Highland International, Inc.

Engineered Paint Systems

Chem-Temp 74-HF Series
Hybrid Epoxy Novolac DTM Liner Coating
Chem-Temp 74-HF Series is a thin film 2-K Hybrid Epoxy Novolac Performance Data
Liner Coating that offers exceptional temperature and chemical
protection. Specifically formulated for tank linings, vessels, and Adhesion > 1800 psi
pipelines, 74-HF Series provides superior barrier properties (ASTM D 4541) – Commercial Blast
against acidic, caustic, and high heat environments. Chem-Temp
Abrasion Resistance Excellent - 124 mg loss
74-HF Series also offers excellent adhesion and corrosion (ASTM D 4060) 1000 Cycles, 100g load
resistance with a temperature rating of 300˚F for immersion and
450˚F for dry heat, making it the premium choice for high Humidity Resistance Excellent – No blistering or
performance against corrosive cargo. (ASTM 4585) 3000 hours other defects observed

Vehicle Type: Hybrid Epoxy Novolac Salt Spray Resistance Excellent - <1 mm creep from
Pigmentation: Lead Free (ASTM B 117) 3000 hours scribe, no blistering
Reducer: Not necessary, however if Chemical Resistance Excellent – MEK – No defects
desired reduced with (ASTM D 1308) observed
Highland #740 Reducer 25% H2SO4 – Slight
Reducer for Hot Application: Highland #101 Reducer discoloration, no other defects
Mix Ratio: 4:1 w/74-AHF-100 observed
Pot Life: 3 Hours @ 77˚F (Decreases at 25% NaOH – slight loss of gloss,
higher temperatures) no other defects observed
Volume Solids: 70%
2
Theoretical Coverage: 1120 ft /gal. @ 1mil DFT Pencil Hardness 6H
VOC: 2.06 lbs/gal. (247 g/L) (ASTM D 3363)
Flash Point: 24˚F (Lowest Flashing
Component) Elongation 5%
Recommended DFT: 10-16 mils DFT (ASTM D 522)

Dry-time: Normal Hot Application Independent Test Data - Autoclave

Recoat: 3-36 Hours 30 Seconds
Topcoat: 6-36 Hours RAE Engineering and Inspection Ltd. May 2011
Tack Free: 6 Hours NACE TM0185 – Evaluation of Internal Plastic Coatings for
To Touch: 4 hours
Corrosion Control of Tubular Goods by Autoclave Testing.
To Handle: 6 Hours
Put in Service (Heat): 24 Hours after final coat Adhesion
Cure Time: 5-7 Days @ 77˚F
Shelf Life: 1 Year from DOM Method: ASTM D4541
Finish: Eggshell System: Two coats 74-HF Series @ 8 mils DFT per coat
Color: Light Yellow, Red & Light Green applied to:
1) SSPC-SP6 Commercial Blast prepared steel
Advantages of 74 Series Chem-Temp 2) No surface preparation
Result: 1) No less than 1400 psi with SPPC-SP6 Commercial
 Next generation polymer technology specifically engineered Blast
for heat stability and chemical resistance 2) No less than 1000 psi with no surface preparation.
 Dry heat stability up to 450°F, immersion up to 300°F
 Superior resistance to a wide variety of chemicals and solvents
Chemical Immersion
 Superior abrasion resistance Method: Continuous Immersion at 93°C (200°F)
 Superior adhesion even over marginally prepared surfaces System: Two coats 74-HF Series @ 8 mils DFT per coat
 Excellent corrosion resistance applied to SSPC-SP5 White Metal Blast prepared
steel. Cured 14 days at 21°C (70°F).
 Ease of application
Result: No cracking, lifting, or delamination after 60 days of
 Specially engineered inert filler package provides superior continuous exposure.
barrier properties Reagents: 10% methanol, 50% methanol, 10% sulfuric acid,
 Superior substrate wetting provides excellent adhesion and 25% sulfuric acid, 10% sodium hydroxide, 50%
corrosion protection Sodium hydroxide.
 Ultra-high crosslink density provides a tough durable film with
long lasting protection
The technical data listed herein has been compiled for your convenience and guidelines are based upon our experience and knowledge. However, since we have no control over the use of
this information or this product, no warranty expressed or implied is intended or given. Highland assumes no responsibility whatsoever for coverage, performance or any other damage,
including injuries from use of this information or products recommended herein.

