Scribd
Upload
62 views

ASTM-Saudi - 5 Testing Methods

The document discusses ASTM testing methods for concrete materials and properties. It provides an overview of sampling methods like C172 and specific tests for temperature (C1064), density (C138), air content (C231/C173), slump (C143), and compressive strength (C39). It emphasizes the importance of proper sampling, curing, and reporting all required information for test results to avoid false conclusions about concrete quality.

Uploaded by

Michael Alexander
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
62 views

ASTM-Saudi - 5 Testing Methods

The document discusses ASTM testing methods for concrete materials and properties. It provides an overview of sampling methods like C172 and specific tests for temperature (C1064), density (C138), air content (C231/C173), slump (C143), and compressive strength (C39). It emphasizes the importance of proper sampling, curing, and reporting all required information for test results to avoid false conclusions about concrete quality.

Uploaded by

Michael Alexander
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 24

ASTM Testing Methods

Richard S. Szecsy, PhD, PE, FACI


President & CEO
Texas Aggregates and Concrete Association

Riyadh, Saudi Arabia


October 27, 2014
Connections between Specifications

C33 C1602 C150 C618 C290 C494


Materials
Agg. Water Cement Ash Air Admix

C49
Material Ready-Mix

Sampling C172 Sampling Fresh Concrete

C39 C231 C143 C1064


Testing Strength Air Slump Temp
Overview

Sampling

Discrete Test Methods


Temperature (C1064)

Density (C138)

Air Content (C231)

Slump (C143)

Strength (C39)
C172 Sampling
1.1 This practice covers procedures for obtaining
representative samples of fresh concrete as
delivered to the project site on which tests are to be
performed to determine compliance with quality
requirements of the specifications under which the
concrete is furnished (Note 1).

NOTE 1Composite samples are required by this


practice, unless specifically excepted by procedures
governing the tests to be performed such as tests to
determine uniformity of consistency and mixer
efficiency. Procedures used to select the specific
test batches are not described in this practice, but it
is recommended that random sampling be used to
determine overall specification compliance.
C172 Sampling
5.2.3 Sampling from Revolving Drum Truck Mixers or
AgitatorsSample the concrete by collecting two or more
portions taken at regularly spaced intervals during discharge
of the middle portion of the batch. Take the samples so
obtained within the time limit specified in Section 4 (15 min)
and combine them into one composite sample for test
purposes. In any case do not obtain samples until after all of
the water and any admixtures have been added to the mixer;
also do not obtain samples from the very first or last
portions of the batch discharge (Note 3).

NOTE 3No samples should be taken before 10% or after


90% of the batch has been discharged. Due to the difficulty
of determining the actual quantity of concrete discharged,
the intent is to provide samples that are representative of
widely separated portions, but not the beginning and the end
of the load.
C1064 Temperature

6.1 It is acceptable to measure the temperature of


freshly mixed concrete in either the transporting
equipment or the forms after discharge provided the
sensor of the temperature measuring device has at
least 75 mm [3 in.] of concrete cover in all
directions.

7.2 Leave the temperature measuring device in the


freshly mixed concrete for at least 2 min but not
more than 5 min, then read and record the
temperature to the nearest 0.5 C [1 F]. Do not
remove the device from the concrete when reading
the temperature.
Density of Concrete (C138)

Three results:
Density (Unit weight)

Theoretical density

Yield

Relative yield
Relative yield is the ratio of the actual volume of concrete
obtained to the volume as designed for the batch
Air Content (C231) or (C173)

Pressure method (C231) or Volumetric (C173)

Test for volume of air content


No bubble spacing or bubble size

Reporting to the nearest 0.1%


Minus the aggregate correction factor
C143 Slump

4.1 This test method is intended to provide the user


with a procedure to determine slump of plastic
hydraulic-cement concretes.

