REGISTRO DE CALIFICACION DEL PROCEDIMIENTO ( PQR )

Company Name TECNASIC

Procedure Qualification Record Nº TEC P1-M Date 9/14/2000
WPS Nº SMAW-TES-02 ( CETI INDURA )
Welding Process(es) GTAW - SMAW
Type(s) ( Manual, Automatic,Semi- Auto.) MANUAL

JOINTS (QW-402)

30º + 5° - 0°

7 mm 1.2 a 2.5 mm.

2-3

Groove Desig of Test Coupon

(For combination qualification, the deposited weld metal Thickness shal be recorded for each filler metal or process used)
BASE METALS (QW-403) POSTWELD HEAT TREATMENT (Q-407)
Material Spec. ASTM A 53 Temperature N/A
Type or Grade Gr B Time N/A
P. Nº 1 Grupo 1 to P. Nº 1 Grupo ### 1 Other N/A
Thickness of Test Coupon 5.5 mm
Diameter of Test Coupon 2"
Other N/A
GAS (QW-408)
PERCENT COMPOSITION
Gas(es) (Mixture) Flow Rate
Shielding ARGON 99,9% 14 - 16 lts/min
Trailing N/A N/A N/A
FILLER METALS (QW-404) GTAW SMAW Backing N/A N/A N/A
SFA Specification 5.18 5.5
AWS Clasification ER 70 S-6 E-7018 ELECTRICAL CHARACTERISTIC (QW-409)
Filler Metal F. Nº 6 4 GTAW SMAW
Weld Metal Analysis A Nº 1 1 Current CONTINUA CONTINUA
Size of Filler Metal 3 / 32 3 / 32 Polarity DIRECTA (-) INVERTIDA (+)
Other N/A N/A Amps. 80 - 100 18 - 22
Volts 22 - 30 23-26
Weld Metal Thickness 2 mm 3 mm Tungsten E. Size SFA 5,12 EWTH 2 N/A
Other N/A N/A
POSITION (QW-405) TECHNIQUE (QW-410)
Position of Groove 6G 6G GTAW SMAW
Weld Progression (Uphill, Downhill) ASCENDENTE ASCENDENTE
Other N/A Travel Speed MANUAL MANUAL
String of Weave Bead ANGOSTO ANGOSTO
Oscillation 0 - 4 mm -
PREHEAT (QW-406) Multipass or Single (per side) 1 VARIOS
Preheat temp N/A Single or Multiple Electrodes UNICO UNICO
Interpass Temp. N/A Other N/A N/A
Other N/A
 QW-483 PROCEDURE QUALIFICATION RECORDS (PQR)

PQR Nº TEC P1-M

TENSILE TEST (QW-150)

Ultimate Ultimate Type of

Specimen Total Load Unit Stress Failure &
Nº Width Thickness Area Kgf Kgf/mm2 Location
T 1 19.00 5.90 112.1 6,423 57.30 METAL BASE - DUCTIL

T 2 19.20 5.90 113.28 6,437 56.82 METAL BASE - DUCTIL

GUIDED-BEND TEST (QW-160)

Type and Figure Nº Result

C1 CUMPLE
C2 CUMPLE
R1 CUMPLE
R2 CUMPLE

Toughness Test (QW-170)

Specimen Notch Specimen Test Impact Values

Nº Location Size Temp. Ft. Lbs % Shear Mils Drop weight Break (Y/N)

Comments:

Fillet-Weld Test (QW-180)

Result-Satisfactory: Yes N/A No N/A Pentration into Parent Metal: Yes N/A No N/A

Macro-Results N/A

Other Test

Type of Test RADIOGRAFICO

Deposit Analisys
Other N/A

Welder's Name RICARDO PLAZA Clock Nº 10.847.864 - 0 Stamp Nº

Test conducted by ERNESTO AGUILAR Laboratory Test Nº
We certify that the statements in this record are correct and that the test weld were prepared, welded, and tested in accordance with the
requirements of Section IX of the ASME Code.
Manufacturer TECNASIC

Date ENERO 18, 2005 By SR. VICTOR GUERRERO SALGADO

TECNASIC CERTIFICA QUE LO ESTABLECIDO EN ESTE INFORME ES CORRECTO Y QUE LAS SOLDADURAS DE ENSAYO FUERON PREPARADAS Y ENSAYADAS DE
ACUERDO CON LOS REUQERIMIENTOS DEL CODIGO ASME SECCION IX