00-P-41 6F

i“October 1991
SUPERSEDING
~-P-416E
18 Aprtl 1986

FEDERAL SPECIFICATION

PLATING, CADMIUM (ELECTRODEPOSITED)

This specification has been approved by the

Commissioner, Federal Supply Service, General Services
Adminlstratlon, for use by all Federal Agencies.

1. SCOPE AND CLASSIFICATION

1.1 Scope. This specification covers the requirements for electro-

deposited cadmium platlng.

1.2 Classification. Cadmium plating shall be of the following types and

classes, as specified (see 6.2):

1.2.1 Types.

I - As plated
II - With supplementary chromate treatment (see 3.2.9.1)
111 - With supplementary phosphate treatment (see 3.2.9.2)

1.2.2 Classes.

1- 0.00050 inch minimum

2- 0.00030 inch minimum
3- 0.00020 Inch mlnlmum

2. APPLICABLE DOCUMENTS

2.1 Government documents.

2.1.1 Specifications and standards. The following specifications and

standards form a part of this document to the extent specified here~n. Unless
otherwise specified, the issues of these documents are those listed in the
issue of the Department of Defense Index of Specifications and Standards
(0001SS) and supplement thereto, cited in the solicitation (see 6.2).

Beneficial comments (recommendations, additions, deletions) and any pertinent

data which may be of use In improving this document should be addressed to:
Naval Air Engineering Center, Systems Engineering and Standardization
Department (Code 5312), Lakehurst, NJ 08733-5100, by using the attached
Standardization Document Improvement Proposal (DD Form 1426), or by letter.

AhiSC N/A AREA MFFP

OISTRIEHJTION STATEMENT A. Approved for public t-elease; distribution is unlimited,

Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z

Check the source to verify that this is the current version before use.
 QQ-P-416F

SPECIFICATIONS

FEDERAL

TT-C-490 - Cleaning Methods For Ferrous Surfaces and

Pretreatments For Organic Coatings

MILITARY

MIL-S-5000 - Steel, Chrome-Nickel-Molybdenum, (E4340), Bars

and Reforging Stock
MIL-S-5002 - Surface Treatments and Inorganic Coatings for
Metal Surfaces of Heapons Systems
MIL-S-8844 - Steel Bars, Reforging Stock, and Mechanical
Tubing, LOW Alloy, Premium Quallty
MIL-C-81562 - Coating, Cadmium, Tin Cadmium and Zinc
(Mechanically Deposited)

STANDARDS

FEDERAL

FED-STD-151 - Metals; Test Methods

t41LITARY

MIL-STD-105 Sampling Procedure and Tables for Inspection

by Attributes
MIL-STD-1312-1 Fastener Test Methods - Method 1, Salt Spray
MIL-STD- 312-5 Fastener Test Methods - Method 5, Stress
Durability
MIL-STD- 312-12 Fastener Test Methods - Method 12, Thickness of
Metallic Coatings
MIL-STD- 312-14 Fastener Test Methods - Method 14, Stress
Durability (Internally Threaded Fasteners)

(Unless otherwise indicated, copies of federal and military specifica-

tions and standards are available fr&n the Standardization Documents Order
Desk, Building 4D, 700 Robblns Avenue, Philadelphia, PA 19111-5094.)

2.2 Non-Government publications. The following documents form a part of

this document to the extent specified herein. Unless otherwise specified,
the issues of the documents which are DoD adopted are those listed in the
issue of the DODISS cited in the solicitation. Unless otherwise specified,
the issues of documents not listed in the DODISS are the issues of the
documents cited in the solicitation (see 6.2).

AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM)

ASTM 8117 - Salt Spray (Fog) Testing

ASTM 6244 - Measurement of Thickness of Anodic Coatings on Alum~num and
of other Nonconductive Coatings on Nonmagnetic Basis Metals
with Eddy-Current Instruments
ASTM 6487 - Measurement of Metal and Oxide Coating Thicknesses by
Microscopical Examination of a Cross Section

Source: http://www.assistdocs.com
7 -- Downloaded: 2008-08-01T13:20Z
Check the source to verify thatLthis is the current version before use.
 (& P-416F

ASTM 8499 - Measurement of Coating Thicknesses by the Magnetic

Method: Nonmagnetic Coatings on Magnetic Basis Metals
ASTM 8504 - Measurement of Thickness of Metallic Coatings by the
Coulometric Method
ASTM B567 - Measurement of Coating Thickness by the Beta Backscatter
Method
ASTM B568 - Measurement of Coating Thickness by X-Ray Spectrometry
ASTM E8 - Tension Testing of Metallfc Mater~als

(Application for copies should be addressed to the American Society for

Testing and Materials (ASTM), 1916 Race Street, Philadelphia, PA 19103-1187. )

(Non-Government standards and other publications are normally available

from the organizations that prepare or distribute the documents. These
documents also may be available in or through ltbrarles or other Informational
services.)