NOTE 1This test method was originally developed to


provide a technique to monitor the consistency of
unhardened concrete. Under laboratory conditions, with
strict control of all concrete materials, the slump is
generally found to increase proportionally with the water
content of a given concrete mixture, and thus to be
inversely related to concrete strength. Under field
conditions, however, such a strength relationship is not
clearly and consistently shown. Care should therefore be
taken in relating slump results obtained under field
conditions to strength.
C143 Slump (Practically)

Measure of concrete
vertical drop under it
own self weight.

Results do NOT
calculate:
Water content
Strength
Cementitous content
C143 Slump
C143 Slump
C143 Slump

Is a practical measurement of fresh concrete


consistency.

Avoid the trap of use as a predictive tool.

Slump is a contracting issue not a


design/engineering issue
C31 Making and Curing Test Specimens (Field)

8. Slump, Air Content, and Temperature


8.1 SlumpMeasure and record the slump of each batch of
concrete from which specimens are made immediately after
remixing in the receptacle, (C143/C143M).

8.2 Air ContentDetermine and record the air content in


accordance with either Test Method C173/C173M or Test
Method C231. The concrete used in performing the air content
test shall not be used in fabricating test specimens.

8.3 TemperatureDetermine and record the temperature in


accordance with Test Method C1064/C1064M.
C31 Making and Curing Test Specimens (Field)

10.1.2 Initial CuringImmediately after molding and


finishing, the specimens shall be stored for a period
up to 48 h in a temperature range from 60 and 80 F
[16 and 27 C] and in an environment preventing
moisture loss from the specimens. For concrete
mixtures with a specified strength of 6000 psi [40
MPa] or greater, the initial curing temperature shall
be between 68 and 78 F [20 and 26 C].
Importance of proper curing
Questionable result?
Questionable result?
Questionable result?
C39 Strength
1.1 This test method covers determination of
compressive strength of cylindrical concrete
specimens such as molded cylinders and drilled
cores. It is limited to concrete having a density in
excess of 800 kg/m3[50 lb/ft3].

4.1 Care must be exercised in the interpretation of


the significance of compressive strength
determinations by this test method since strength is
not a fundamental or intrinsic property of concrete
made from given materials. Values obtained will
depend on the size and shape of the specimen,
batching, mixing procedures, the methods of
sampling, molding, and fabrication and the age,
temperature, and moisture conditions during curing.
C39 Strength

4.2 This test method is used to determine


compressive strength of cylindrical specimens
prepared and cured in accordance with Practices
C31/C31M, C192/C192M, C617, and C1231/C1231M
and Test Methods C42/C42M and C873.

4.3 The results of this test method are used as a


basis for quality control of concrete proportioning,
mixing, and placing operations; determination of
compliance with specifications; control for
evaluating effectiveness of admixtures; and similar
uses.
C39 Strength

9.1 Report the following information:


9.1.1 Identification number,
9.1.2 Average measured diameter (and measured length, if
outside the range of 1.8 D to 2.2 D), in millimetres [inches],
9.1.3 Cross-sectional area, in square millimetres [square inches],
9.1.4 Maximum load, in kilonewtons [pounds-force],
9.1.5 Compressive strength to the nearest 0.1 MPa [10 psi],
9.1.6 Type of fracture (see Fig. 2),
9.1.7 Defects in either specimen or caps, and,
9.1.8 Age of specimen.
9.1.9 When determined, the density to nearest 10 kg/m3[1 lb/ft3].
Impact

Uniformity in test methods is highly beneficial


Properly trained testing technicians
Certified testing labs

Implicit results are dangerous


Assumptions based on NON-REPORTED information
can create FALSE conclusions.

User based experience can be incorporated into


changes to standards
Questions

Richard S. Szecsy, PhD, PE


President

Texas Aggregates and Concrete Assoc.


900 Congress
Austin, Texas 78701
214-202-1379 cell
512-451-5100 ofc

[email protected]
www.tx-taca.org

You might also like