Chapter 16. Magnetic properties

Learning objectives:
-

To understand the genesis of magnetism, different types of magnetism,

mechanism that explains the permanent magnetic behavior of some materials
and the process to alter and in some cases tailor the magnetic properties.

Material Science
Prof. Satish V. Kailas
Associate Professor
Dept. of Mechanical Engineering,
Indian Institute of Science,
Bangalore 560012
India

Chapter 16. Magnetic properties

Highlights, Motivation and Critical Concepts:
Engineering materials are important in everyday life because of their versatile structural properties.
Other than these properties, they do play an important role because of their physical properties. Prime
physical properties of materials include: electrical properties; thermal properties; magnetic properties;
and optical properties.
Magnetic properties play an important role in daily life. Magnetic materials are used in electric motors,
generators, transformers. Modern-day devices use data storage technology that is based on magnetic
particles. Magnetic materials are used in devices like telephones, televisions, supercomputers, etc. they
are also used in medical technology, for example DNA sequencing. This chapter deals with the genesis
of magnetism, different types of magnetism, and finally different types of magnets.

Multiple Choice Questions Bank:

1. Basic source of magnetism ______________.

(a) Charged particles alone
(c) Magnetic dipoles

(b) Movement of charged particles

(d) Magnetic domains

2. Units for magnetic flux density

(a) Wb / m2

(b) Wb / A.m

(c) A / m

(d) Tesla / m

(c) A / m

(d) Tesla / m

(c) Tesla / m

(d) Henry / m

(c) A / m

(d) Tesla / m

3. Magnetic permeability has units as

(a) Wb / m2

(b) Wb / A.m

4. Magnetic permeability has units as

(a) Tesla

(b) Henry

5. Magnetic field strengths units are

(a) Wb / m2

(b) Wb / A.m

6. Example for dia-magnetic materials

(a) super conductors (b) alkali metals

(c) transition metals

(d) Ferrites

(c) transition metals

(d) Ferrites

(c) transition metals

(d) Ferrites

7. Example for para-magnetic materials

(a) super conductors (b) alkali metals

8. Example for ferro-magnetic materials

(a) super conductors (b) alkali metals

9. Example for anti-ferro-magnetic materials

(a) salts of transition elements

(b) rare earth elements

(c) transition metals

(d) Ferrites

(c) transition metals

(d) Ferrites

10. Example for ferri-magnetic materials

(a) salts of transition elements

(b) rare earth elements

11. Magnetic susceptibility para-magnetic materials is

(a) +10-5

(b) -10-5

(c) 105

(d) 10-5 to 10-2

12. Magnetic susceptibility dia--magnetic materials is

(a) +10-5

(b) -10-5

(c) 105

(d) 10-5 to 10-2

13. Magnetic susceptibility ferro-magnetic materials is

(a) +10-5

(b) -10-5

(c) 105

(d) 10-5 to 10-2

14. Typical size of magnetic domains ______ (mm).

(a) 1-10

(b) 0.1-1

(c) 0.05

(d) 0.001

15. Typical thickness of Bloch walls ______ (nm).

(a) 0.1-1

(b) 1-10

16. Example for soft magnet

(c) 10-50

(d) 100

(a) 45 Permalloy

(b) CrO2

(c) Fe-Pd

(d) Alnico

(c) Fe-Pd

(d) Alnico

17. Example for hard magnet

(a) 45 Permalloy

(b) CrO2

18. Example for magnetic material used in data storage devices

(a) 45 Permalloy

Answers:
1. b
2. a
3. b
4. d
5. c
6. a
7. b
8. c
9. a
10. d
11. d
12. b
13. c
14. c
15. d
16. a
17. d
18. b

(b) CrO2

(c) Cunife

(d) Alnico

Material Science
Prof. Satish V. Kailas
Associate Professor
Dept. of Mechanical Engineering,
Indian Institute of Science,
Bangalore 560012
India