2.3 Order of precedence. In the event of a conflict between the text of

this document and the references cited herein, the text of this document takes
precedence. Nothing In this document, however, supersedes applicable laws and
regulations unless a specific exemption has been obtained.

3. REQUIREMENTS

3.1 Materials. The materials used shall be such as to produce platings

which meet the requirements of this specification.

3.2 General requirements.

3.2.1 High tensile strength parts. Unless otherwise specified (see 6.2),
parts having an ultimate tensile strength of greater than 200 ksi (or ttRC 43)
shall not be plated in accordance with this specification.

3.2.2 Stress relief treatment. Unless otherwise specified (see 6.2),

parts which have been machined, ground, cold formed, or cold straightened
after heat treatment, shall receive a stress relief treatment in accordance
with Table I or Table IA, as applicable, prior to shot peening, cleaning, and
plating for the relief of damaging residual tensile stresses. For fastener
hardware, cold working of the head-to-shank fillet radius and thread rolling
after heat treat produce compressive stresses and a stress relief treatment
is not required on parts thus affected.

3.2.3 Cleaning. Unless otherwise specified (see 6.2), all parts shall
be cleaned in accordance with MIL-S-5002. Fasteners heat treated to 160 ksi
(or HRC 36) or above, shall be cleaned in accordance with MIL-S-5002 and the
following:

a. Abrasive cleaning shall be used for removal of heat treat scale

and oxidation as applicable (pickling Is not permitted).

b. Alkaline cleaning shall be used as applicable with anodic

(reverse) current or no current. Cathodic (direct) current
cleanlng with the part serving as the cathode shall not be
used.

Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z

Check the source to verify that this is the current version before use.
 QQ-P-416F

c. A clean water rinse shall be used as applicable following each

cleaning or plating operation.

3.2.4 Plating application. Unless otherwise specified (see 6.2), the

plating sha’ I be applied after all basis metal heat treatments and mechanical
operations, such as machining, brazing, welding, forming, and perforating of
the article, have been completed.

3.2.S Underplaying. Unless otherwise specified (see 6.2), cadm~um shall

be depositec directly on the basis metal without a preliminary plating of other
metal, except in the case of parts made of corrosion resistant alloys on which
a preliminary plating of nickel or copper may be necessary, or on parts made
of aluminum on which a preliminary treatment, such as the zincate process, may
be necessary.

3.2.6 Coverage. Unless otherwise specified (see 6.2), the plating shall
cover all surfaces as stated In 3.3.1, including roots of threads, corners,
and recesses.

3.2.7 Luster. Unless otherwise specified in the engineering drawing or

procurement specification (or in 3.2.7.1), the use of brightening agents, or
other additives which produce brightened deposits, in the plating solution is
prohibited on components with an ultimate tensile strength of 160 ksi (or iiRC
36) or higher. Either a bright (not caused by brightening agents) or dull
luster shall be acceptable (see 6.2).

3.2.7.1 Use of brighteners with bearings. Unless otherwise specified in

the engineering drawing or procurement specification: the use of brighteners
is permitted for annular bearings. For rod end bearing bodies, track roller
studs, and end washers of needle track roller bearings, the amount of brighten-
er added to the plating bath shall be limited to 20% of the normal charge.

3.2.8 Hydrogen embrittlement relief treatment. Unless otherwise

specified in the contract or order (see 6.2), or stated in the end product
specification or drawing, all parts shall be baked within 4 hours after the
plating operation is completed as specified in Table I or Table IA, as
applicable. Plated springs and other parts subject to flexure shall not be
flexed prior to hydrogen embrittlement relief treatment. In the case of Types
II and 111 treated parts which require baking, the baking treatment shall be
done prior to the application of the supplementary coatings. Cadmium plated
surfaces passivated as a result of the baking operation shall be reactivated
prior to receiving the Type II supplementary chromate treatment (see 6.S).

3.2.9 Supplementary treatments. Unless otherwise specified in the

contract or order (see 6.2), the cadmium plating shall be Type II on parts
that will not subsequently be completely coated and Type III on parts that
will subsequently be completely coated (see 6.1.2 and 6.1-3).

3.2.9.1 Chromate treatment. Unless otherwise specified in the contract

or order (see 6.2), the chromate treatment requ~red for conversion to Type II
shall be a treatment in or with an aqueous solution of salts, acids, or both,
to produce a continuous smooth, distinct protective film, distinctly colored
iridescent bronze to brown includ~ng olive drab, yellow, and forest green.
The articles so treated shall be throughly rinsed and dried in accordance with
the requirements of the process used. Usual chromic and nitric acid bright
dips for cadmium are not chromate treatments.

