DESIGN OF PLAIN CEMENT CONCRETE PAVEMENT
Name of the work :- Providing BT to the Road from Yetigairammapeta to Arla via B.B Patnam , Ratnampeta
and Panasalapadu
Name of the sub work:- CC Road
The design of the cement concrete pavement is done as per the guide lines of Indian Roads Congress IRC : SP : 62 -
2004 (July 2006)
Design.
1) Wheel (Design ) Load from para 2.1, taken as per SP 62 : : 51.00KN i.e 51000N
2004
2) Tyre pressure : 0.50 Mpa
3) Designed Life period : 20.00 Years
4) C.B.R Value taken : 4.00
5) Traffic Volume : 196 Veh / day
6) K Value from table 3.to a CBR Value of 4.00 : 35.00 x10^-3 N/sqmm/mm.
(Page 4, of SP62:2004 )
7) Sub - base with Granular material course 75 to 150 mm : 150 mm
8) Effective K Value increased by 20% from para 3.5 , SP62- : 20 %
2004 page no 4
Effective K Value 1.2 X 35.00 : 42.00 x10^-3 N/sqmm/mm.
9) 28 day compressive strength for M30 concrete (fc) : 30 Mpa
10) Flexural strength Ff = 0.70sqrt(fc) :
=0.70sqrt(30) 3.834 Mpa (ie N/ mm^2)
11) 28 day Flexural strength : 3.834 Mpa
12) 90 day Flexural strength 1.20 x 3.834 = 4.60 Mpa
13) Dimensions of the Cement Concrete slab 3750mm X 3750mm
14) = Poissons ratio for concrete 0.15
(As per Clause 3.7 , page 8 of SP62:2004 )
15) E = modulus of Elasticity for concrete , 3 * 10^4 Mpa
(As per Clause 3.7 , page 8 of SP62:2004 )
Trial 1
Let Thickness of road be h : 150 mm
l = radius of relative Stiffness = 4 Sqrt {(E * h^3) / (12*(1 - ^2 )*K) }
=4 th Sqrt( (3*10^4*150^3)/(12*(1-0.15^2)* 42.000))
673.31 mm
a) Edge Load Stress :
Wheel Load = 51.00KN k = 42.00 x10^-3 N/sqmm/mm.
Pavement thickness = 150mm
From The Graph Edge load Stress (Fig 2 of SP62:2004) = 4.00 Mpa
b) Edge temparature Stress
For the state of Andhra Pradesh the temperature differentials ( Dt ) for 150mm thick slab is 17.3 oC
Alpha = Coefficient of Thermal expansion of Concrete = 10 X Power(10, -6)
(As per Clause 3.8 , page 8 of SP62:2004 )
L/ l = 3750 / 673.31 : 5.569
W/ l = 3750 / 673.31 : 5.569
FOR L / l = 5.569
Bradbury's coefficient C from Fig. 1, (Page 9,SP 62:2004)
By interpolation C value may be arriaved = (0.72+(0.92-0.72)*(5.569-5)/(6-5))
= 0.834
From The Graph Edge Temperature Stress (Fig 1, page 9 of SP62:2004) = 2.15 Mpa
c) Total Stress
Total Stress = Edge Load Stress + Edge Temperature Stress
= 6.15 Mpa
This value is greater than the allowable flexural strength 4.6 Mpa
So, Slab thickness 150 mm assumed is inadequate.
Trial 2
Let Thickness of road be h : 200 mm
l = radius of relative Stiffness = 4 Sqrt {(E * h^3) / (12*(1 - ^2 )*K) }
=4 th Sqrt( (3*10^4*200^3)/(12*(1-0.15^2)* 42.000))
835.44 mm
a) Edge Load Stress :
Wheel Load = 51.00KN k = 42.00 x10^-3 N/sqmm/mm.
