Endorsed by Manufacturers Standardization Society

of the Valve and Fittings Industry

Endorsed by American Foundrymens Society
Used in USDOE-NE Standards

Designation: A 216/A 216M 07

Standard Specification for

Steel Castings, Carbon, Suitable for Fusion Welding, for

High-Temperature Service1
This standard is issued under the fixed designation A 216/A 216M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.

//^:^^#^~^^""~:@":^*^~$~"#:*~~#@"@:"*"~^$^~:^":^@::~*\\

1. Scope*
1.1 This specification2 covers carbon steel castings for
valves, flanges, fittings, or other pressure-containing parts for
high-temperature service and of quality suitable for assembly
with other castings or wrought-steel parts by fusion welding.
1.2 Three grades, WCA, WCB, and WCC, are covered in
this specification. Selection will depend upon design and
service conditions, mechanical properties, and the high temperature characteristics.
1.3 The values stated in either inch-pound units or SI units
are to be regarded separately as standard. Within the text, the
SI units are shown in brackets. The values stated in each
system are not exact equivalents; therefore, each system must
be used independently of the other. Combining values from the
two systems may result in nonconformance with the specification.

SP 55 Steel Castings for Valve, Flanges, and Fittings, and

Other Components (Visual Method)
3. General Conditions for Delivery
3.1 Except for investment castings, castings furnished to
this specification shall conform to the requirements of Specification A 703/A 703M, including any supplementary requirements that are indicated in the purchase order. Failure to
comply with the general requirements of Specification A 703/
A 703M constitutes nonconformance with this specification. In
case of conflict between the requirements of this specification
and Specification A 703/A 703M, this specification shall prevail.
3.2 Steel investment castings furnished to this specification
shall conform to the requirements of Specification A 985/
A 985M, including any supplementary requirements that are
indicated in the purchase order. Failure to comply with the
general requirements of Specification A 985/A 985M constitutes nonconformance with this specification. In case of conflict between the requirements of this specification and Specification A 985/A 985M, Specification A 985/A 985M shall
prevail.

2. Referenced Documents
2.1 ASTM Standards: 3
A 488/A 488M Practice for Steel Castings, Welding, Qualifications of Procedures and Personnel
A 703/A 703M Specification for Steel Castings, General
Requirements, for Pressure-Containing Parts
A 985/A 985M Specification for Steel Investment Castings
General Requirements, for Pressure-Containing Parts
E 165 Test Method for Liquid Penetrant Examination
E 709 Guide for Magnetic Particle Examination
2.2 Manufacturers Standardization Society of the Valve
and Fittings Industry Standard:4

4. Ordering Information
4.1 The inquiry and order should include or indicate the
following:
4.1.1 A description of the casting by pattern number or
drawing (dimensional tolerances shall be included on the
casting drawing),
4.1.2 Grade of steel,
4.1.3 Options in the specification,
4.1.4 Whether the castings are to be produced using the
investment casting process, and
4.1.5 The supplementary requirements desired including the
standards of acceptance.

1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
A01.18 on Castings.
Current edition approved May 1, 2007. Published May 2007. Originally
approved in 1939. Last previous edition approved in 2004 as A 216/A 216M 04.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-216/SA-216M in Section II of that code.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at [email protected]. For Annual Book of ASTM
Standards volume information, refer to the standards Document Summary page on
the ASTM website.
4
Available from Manufacturers Standardization Society of the Valve and Fittings
Industry (MSS), 127 Park St., NE, Vienna, VA 22180-4602, http://www.msshq.com.

5. Heat Treatment
5.1 All castings shall receive a heat treatment proper to their
design and chemical composition.
5.2 Castings shall be furnished in the annealed, or normalized, or normalized and tempered condition unless Supplementary Requirement S15 is specified.

*A Summary of Changes section appears at the end of this standard.

Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
--`,,```,,,,````-`-`,,`,,`,`,,`---

Copyright ASTM International

Provided by IHS under license with ASTM
No reproduction or networking permitted without license from IHS

1
Not for Resale

A 216/A 216M 07

6. Temperature Control
6.1 Furnace temperatures for heat treating shall be effectively controlled by pyrometer.

Tensile strength, ksi

[MPa]
Yield strength,A min,
ksi [MPa]
Elongation in 2 in.
[50 mm], min, %B
Reduction of area,
min, %

7. Chemical Composition
7.1 The steel shall be in accordance with the requirements
as to chemical composition prescribed in Table 1.

9. Quality
9.1 The surface of the casting shall be examined visually
and shall be free of adhering sand, scale, cracks, and hot tears.
Other surface discontinuities shall meet the visual acceptance
standards specified in the order. Visual Method SP-55 or other
visual standards may be used to define acceptable surface
discontinuities and finish. Unacceptable visual surface discontinuities shall be removed and their removal verified by visual
examination of the resultant cavities.

Composition, %

0.25C
1.20C
0.04
0.045
0.60

0.30
0.50
0.50
0.20
0.03
1.00

0.30
0.50
0.50
0.20
0.03
1.00

0.30
0.50
0.50
0.20
0.03
1.00

A
For each reduction of 0.01 % below the specified maximum carbon content, an
increase of 0.04 % manganese above the specified maximum will be permitted up
to a maximum of 1.10 %.
B
For each reduction of 0.01 % below the specified maximum carbon content, an
increase of 0.04 % Mn above the specified maximum will be permitted up to a
maximum of 1.28 %.
C
For each reduction of 0.01 % below the specified maximum carbon content, an
increase of 0.04 % manganese above the specified maximum will be permitted to
a maximum of 1.40 %.
D
Not applicable when Supplementary Requirement S11 is specified.

Copyright ASTM International

Provided by IHS under license with ASTM
No reproduction or networking permitted without license from IHS

70 to 95
[485 to 655]
36 [250]

70 to 95
[485 to 655]
40 [275]

24

22

22

35

35

35

--`,,```,,,,````-`-`,,`,,`,`,,`---

0.30B
1.00B
0.04
0.045
0.60

60 to 85
[415 to 585]
30 [205]

10. Repair by Welding

10.1 Repairs shall be made using procedures and welders
qualified under Practice A 488/A 488M.
10.2 Weld repairs shall be inspected to the same quality
standards that are used to inspect the castings. When castings
are produced with Supplementary Requirement S4 specified,
weld repairs shall be inspected by magnetic particle examination to the same standards that are used to inspect the castings.
When castings are produced with Supplementary Requirement
S5 specified, weld repairs on castings that have leaked on
hydrostatic test, or on castings in which the depth of any cavity
prepared for repair welding exceeds 20 % of the wall thickness
or 1 in. [25 mm], whichever is smaller, or on castings in which
any cavity prepared for welding is greater than approximately
10 in.2[65 cm2], shall be radiographed to the same standards
that are used to inspect the castings.
10.3 Castings containing any repair weld that exceeds 20 %
of the wall thickness or 1 in. [25 mm], whichever is smaller, or
that exceeds approximately 10 in.2[65 cm2] in area, or that was
made to correct hydrostatic test defects, shall be stress relieved
or heat treated after welding. This mandatory stress relief or
heat treatment shall be in accordance with the procedure
qualification used.

Grade
Grade
Grade
WCC
WCB
WCA
UNS J02502 UNS J03002 UNS J02503
0.25A
0.70A
0.04
0.045
0.60

Grade
WCC

9.2 When additional inspection is desired, Supplementary

Requirements S4, S5, and S10 may be ordered.
9.3 The castings shall not be peened, plugged, or impregnated to stop leaks.

TABLE 1 Chemical Requirements

Carbon, max
Manganese, max
Phosphorus, max
Sulfur, max
Silicon, max
Specified residual elements:
Copper, max
Nickel, max
Chromium, max
Molybdenum, max
Vanadium, max
Total of these specified residual
elements, maxD

Grade
WCB

A
Determine by either 0.2 % offset method or 0.5 % extension-under-load
method.
B
When ICI test bars are used in tensile testing as provided for in Specification
A 703/A 703M, the gage length to reduced section diameter ratio shall be 4 to 1.

