Nitomortar ECL constructive solutions

Epoxy cementitious sealing mortar

Uses Properties

A trowellable epoxy cementitious mortar with excellent The following properties were obtained at a temperature of
o
chemical and abrasion resistance for the protection of 25 C unless otherwise specified.
concrete and similar substrates. Ideal lining for outfalls,
sewage works, marine water and all similar structures Test method Typical result
which are in contact with chemical contaminants. Compressive strength:
2
(BS 6319, Part 2) 40 N/mm
2 0.5
Water absorption 0.03 kg/m .h
Advantages Coefficient ‘A’: (approximately)
-6 o
Coefficient of thermal 18.10 m/m per C
Excellent optimal pore sealer. expansion (approximately)
o
Pot life: 1 hour at 20 C
Unaffected by a wide range of acids, alkalis, sea water o
30 min. at 35 C
and sewage. o
Initial hardness: 24 hours at 20 C
o
Excellent resistance to abrasion and impact. Full cure: 7 days at 20 C
3
Fresh wet density: Approximately 1850 kg/m (full
Superior bond strength to virtually all substrates, dry or compacted)
damp. Chemical resistance: Good chemical resistance.
No need for primer on most concrete surfaces. The low permeability of
Nitomortar ECL retards
Early development of strength minimises disruption. chemical attack in aggressive
environments.
Cured material provides a long lasting waterproof Bond adhesion: Greater than concrete
barrier. cohesion.
2
It can be applied on fresh hardening concrete and on Normal result > 2 N/mm .
damp surfaces.
Pre-weighed components ensure consistency. Application clauses

Cured coating is yet water vapour permeable. Abrasion-resistant epoxy cementitious lining mortar

Nitomortar ECL, a three-component solvent-free epoxy

Description cementitious resin mortar with a density not greater than
3
1850 kg/m .
Nitomortar ECL is based on Ordinary Portland Cement,
fine fillers and high quality solvent-free epoxy resin system.
The special silica aggregates provide high strength and Application instructions
excellent abrasion resistance. Nitomortar ECL is a three-
component material supplied in pre-weighed quantities Preparation
ready for on-site mixing and use.
Clean the surface and remove any dust, unsound or
contaminated material, plaster, oil, paint, grease, corrosion
Technical support deposits or algae.
Fosroc offers a comprehensive range of high performance, Surface should preferably be prepared using high pressure
high quality construction products. In addition, the water jetting or light abrasive blasting, followed by thorough
company offers a technical support package to specifiers, washing to remove dust and remaining particles, grinding
end-users and contractors, as well as on-site technical using carborandum stone is an acceptable means of
assistance in locations all over the world. preparation.

Design criteria Oil and grease deposits should be removed by steam

cleaning, detergent scrubbing or the use of a proprietary
degreaser. The effectiveness of decontamination should
Nitomortar ECL can be applied in section up to 0.5 - 3.0
then be assessed by a pull-off test.
mm thickness in vertical and overhead locations in a single
application without the use of formwork. Greater
Prior to the application of Nitomortar ECL, all active
thicknesses than those specified can be achieved by
hydrostatic leaks must be stopped by using Renderoc Plug,
application of subsequent layers. Consult the local Fosroc
hydraulic cement specifically formulated to stop water
office for further information.

Page 1
Nitomortar ECL

ingress) or Nitofill WS60 and Nitofill UR63 expanding

polyurethane crack injection and water stop system. Finishing

Mixing Nitomortar ECL is finished by the use of a wood float and

closed with a steel trowel. The completed surface should
Care should be taken to ensure that Nitomortar ECL is not be overworked.
thoroughly mixed to produce a fully homogeneous
trowellable mortar. Important note: Do not use solvent to thin components or
to lubricate trowel as this will prevent proper cure.
Nitomortar ECL must be mixed by mechanical means. The
‘hardener’ and ‘base’ components must be stirred High temperature working
thoroughly to disperse any settlement before mixing them
o
together. The entire contents of the ‘hardener’ and ‘base’ At ambient temperatures above 35 C Nitomortar ECL will
components should then be emptied into a suitable, clean have shorter pot life and working life. The materials should
mixing drum and thoroughly mixed using a slow speed be stored in the shade or in air-conditioned environments
electric drill (350 to 500 rpm) fitted with an approved spiral and should not be applied in direct sunlight.
stirrer for approximately 5 minutes until a uniform colour
and gel-like consistency has been produced. Curing

