted by
and wet machining. Composites are slightly harder to selecting a suitable milling template.
process due to their ceramic part.

Order information
These milling blanks are a standard size at Ø 98 mm with 10 mm fold:
breCAM.multiCOM
Colour 16 mm 20 mm
bre.CAM.multiCOM A1 REF 540 0301 0 REF 540 0301 5
bre.CAM.multiCOM A3 REF 540 0303 0 REF 540 0303 5 W
bre.CAM.multiCOM A3,5 REF 540 0304 0 REF 540 0304 5
bre.CAM.multiCOM B2 REF 540 0306 0 REF 540 0306 5
These milling blanks are suitable for processing in ZZ systems with a diameter of Ø 95 mm:
bre.CAM.multiCOM A3 REF 540 0313 0 REF 540 0313 5 ZZ
bre.CAM.multiCOM A3,5 REF 540 0314 0 REF 540 0314 5
bre.CAM.multiCOM B2 REF 540 0316 0 REF 540 0316 5
These milling blanks are suitable for processing in AG systems with a diameter of Ø 84,5 mm:
bre.CAM.multiCOM A1 - REF 540 0321 5
bre.CAM.multiCOM A2 - REF 540 0322 5
bre.CAM.multiCOM A3 - REF 540 0323 5 AG
bre.CAM.multiCOM A3,5 - REF 540 0324 5
bre.CAM.multiCOM B2 - REF 540 0326 5
13
DEFINITIVE
breCAM.HIPC
HIPC: technical “High Impact Polymer Composite” of dental glass and light-curing plastic ensures a
for long-term dental prostheses. breCAM.HIPC is high level of colour retention and plaque resistance
an amorphic, cross-linked composite and therefore (comparable with direct ceramic veneers or press
offers definitely higher physical values than conven- ceramics).
tional PMMA. Manufacturing is carried out under
pressure and in heated conditions similar to prefab- HIPC originates from the development of the visio.
ricated teeth made from plastic at approximately lign system and corresponds to novo.lign veneers in
120 °C and 250 bars of pressure. Avoiding the use chemical terms, with this material being extremely
well-suited for a long-term dental prosthesis.
for a long-term dental prosthesis - HIPC has high level of strength/long-term stability
already been tested in vivo and approved for over »» As a high-performance polymer, HIPC does not
7 years lose its strength in comparison with ceramic,
»» clinically-proven material ceramic “ages”.
»» Safety in use and indications »» Material reliability and long-term stability of
breCAM.HIPC leads
plaque-resistant to fewer complaints and repairs.
»» Excellent gingiva compatibility and resistance to
discolourations lead to a higher level of the material is more aesthetic, translucent and
patient acceptance. opalescent
»» excellent colour effect with minimally invasive
universal & economical, removable & fixed, mono- forms of restoration
lithic & can be veneered »» Complicated cases with a lack of space can be
»» The most diverse indications can be covered with neatly resolved with HIPC.
a single material.
»» Costs can be saved and the system diversity and
breCAM.HIPC
processing techniques can be minimised in the

laboratory.

Permanent dental Removable Gingival Framework Lasting adhesion

prosthesis dental prosthesis management
Crowns & Bridges Secondary bridge Braces Can be veneered Temporary cement
Primary telescope Secondary telescope Table tops Monolithic Implant-supported

temporary adhesive
Implant-supported Tertiary framework Pressure-absorbing Metal-free Implant-supported
breCAM.HIPC
temporary cement
Inlay/Onlay/Veneer
Framework design
≥ 0.7 occlusal max. 2 ≥ 9 mm2 ≥ 12 mm2

≥ 1.0 mm cervical
implant-supported ≥ 1 mm
15
DEFINITIVE
Material properties
> 2200 MPa ≥120 MPa ≤ 0.3 μg/mm³ ≤ 16 μg/mm³ < 0.5% permanent
Processing
Metal cutting using mills can be carried out in dry conditions. In the case of HSC mills, single or double-edged
tools with large air gaps should be used.