4
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that this is the current version before use.
 QQ-P-41 6F

3.2.9.2 Phosphate treatment. Unless otherwise specified in the con-

tract or order (see 6.2), the phosphate treatment required for conversion to
Type III shall produce a tightly adherent film conforming to Type I of
TT-C-490.

3.3 Detail requirements.

3.3.1 Thickness of plating. Unless otherwise specified (see 6.2), the

minimum thicknesses of cadmium plating shall be as specified for each class in
Table II. If not specified, the maximum shall be the minimum plus 0.0003
inch. Hhen a class is not specified, it shall be Class 2, For Types 11 and
III, the minimum cadmium thickness requirements shall be met after the
supplementary treatment. Internal surfaces, including parts with internal
threads, shall not be subject to thickness requirements due to processing
limitations that may result in incomplete coverage. When corrosion protection
is required on Internal surfaces, the method of protection shall be specified
(see 6.1.1 .1.2 and 6.2).

3.3.2 Adhesion. The adhesion of the plating shall be such that when
examined at a magnification of 4 to 10 diameters, the plating shall not show
separation from the basis metal nor from any underplaying at the interface,
nor shall any underplate show separation from the basis metal at the interface
when subjected to the tests described in 4.6.2 and Table III. The interface
between the underplate and the basis metal is the surface before plating. The
formation of cracks in the plating caused by rupture of the basis metal, the
underplate or combination of both which do not result in flaklng, peeling or
blistering of the plating shall not be considered as nonconformance to this
requirement.

3.3.3 Corrosion resistance. Type 11 areas required to be covered (see

3.3.1) shall not show white corrosion products of cadmium, pitting, or basis
metal corrosion products at the end of 96 hours when tested by continuous
exposure to the salt spray in accordance with 4.6.3 and Table III. The
appearance of corrosion products visible to the unaided eye shall be cause for
rejection, except that white corrosion products at the edges of specimens (see
4.5.2) shall not constitute failure.

3.3.4 Hydrogen embritt?ement relief test. Unless otherwise specified,

hydrogen embrittlement testing is required for parts heat treated to 160 ksi
(or HRC 36) or above, but is not required for bearings, except rod end bearing
bodies, track roller bearing studs, and end washers on needle track roller
bearings. Unless otherwise specified In the product specification or drawing,
testing shall be in accordance with 4.6.4 as specified in 4.4.2.3 and 4.4.3.
Rod end bearing bodies, track roller bearing studs and end washers of needle
track roller bearings shall be tested as specified in 4.6.4.3. There shall be
no cracking or fracture of the plated parts or the prepared test specimens.

3.4 Environmental requirements. All cadmium plating facilities and

equipment shall comply with EPA and Federal, State, and local guide~~nes
(see 6.6).

3.5 blorkmanship.

3.5.1 Basis metal. The basis metal shall be free from visible defects
that will be detrimental to the appearance or protective value of the plating.

5
.-
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that this is the current version before use.
 QQ-P-416F

3.5.2 Appearance. The cadre urnplating shall be smooth, adherent, uniform

in appearance. free fTom blisters pits, nodules, burning, and other defect.
The plating shall show no indicat on of contamination or improper operation of
equipment used to produce the cadmium deposit, such as excessively powdered or
darkened plating. Superficial staining, which has been demonstrated as
resulting from rinsing, or slight discoloration resulting from any drying or
baking operations as specified shall not be cause for rejection.

4. QUALITY ASSURANCE PROVISIONS

4.1 Responsibility for inspection. Unless otherwise specified in the

contract or purchase order, the contractor is responsible for the performance
of all inspection requirements (examinations and tests) as specified herein.
Except as otherwise speclfled In the contract or purchase order, the con-
tractor may use his own or any other facilities suitable for the performance
of the inspection requirements specified herein, unless disapproved by the
Government. The Government reserves the right to perform any of the
inspections set forth in this specification where such inspections are deemed
necessary to ensure supplies and services conform to prescribed requirements.

4.1.1 Responsibility for compliance. All items shall meet all

requirements of sections 3 and 5. The inspection set forth in this
specification shall become a part of the contractor’s overall inspection
system or quality program. The absence of any inspection requirements in the
specification shall not relieve the contractor of the responsibility of
ensuring that all products or supplies submitted to the Government for
acceptance comply with all requirements of the contract. Sampling inspection,
as part of manufacturing operations, is an acceptable practice to ascertain
conformance to requirements, however, this does not authorize submission of
known defective material, either indicated or actual, nor does it commit the
Government to accept defective material.

4.2 Classification of inspections. The inspection requirements specified

herein are classified as quality conformance inspections and tests (see 4.4).

4.3 Inspection conditions. All inspections shall be performed in

accordance with the test conditions specified in the applicable test method or
applicable paragraph in this specification.