Highland International, Inc. 800-444-1438 www.highland-international.com

1 of 3 Revised 12-2-2011
 Highland International, Inc.
Engineered Paint Systems
Chem-Temp 74-HF Series
Hybrid Epoxy Novolac DTM Liner Coating
Heat Resistance System: Two coats 74-HF Series @ 5-8 mils DFT per coat applied
Method: Continuous heat exposure at 232°C (450°F) to SSPC-SP 5 White Metal Blast prepared steel.
System: Two coats 74-HF Series @ 8 mils DFT per coat
Cycle 1 Results:
applied to:
1) SSPC-SP56 Commercial Blast prepared steel
Blistering – the test panel remained free of blisters in all three
2) No surface preparation phases
3) No surface preparation with tight rust. Adhesion – The maintained an A rating in all three phases
Cured 14 days at 21°C (70°F). Depressurization – no effect from 1500psi to atmospheric over
Result: No cracking, lifting, or delamination of the film after duration of 120 minutes
3000 hours of continuous exposure. Cycle 2 Results: (Additional 48 Hours Test with Rapid
Decompression from 1800psi to atmospheric in 5 Minutes at
Acid Condensation Bath 95°C/203°F)
Method: Coated panels exposed to a condensation bath with Blistering – The coating showed reactions to the rapid decompression
50% sulfuric acid and water. The test duration was condition as indicated by minor blistering (D#6), the blisters did not
1000 hours total at 177°C (350°F) and the panels extend to substrate. No holidays were detected.
were scribed with an “X” to evaluate corrosion. The
acid bath was performed in an enclosed apparatus Adhesion – The coating maintained excellent adhesion (rating A) after
that retained the sulfuric acid condensation, and the exposure.
panels were suspended in the headspace.
System: Single coat as well as two coats 74-HF Series @ 8 mils Typical Systems
DFT per coat applied to SSPC-SP6 Commercial Blast
prepared steel. Cured 24 hours at 21°C (70°F). Direct to Metal
Result: No rust creepage, softening, cracking or 74-HF Series (8-16 mils DFT @ 5-8 mils DFT/coat)
Delamination of the film after 1000 hours of
continuous exposure. Surface Preparation
Sulfuric Acid Spot Testing 1) Surface preparation should be in accordance with SSPC-SP10 Near
Method: Continuous heat at 177°C (350°F) for 1500 hours. White Metal Blast Cleaning. When Near White Metal Blast is not an
After 1500 hours, spot testing was performed with option, SSPC-SP6 Commercial Blast Cleaning is acceptable and provides
good results. All surfaces to be painted should be clean, dry and free of
98% sulfuric acid for 72 hours.
all foreign contaminants.
System: Two coats 74-HF Series @ 8 mils DFT per coat
applied to SSPC-SP6 Commercial Blast prepared
2) For immersion, minimum surface preparation should be in
steel. Cured 24 hours at 21°C (70°F).
accordance with SSPC-SP5 White Metal Blast Cleaning. All Surfaces to
Result: No softening or cracking of the film (some be painted should be cry and free of all foreign contaminants.
Discoloration was observed.

Independent Test Data – Autoclave Continued Mixing and Application Requirements

Charter Coating Service Ltd. July 2011: 1) Mix 1 Part “A” Activator with 4 parts “B” Base by volume.
2) Mixed material is ready for use after a 30 minute induction period.
Method: NACE TM0185 – Evaluation of Internal Plastic Coatings 3) Reduction is not necessary, but if desired, you may reduce up to 10%
for Corrosion Control of Tubular Goods by Autoclave Testing. with Highland #740 Reducer.
4) Apply a minimum of 4 mils DFT per coat
Test Conditions: 5) Apply at a rate of 70-112 square feet per gallon to obtain the
Temperature: 45°C/ 203°F recommended dry film thickness.
Pressure: 1800 psi 6) Allow one week @ 77˚F before being put into service for immersion.
Gas Phase: 5% H2S, 5% CO2, 90% CH4 7) The second coat/topcoat must be applied within 36 hours @ 77˚F or
Organic Phase: Toluene: Xylene 1:1 ratio the surface will need to be scuffed.
Aqueous Phase: 5% NaCl
Duration: Cycle 1 - 96 hours/ Cycle 2 – additional
48 hours (rapid depressurization)

The technical data listed herein has been compiled for your convenience and guidelines are based upon our experience and knowledge. However, since we have no control over the use of
this information or this product, no warranty expressed or implied is intended or given. Highland assumes no responsibility whatsoever for coverage, performance or any other damage,
including injuries from use of this information or products recommended herein.

Highland International, Inc. 800-444-1438 www.highland-international.com

2 of 3 Revised 12-2-2011
 Highland International, Inc.
Engineered Paint Systems
Chem-Temp 74-HF Series
Hybrid Epoxy Novolac DTM Liner Coating

Special Notes for Hot Surface Application Safety Precautions

Chem-Temp 74-HF Hot Application formula may be applied directly to 1) Use normal precautions such as gloves, facemasks and barrier
hot surfaces not exceeding 400˚F. creams.
2) Adequate ventilation must be maintained. In confined areas,
1) Mix 1 Part “A” Activator with 4 Parts “B” Base (4 to 1 by volume). workmen must wear constant flow airline respirators.
3) If product comes into contact with skin, wash thoroughly with
2) Mixed material is ready for reduction after a 30 minute induction lukewarm water or diluted Boric Acid, and obtain immediate medical
period. attention.
4) This product contains FLAMMABLE materials. Keep away from
3) Reduce 20% with Highland #101 Hot Application Reducer. sparks and open flames. Observe NO SMOKING regulations.
5) All electrical equipment and installations should conform to NEC
4) To achieve the recommended film thickness, apply in multiple regulations. In areas where explosion hazards exist, workmen should be
subsequent coats not exceeding 2 mils DFT per coat. required to use non-ferrous tools, and to wear conductive, non sparking
shoes.
6) Observe low flash regulations.
Method of Application 7) Refer to Material Safety Data Sheet (MSDS) for complete safety
instructions.
Conventional Gun: DeVilbiss MBC-510
Fluid Tip: E
Air Cap: 704
Atomizing Pressure: 70 psi
Pot Pressure: 15-20 psi
Hose: ½ inch ID
Airless Gun: Graco 205-591
Pump: 30:1/45:1/60:1, Gas pump acceptable
Tip Range: 3.013 – 4.017
Pump Pressure: 1800 psi minimum
Hose: 3/8 inch ID
Brush or Roller: Natural or synthetic bristle
Clean Up: Clean all equipment with MEK

The technical data listed herein has been compiled for your convenience and guidelines are based upon our experience and knowledge. However, since we have no control over the use of
this information or this product, no warranty expressed or implied is intended or given. Highland assumes no responsibility whatsoever for coverage, performance or any other damage,
including injuries from use of this information or products recommended herein.

Highland International, Inc. 800-444-1438 www.highland-international.com