Order information
breCAM.HIPC
W AG ZZ
Colour 20 mm 16 mm 20 mm 20 mm
breCAM.HIPC bleach REF 5400339 8 REF 540 0341 8 REF 540 0345 8 REF 540 0343 8
bre.CAM.HIPC A1 REF 540 0339 9 REF 540 0341 9 REF 540 0345 9 REF 540 0343 9
bre.CAM.HIPC A3,5 REF 540 0340 2 REF 540 0342 2 REF 540 0346 2 REF 540 0344 2
bre.CAM.HIPC B2 REF 540 0340 4 REF 540 0342 4 REF 540 0346 4 REF 540 0344 4
bre.CAM.HIPC B3 REF 540 0340 5 REF 540 0342 5 REF 540 0346 5 REF 540 0344 5
bre.CAM.HIPC C2 REF 540 0340 6 REF 540 0342 6 REF 540 0346 6 REF 540 0344 6
bre.CAM.HIPC C3 REF 540 0340 7 REF 540 0342 7 REF 540 0346 7 REF 540 0344 7
bre.CAM.HIPC D2 REF 540 0340 8 REF 540 0342 8 REF 540 0346 8 REF 540 0344 8
bre.CAM.HIPC D3 REF 540 0340 9 REF 540 0342 9 REF 540 0346 9 REF 540 0344 9
bre.CAM.HIPC clear REF 540 0341 0 REF 540 0343 0 REF 540 0347 0 REF 540 0345 0

Physiological
breCAM.BioHPP
BioHPP is a partly crystalline poly ether ether ketone The improvement with ceramic fillers enabled the mate-
(PEEK) that is strengthened using ceramic. The bonding rial properties to be significantly improved once more
forces of the polymer chains are more effective if the (strength, abrasion properties, ability to be veneered)
chains are aligned in parallel. Areas like this are known and has therefore been adjusted and optimised es-
as crystalline. pecially to suit the requirements and uses in dental
The main component of breCAM.BioHPP has been suc- medicine.
cessfully implemented in implantology in human medi-
cine for 30 years already (for 20 years as an interverte-
bral disc, hip joint prostheses).
breCAM.BioHPP
for long-term use heat conduction properties similar to teeth
»» BioHPP is the new reference for a permanent »» comfortable feeling when worn
dental prosthesis. »» no difference in perception with regard to warm/
anti-allergens cold meals
»» metal-, oxide- and monomer-free Red-white look
»» no allergic reactions or discolourations of the »» The white material colour is in keeping with the
gingiva known to date tooth substance and does not show dark gingival
»» The perfect solution for those with allergies. edges in the case of possible resorption of the sur-
light/similar to bone rounding soft tissue.
»» optimal biocompatibility and integration in the low abrasion properties
jaw »» BioHPP as a monolithic dental prosthesis protects
no galvanic effect the remaining residual teeth due to its
»» no oxidation or metal taste low abrasive potential.
off-peak effect universal material

»» BioHPP can reduce compression and torsion »» The broadest range of indications can be covered
caused by chewing and can partly with this material:
compensate for this. This results in a periodontic monolithic, can be veneered, fixed, removable,
effect and an increase in wearing comfort. fricative, as prostheses - brace bases
17
Physiological
Permanent dental Removable Braces Framework Lasting adhesive

prosthesis dental prosthesis
Crowns & Bridges Secondary bridge Pressure-absorbing Can be veneered Temporary cement
Primary telescope Secondary telescope Monolithic Implant-supported

temporary adhesive
breCAM.BioHPP
Implant-supported Tertiary framework Metal-free
Implant-supported Prosthesis
bridge
Framework design
≥ 0.7 occlusal max. 2 ≥ 9 mm2 ≥ 12 mm2