4.4 Quality conformance inspection and tests. The quality conformance

inspection shall consist of the following:

a. Process control inspection (4.4.1)

b. Lot sampling inspection (4.4.2)
c. Production control testing (4.4.3)

4.4.1 Process control inspection.

4.4.1.1 Control records. The processor shall maintain a record of the

history of each processing bath, showing all additions of chemicals or
treatment solutions to the unit, and the results of all chemical analyses
performed. Upon request of the acquisition activity or government inspector,
such records, as well as reports of the test results, shall be made avail-
able, These records shall be maintained for not less than one year after
completion of the contract or purchase order.
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that 6this is the current version before use.
 QQ-P-416F

4.4.2 Lot sampling inspection. The lot samp’ ing inspection shall
consist of the examinations and tests specified in 4.4.2.2. When specified in
the contract or order (see 6.2), hydrogen embrittl( ment testing shall be
conducted as specified in 4.4.2.3.- -

4.4.2.1 @t: A lot shall consist of plated articles of the same basis
metal composition, class, and type plated and treated under the same conditions
and submitted for InspectIon at one time.

4.4.2.2 Sampling for visual examination and thickness of plating.

Sampling for visual examination and thickness of plating tests shall be con-
ducted. - A sample of plated parts or articles, except for those barrel
plated, shall be taken at random from each lot, the number of articles in
. accordance with MIL-STD-105, inspection Level II with an acceptable quality
level (AQL) of 1.5 percent defective, or as indicated in Table IV. The
sampllng chosen shall be the option of the plater. Barrel plated parts or
articles shall be sampled in accordance with inspection level S-3 of
MIL-STD-105 with an AQL of 4.0 percent defective. The lot shall be accepted
or rejected according to the procedures in 4.4.2.2.1 for visual examination
and 4.4.2.2.2 for plating thickness.

4.4.2.2.1 Visual examination. Samples selected in accordance with

4.4.2.2 shall be examined for compliance with requirements of 3.5.2 after
plating. If the number of nonconforming items exceeds the acceptance number
for the sample, the lot represented by the sample shall be rejected. Separate
specimens (4.5) shall not be used for visual examination tests.

4.4.2.2.2 Thickness of plating. Samples selected in accordance with

4.4.2.2 shall be inspected and the plating thickness measured by the
applicable test detailed fn 4.6.1 at several Iocatlons on each article in
order to ensure compliance with the requirements of 3.3.1. Measurements on
fastener hardware shall be made at locations defined in MIL-STD-1312-12.
The part or article shall be considered nonconforming if one or more
measurements fall to meet the specif~ed minimum thickness. If the number of
defective items in any sample exceeds the acceptance number for the specified
sample, the lot represented by the sample shall be rejected. Separate
specimens (4.5) shall not be used for thickness measurements.

4.4.2.3 Hydrogen Embrittlement Relief Test (Lot Testing). When

specified in the contract or order (see 6.2), hydrogen embrlttlement testtng
shall be performed on each lot. Sampling shall be as specified (see 6.2).
Unless otherwise specified, the test method shall be in accordance with
4.6.4.

4.4.3 Production Control Tests. Unless otherwise specified, production

control tests shall consist of all the tests specified in Table III. If
hydrogen embrittlement relief testing is performed on each iot (4.4.2.3) and
the lot size is such that the frequency of testing is greater than that
detailed In 4.4.3.2, the production control test for hydrogen embrittlement
may be waived.

4.4.3.1 Sampling for production control tests. Four plated parts or

prepared test specimens (4.5) for each of the required tests specified in
Table 111 shall be sampled from production at the times specified in 4.Ll.3.?.

Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z

Check the source to verify that this is the current version before use.
 QQ-P-416F

4.4.3.2 Frequency of tests, The production control test schedule shall

be as follows:

a. The first products or specimens plated at start of first,

second and third week of production shall be tested.

b. The first products or specimens plated at start of fifth and

seventh week of production and then at the start of production
every four weeks thereafter shall be tested.

c. Any failure shall immediately halt production. All parts

produced since the last acceptable test shall be considered
suspect. The reason for failure shall be determined and
corrected before production resumes. The lots of platings
produced using the faulty procedure or material shall not
be acceptable.

4.4.3.3 Procedure for follow on contracts. When a processor is in

continuous production of plating from contract to contract; and there have
been no failures in production control tests, the processor may continue
testing at his current frequency of test level to start the new contract

4.5 Separate specimen preparation. ilhen the plated articles are of such
form, shape, size, or value as to prohibit use thereof, or are not readi’ Y
adaptable to a test specified herein. or when destructive tests of small lot
sizes are required, the test shall be made by the use of separate specimens
plated concurrently with the articles represented. The specimens shall be as
specified in 4.5.1, 4.5.2, 4.5.3, and Table III and shall be distributed such
that the tests are performed on each plating bath. When it is impractical to
forge separate test specimens, hot-rolled steel specimens may be used to
represent forged steel articles. Hhen ferrous alloy castings are being
plated, the separate specimens may be cut from scrap castings.

