Cored welding wire

Technical
data sheet
CABB231009
F-EHCr 65
CLASSIFICATION
DIN 8555: MF 10-GF-65-GRZ
EN 14700: T Fe16

DESCRIPTION
• Tubular wire for self shielded metal arc hardfacing
• High chromium cast iron for hardsurfacing components subject to extremely severe abrasive wear and
moderate impact up to 600°C

APPLICATIONS
THERO F-EHCr 65 is designed to give a weld deposit of particularly high hardness and wear resistance on
account of the dispersion of complex carbides it contains. This gives superior performance compared to
standard chromium cast irons. Relief checking is normal.

Examples
Ore sintering, crushing, riddling, blast furnace hoppers and throats, ovens…

TYPICAL ALL-WELD METAL ANALYSIS


C Mn Si Cr Nb Mo W V
5.50 0.50 1.50 22.0 6.00 5.50 2.00 1.00
Structure: hard primary chromium and complex carbides in a tough secondary carbide eutectic matrix

TYPICAL ALL-WELD METAL MECHANICAL PROPERTIES


Hardness – 3-layer deposit on mild steel: 65 HRc

CONDITIONS OF USE
Current type Protection
DC (+) Self shielded

OPERATING CONDITIONS
Diameter Amperage [A] Tension [V] Stick-out [mm]
[mm] Range Optimum Range Optimum Range Optimum
1.6 150 - 350 270 24 - 28 24 25 - 50 25
2.0 200 - 400 300 26 - 30 26 25 - 50 35
2.4 250 - 450 350 26 - 30 28 25 - 50 40
2.8 250 - 450 400 28 - 32 30 25 - 50 40
3.2 250 - 500 450 28 - 32 30 25 - 50 40
Recovery: 90 %

WELDING POSITIONS
Flat, half up, half down

STANDARD DIAMETERS (mm)


1.6, 2.0, 2.4, 2.8, 3.2
Other diameters: please consult us

PACKAGING
Diameter ≤ 2.4 mm ≥ 2.4 mm
Standard packaging Spool EN ISO 544 : BS 300 Coil Drum
Weight 15 kg 25 kg Up to 330 kg
Other packaging: please consult us

Welding products and techniques evolve constantly. All descriptions, illustrations and properties given in this data sheet are subject to
change without notice and can only be considered as suitable for general guidance. This document is intended to help the user make
the correct choice of product. It is his responsibility to assess its suitability for his intended application.