≥ 1.0 mm cervical

breCAM.BioHPP
Thermoplastic materials (BioHPP) generally place processing properties need to be observed in fa-
high demands on the expert metal cutting in dry ma- voured wet machining with standard PMMA milling
chining due to their sensitivity to heat and therefore templates. The patented cutter “breCAM.cutter” is
the associated risk of deformities. Special cutters and recommended for special dry and wet machining of
adapted milling templates with a reduced cutting this material, with which thermoplastic materials
speed must be used here. No special adjustments or (BioHPP) can be either dry machined or wet ma-
chined.
Material properties
E-modulus Flexural strength Water solubility Water absorption Wearing time
permanent
> 4550 MPa > 180 MPa < 0.3 μg/mm³ < 6.5 μg/mm³ > 7 years
Processing
breCAM.BioHPP
Rough machining (Ø 2 mm) Smooth machining (Ø 1 mm)

19,000 U/min - Feed of 15 mm/s – Delivery 0.5 mm 25,000 U/min – Feed 25 mm/s
Order information
These milling blanks are a standard size at Ø 98,5 mm with 10 mm fold:
12 mm 16 mm 20 mm 24 mm 25 mm
breCAM.BioHPP REF 540 0202 9 REF 540 0203 0 REF 540 0203 1 REF 540 0203 2 x W
breCAM.BioHPP dentin-shade 2 REF 540 0206 9 REF 540 0207 0 REF 540 0207 1 REF 540 0207 2 x
These milling blanks are suitable for processing in ZZ systems with a diameter of Ø 95 mm:
breCAM.BioHPP REF 540 0208 9 x REF 540 0209 1 x REF 540 0209 2
breCAM.BioHPP dentin-shade 2 REF 540 0209 9 x REF 540 0210 1 x REF 540 0210 2
ZZ
These milling blanks are suitable for processing in AG systems with a diameter of Ø 84,5 mm:
breCAM.BioHPP x x REF 540 0211 1 x x
breCAM.BioHPP dentin-shade 2 x x REF 540 0212 1 x x
AG
19
Physiological
BioHPP elegance prefab
The world‘s first individual physiological The thermoplastic integrated titanium base here
Hybridabutment combines homogeneously and free of gaps with the
BioHPP.
By using BioHPP it is now possible to produce an indi-
vidual hybrid abutment with physiological properties. BioHPP elegance prefabs are indicated for restorations
The ductile properties of BioHPP and the associated with an angulation of up to 20° to the implant axis.
OFF-PEAK effect, a similar effect comparable to the
Periodontium, there is a unique wearing comfort that With this solution it is possible for the first time to
metallic and or ceramic abutments cannot deliver. produce individual, permanent abutments of the lea-
ding implant systems in your own laboratory using soft
machining and exploiting the full value of the CAD/
CAM system.
Physiological restorations; by the Periodontium The BioHPP SKY elegance prefab abutment is suit-
similar shock absorption (OFF-PEAK) the load input able for immediate loading
is delayed and damped over time to the implant. »» Immediate definitive restoration, no trauma to
»» High wear and chewing comfort, lower gingival tissue, shorter regeneration phase
Implant failure due to overloading
Gingival Management with BioHPP
Homogeneous, gap-free material bond of titanium »» Using a carbide bur it is possible to modify BioHPP,
grade 4/BioHPP having the best mechanical and when necessarily orally, if gingival contouring is
biological properties. subsequently required. A subsequent Intraoral scan
»» No aging/fatigue of adhesive bond without removing the abutments is possible.
lack of adhesive/adhesive gap
»» Security against germs
Advantages of BioHPP restorations
»» Maximum customizability
»» Unbeatable convenient processing
»» Cuts like dentin, also intraorally
»» NO chipping
»» Conserving the antagonists

»» Optimal Osseointegration
»» Optimal gingival management
»» Longevity of the restoration
»» Natural oral feeling

»» Natural chewing sensation
»» Natural aesthetics
»» Prevents CMD
»» Allows immediate restoration

»» Allows one time treatment
»» Analog or digital workflow
»» Laboratory and chair side solutions

Processing
The BioHPP elegance prefab can be processed dry or Please refer to the recommended machining para-
wet on many milling systems for example with meters and special tools.
Roland/imes.icore/Datron and other systems.
External Milling Centers can be found at
www.caelo-dental.net
Shock Absorption