4.5.1 Specimens for adhesion tests. If separate specimens for ad-

hesion tests are required, they shall be strips approximately 1 inch wide,
4 inches long, and 0.04 inch thick.

4.5.2 Specimens for corrosion resistance tests. If separate specimens

for corrosion resistance test are required, they shall be panels not less than
6 inches In length, 4 tnches In width, and approximately O.04 inch thick.

4.5.3 Specimens for embrittlement relief test. Separate specimens for

the embrittlement relief test shall be four round notched specimens, one or
more heats of alloy steel 4340 conforming to MIL-S-5000 or MIL-S-8844, Class
i, or the same material as the part being represented, heat treated to the
same tensile strength or higher than the parts represented. The configuration
shall be in accordance with Figure 8 of ASTM E8 for rounded specimens.
Specimens shall have a 60 degree V-notch located approximately at the center
of the gage length. The cross section area at the root of the vee shall be
approximately equal to half the area of the full cross section area of the
specimen’s reduced section. The vee shall have a 0.010 ~ 0.0005 inch radius
of curvature at the base of the notch. Specimens plated with the part lot to
represent the parts for testing purposes shall be prepared so that the load is
applied in the longitudinal grain direction.

Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z

Check the source to verify that this is the current version before use.
 QQ-P-416F

4.6 Tests.

4.6.1 Thickness (Lot by lot inspection). For nondestructive measuring

of Dlating thickness. procedures in accordance with FED-STD-151, method 520
(electronic test), ASTM 6499 (magnetic test), ASTM B244 (eddy current), ASTM
6567 (test by beta radiation backscatter principle) or ASTM 6568 (X-ray
spectrometry) shall be used. For destructive measuring of plating thickness,
procedures In accordance with ASTM 6487 (microscopic) or ASTM 6504
(coulometric) shall be used. In addition to the above, the other procedures
embodied in MIL-STD-1312-12 may be used for thickness measurement of
plating fastener hardware. Thickness measurements of cadmium platings, Types
II and III, shall be made after application of the supplementary treatments.
Nhen the coulometric test is used, the supplementary treatment shall be
removed prior to testing. The chromate film may be removed from the Type II
coating by using a very mild abrasive (a paste of levigated alumina rubbed on
with the finger). The phosphate coating may be removed from the Type 111
coating by immersing the specimen in a 10 percent solution of NaOH and
scrubbing with a rubber policeman (usually takes from 10 to 15 minutes).

4.6.2 Adhesion (Production control test). Adhesion shall be determined

by scraping the surface or shearing with a sharp edge, knife, or razor through
the plating to the basis metal and examining at four to ten diameters magnifi-
cation for evidence of non-adhesion. Alternately, the article or specimen may
be clamped in a vise and the projecting portion bent back and forth until
rupture of the basis metal and/or plating occurs. If the edge of the ruptured
plating can be peeled back or if separation between the plating and basis
metal can be seen at the point of rupture when examined at four diameter
magnification, adhesion is not satisfactory. If adhesion is not satisfactory.
the pre-plating, cleaning, and plating pro~esses, as well as the materials, ‘-
sha’ 1 be evaluated and the cause of failure eliminated.

4.6.3 Corrosion resistance (Production control test). Corrosion

res stance shall be conducted in accordance with ASTM B117 (salt sDrav test)
for 96 hours or, for fastener hardware, in accordance with MIL-STD~1312-l.
To \ecure uniformity of results, Type 11 supplementary coatings shall be aged
at room temperature for 24 hours minimum before subjection to-the salt spray.

4.6.4 Hydrogen embrittlement relief test.

4.6.4.1 Specimens. Specimens (4.5.3) plated with the parts lot shall
have the same supplementary treatment as the parts and shall be subjected to a
sustained tensile load equal to 75 percent of the notched ultimate tensile
strength of the material. The specimens shall be subjected to the sustained
load for not less than 200 hours, then examined for compliance with 3.3.4.

4.6.4.2 Fasteners. Externally threaded or grooved fasteners which can

be loaded in tension by an axial application of a load up to 20,000 pounds or
reasonable load limits of test equipment, shall be tested as specified in
MIL-STD-1312-5. When the load requirement is greater than the reasonable
limits of the test equipment, the notched specimen procedure (4.6.4.1) shall
be used. Internally threaded fasteners shall be tested as specified in
MIL-STD-1312-14. The minimum test load shall be 85 percent of the minimum
ultimate tension load specified in the end product specification. The load
shall be sustained for not less than 72 hours. The fasteners shall be
examined for conformance to 3-3.4.

