    The document provides information on Densit WearFlex 2000 HT, a chemically bonded corundum-ceramic wear resistant lining. It details the product's properties, applications, installation process, and technical specifications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Pro Wearflex2000ht Uk

    Uploaded by

    Jagadeesh Gutti
    107 views1 page
    The document provides information on Densit WearFlex 2000 HT, a chemically bonded corundum-ceramic wear resistant lining. It details the product's properties, applications, installation process, and technical specifications.

    Original Description:

    ghhjhjhj

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document provides information on Densit WearFlex 2000 HT, a chemically bonded corundum-ceramic wear resistant lining. It details the product's properties, applications, installation process, and technical specifications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    107 views1 page

    Pro Wearflex2000ht Uk

    Uploaded by

    Jagadeesh Gutti
    The document provides information on Densit WearFlex 2000 HT, a chemically bonded corundum-ceramic wear resistant lining. It details the product's properties, applications, installation process, and technical specifications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    Data sheet

    Densit WearFlex 2000 HT


    - Chemically bonded Corundum-Ceramic
    Densit WearFlex 2000 HT wear resistant linings provide supe-
    rior protection against heavy erosive wear at temperatures up to
    1200C (2190F).

    DENSIT WEARFLEX 2000 HT The bags must be stored on a dry stock


    Consumption at 25 mm
    Densit WearFlex 2000 HT 71 kg/m2 Install mesh to maintain the good properties of the
    Steel fibres *) 3.2 kg/m2
    Densit Anchoring mesh 1 m2/m2 Mix dry compound for 1 minute compound.
    Densit Curing Compound 0.25 l/m2
    Add water and mix for 6 minutes A paddle mixer must be used for
    Consumption at 40 mm
    Densit WearFlex 2000 HT 113 kg/m2 Add appropriate steel fibres *) mixing the compound. A signifi-
    Steel fibres *) 5.1 kg/m2 and mix another 3 minutes cant change in consistency of the
    Densit Anchoring mesh 1 m2/m2
    Densit Curing Compound 0.25 l/m2 Trowel mix onto mesh material (from dry to plastic) must be
    *) Steel fibre selection depends on temperature Apply Densit Curing Compound observed within 3 minutes from addition
    and chemical environment. See the data sheet
    for steel fibres For more details refer to the of water.
    Densit WearFlex Manual Avoid Densit compound to make con-
    tact with aluminium or galvanised steel.
    Densit WearFlex 2000 HT is a Densit WearFlex 2000 HT should be in-
    trowellable one-component ready-mix stalled on a standard expanded metal
    delivered in 25 kg bags. mesh welded on the steel casing and can
    even be installed over head.
    Technical data PROPERTIES Standard Densit WearFlex 2000 HT
    Density kg/m3 (lb/ft3) EN 1015-6 2900 (181)
    Compressive strength MPa EN 12190 133
    Flexural strength MPa EN 196-1 15
    Engineered Polymers Dynamic E-modul MPa EN 70-80 103
    Densit
    De
    Den si
    sit Casting shrinkage vol. % 0.2
    00 HT

    WearFlex
    W
    Wea rFl
    Flex
    ex 200
    20000 H
    HTT
    Thermal conductivity w/mC 1.5
    Densit WearFlex 2000

    Coeff. of thermal expansion 1/C (1/F) EN 1770 6.9x10-6 (3.8x10-6)


    Heat capacity KJ/kgC 0.9-1.0
    Max. service temperature C (F) 1200 (2190)
    Shrinkage after firing at 500C % 0.1
    Shrinkage after firing at 800C % 0.3
    Engineered Polymers
    WEAR & ABRASION Shrinkage after firing at 1200C % 0.3
    Abrasion resistance cm3/50cm2 DIN 52108 0.5-1.0
    Erosive resistance min/cm3 140
    % CaO 4-8
    % SiO2 4-8
    Chemical composition % Al2O3 + TiO2 70-90
    % Fe2O3 <2
    The figures given are typical values.
    % Cr6+ EN 196-10 <0.0002
    Please contact ITW Engineered Polymers or the nearest
    Bag size kg 25
    distributor for further information. Pallet size kg 1250

    Engineered Polymers

    ITW Engineered Polymers ApS | Gasvrksvej 46 | DK-9000 Aalborg | T: +45 9816 7011 | E: [email protected] | www.itwengineeredpolymers.com