Micro Laser

Rods and Wires

www.fsh-welding.com

Products for Micro Laser Applications

For Micro-Laser applications we produce a selection of the alloys which you can find below in the
dimensions:

Rods Spools

0.3x1000 mm 0,3 mm x 50 m
0.4x1000 mm 0,4 mm x 50 m
0.5x1000 mm 0,5 mm x 50 m

Further alloys, see MIG-wires, can be produced on request in these dimensions.

FSH WELDING GROUP: www.fsh-welding.com - [email protected] 1

 Micro Laser
Rods and Wires
www.fsh-welding.com

Technical details

AWS A5.9 Typical Applications

Inox
EN 12072 Wire
AMS Analysis ( % )
Mat. No
ER308L C 0,015 Welding and surfacing of stainless steels 304,
ML308L
W 19 9 L Si 0,42 304L; X5CrNi18-10 ; X2CrNi19-11
-- Mn 1,8
1.4316 Cr 19,5
Ni 9,8
ER312 C 0,1 For dissimilar joints- stainless to carbon steels
ML312
W 29 9 Si 0,4 and for surfacing.
-- Mn 1,8
1.4337 Cr 30,2
Ni 9,3
Mo 0,15
ER316L C 0,02 Welding and surfacing of stainless steels 316,
ML316L
W 19 12 3 L Si 0,45 316L ; X5CrNiMo17-12-2 ; X2CrNiMo17-12-2
-- Mn 1,8
1.4430 Cr 18,6
Ni 12,4
Mo 2,8
ER321 C 0,03 Welding and surfacing of stainless steels
ML321
-- Si 0,5 321,347 ; X6CrNiTi18-10 , X6CrNiNb18-10
-- Mn 1,5
1.4541 Cr 18,0
Ni 10,5
Ti 0,2
--- C 0.02 For welding and surfacing of medical stainless
ML M25W
W 18 15 3L Si 0.3 steels 316L
-- Mn 1.5
1.4441 Cr 18
Ni 14
Mo 3
ER410 C 0,03 For welding and surfacing 13% Cr steels, AISI
ML410
-- Si 0,3 410 ; X12Cr13
5776 Mn 0,5
1.4009 Cr 13,1
ER420 C 0.3 For surfacing 13% Cr steels.
ML420
-- Si 0.3
-- Mn 0.4
1.4028 Cr 13
Ni 0.3
Mo 0.05
Cu 0.1

FSH WELDING GROUP: www.fsh-welding.com - [email protected] 2

 Micro Laser
Rods and Wires
www.fsh-welding.com

ER430 C 0,05 For welding and surfacing 17% Cr steels also

ML430
Si 0,4 for surfacing of valves.
Mn 0,5
Cr 16,5
Ni 0,3
Mo 0,1
ER630 C 0,03 For welding and surfacing 17-4PH,
ML630
-- Si 0,5 X4CrNiCuNb16-4, turbine blades and wheels.
5825 Mn 0,6
1.4548 Cr 16,0
Ni 5,0
Cu 3,5
Nb 0,2
-- C 0,05 For welding and surfacing Pelton turbines
ML17-4Mo
-- Si 0,3 made on CA6-NM , GX5CrNi13-4 or
-- Mn 0,9 GX5CrNiMo16-5
1.4405 Cr 16,0
Ni 4,4
Mo 1,0
Nb 0,2
-- C 0,12 For the repair of turbine wheels and blades (
ML
-- Si 0,3 X12CrNiMoV12, 1.4938 , 1.4939).
Z12CNDV12
-- Mn 0,7
1.4939 Cr 11,8
Ni 2,7
Mo 1,7
V 0,3

AWS A5.14 Typical Applications

Nickel
ISO/EN 18274 Wire
AMS Analysis ( % )
Mat. N
ERNiCrMo-3 C 0,015 For welding and cladding of alloy 625, UNS
ML Ni625
S-NiCr22Mo9Nb Si 0,1 N06625, NiCr22Mo9Nb and special stainless
Ni6625 Mn 0,2 steels.
5837 Cr 21,9
2.4831 Mo 8,9
Nb 3,5
Fe 1
ERNiFeCr-2 C 0,04 For welding and cladding of Nickel alloy 718
ML Ni718
S-NiFe19Cr19Nb5Mo3 Si 0,2 and X750; 2.4668.
Ni7718 Mn 0,2
5832 Cr 19,0
2.4667 Mo 3,0
Nb 5,0
Ni 52
Al 0,5
Ti 0,9
Fe rest
FSH WELDING GROUP: www.fsh-welding.com - [email protected] 3
 Micro Laser
Rods and Wires
www.fsh-welding.com