9
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that this is the current version before use.
 QQ-P-416F

4.6.4.3 Bearings. Test pieces for rod end bearing bodies, track roller
bearing studs, and end washers of needle track roller bearings shall be either
the plated bearing component or notched specimens, at the option of the
bearing manufacturer. Notched specimens shall conform to 4.5.3 and shall be
plated with the bearing parts lot they represent. They shall be subjected to
a sustained tensile load equal to 75 percent of Its notched ultimate tensile
strength. The bearing component shall be loaded in tension to produce a
stress level of 75 percent of its ultimate tensile strength. Loads shall be
maintained for not less than 72 hours and specimens or bearings shall be
examined for compliance with 3.3.4. At the bearing manufacturer’s option,
end washers may be tested simultaneously with the needle bearing track roller
stud.

4.6.4.4 Other parts or articles. Parts such as spring pins, lock rings,
etc., which are installed in holes or rods, shall be similarly assembled using
the applicable parts specifications or drawing tolerances which impose the
maximum sustained load on the plated part. The articles or parts shall be
subjected to the sustained load for not less than 200 hours then examined for
conformance to 3.3.4.

5. PACKAGING (This section Is not applicable to this specification. )

6. NOTES

(This section contains information of a general or explanatory nature

that may be helpful, but is not mandatory.)

6.1 Intended use.

6.1.1 General usage. The electrodeposited cadmium platings covered by

this specification are intended for use as corrosion protective coatings.
Processes used for cleaning and cadmium deposition on” parts heat-treat~d to,
or having ultimate tensile strength of 160 ksi (or HRC 36) or greater, should
be such that hydrogen embrlttlement is minimized.

6.1.1.1 Limitations.

6.1 .1.1.1 Temperatures. Cadmium plating should not be used on parts for
space applications or on parts which in service reach a temperature of 450”F
(232”C) or higher or come in contact with other parts which reach those
temperatures. Cadmium plating should not be used on titanium parts, and
cadmium plated parts should not be used in contact with titanium parts.

6.1 .1.1.2 Plating of internal diameters. Hhen process limitations will

not allow cadmium to be deposited on internal diameters that require corrosion
protection, an alternate method of protection should be specified in a drawing
or acquisition document.

6.1.1.2 Mechanical deposition. To avoid problems of hydrogen embrittle-

ment on hardened steel parts, such as chains and springs, it may be helpful to
use the mechanical deposition method of cadmium plating. (This process is
covered in MIL-C-81562 and ASTM 8696.)

10
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
—
Check the source to verify that this is the current version before use.
 QQ-P-416F

6.1.2 Type II treatment. The prime purpose of chromate finishes (Type

II) on electrodeposited cadmium platings is to retard or prevent the formation
of white corrosion products on surfaces exposed to stagnant water, high
humidity atmospheres, salt water, marine atmospheres, or cyclic condensation
and drying. Type II treatments are preferred for parts that will not sub-
sequently be completely coated.

6.1.2.1 Type 11 temperature llmltatlons. Chromate treatments (Type II)

should not be used on plated parts that will not be coated and which will be
continuously exposed to temperatures in excess of 150”F (66”C) or inter-
mittently exposed for short periods to temperatures of approximately 300”F
(149”C) or nmre. However, these treatments may be used to prevent finger
marking and corrosion which may occur at room temperature during assembly and
storage.

6.1.2.2 Type 11 handling precautlon. Chromate treatments (Type II),

which involve only dipping in chemical soluttons, normally require a suffic ent
per~od of drying, approximately 24 hours at 70°F to 90°F (21eC to 32”C), to
render the parts suitable for handlinq without damaqe to the coating while n
gelatinous forms; and it is important-with such coa~ings that the workmanship
be such that the coating is not excessively damaged while wet. Type 11
platings should be dry for 24 hours before painting.

6.1.3 Type 111 treatment. The prime purpose of phosphate finishes (Type
III) on electrodeposited cadmium platings is to form a coating base. Because
of the enhanced adhesion properties, phosphate finishes are preferred for
parts that wI1l subsequently be completely coated.

6.2 Acquisition requirements. Acquisition documents must specify the

following:
a. Title, number, and date of the specification
b. Type and class required (see 1.2, 3.2.9, and 3.3.1)
c. Issue of DODISS to be cited in the solicitation,
and if required, the specific issue of individual
documents referenced (see 2.1 and 2.2)
d- 14hen plating is to be applied and areas to be
covered, If other than specified (see 3.2.1,
3.2.4, 3.2.6 and 3.3.1)
e. Stress relief treatment, if other than speci-
fied (see 3.2.2)
f. Cleaningof steel, if other than specified
(see 3.2.3)
9. Underplatlng required, if other than specified
(see 3.2.5)
h. Luster required, if other than spectfied (see 3.2.7)
i. Hydrogen embrittlement relief treatment, if other
than specified (see 3.2.8)
j. Type of chromate treatment required for conversion
to Type II, if other than specified - for example,
colorless (see 3.2.9.1)
k. Type of phosphate treatment requtred for conversion
to Type III, if other than specified (see 3.2.9.2)
1. Thickness of plating, if other than specified (see 3.3.1)
m. Lot Hydrogen Embrittlement testing if required (see 4.4.2)
and sampling (see 4.4.2.3)