Chapter 16. Magnetic properties

Engineering materials are important in everyday life because of their versatile structural
properties. Other than these properties, they do play an important role because of their
physical properties. Prime physical properties of materials include: electrical properties;
thermal properties; magnetic properties; and optical properties. Magnetic properties play
an important role in daily life. Magnetic materials are used in electric motors, generators,
transformers. Modern-day devices use data storage technology that is based on magnetic
particles. Magnetic materials are used in devices like telephones, televisions,
supercomputers, etc. they are also used in medical technology, for example DNA
sequencing.
This chapter shall describe magnetic properties like dia-, para-, and ferro-magnetism
along with anti-ferro- and ferri- magnetism. It also includes discussion about temperature
effects on magnetic behavior, followed by magnetic domains and hysteresis.
Magnetism is a phenomenon by which a material exerts either attractive or repulsive
force on another. Basic source of magnetic force is movement of electrically charged
particles. Magnetic behavior of a material can be traced to the structure of atoms.
Electrons in atoms have a planetary motion in that they go around the nucleus. This
orbital motion and its own spin cause separate magnetic moments, which contribute to
the magnetic behavior of materials. Thus every material can respond to a magnetic field.
However, the manner in which a material responds depend much on its atomic structure,
and determines whether a material will be strongly or weakly magnetic.
Magnetic moment due to spin of an electron is known as Bohr magneton,MB, is the most
fundamental magnetic moment.
MB =

qh
= 9.274 X 10 24 A.m 2
4me

where q is the charge on the electron, h Plancks constant, me mass of electron. This
moment is directed along the axis of electron spin. Magnetic moment resulted from

particles in nucleus is much smaller than that result from spin of electron, so it is ignored.
If magnetic moment of electrons could sum up, then the world would be a magnetic
place. Fortunately, two reasons are found to explain this phenomenon:- First: according
to Pauli exclusion rule, two electrons with same energy level must have opposite spins
thus so are their magnetic moments, which cancel out each other. Second: orbital
moments of electrons also cancel out each other thus no net magnetic moments if there
is no unpaired electron(s). Some elements such as transition elements, lanthanides, and
actinides have a net magnetic moment since some of their energy levels have an unpaired
electron.
Magnetic dipoles are found to exist in magnetic materials, analogous to electric dipoles.
A magnetic dipole is a small magnet composed of north and south poles instead of
positive and negative charges. Within a magnetic field, the force of field exerts a torque
that tends to orient the dipoles with the filed. Magnetic forces are generated by moving
electrically charged particles. These forces are in addition to any electrostatic forces that
may already exist. It is convenient to think magnetic forces in terms of distributed field,
which is represented by imaginary lines. These lines also indicate the direction of the
force. If a magnetic field is generated by passing current I through a coil of length l and
number of turns n, then the magnetic field strength is given by:
H =

nI
l

Units for magnetic field strength, thus, are A/m.

Magnetic flux density (induction) is the measure of lines within a medium. It has units as
weber (Wb) /m2 or tesla.
B = H

where permeability. It is a specific property of the medium, and has units as Wb/A.m
or henries (H) /m.
Flux density, B, is determined by the manner in which induced and permanent dipoles
interact with the applied field. If the magnetic moments reinforce the applied field i.e.
greater number of lines of flux are created, and the field is magnified. This is represented
as

> 0
where 0 magnetic permeability of vacuum.
Several parameters may be used to describe magnetic properties of solids. One of them is
relative permeability (r). It is a measure of the degree to which the material can be
magnetized.

r =

Another field quantity called magnetization, M, is defined as

B = 0 H + 0 M = 0 r H
M = mH
m is called the magnetic susceptibility.

