Latapoxy Sp-100

Latapoxy SP-100 is a grout used to fix spacers between tiles and grout tiles. It conforms to ANSI A118.3 and ISO 13007-4/EN13888 standards. The grout has strong bonding strength and compressive strength, is water cleanable, and resistant to chemicals. Installation should follow Laticrete's method statement. Laticrete supplies are manufactured by MYK LATICRETE India Pvt Ltd.

Uploaded by

RajuNSanaboina
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
98 views2 pages

Latapoxy Sp-100

Latapoxy SP-100 is a grout used to fix spacers between tiles and grout tiles. It conforms to ANSI A118.3 and ISO 13007-4/EN13888 standards. The grout has strong bonding strength and compressive strength, is water cleanable, and resistant to chemicals. Installation should follow Laticrete's method statement. Laticrete supplies are manufactured by MYK LATICRETE India Pvt Ltd.

Uploaded by

RajuNSanaboina
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

LATAPOXY SP-100

Providing and fixing spacer between tiles as per architecture requirement and grouting the same with
Latapoxy SP-100.
For detailed installation and laying procedure follow MYK LATICRETE Method Statement.
Laticrete products supplied shall be as Manufactured by MYK LATICRETE India Pvt Ltd.

Performance Properties SP 100:

Applicable Standards:

ANSI A118.3; ISO 13007 – 3 (RG) / EN 13888


ANSI Data
Property / Test Method Requirement Typical Values
Water cleanability: ANSI A118.3: >80 Minutes 90-120 Minutes
Clause 5.1
Initial Setting Time: ANSI A118.3: >120 Minutes 200 - 260 Minutes
Clause 5.2
Service Setting Time: ANSI A118.3: ≤ 7 Days 48 Hours – 72 Hours
Clause 5.2
Shrinkage after 7 days: ANSI A118.3: < 0.25% < 0.10%
Clause 5.3
Sag in Vertical Joints: ANSI A118.3: No change in Pass. No change in shape of joint
Clause 5.4 shape of joint
Bond strength to Quarry Tile: ANSI >1000 psi (6.87
A118.3: Clause 5.5 Mpa) >1100 psi (7.86 Mpa)

Compressive Strength after 7 days: >3500 psi (24.06 7500 – 8200 psi (51.56 – 56.37 Mpa)
ANSI A118.3: Clause 5.6 Mpa)
Tensile Strength after 7 days: ANSI >1000 psi (6.87 2300 – 2600 psi (15.81 – 17.87 Mpa)
A118.3: Clause 5.7) Mpa)
Thermal Shock ANSI A118.3: Clause >500 psi (3.43
5.8) Mpa) 1000 – 1100 psi (6.87 – 7.86 Mpa)

The grout mortar conforms to ANSI A 118.3


ISO / EN Data
Property / Test Method Requirement Typical Values

Abrasion resistance: ISO 13007 – ≤ 250 mm³ Pass


4: Clause 4.4; EN 12808 - 2
Flexural strength under standard
conditions: ISO 13007 – 4: Clause ≥ 30 N / mm² 38 - 40 N / mm²
4.1.3; EN 12808 - 3
Compressive Strength under
standard conditions: ISO 13007 – ≥ 45 N / mm² 55 – 57 N / mm²
4: Clause 4.1.4; EN 12808 – 4
Shrinkage: ISO 13007 – 4: Clause < 1.5mm / m 0.6 – 0.8 mm /m
4.3 : EN 12808 – 4
Water Absorption after 240
Minutes: ISO 13007 – 4: Clause ≤0.1 g 0.015 – 0.040 g
4.2; EN 12808 – 5
Chemical Resistance See Chemical resistance chart

The grout mortar conforms to ISO 13007 – 4 (RG) / EN 13888.

CHEMICAL RESISTANCE CHARTS: At 23° C


Acid Based Chemicals
Chemical Concentration PE IE SE
2.5% VG VG VG
Acetic Acid
5% G VG VG
• HCL 10% VG VG VG
20% VG VG VG
• H2SO4
50% P G G
• Formic Acid 2.5% VG VG VG
10% P P P
Nitric Acid 10% P G VG
Citric Acid 10% VG VG VG
Tartaric Acid 50% VG VG VG
Tannic Acid 50% VG VG VG
Benzoic Acid 5% VG VG VG
Oxalic Acid 10% VG VG VG

PE: Prolonged Exposure; IE: Intermittent Exposure: SE: Splash Exposure; P: Poor: G: Good;
VG: Very Good;