11
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that this is the current version before use.
 QQ-P-416F

6.3 Consideration of data requirements. The following data requirements

should be considered when this specification is applied on a contract. The
applicable Data Item Descriptions (DID’s) should be reviewed in conjunction
with the specific acquisition to ensure that only essential data are requested/
provided and that the DID’s are tailored to reflect the requirements for the
specific acquisition. To ensure correct contractual application of the data
requirements, a Contract Data Requirements List (DD Form 1423) must be pre-
pared to obtain the data, except where DOD FAR Supplement 27.475-1 exempts the
requirement for a DD Form 1423.

Reference Paragraph DID Number DID Title

4.4.1.1 DI-MISC-80653 Test Reports

The above DID’s were those cleared as of the date of this specification. The
current issue of 000 501O.12-L, Acquisition Management Systems and Data
Requirements Control List (AMSOL), must be researched to ensure that only
current, cleared DID’s are cited on the 00 Form 1423.

6.4 Stress relief. There Is a hazard that hardened and tempered cold-
worked or cold-straightened steel parts may crack during cleaning and plating.
Such parts should have a suitable heat treatment for stress rellef prior to
cleaning and plating (see 3.2.2).

6.5 Reactivation. Surfaces of cadmium plating intended for conversion

to Type II and which have become passive as a result of the baking operation
may be reactivated by brief immersion in dilute acid. For example, If the
chromatlng solution is acidified with sulfurlc acid, then the reactivating
solution should be 1 part sulfuric acid (sp. gr. 1.83) by volume added to 99
parts water, or if the chromating solutlon is acidified with hydrochloric
acid, then the activating solution should be 1 part hydrochloric acid (sp, gr.
1.16) by volume added to 99 parts water. The duration of immersion should be
as brief as is consistent of the nature of the work. For example, a per-
forated container of barrel-plated parts would be expected to be reactivated
in approximately 15 seconds and separately racked items in approximately 5
seconds. The surfaces should be reactivated as soon as possible following
baking operation and should be handled carefully to avoid contamination by
dirt or grease.

6.6 Toxicity. Cadmium, because of its toxicity, should not be employed

as a plating for any object intended for use as a food container, cooking
utensil, or for any object likely to come in contact with food. Cadmium plated
sheets and any other structural shapes which may be subjected to heat from
welding, brazing or soldering operations should be so labeled because of the
danger from poisonous vapors during operations.

6.6.1 Alternative Coatings. Because of the hazards involved with

cadmium use, alternative coatings should be considered when possible. The
advantages and disadvantages of substitution should be carefully examined for
each unique application. Some possible alternative coattngs are:

Aluminum (vapor deposition) Zinc (electrodeposi tion; mechanical

Cd-Ti (electrodeposltlon) plating; diffusion)
Lead (electrodeposi tion) Zn-Cd (electrodeposi tion)
Nickel (electroless Zn-Ni (electrodeposi tion)
deposition) Acrylic (spray; brush)
Source: http://www.assistdocs.com
1’) -- Downloaded: 2008-08-01T13:20Z
ILthis is the current version before use.
Check the source to verify that
 QQ-P-416F

Ni-Cd (electrodepositlon) Epoxy (spray; brush; electro-

Tin (mechanical plating; static spray)
electroless deposition) Fluorocarbons (dip; spray; electro-
Sri-Cd (electrodeposition; static spray; fuse)
mechanical plating) Nylon (fluidized bed; electrostatic
Sn-Ni (electrodeposition) spray; fuse)
Sn-Zn (electrodeposition; Polyester (electrostatic spray)
mechanical plating) Polyurethane (spray; brush)

6.7 Packaging” llmitatlons. Cadmium plated articles should not be packed

in non-ventilated containers, either together or in contact with electrical
equipment, because of the danger of deleterious effect on cadmium plating from
unstable organic electrical insulation. In addition toorganlc electrical
insulation, phenolic resinous substances and others containing unsaturated
carbon-to-carbon linkages, such as oil, paint and impregnated paper, etc.,
cause an abnormal attack on cadmium by setting free, in the presence of
moisture, formic acid, butyric acid, etc. Corrosion of cadmium coatings and
steel basis metal has been noted when cadmium plated articles have been
packaged in direct contact with container materials such as wood or cardboard.
Corrosion has been especially severe if the container materials have become
wet or have been stored under conditions of high humidity.