While mixing continuously, the entire bag of aggregate Curing protection is not necessary for Nitomortar ECL.
should then be added slowly and the three components
blended together for a further 2 to 3 minutes, ensuring that
the aggregate is thoroughly wetted out with the mixed Cleaning
resin. Under no circumstances should part packs be used.
Nitomortar ECL should be removed from tools, equipment
Large quantities can be mixed in suitable forced action and mixers with Fosroc Solvent 102 immediately after use.
mixer (e.g. Cretangle or Pennine) but no more than can be
reasonably used within the pot life of the product should be Limitations
prepared at any one time.
Do not mix part packs under any circumstances.
Application Nitomortar ECL should not be exposed to moving water
during application. Expose to heavy rainfall prior to final set
Surface to be applied can be pre wetted to a saturated may result in surface scour. If any doubt arises concerning
surface dry condition (SSD) while ensuring no standing temperature or substrate condition, consult the local Fosroc
water. office.
Apply the mixed Nitomortar ECL to the prepared substrate
at a minimum thickness of 0.5 mm by spatula or steel float, Estimating
pressing firmly into place to ensure positive adhesion and
full compaction. Supply

Application thickness will vary with profile and alignment of Nitomortar ECL: 21 kg pack
substrate. Where necessary mortar should be built up in Fosroc Solvent 102: 4 and 25 litre pack
layers.
Coverage and yield
Build-up
Nitomortar ECL: 21 kg pack yield 11.35 litre per
Additional build-up can be achieved by application of pack and covers 11.35 m at
2

multiple layers. Where thicker sections are required, the 1.0 m thickness
surface of the intermediate applications should not be
closed, to provide a suitable surface for subsequent layers.
The application of additional layers should follow between
o
24 and 36 hours at 20 C after the first application. This
time should be reduced at higher temperature. Application
of Nitomortar ECL may then proceed.

constructive solutions Page 2

Nitomortar ECL

Storage Additional information

Shelf life Fosroc manufactures a wide range of complementary

products which include:
o
All products have a shelf life of 12 months at 30 C if kept in
a dry store in the original, unopened bags or packs. Waterproofing membranes & Waterstops
Joint sealants & filler boards
Storage conditions Cementitious & epoxy grouts
Specialized flooring materials
Store in dry conditions in the original, unopened bags or
packs. If stored at high temperatures and/or high humidity Fosroc additionally offers a comprehensive package of
conditions the shelf life may be reduced to 4 to 6 months. products specifically designed for the repair and
refurbishment of damaged concrete. Fosroc’s ‘Systematic
Precautions Approach’ to concrete repair features the following:

Health and safety Hand-placed repair mortars

Spray grade repair mortars
Fluid micro-concretes
Fosroc Solvent 102 is flammable. Nitomortar ECL and
Chemically resistant epoxy mortars
Fosroc Solvent 102 should not come into contact with the
Anti-carbonation/anti-chloride protective coatings
skin, eyes or be swallowed. When using Fosroc Solvent
Chemical and abrasion resistant coatings
102 ensure adequate ventilation and avoid inhalation of
vapour. Some people are sensitive to resins, hardeners
For further information on any of the above, please consult
and solvent. Wear suitable protective clothing, gloves, and
your local Fosroc office - as below.
eye protection. The use of barrier creams provides
additional skin protection. In case of contact with eyes,
rinse immediately with plenty of clean water and seek
medical attention immediately. If swallowed seek medical
attention immediately. Do not induce vomiting.

Fire

Nitomortar ECL is non-flammable. Fosroc Solvent 102 is

flammable. Keep away from sources of ignition. No
smoking. In the event of fire, extinguish with CO 2 or
foam. Do not use a water jet.

Flash Points
o
Fosroc Solvent 102: 33 C

For further information, refer to the Product Material Safety

Data Sheet.

constructive solutions Page 3

Nitomortar ECL

Important note:
Fosroc products are guaranteed against defective materials and manufacture and are sold subject to its standard Conditions for the
Supply of Goods and Services, copies of which may be obtained on request. Whilst Fosroc endeavours to ensure that any advice,
recommendation, specification of information it may give is accurate and correct, it cannot, because it has no direct or continuous
control over where or how its products are applied, accept any liability either directly or indirectly arising from the use of its products,
whether or not in accordance with any advice, specification, recommendation of information given by it.

Fosam Company Limited

Telephone: +966 2 637 5345 Fax: +966 2 637 5891 email: [email protected]
Head Office
Post Box 11081 Regional Offices
Jeddah Sales Office Tel: (02) 608 0999 Fax: (02) 638 0693 Yanbu Tel: (04) 322 4280 Fax: (04) 391 2980
Jeddah - 21453 Jeddah Showroom Tel: (02) 665 0187 Fax: (02) 667 4844 Makkah Tel: (02) 542 0869 Fax: (02) 542 0869
Saudi Arabia Riyadh Tel: (01) 482 9303 Fax: (01) 482 7562 Medinah Tel: (04) 855 0091 Fax: (04) 855 0047
Dammam Tel: (03) 814 1282 Fax: (03) 814 1581 Jubail Tel: (03) 362 3904 Fax: (03) 362 3875

www.fosroc.com
Khamis Mushayt Tel: (07) 250 0469 Fax: (07) 250 0469 CSD Tel (02) 608 0999 Fax (02) 638 0693
Registered Office: Industrial Area, Phase 4, Road No. 414, Street No. 407
Page 4 FO SA/NITOMORTAR ECL/09/05/07/A