8. Tensile Requirements
8.1 Steel used for the castings shall be in accordance with
the requirements as to tensile properties prescribed in Table 2.

Element

Grade
WCA

11. Keywords
11.1 carbon steel; high temperature; pressure-containing
parts; steel castings

2
Not for Resale

//^:^^#^~^^""~:@":^*^~$~"#:*~~#@"@:"*"~^$^~:^":^@::~*\\

TABLE 2 Tensile Requirements

5.3 Heat treatment shall be performed after castings have

been allowed to cool below the transformation range.

A 216/A 216M 07
SUPPLEMENTARY REQUIREMENTS
The following supplementary requirements shall not apply unless specified in the purchase order. A
list of standardized supplementary requirements for use at the option of the purchaser is included in
Specification A 703/A 703M. Those which are ordinarily considered suitable for use with this
specification are given below. Others enumerated in Specification A 703/A 703M may be used with
this specification upon agreement between the manufacturer and purchaser.
S1. Unspecified Elements

S16.2 The maximum carbon equivalent shall be as follows:

CE maximum
Maximum specified section thickness less than or equal to 1 in. [25
0.43
mm]
Maximum specified section thickness greater than 1 in. [25 mm]
0.45

S2. Destruction Tests

S3. Bend Test
S4. Magnetic Particle Inspection

S16.3 Determine the carbon equivalent (CE) as follows:

Mn ~Cr 1 Mo 1 V! ~Ni 1 Cu!
CE 5 C 1 6 1
1
5
15

S5. Radiographic Inspection

S10. Examination of Weld Preparation
S10.1 The method of performing the magnetic particle or
liquid penetrant test shall be in accordance with Guide E 709 or
Test Method E 165.

S16.4 Vanadium and niobium maximum content based upon

heat analysis shall be:
NOTE 1Niobium = columbium
Maximum vanadium
Maximum niobium
Maximum vanadium plus niobium

S11. Carbon Equivalent

S11.1 When specified on the order, the maximum carbon
equivalent shall be:
Grade
WCA
WCB
WCC

0.02 wt %
0.02 wt %
0.03 wt %

S16.5 The sum of the nickel and copper contents, based

upon heat analysis, shall not exceed 0.15 wt %.
S16.6 The minimum carbon content shall be 0.18 wt %. The
maximum carbon content shall be as required for the appropriate grade.
S16.7 Welding consumables for repair welds shall be of the
low-hydrogen type. E60XX electrodes shall not be used and
the resulting weld chemistry shall meet the same chemistry
requirements as the base metal.
S16.8 In addition to the requirements for product marking in
the specification, an HF-N stamp or marking shall be
provided on each casting to identify that the casting complies
with this supplementary requirement.

Carbon Equivalent, max

0.50
0.50
0.55

S11.2 Carbon equivalent (CE) shall be determined as follows:

Mn Cr 1 Mo 1 V Ni 1 Cu
CE 5 C 1 6 1
1 15
5

S15. Quench and Temper Heat-Treatment

S16. Requirements for Carbon Steel Castings for
Hydrofluoric Acid Alkylation Service
S16.1 Castings shall be provided in the normalized or
normalized and tempered heat-treated condition.

SUMMARY OF CHANGES
Committee A01 has identified the location of selected changes to this standard since the last issue
(A 216/A 216M - 04) that may impact the use of this standard. (Approved May 1, 2007.)

//^:^^#^~^^""~:@":^*^~$~"#:*~~#@"@:"*"~^$^~:^":^@::~*\\

(1) Revised Supplementary Requirement S16.1 to permit the

normalized and tempered condition.

--`,,```,,,,````-`-`,,`,,`,`,,`---

Copyright ASTM International

Provided by IHS under license with ASTM
No reproduction or networking permitted without license from IHS

3
Not for Resale

A 216/A 216M 07

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.

--`,,```,,,,````-`-`,,`,,`,`,,`---

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website
(www.astm.org).

Copyright ASTM International

Provided by IHS under license with ASTM
No reproduction or networking permitted without license from IHS

4
Not for Resale
//^:^^#^~^^""~:@":^*^~$~"#:*~~#@"@:"*"~^$^~:^":^@::~*\\