6.8 Subject term (key word) listing.

Bearings
Chromate
Corrosion Resistance
Embrittlement Relief
Fasteners
Hydrogen Embrittlement
Phosphate
Supplementary Treatments
Toxic
Vapors, poisonous

6.9 Chanqes from previous issue. Asterisks are not used in this revi-
sion to identify changes with respect to the previous issue due to the exten-
siveness of the changes.

13
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that this is the current version before use.
 ——

!!
-w
u
w
m

Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z

Check the source to verify that this is the current version before use.
 K)-P-416F

en

n n I
00 Lv LLu
me em ● 0
mJ - me me
ti - mJ - c
(e
** I +4+4
+
L(J u-v e
● 0
‘m‘o mo u
r--~ f-m w
u m.
w
I w

VI

1%1

m “E

u++ +++4
u-v
*O
lno
l-m
m.
w w w

n n

Uk?:
s 0
u td i-n
c Om
m -w
Zwz
>@
00
Wow
-b -mm

15
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that this is the current version before use.
 w-P-41 6 F

TABLE II. Platinq Thickness

Minimum Thickness ~/

For external surfaces which For external surfaces which

Class can be touched by a ball can not be touched by a
0.75 inch in diameter ball 0.75 inch in diameter

inch micrometers inch micrometers

(approximate) (approximate)

1 0.00050 13 0.00030 8
2 0.00030 8 0.00020 5
3 0.00020 5 0.00015 4

~/ 0.001 inch = 1 mil = 25.4 micrometers (microns)

TABLE III. Production control tests and specimens 2/

.. ..——-_— —

Reference Paragraph

Specimen Test
Requirement Preparation Method
--..— .—. .... .

Adhesion 3.3,2 4.5 and 4.6.2

4.5.1 ~/

Corrosion resistance 3.3.3 4.5 and 4.6.3

4.5.2 ~/

Hydrogen embrittlement 3.3.4 4.5 and 4.6.4

4.5.3

1/ Standard alloy steel shall be used for production control specimens.

Alloy steels such as AISI or SAE number 4130 heat treated to the same
tensile strength or higher than the parts being represented shall be used.

gl Tests are for all types, except for corrosion resistance which is for
Type II only.

Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z

Check the source to verify that. ,-
this is the current version before use.
 QQ-P-416 3?

TABLE IV. Sampling for visual examination and nondestructive tests.

—.
Acceptance number
Number of items Number of items (maximum number of
in lot in samples sample items noncon-
(randomly selected) ~/ forming to any test)

15 or less 7 0
16 to40 10 0
41 to 110 15 0
111 to300 25 1
301 to 500 35 1
501 to 700 50 2
701 to 1200 75 2
1201 and over 125 3

~/ If the number of Items in the Inspection lot is 7 or less, the number of

items in the sample shall equal the number of items in the inspection lot.

MILITARY INTEREST: CIVIL AGENCYCOORDINATING

ACTIVITIES:

Custodians GSA - FSS

CM - NBS
Army - MR
Navy - AS
Air Force - 11
PREPARING ACTIVITY:

Review Activities NAVY - AS

DOD Project MFFP-0377

Army - AL, AR, ER, GL
Navy - Sti
Alr Force - 70, 99, 82, 84
DLA - IS(E)

User Activities

Army - AT, ME, MI

Navy - MC, YD

17
Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z
Check the source to verify that this is the current version before use.
 STANDARDIZATION DOCUMENT IMPROVEMENT PROPOSAL
lNSTRKTIOt4s
must complete blocks1,2,3,and 8. In block 1, kth
1. The preparingactivity * d~ument number and revision
letter should be given.
2. The submitter of this form must completeblocks 4.5,6, and 7.
3. The preparing activity must provide a reply within 30 days from receipt of the form.
NOTE: This form may not be used to requestcopiesof documents,nor to rqum Waivers,or clarification of
requirements on current contracts. Comments submitted on this form do not constitute or imply authorization to
waive any portion of the referenced document(s) or to amend contractual requirements.

.-

i.SEASONFORRECOMMENDA~lON

,...:<.
,A.:.. .,... ,,, ,,, ,,,

L PREPARINGACTIVITY

‘“ ‘E CZmmnding Officer b. TELEPHONE (ti Ar?aCode)

(1)Commercial (2) AUTOVON
Naval Air Engineering Mter (908) 323-2487 624-2487
1
:, ADORESS
Ondlde zipcode) I IF YOU 00 NOT RECEIW A REPLY WTI+IN 45 OAYS, CONTACT:
SESD Cc& 5312 Oefetne Quslity ●nd Standarduation OfficQ
5203 Leesburg Pike. Suite 1403. Falls Church, VA 22041-3466
Iiikehurst, NJ 08733-5100 Telephone (703) 756-2340 AUTOVON 289-2340
I

Source: http://www.assistdocs.com -- Downloaded: 2008-08-01T13:20Z

Check the source to verify that this is the current version before use.