ERNiMo-3 C 0,03 For welding dissimilar alloys known as

ML NiW
S-NiMo25Cr5Fe5 Si 0,2 HASTELLOY W..
Ni1004 Mn 0,4 Used in the aeronautical industry for
5786 Cr 5,0 reparation and maintenance of engines.
Mo 24
Fe 6,0
ERNiCrMo-2 C 0,07 Popularly known as HASTELLOY X .
ML NiX
S-NiCr21Fe18Mo9 Si 0,3 Nickel Base alloy generally used for turbines
Ni6002 Mn 0,6 and engines.
5798 Cr 22,0 Best compromise between resistance to
Fe 19,3 oxidation and mechanical characteristics at
Co 1,0 high temperature. Used in the aeronautical
W 0,8 industry (combustion chamber, etc).
Al 0,3

AWS A5.7 Typical Applications

Copper
ISO EN 14640 Wire
Mat. N Analysis ( % )

ERCuSn-A Sn 6,0 For welding and surfacing of copper alloys,

ML Cu114
S Cu5180 (CuSn6P) P 0,2 tin-bronzes; for bearings and sliding surfaces.
2.1022 Pb <0,01
Cu base

AWS A5.10 Typical Applications

Aluminium
ISO EN 18273 Wire
AMS Analysis ( % )
Mat. N
ER2319 Si 0,2 For aerospace industries.
ML AlCu6
S Al2319 Fe 0,1
(CuAl6MnZrTi) Cu 6,5
4191 Mn 0,3
-- Zr 0,12
Ti 0,16
V 0,08
ER4043 Si 5,0 For welding and surfacing aluminium alloys
ML AlSi5
S Al4043 (AlSi5) Fe <0,4 with up to 7% Si ; 6005, 6061;6063; 6101;
4190 Mn 0,05 6201.
3.2245
ER4047 Si 12 For welding and surfacing aluminium alloys
ML AlSi12
S Al4047 (AlSi12) Fe <0,5 with more than 7% Si , mainly Aluminium
4185 Mn 0,05 castings. Also for dissimilar joints.
3.2585
ER5356 Si 0,05 For welding and surfacing of high strength
ML AlMg5
S Al5356 (AlMg5Cr) Fe 0,13 aluminium alloys: 5154; 5254; 5454; 5456.
-- Mn 0,15
3.3556 Mg 4,8
Cr 0,1
Ti 0,13

FSH WELDING GROUP: www.fsh-welding.com - [email protected] 4

 Micro Laser
Rods and Wires
www.fsh-welding.com

R-357.0 Si 6.8 For repairing aluminium castings like AlSi7

ML AlSi7Mg6
---- Fe 0.1 ( AS7); 4343
4246 Cu 0.05
-- Mn 0.01
Mg 0.5
Ti 0.15

AMS Typical Applications

Cobalt
Mat. N Wire
Analysis ( % )
5796 C 0,1 For welding and surfacing alloy Co 25,
ML Co25
2.4964 Si 0,8 CoCr20W15Ni , 2.4964 used for gas turbines,
Mn 1,5 high temperature equipment, valves.
Cr 20,0
Ni 10,0
W 15,0
Fe <3,0
C 0.85 Corrosion and heat resistant for aeronautical
ML Co694
Si <1 applications.
Mn <1 Hardfacing of gas turbine blade shroud
Cr 27 interlock surfaces and other wear attacked
Ni 5 areas.
Mo -
W 20
V 1
Co base
5801 C 0,1 Welding and surfacing of oxidation and creep
ML Co188
2.4683 Si 0,35 resisting alloy like alloy 188 , UNS R30188,
Mn 1,25 AMS 5608 , Material N 2.4683 , CoCr22NiW
Cr 22 and similar.
Ni 22 Gas turbine engine combustor cans, spray
Mo - bars, flame-holders, after-burner liners,
W 14 Very good resistance against oxidation up to
La 0.04 1150C.
Co base

Typical Applications
Hardfacing
Wire
Analysis ( % )
15CrMoV6 C 0,14 For welding and hardfacing of steels like
ML SCVS
1.7734 Si 0,15 15CrMoV6, 25CrMo4, 35CrMo4, 20CrMo12
Mn 1,0 Rp0,2 930 MPa
Cr 1,4
Mo 0,9
V 0,25 Hardness: ~ 42 HRC

