Lot Code Material Coating Thickness Ys Uts Ype (MM) (Mpa) (Mpa) (%)

The document contains material property test results for a DP600 steel coated with galvanized iron (GI) including yield strength, ultimate tensile strength, elongation and Bauschinger effect under various prestrain levels. It also reports uniform elongation, total elongation, strain hardening exponent and C-bar for the material. Fatigue properties including coefficients and exponents are provided from strain life and cyclic tests.

Uploaded by

Chenthil Kumar K
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as XLS, PDF, TXT or read online on Scribd
38 views3 pages

Lot Code Material Coating Thickness Ys Uts Ype (MM) (Mpa) (Mpa) (%)

The document contains material property test results for a DP600 steel coated with galvanized iron (GI) including yield strength, ultimate tensile strength, elongation and Bauschinger effect under various prestrain levels. It also reports uniform elongation, total elongation, strain hardening exponent and C-bar for the material. Fatigue properties including coefficients and exponents are provided from strain life and cyclic tests.

Uploaded by

Chenthil Kumar K
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as XLS, PDF, TXT or read online on Scribd
You are on page 1/ 3

Thickness YS UTS YPE

Lot Code Material Coating


(mm) (MPa) (MPa) (%)
1P DP600 GI 0.96 379 624 0.00

0.2% Yield Maximum 0.2% Yield


Test Maximum Bauschinger
Lot Strength (MPa) Stress Strength (MPa)
number Prestrain Effect
Tension (MPa) Comp.
1P 26 407.27 0.0049 418.90 -340.19 -0.812
24 408.38 0.0049 418.01 -329.32 -0.788
30 402.88 0.0099 440.35 -285.12 -0.647
21 402.26 0.0099 444.70 -290.50 -0.653
27 408.59 0.0196 505.28 -294.49 -0.583
31 412.83 0.0197 506.19 -299.36 -0.591
28 407.29 0.0486 623.34 -295.18 -0.474
22 409.78 0.0488 620.32 -298.70 -0.482
UE TE n bar R-bar
(%) (%) (6-12%)
16.01 23.51 0.182 0.855
YS UTS UE TE n
DP600-GI 412 666 15.3 23.2 0.156

* Measured from the hysteresis loop of the half life cycle

Strain life data

fatigue strength coefficient 983


fatigue ductility coefficient 0.211
fatigue strength exponent -0.101
fatigue ductility exponent -0.457
cyclic strength coefficient 1363
cyclic strain hardening exponent 0.219

Note: E used for obtaining the fatigue strength coefficient was 206824MPa.