1.2714 en

This document provides information on the material 1.2714 55NiCrMoV7, including its chemical composition, properties, applications, delivery conditions, and heat treatment instructions. Key points: - The material is a nickel alloyed die steel with excellent toughness and good through-hardening properties, similar to AISI L6. - Its main applications are for forging dies, hot shear knives, punches, backing plates, and die holders. - It can be delivered either soft annealed to a maximum of 248 HB, or quenched and tempered to 1100-1350 N/mm2.

Uploaded by

reza razavi
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
179 views2 pages

1.2714 en

This document provides information on the material 1.2714 55NiCrMoV7, including its chemical composition, properties, applications, delivery conditions, and heat treatment instructions. Key points: - The material is a nickel alloyed die steel with excellent toughness and good through-hardening properties, similar to AISI L6. - Its main applications are for forging dies, hot shear knives, punches, backing plates, and die holders. - It can be delivered either soft annealed to a maximum of 248 HB, or quenched and tempered to 1100-1350 N/mm2.

Uploaded by

reza razavi
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

Material No.

: Code: DE - Brand:

1.2714 55NiCrMoV7 A50


Chemical composition: C Cr Mo Ni V
(Typical analysis in %)
0,55 1,10 0,50 1,70 0,10

Steel properties: Ni alloyed die steel with excellent toughness and good
through hardening properties. Similar to AISI L6.

Applications: Standard material for forging dies, hot shear knives,


punches, backing plates, die holders, hot punching tools.

Condition of delivery: a) Soft annealed to max. 248 HB


b) Quenched and tempered, 1100 - 1350 N/mm²

Physical properties:
10-6⋅m 20-100°C 20-300°C 20-500°C 20-600°C
Thermal expansion coefficient
m⋅K 12,3 13,4 14,1 14,4

W 20°C 350°C 700°C


Thermal conductivity
m⋅K 35,9 38,2 34,8

Heat treatment:
Temperature Cooling Hardness
Soft annealing
650 - 700°C furnace max. 248 HB

Stress relief annealing Temperature Cooling


The recommendation 600 - 650°C is valid for the soft
annealed condition. 600 - 650°C furnace

Temperature Cooling Tempering


Hardening oil, pressure gas (N2), see tempering
840 - 890°C
air diagram
05/06

Dörrenberg Edelstahl GmbH · Hammerweg 7 · D-51766 Engelskirchen A company of the


Tel.: +49 22 63 / 79 1 · Fax: +49 22 63 / 79 20 5 · www.doerrenberg.de GESCO group
(1.2714) Thermal Cycle Diagram
Stress relief annealing Hardening Tempering

Intermediate
hardening temperature

machining

machining
machining
Rough

Finish
cooling slowly 2nd preheating

Temperature
in furnace step cooling
½ min. / mm oil, air, pressure
600-650°C ~650°C gas (N2)

1st preheating
step tempering
½ min. / mm 1 h / 20 mm
~400°C at least 2 h

equalisation
1 h / 100 mm

Time

Continuous Cooling Transformation Diagram (CCT)


Austenitizing temperature: 850°C
1200

1000

800 Ac1e
Temperature [°C]

Ac1b
P 100
600 15
A+C

400
B 80
88
Ms 15
200
M
760 758 705 450 380 HV 240
0 2 3 4 5 6
0,1 1 10 10 10 10 10 10
Time [s]

Tempering Diagram

70

65

60
Hardness [HRc]

55

50

45

40 Test specimen:
= 30 mm, h = 40 mm
35 quenched from 870°C
in oil
30
0 100 200 300 400 500 600 700
Tempering temperature [°C]

Remarks: All technical information is for reference only.