FSH WELDING GROUP: www.fsh-welding.com - [email protected] 5

 Micro Laser
Rods and Wires
www.fsh-welding.com

25CrMo4 C 0,23 For welding and hardfacing of steels like

ML F66S
1.7218 Si 0,2 25CrMo4, 35CrMo4, 20CrMo12.
Mn 0,7 For Aeronautic constructions.
Cr 1,2
Mo 0,2
Ni 0,15 Hardness: ~ 46 HRC
36NiCrMo16 C 0,35 For welding and hardfacing of cold working
ML819BS cu
1.6773 Si 0,3 tools, swages for forging and punching tools
Mn 0,4 as well as for moulds for plastics.
Cr 1,7
Mo 0,3
Ni 3,8 Hardness: ~ 48 HRC
10CrMo3 C 0,1 For welding and surfacing of heat resistant
ML 80SB2
AWS A5.28:ER80S-B2 Si 0,5 CrMo steels like A537 - A299 A355 GrP11 u.
1.7339 Mn 0,6 P12; 13 CrMo 4.4 - 15CrMo3 - 13CrMoV42
Cr 1,3
Mo 0,5
Cu 0,2
8CrMo12 C 0,06 For welding13 CrMo 4.4 - 15CrMo3 -
ML BMS cu
1.7734 Si 0,7 13CrMoV42 and for hardfacing of plastic
Mn 1,1 moulds.
Cr 2,7
Mo 1,0 Hardness: ~ 36 HRC
X38CrMoV5-1 C 0,38 For hardfacing steels of similar chemical
ML SMV3S
1.2343 Si 0,9 composition, for forging and drawing dies, for
Mn 0,3 cast moulds.
Cr 5,0
Mo 1,3
V 0,5 Hardness: ~ 58 HRC
X50CrMoWV5 C 0,5 Mainly used for build up on equipments
ML MV5S
Cr 5,0 stressed by high impact and abrasion.
Mo 1,3 Resistant to temperatures up to 550C.
W 1,3 General applications : moulds for plastic
V 0,3 injections, cold working tools, shredder
hammers. Hardness: ~ 60 HRC
100MoCrVW8 C 1,0 Composition of a high speed steel, used for
ML HBC62
S 2-9-2 Si 0,4 hardsurfacing cold working tools as lathe
1.3348 Mn 0,2 tools, drilling tools, cutting tools.
Cr 3,6 For hardfacing and repairing of high speed
Mo 8,5 steels like 85WMoCrV6.5.4.2, ( 1.3339 ),
W 1,6 1.3333 and others.
V 1,8 Hardness: ~ 62 HRC
X40CrMo17-1 C 0,4 Used for hardsurfacing parts subject to
ML
1.4122 Si 0,5 corrosion and heat as well as cold working
HB CrMo17-1 Mn 0,5 tools. For gas, water and steam valves with
Cr 16,5 service temperatures up to 500C.
Mo 1,1 Hardfacing and welding of base metals
X55CrNiMoV12, X55Cr14, X160CrMoV12
Hardness: ~ 53 HRC
FSH WELDING GROUP: www.fsh-welding.com - [email protected] 6
 Micro Laser
Rods and Wires
www.fsh-welding.com

X2NiCoMo18-8-5 C <0,01 For building up dies for extrusion of Al-

ML
1.6359 Si <0,1 castings and plastics, for hot working tools ,
MARVAL 18S Mn <0,1 for moulds, etc.
Ni 18,0 Also used in Aeronautic to weld Maraging
Co 8,5 steels like X2NiCoMo18-9-5 , 1.6358 and
Mo 5,0 others ( Maraging 200 250 ).
Ti 0,5
Al 0,1 Hardness: ~ 36 HRC
X1CrNiMoAlTi12-9 C <0,01 Used to weld and to repair parent metals like
ML MARVAL
1.4530 Si 0,05 X1CrNiMoAlTi12-9 and others.
MX12
Mn 0,02 For plastic injection moulds.
Cr 12,0
Ni 9,4
Mo 2,0
Ti 0,3
Al 0,7 Hardness: ~ 32 HRC
X38CrMoV5-1 C 0,4 For hardfacing steels of similar chemical
ML MVS
1.2343 Si 0,9 composition , used for plastic and glass
Mn 0,4 moulds.
Cr 5,0
Mo 1,3
Ni 0,1
V 0,5 Hardness: ~ 60 HRC
X45CrSi9 C 0,45 Used for hardfacing parts subject to high
ML R600B
1.4718 Si 3,0 impact and medium abrasion as well as for
Mn 0,4 cutting edges.
Cr 9,2
Ni 0,17 Hardness: ~ 60 HRC
X35CrMoV5-1 C 0,35 For hardfacing of similar chemical composition
ML SR3S
Si 0,3 steels, for light metals injection moulds and
Mn 0,4 drawing dies.
Cr 5,1
Mo 1,3
V 0,5 Hardness: ~ 55 HRC

AWS A5.16 Typical Applications

Titanium
AMS Wire
Mat. No Analysis ( % )
ERTi-5 C <0,02 Main applications are in aeronautical industry.
ML TA6V4
4954 N2 <0,01 Welding of similar titanium alloys.
3.7165 H2 <0,005
O2 <0,20
Fe <0,25
Al 6,0
V 4,0

ind.07

FSH WELDING GROUP: www.fsh-welding.com - [email protected] 7