Defects Hydrogen Cracks Identification

Defects - hydrogen cracks in steels -
identification
Preheating to avoid hydrogen cracking
Hydrogen cracking may also be called cold cracking or delayed cracking. The principal
distinguishing feature of this type of crack is that it occurs in ferritic steels, most often
immediately on welding or after a short time after welding.
In this issue, the characteristic features and principal causes of hydrogen cracks are
described.
Identification
Visual appearance
Hydrogen cracks can be usually be distinguished due to the following characteristics:

 In C-Mn steels, the crack will normally originate in the heat affected zone (HAZ) but
may extend into the weld metal (Fig 1).
 Cracks can also occur in the weld bead, normally transverse to the welding direction
at an angle of 45° to the weld surface. They are essentially straight, follow a jagged
path but may be non-branching.
 In low alloy steels, the cracks can be transverse to the weld, perpendicular to the
weld surface, but are non-branching and essentially planar.
Fig. 1 Hydrogen cracks originating in the HAZ (note,
the type of cracks shown would not be expected to
form in the same weldment)
On breaking open the weld (prior to any heat treatment), the surface of the cracks will
normally not be oxidised, even if they are surface breaking, indicating they were formed
when the weld was at or near ambient temperature. A slight blue tinge may be seen from
the effects of preheating or welding heat.
Metallography
Cracks which originate in the HAZ are usually associated with the coarse grain region, (Fig
2). The cracks can be intergranular, transgranular or a mixture. Intergranular cracks are
more likely to occur in the harder HAZ structures formed in low alloy and high carbon
steels. Transgranular cracking is more often found in C-Mn steel structures.
In fillet welds, cracks in the HAZ are usually associated with the weld root and parallel to the weld.
In butt welds, the HAZ cracks are normally oriented parallel to the weld bead.
Fig. 2 Crack along the coarse grain

structure in the HAZ
Causes
There are three factors which combine to cause cracking:
 hydrogen generated by the welding process
 a hard brittle structure which is susceptible to cracking
 residual tensile stresses acting on the welded joint
Cracking is caused by the diffusion of hydrogen to the highly stressed, hardened part of the
weldment.
In C-Mn steels, because there is a greater risk of forming a brittle microstructure in the
HAZ, most of the hydrogen cracks are to be found in the parent metal. With the correct
choice of electrodes, the weld metal will have a lower carbon content than the parent metal
and, hence, a lower carbon equivalent (CE). However, transverse weld metal cracks can
occur especially when welding thick section components.
In low alloy steels, as the weld metal structure is more susceptible than the HAZ, cracking
may be found in the weld bead.
The effects of specific factors on the risk of cracking are::
 weld metal hydrogen

 parent material composition
 parent material thickness
 stresses acting on the weld
 heat input
Weld metal hydrogen content
The principal source of hydrogen is the moisture contained in the flux ie the coating of
MMA electrodes, the flux in cored wires and the flux used in submerged arc welding. The
amount of hydrogen generated is determined mainly by the electrode type. Basic
electrodes normally generate less hydrogen than rutile and cellulosic electrodes.
It is important to note that there can be other significant sources of hydrogen eg moisture
from the atmosphere or from the material where processing or service history has left the
steel with a significant level of hydrogen. Hydrogen may also be derived from the surface of
the material or the consumable.
Sources of hydrogen will include:
 oil, grease and dirt

 rust
 paint and coatings
 cleaning fluids
Parent metal composition
This will have a major influence on hardenability and, with high cooling rates, the risk of forming a
hard brittle structure in the HAZ. The hardenability of a material is usually expressed in terms of its
carbon content or, when other elements are taken into account, its carbon equivalent (CE) value.
The higher the CE value, the greater the risk of hydrogen cracking. Generally, steels with a
CE value of <0.4 are not susceptible to HAZ hydrogen cracking as long as low hydrogen
welding consumables or processes are used.
Parent material thickness
Material thickness will influence the cooling rate and therefore the hardness level,
microstructure produced in the HAZ and the level of hydrogen retained in the weld.
The 'combined thickness' of the joint, ie the sum of the thicknesses of material meeting at
the joint line, will determine, together with the joint geometry, the cooling rate of the HAZ
and its hardness. Consequently, as shown in Fig. 3, a fillet weld will have a greater risk
than a butt weld in the same material thickness.
Fig.3 Combined thickness measurements for butt and

fillet joints
Stresses acting on the weld
The stresses generated across the welded joint as it contracts will be greatly influenced by
external restraint, material thickness, joint geometry and fit-up. Areas of stress
concentration are more likely to initiate a crack at the toe and root of the weld.
Poor fit-up in fillet welds markedly increases the risk of cracking. The degree of restraint
acting on a joint will generally increase as welding progresses due to the increase in
stiffness of the fabrication.
Heat input
The heat input to the material from the welding process, together with the material
thickness and preheat temperature, will determine the thermal cycle and the resulting
microstructure and hardness of both the HAZ and weld metal.
A high heat input will reduce the hardness level.
Heat input per unit length is calculated by multiplying the arc energy by an arc efficiency
factor according to the following formula:
V = arc voltage (V)

A = welding current (A)
S = welding speed (mm/min)
k = thermal efficiency factor
In calculating heat input, the arc efficiency must be taken into consideration. The arc
efficiency factors given in BS EN 1011-1: 1998 for the principal arc welding processes, are:
Submerged arc 1.0

(single wire)
MMA 0.8
MIG/MAG and flux cored wire 0.8
TIG and plasma 0.6
In MMA welding, heat input is normally controlled by means of the run-out length from each
electrode which is proportional to the heat input. As the run-out length is the length of weld
deposited from one electrode, it will depend upon the welding technique eg weave width
/dwell.

Defects Hydrogen Cracks Identification

Uploaded by

Copyright:

Available Formats

Defects Hydrogen Cracks Identification

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Defects Hydrogen Cracks Identification

Uploaded by

Copyright:

Available Formats

Defects - hydrogen cracks in steels -

Preheating to avoid hydrogen cracking

Hydrogen cracks can be usually be distinguished due to the following characteristics:

Fig. 2 Crack along the coarse grain

The effects of specific factors on the risk of cracking are::

 weld metal hydrogen

Weld metal hydrogen content

Sources of hydrogen will include:

 oil, grease and dirt

Parent metal composition

Parent material thickness

Fig.3 Combined thickness measurements for butt and

Stresses acting on the weld

V = arc voltage (V)

Submerged arc 1.0