Pavement thickness = 200mm
From The Graph Edge load Stress (Fig 2 of SP62:2004) = 2.75 Mpa
b) Edge temparature Stress
For the state of Andhra Pradesh the temperature differentials ( Dt ) for 200mm thick slab is 17.3 oC
Alpha = Coefficient of Thermal expansion of Concrete = 10 X Power(10, -6)
(As per Clause 3.8 , page 8 of SP62:2004 )
L/ l = 3750 / 835.44 : 4.489
W/ l = 3750 / 835.44 : 4.489
FOR L / l = 4.489
Bradbury's coefficient C from Fig. 1, (Page 9,SP 62:2004)
By interpolation C value may be arriaved = (0.44+(0.72-0.44)*(4.489-4)/(5-4))
= 0.577
From The Graph Edge Temperature Stress (Fig 1, page 9 of SP62:2004) = 1.50 Mpa
c) Total Stress
Total Stress = Edge Load Stress + Edge Temperature Stress
= 4.25 Mpa
This value is less than the allowable flexural strength 4.6 Mpa
So, Slab thickness 200 mm assumed is adequate.
2 Corner Load Stress
Wheel Load = 51.00KN k = 42.00 x10^-3 N/sqmm/mm.
Pavement thickness = 200mm
From The Graph Corner Load Stress (Fig 3 of SP62:2004) = 3.00 Mpa
This value is less than the allowable flexural strength 4.6 Mpa
So, Slab thickness 200 mm assumed is adequate.
DESIGN OF JOINTS
Spacing of Contraction Joint (Lc) :
4 Sc = Allowable stresses in tension during initial period of curing = 0.8kg/Sqcm.
2 Sc10
Lc= f = Coefficient of friction at interface = 1.4
Wf
W = Unit weight of cement concrete = 2400 kg/Cum.
Lc = 4.76 m
IRC specifies maximum spacing of 4.50m the design value is 3.75m (<4.50m).
Hence, the longitudinal dimension of 3.75m for the slab is safe.
Spacing of Expansion Joint (Le) :
Le=
100 c (t 2 t 1 )
Le = 57.80 m
Spacing of expansion joint is 3.75 x 15 = 56.25 m
After 15 slabs, an expansion joint of width 20mm (2cm) is provided.
in the above equation is half the width of the joint.
Hence, after 14 contraction joints an expansion joint is provided.
At expansion joint (of joint width 20mm), dowel bars of 25mm diameter, 500mm long shall be placed at a spacing of
250mm center to center. The first dowel bar is placed at a distence of 150mm from the free edge of pavement.
At the expansion joint dowel bars with metal caps partially filled with cotton are used. Half the length of dowel bar near
the metal cap is lubricated to ease movement of the slab due to temparature variation.
The contraction joints are provided as dummy joints with saw cuts to a depth of 1/3rd or 1/4th thickness of the slab
from the top. The load transfer at the joints is provided through the physical interlocking by the aggregates projecting out at
the joint faces.
The gap between the joint faces should be filled with filler and at the top, elastomeric material should be used as a
joint sealant to prevent ingress of rain water and grit.
Table - 1
Approximate K Value corresponding to C.B.R. values
Soaked CBR% 2 3 4 5 7 10 15 20 50
K Valuex10^-3
N/mm2/mm 21 28 35 42 48 55 62 69 140
Table - 2
Expected Values of standard Deviation of Compressive Strength
Grade of Concrete Standard Deviation for different degrees of control, Mpa
Very good Good Fair
M 30 5.0 6.0 7.0
M 35 5.3 6.3 7.3
M 40 5.6 6.6 7.6
Table - 3 Table - 4
Values of co-efficient '
C' based on Bradbury's
Chart Recommended Temperature Differentials for Concrete Slabs
Temperature Differentials, C in
L / I and W / I C Slabs of thickness in cms
1 0.000 Zone States 15 20 25
2 0.040 III A.P. 17.3 19.0 20.3
3 0.175
4 0.440
5 0.720
6 0.920
7 1.030 Mix Mix type
8 1.075 20 1.2.4
9 1.080 30 1.1.5.3
10 1.075
11 1.050
12and above 1.000
A B C D E F G H I J K L M N O P Q R S T U V W X
a b c d e f g h i j k l m n o p q r s t u v w x
A B C D E F G H I J K L M N O P Q R S T U V W X
a b c d e f g h ijk lm n o p q r s t u v w x
Y Z
y z
Y Z
yz