Test - API 577 - 9 Quizlet PDF

The document contains a 9 question multiple choice quiz about heat treatment temperatures according to API 577. The questions cover topics like effective stress relieving temperatures for carbon steel, temperature ranges that may cause carbide precipitation in austenitic stainless steel welds, appropriate preheat temperatures for welds based on flow rates, allowable temperature differences for UT calibration standards, and maximum service temperatures for post-weld heat treatment of welds and cold formed areas in caustic solutions.

Uploaded by

Anonymous Q4YUvR
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
230 views2 pages

Test - API 577 - 9 Quizlet PDF

The document contains a 9 question multiple choice quiz about heat treatment temperatures according to API 577. The questions cover topics like effective stress relieving temperatures for carbon steel, temperature ranges that may cause carbide precipitation in austenitic stainless steel welds, appropriate preheat temperatures for welds based on flow rates, allowable temperature differences for UT calibration standards, and maximum service temperatures for post-weld heat treatment of welds and cold formed areas in caustic solutions.

Uploaded by

Anonymous Q4YUvR
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

1/16/2019 Test: API 577 Temperatures | Quizlet

NAME

9 Multiple choice questions

1. Heat treatment at or above ___°F is considered an effective stress relieving heat treatment for carbon steel to resist SCC.

A. Greater than 1350

B. 800 to 1650

C. 900

D. 1150

2. When welding Austentic SS, areas exposed to temps between ___ to ___ for a long enough time may precipitate carbides at the
grain boundaries.

A. 900

B. 800 to 1650

C. 1150

D. Greater than 1350

3. If flow rates are higher and the weld cools too fast the weld area should be preheated to what temp?

A. 120

B. 25

C. 125

D. 70

4. The temperature of the UT calibration standard should be within ___ of the part to be examined.

A. 25

B. 120

C. 70

D. 125

5. Welds and steel cold formed areas should be PWHT if service conditions are anticipated to exceed ___°F for 50% caustic
solution.

A. 120

B. 70

C. 25

D. 125

https://quizlet.com/243346894/test?answerTermSides=4&promptTermSides=6&questionCount=9&questionTypes=4&showImages=true 1/2
1/16/2019 Test: API 577 Temperatures | Quizlet

6. What temperature is considered to be an effective stress relieving heat treatment for carbon steel to resist stress corrosion
cracking?

A. 1150

B. Greater than 1350

C. 900

D. 800 to 1650

7. ACFM can be used at elevated temps up to ___?

A. 1150

B. 900

C. 800 to 1650

D. Greater than 1350

8. Standard PT systems are limited to what temp?

A. 25

B. 70

C. 125

D. 120

9. In carbon steels, the HAZ includes those regions heated to ___?

A. 900

B. 800 to 1650

C. Greater than 1350

D. 1150