    Matweb:, The Online Materials Database Aluminum 6201-T6

    Uploaded by

    Raj Prasanth
    Al.6201

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Matweb:, The Online Materials Database Aluminum 6201-T6

    Uploaded by

    Raj Prasanth
    191 views2 pages
    Al.6201

    Original Title

    6201

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Al.6201

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    191 views2 pages

    Matweb:, The Online Materials Database Aluminum 6201-T6

    Uploaded by

    Raj Prasanth
    Al.6201

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    MatWeb - Online Material Data Sheet Page 1 of 2

    MatWeb, The Online Materials Database

    Aluminum 6201-T6

    Subcategory: 6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal

    Close Analogs:

    Composition Notes:
    Aluminum content reported is calculated as remainder.
    Composition information provided by the Aluminum Association and is not for design.

    Key Words: UNS A96201; Aluminium 6201-T6; AA6201-T6

    Component Wt. % Component Wt. % Component Wt. %

    Al 97.3 - 98.9 Fe Max 0.5 Other, total Max 0.1


    B Max 0.06 Mg 0.6 - 0.9 Si 0.5 - 0.9
    Cr Max 0.03 Mn Max 0.03 Zn Max 0.1
    Cu Max 0.1 Other, each Max 0.03

    Material Notes:
    Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR
    DESIGN.

    Physical Properties Metric English Comments

    Density 2.69 g/cc 0.0972 lb/in³ AA; Typical

    Mechanical Properties

    Hardness, Brinell 90 90 500 kg load with 10 mm ball


    Hardness, Knoop 114 114 Converted from Brinell Hardness
    Value
    Hardness, Rockwell A 38.2 38.2 Converted from Brinell Hardness
    Value
    Hardness, Rockwell B 56 56 Converted from Brinell Hardness
    Value
    Hardness, Vickers 101 101 Converted from Brinell Hardness
    Value
    Tensile Strength, Ultimate 220 MPa 31900 psi
    Tensile Strength, Yield 195 MPa 28300 psi
    Elongation at Break 15 % 15 % In 5 cm; Sample 13mm diameter
    Modulus of Elasticity 69 GPa 10000 ksi Average of Tension and Compression.
    In Aluminum alloys, the compressive
    modulus is typically 2% greater than
    the tensile modulus. Estimated from
    trends in similar Al alloys.
    Poisson's Ratio 0.33 0.33 Estimated from trends in similar Al

    http://www.matweb.com/search/SpecificMaterialPrint.asp?bassnum=MA6201T6 5/30/2007
    MatWeb - Online Material Data Sheet Page 2 of 2

    alloys.
    Shear Modulus 26 GPa 3770 ksi Estimated from similar Al alloys.
    Shear Strength 135 MPa 19600 psi Calculated value.

    Electrical Properties

    Electrical Resistivity 3.2e-006 ohm-cm 3.2e-006 ohm-cm Estimated from other heat treatments.

    Thermal Properties

    CTE, linear 68°F 23.4 µm/m-°C 13 µin/in-°F AA; Typical; Average over 68-212°F
    range.
    CTE, linear 250°C 25.2 µm/m-°C 14 µin/in-°F Average over the range 20-300ºC
    Specific Heat Capacity 0.895 J/g-°C 0.214 BTU/lb-°F
    Thermal Conductivity 205 W/m-K 1420 BTU-in/hr-ft²-°F Estimated from other heat treatments.
    Melting Point 607 - 654 °C 1125 - 1210 °F AA; Typical range based on typical
    composition for wrought products 1/4
    inch thickness or greater; Eutectic
    melting can be completely eliminated
    by homogenization.
    Solidus 607 °C 1125 °F AA; Typical
    Liquidus 654 °C 1210 °F AA; Typical

    Processing Properties

    Solution Temperature 510 °C 950 °F


    Aging Temperature 149 °C 300 °F hold at temperature approximately 4 hr

    References are available for this material.

    Copyright 1996-2007 by Automation Creations, Inc. The information provided by MatWeb is intended for personal, non-commercial use. The
    contents, results, and technical data from this site may not be reproduced either electronically, photographically or substantively without
    permission from Automation Creations, Inc. No warranty, neither expressed nor implied, is given regarding the accuracy of this information. The
    user assumes all risk and liability in connection with the use of information from MatWeb.

    http://www.matweb.com/search/SpecificMaterialPrint.asp?bassnum=MA6201T6 5/30/2007

    You might also like