The OFF-PEAK property significantly dampens chewing
force peaks compared to titanium, zirconium or ceramic.
N
Titanium or Zironium
BioHPP
The forces acting on healing bone is in contrast to pre- long-term bone preservation. At the same time BioHPPs
vious materials remained in its natural context, so that damping characteristic, prevents chipping.
will help curtail (resorbtion/ Athrophierung) and osse-
ointegration can be initiated - the optimal basis for the
10 mm
13 mm 14 mm 3,9 mm
Order information
Set 3 pieces 6 pieces 9 pieces 12 pieces
BioHPP elegance prefab REF 540 0EP0 3 REF 540 0EP0 6 REF 540 0EP0 9 REF 540 0EP1 2
for bredent SKY
21
STARK
STARK
breCAM.cutter
The breCAM.cutter has been specially developed for dry machining of thermoplastic materials
(PMMA / PEEK / Wax) in CNC milling machines.
Technical specifications of the breCAM.cutter:

Thanks to a special cutting geometry, it is also possible to take thermoplastic

materials, which have properties which allow them to spread quickly and clog
up the tool, and mill them without water cooling.
REF Machine type Type Shaft Working area Total Working area length
diameter diameter length with release
breCAMX47 Wieland, Imes Icore, Coritec, 340i, Radius mill 3.0 1.0 38.2 15.0
450i, 440i
breCAMX48 Wieland, Imes Icore, Coritec, 340i, Radius mill 3.0 2.0 38.2 15.0
450i, 440i
breCAMX49 3M Espe, LAVA Form System 400, Radius mill 3.0 1.0 38.0 15.0
500, Charly Robot
breCAMX50 3M Espe, LAVA Form System 400, Radius mill 3.0 2.0 38.0 15.0
breCAM.cutter
500, Charly Robot

breCAMX53 Roland DWX 40, DWX 50, Calidia, Radius mill 4.0 1.0 50.0 15.0
TDS, DMG U-Serie, Yenadent, Origin
breCAMX54 Roland DWX 40, DWX 50, Calidia, Radius mill 4.0 2.0 50.0 15.0
TDS, DMG U-Serie, Yenadent, Origin
breCAMX67 VHF, FinoCAM, Jeneric Pentron, Radius mill 3.0 1.0 34.0 15.0
Schütz, Trendgold
breCAMX69 VHF, FinoCAM, Jeneric Pentron, Radius mill 3.0 2.0 34.0 15.0
Schütz, Trendgold
breCAMY28 breCAM.cutter Ceramill mill Radius mill 3.0 0.6 47 15.0
breCAMY55 breCAM.cutter Coritec mill Radius mill 6.0 0.6 45 15.0
breCAMY53 breCAM.cutter Zirkonzahn mill Radius mill 3.0 0.6 57 15.0
breCAMY22 breCAM.cutter Cercon mill Radius mill 3.5 1.0 50 15.0
breCAMY77 breCAM.cutter WIELAND T1 Radius mill 3.4 2.4 50 24.5

breCAM.cutter templates
The recommended milling templates are developed further on a continuous basis.
For more information visit:
for up-to-date information and any possible amendments.
wax resin/colour resin/transpa multiCOM HIPC BioHPP
Ø 2 mm 20 15 15 15 15 15
Feed (mm/sec) ≤ 1 mm 19 22 22 22 22 22
≥ Ø 2 mm 11 7 7 7 7 7
Lateral feed (mm/sec) ≤ Ø 1 mm 11 11 11 11 11 8
≥ Ø 2 mm 16.000 19.000 13.000 19.000 19.000 18.000
Rotational speed (RMP) ≤ Ø 1 mm 25.000 22.000 22.000 25.000 25.000 20.000
breCAM.cutter
≥ Ø 2 mm 0.5 0.5 0.5 0.5 0.5 0.40
Delivery Z (mm)
≥ Ø 2 mm 0.05 0.05 0.05 0.05 0.05 0.05
Offset (mm) ≤ Ø 1 mm 0 0 0 0 0.5 0
≥ Ø 2 mm 50 % 50 % 50 % 50 % 50 % 50 %
Path intersection (%)
≥ Ø 1 mm 0.075 0.05 0.05 0.05 0.05 0.05

