2007 SECTION II, PART A SA-283/SA-283M

--```,,,``,``,`,`,,,,``,`,`,,,`-`-`,,`,,`,`,,`---

SPECIFICATION FOR LOW AND INTERMEDIATE

TENSILE STRENGTH CARBON STEEL PLATES

SA-283/SA-283M

(Identical with ASTM Specification A 283/A 283M-03.)

1. Scope 3.2 Coils are excluded from qualification to this speci-

1.1 This specification covers four grades (A, B, C, and fication until they are processed into finished plates. Plates
D) of carbon steel plates of structural quality for general produced from coil means plates that have been cut to
application. individual lengths from a coil. The processor directly con-
trols, or is responsible for, the operation involded in the
1.2 When the steel is to be welded, a welding procedure
processing of a coil into finished plates. Such operations
suitable for the grade of steel and intended use or service
include decoiling, leveling, cutting to length, testing,
is to be utilized. See Appendix X3 of Specification
inspection, conditioning, heat treatment (if applicable),
A 6/A 6M for information on weldability.
packaging, marking, loading for shipment, and certifi-
1.3 The values stated in either inch-pound units or SI cation.
units are to be regarded separately as the standard. Within
the text, the SI units are shown in brackets. The values NOTE 1 For plates produced from coil and furnished without heat
stated in each system are not exactly equivalents, therefore treatment or with stress relieving only, two test results are to be reported
for each qualifying coil. Additional requirements regarding plate produced
each system is to be used independently of the other, with-
from coil are described in Specification A 6/A 6M.
out combining values in any way.
1.4 For plate produced from coil and furnished without
heat treatment or with stress relieving only, the additional
requirements, including additional testing requirements 4. Process
and the reporting of additional test results, of Specification 4.1 The steel shall be made by one or more of the
A 6/A 6M apply. following processes: open-hearth, basic-oxygen, or elec-
1.5 This specification contains notes or footnotes, or tric-furnace.
both, that provide explanatory material. Such notes and
footnotes, excluding those in tables and figures do not
contain any mandatory requirements. 5. Chemical Requirements
5.1 The heat analysis shall conform to the requirements
2. Referenced Document prescribed in Table 1.
2.1 ASTM Standard:
A 6/A 6M Specification for General Requirements for 5.2 The steel shall conform on product analysis to the
Rolled Structural Steel Bars, Plates, Shapes, and Sheet requirements prescribed in Table 1, subject to the product
Piling analysis tolerances in Specification A 6/A 6M.

3. General Requirements for Delivery

3.1 Plates furnished under this specification shall con- 6. Tensile Requirements
form to the requirements of the current edition of Specifi- 6.1 Material as represented by the test specimens shall
cation A 6/A 6M, for the specific date ordered, unless a conform to the requirements as to tensile properties pre-
conflict exists in which case this specification shall prevail. scribed in Table 2.

473
Copyright ASME International
Provided by IHS under license with ASME Licensee=Setal Engenharia Construcoes e Perfuracoes S.A./5941776001, User=Gome
No reproduction or networking permitted without license from IHS Not for Resale, 08/17/2007 12:31:51 MDT
 SA-283/SA-283M 2007 SECTION II, PART A

TABLE 1
CHEMICAL REQUIREMENTS
Heat Analysis, %
Elements Grade A Grade B Grade C Grade D

Carbon, max 0.14 0.17 0.24 0.27

Manganese, max 0.90 0.90 0.90 0.90
Phosphorus, max 0.035 0.035 0.035 0.035
Sulfur, max 0.04 0.04 0.04 0.04
Silicon
Plates 112 in. [40 mm] and under, max 0.40 0.40 0.40 0.40
Plates over 112 in. [40 mm] 0.150.40 0.150.40 0.150.40 0.150.40
Copper, min % when copper is specified 0.20 0.20 0.20 0.20

TABLE 2
TENSILE REQUIREMENTSA
Grade A Grade B Grade C Grade D

Tensile strength, ksi [MPa] 4560 [310415] 5065 [345450] 5575 [380515] 6080 [415550]
Yield point, min, ksi [MPa] 24 [165] 27 [185] 30 [205] 33 [230]
Elongation in 8 in. [200 mm], min, % B 27 25 22 20
Elongation in 2 in. [50 mm], min, % B 30 28 25 23
A
See Specimen Orientation under the Tension Tests section of Specification A6/A 6M.
B
For plates wider than 24 in. [600 mm], the elongation requirement is reduced two percentage points. See elongation requirement adjust-
ments in the Tension Tests section of Specification A 6/A 6M.

474
Copyright ASME International
Provided by IHS under license with ASME Licensee=Setal Engenharia Construcoes e Perfuracoes S.A./5941776001, User=Gome
No reproduction or networking permitted without license from IHS Not for Resale, 08/17/2007 12:31:51 MDT
 2007 SECTION II, PART A SA-283/SA-283M

SUPPLEMENTARY REQUIREMENTS

Supplementary requirement shall not apply unless specified in the order or contract. Stan-
dardized supplementary requirements for use at the option of the purchaser are listed in
Specification A 6/A 6M. Those that are considered suitable for use with this specification
are listed by title:

S2. Product Analysis, S8. Ultrasonic Examination, and

S3. Simulated Post-Weld Heat Treatment of S15. Reduction of Area
Mechanical Test Coupons,
S97. Limitation on Rimmed or Capped Steel:
S5. Charpy V-Notch Impact Test, S97.1 The steel shall be other than rimmed or capped.
S6. Drop Weight Test,

475
--```,,,``,``,`,`,,,,``,`,`,,,`-`-`,,`,,`,`,,`---

Copyright ASME International

Provided by IHS under license with ASME Licensee=Setal Engenharia Construcoes e Perfuracoes S.A./5941776001, User=Gome
No reproduction or networking permitted without license from IHS Not for Resale, 08/17/2007 12:31:51 MDT
 --```,,,``,``,`,`,,,,``,`,`,,,`-`-`,,`,,`,`,,`---
476
Copyright ASME International