1. X8CrNiS18-9 is an austenitic stainless steel with the following chemical composition: C max 0.10%, Si max 1.00%, Mn max 2.00%, P max 0.045%, S 0.15-0.35%, Cr 17.0-19.0%, Ni 8.0-10.0%, N max 0.11%, Cu max 1.00%. 2. It has a melting range of 1420-1400°C and can be hot formed between 1200-900°C or solution annealed between 1150-1040°C. 3. As a hot formed steel, its mechanical properties include a yield strength between 500-

Uploaded by

shahid khan
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
363 views1 page

Astm A1

1. X8CrNiS18-9 is an austenitic stainless steel with the following chemical composition: C max 0.10%, Si max 1.00%, Mn max 2.00%, P max 0.045%, S 0.15-0.35%, Cr 17.0-19.0%, Ni 8.0-10.0%, N max 0.11%, Cu max 1.00%. 2. It has a melting range of 1420-1400°C and can be hot formed between 1200-900°C or solution annealed between 1150-1040°C. 3. As a hot formed steel, its mechanical properties include a yield strength between 500-

Uploaded by

shahid khan
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Quality X8CrNiS18-9 Austenitic Technical card

Number 1.4305 Stainless Steel Lucefin Group


Chemical composition
C% Si% Mn% P% S% Cr% Ni% N% Cu%
max max max max max max
0,10 1,00 2,00 0,045 0,15-0,35 17,0-19,0 8,0-10,0 0,11 1,00 EN 10088-1: 2005
± 0.01 + 0.05 + 0.04 + 0.005 + 0.02 ± 0.2 ± 0.1 ± 0.01 ± 0.07
Product deviations are allowed

Temperature °C
Melting range Hot-forming Solution annealing Stabilizing MMA welding – AWS electrodes
(Solubilization) pre-heating post welding
1420-1400 1200-900 1150-1040 not necessary not recommended
water / air joint with steel
Sensitization Quenching Tempering Soft annealing carbon CrMo alloyed stainless
butter E309 - E312, the same as E308 - E312
sensitization not suitable not suitable not suitable finish with E308 carbon steels
test at cosmetic welding
800-450 E308 – E312

Mechanical properties
Hot-formed EN 10088-3: 2005 in conditions 1C, 1E, 1D, 1X, 1G, 2D
size Testing at room temperature
mm R Rp 0.2 A% (L) A% (T) Kv +20 °C (L) Kv +20 °C (T) HB a)
from to N/mm2 N/mm2 min min J min J min max
160 500-750 190 35 230 +AT solubilization
a) for information only (L) = longitudinal (T) = transversal
Cold-processed EN 10088-3: 2005 in conditions 2H, 2B, 2G, 2P
size Testing at room temperature
mm R Rp 0.2 A% (L) A% (T) Kv +20 °C (L) Kv +20 °C (T)
from to N/mm2 N/mm2 min min min J min J min
10 b) 600-950 400 15
10 16 600-950 400 15 +AT solubilization
16 40 600-850 190 20 100
40 63 500-850 190 20 100
63 160 500-750 190 35 100
b) in the range of 1 mm < d < 5 mm, values are valid only for rounds – the mechanical properties of non round bars of < 5 mm of

thickness have to be agreed at the time of request and order


(L) = longitudinal (T) = transversal
Forged (ASTM A 473-99 steel ASTM 303)
size Testing at room temperature
mm R Rp 0.2 A% (L) C% Kv +20 °C (L) Kv +20 °C (T)
from to N/mm2 min N/mm2 min min min J min J min
515 205 40 50 +AT solubilization
Work-hardned by cold-drawing EN 10088-3: 2005 in condition 2H (ex. +AT+C)
size Testing at room temperature
mm R Rp 0.2 A%
from to N/mm2 N/mm2 min min
35 700-850 350 20 +AT+C700 cold-drawn material
25 800-1000 500 12 +AT+C800 cold-drawn material
Transition curve determined by Kv impacts. Material solubilized at 1050 °C
Average J 212 222 230 238 244 250 258
Test at °C -160 -120 -80 -40 0 +40 +80
Effect of cold-working (hot-rolled +AT+C). Approximate values
R N/mm2 610 660 670 695 745 765 795 815 855 895 940
Rp 0.2 N/mm2 240 400 450 470 520 540 560 580 630 650 720
A % 40 22 20 20 18 16 16 14 14 12 12
Reduction % 0 5 6 8 10 12 14 16 18 20 24