Path distance (mm)
23
GmbH & Co. KG · Weissenhorner Str. 2 · 89250 Senden · Germany · T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44
www.bredent.com · @: [email protected]
Mistake and subject to change reserved 000500GB-20160615

Bredent GB

Uploaded by

Copyright:

Available Formats

Bredent GB

Uploaded by

Document Information

Original Description:

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Bredent GB

Uploaded by

Copyright:

Available Formats

breCAM

2 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

Machined plastic frames have no Dimensions and thermally stable material

breCAM.cast may be processed using CAD/CAM

Shore Flexural strength Density

> 2800 MPa ≥ 60 MPa > 1.1g/cm2

Dry machining Wet machining Dry machining

4 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

High-performance model plastic CAD/CAM processing

Dry machining Wet machining Dry machining

The cutting preparation of wax cutting blanks in a den-

Images: Lab. Od. Lazetera Antonio - Savona (IT)

6 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

Metal casting Press ceramics Wax-up

The disadvantage of the otherwise frequent chemo-

The beneficial material properties of a thermoplas-

longer molecular chains, higher levels of stability

»» Better long-term stability and resistance leads

Images: Lab. Od. Lazetera Antonio - Savona (IT)

8 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

Permanent dental Braces Framework Temporary cement

Crowns & Bridges Table tops Can be veneered

> 1,00 occlusal max. 1 > 10 mm2 > 15 mm2

≥ 2800 MPa ≥ 100 MPa ≤ 0.6μg/mm³ ≤ 24 μg/mm³ ≤ 0.24 % up to 6 months

Rough machining (Ø 2 mm) Smooth machining (Ø 1 mm)

Dry machining Wet machining Dry machining

10 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

Images: Lab. Od. Lazetera Antonio - Savona (IT)

Permanent dental Braces Can be veneered Temporary cement

Crowns & Bridges Table tops Monolithic

> 1.00 occlusal max. 1 > 10 mm2 > 15 mm2

≥ 2200 MPa ≥ 100 MPa ≥ 8 μg/mm³ ≤ 20 μg/mm³ ≤ 0.7 % up to 2 years

12 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

Dry machining Wet machining Dry machining

processing techniques can be minimised in the

Images: Lab. Od. Lazetera Antonio - Savona (IT)

14 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

Permanent dental Removable Gingival Framework Lasting adhesion

Primary telescope Secondary telescope Table tops Monolithic Implant-supported

Implant-supported Tertiary framework Pressure-absorbing Metal-free Implant-supported

≥ 0.7 occlusal max. 2 ≥ 9 mm2 ≥ 12 mm2

> 2200 MPa ≥120 MPa ≤ 0.3 μg/mm³ ≤ 16 μg/mm³ < 0.5% permanent

Dry machining Wet machining Dry machining

These milling blanks are a standard size at Ø 98.5 mm with 10 mm fold.

16 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

Images: Lab. Od. Lazetera Antonio - Savona (IT)

off-peak effect universal material

Permanent dental Removable Braces Framework Lasting adhesive

Primary telescope Secondary telescope Monolithic Implant-supported

Implant-supported Tertiary framework Metal-free

≥ 0.7 occlusal max. 2 ≥ 9 mm2 ≥ 12 mm2

18 T: (+49) 0 73 09 / 8 72-4 41 · F: (+49) 0 73 09 / 8 72-4 44 · www.bredent.com · @: [email protected]

E-modulus Flexural strength Water solubility Water absorption Wearing time

Rough machining (Ø 2 mm) Smooth machining (Ø 1 mm)

Advantages of BioHPP restorations

»» Conserving the antagonists

»» Natural oral feeling

»» Allows immediate restoration