m = r 1
There are many ways a material can be magnetized i.e. many types of magnetism. Three
basic magnetisms are: dia-magnetism, para-magnetism and ferro-magnetism. Anti-ferromagnetism and ferri-magnetisms are considered as subclasses of ferro-magnetism. A
material exhibits one of these magnetisms.
16.1 Dia-, Para-, and Ferro-magnetism
Dia-magnetism is very weak form of magnetism. It exists only when an external field is
applied, and is non-permanent. The applied external field acts on atoms of a material,
slightly unbalancing their orbiting electrons, and creates small magnetic dipoles within
atoms which oppose the applied field. This action produces a negative magnetic effect
known as diamagnetism. The induced magnetic moment is small, and the magnetization
(M) direction is opposite to the direction of applied field (H). Thus the relative
permeability is less than unity i.e. magnetic susceptibility is negative, and is in order of 10-5. Dia-magnetism is virtually found in all materials; however it is observable only in
absence of other magnetisms. This form of magnetism is of no practical importance.
Materials such as Cu, Ag, Si, Ag and alumina are diamagnetic at room temperature.
Superconductors are perfect dia-magnets (m=-1); they lose their superconductivity at
higher temperatures or in the presence of a magnetic field.
Materials which exhibit a small positive magnetic susceptibility in the presence of a
magnetic field are called para-magnetic, and the effect is termed as para-magnetism.
When materials have unpaired electrons, a net magnetic moment due to electron spin is
associated with each atom. In the absence of an external field, the orientations of these
atomic magnetic moments are random leading to no net magnetization. When an external
field is applied dipoles line-up with the field, resulting in a positive magnetization.
However, because the dipoles do not interact, extremely large magnetic fields are
required to align all of the dipoles. In addition, the effect is lost as soon as the magnetic
field is removed. Since thermal agitation randomizes the directions of the magnetic
dipoles, an increase in temperature decreases the paramagnetic effect. Para-magnetism is
produced in many materials like aluminium, calcium, titanium, alloys of copper.

Magnetic susceptibility of these materials is slightly positive, and lies in the range 10-5 to
10-2.
Both dia- and para- magnetic materials are considered as non-magnetic because they
exhibit magnetization only in presence of an external field. Certain materials possess
permanent magnetic moments even in the absence of an external field. This is result of
permanent unpaired dipoles formed from unfilled energy levels. These dipoles can easily
line-up with the imposed magnetic field due to the exchange interaction or mutual
reinforcement of the dipoles. These are chrematistics of ferro-magnetism. Materials with
ferro-magnetism (Examples: Fe, Co, Ni, Gd) possess magnetic susceptibilities
approaching 106. Consequently,
H << M , and B 0 M

The mutual spin alignment in ferro-magnetic materials exists over relatively large volume
regions of the crystal called domains. The susceptibility of ferro-magnetic materials
depends upon the intensity of the applied field. Above the Curie temperature, ferromagnetic materials behave as para-magnetic materials and their susceptibility is given by
the Curie-Weiss law, defined as follows:

m =

C
T Tc

where C material constant, T temperature, Tc Curie temperature.

In some materials such as Mn, Cr, MnO, NiO, CoO, MnCl2 the magnetic moments
produced in neighboring dipoles line up in opposition to one another in the magnetic
field, even though the strength of each dipole is very high. This will result in zero
magnetization, and the effect is called anti-ferro-magnetism. Exchange interaction which
is responsible for parallel alignment of spins is extremely sensitive to inter-atomic
spacing and to the atomic positions. This sensitivity causes anti-parallel alignment of
spins. When the strength of anti-parallel spin magnetic moments is equal, no net spin
moment exists, and resulting susceptibilities are quite small. One noticeable characteristic
of anti-ferro-magnets is they attain maximum susceptibility at a critical temperature
called Neel temperature. At temperatures above this, anti-ferro-magnets become paramagnetic.
On the other hand, some ceramic materials exhibit net magnetization. This is because of
either the strength or number of opposing dipoles is not equal. In a magnetic field, the
dipoles of a cation may line up with the field, while dipoles of other cation may not.
These ceramics are called ferrites, and the effect is known as ferri-magnetism. Ferrimagnetism is similar to anti-ferro-magnetism in that the spins of different atoms or ions
line up anti-parallel. However, the spins do not cancel each other out, and a net spin
moment exists. Below the Neel temperature, therefore, ferromagnetic materials behave
very much like ferromagnetic materials and are paramagnetic above the Neel
temperature. These materials exhibit a large but field dependent magnetic susceptibility

similar to ferro-magnets. They also show Curie-Weiss behavior. As these ceramics are
good insulators, electrical losses are minimal, and hence ferrites have lot of applications
in devices such as high frequency transformers. Examples: Fe3O4, NiFe2O4,
(Mn.Mg)Fe2O4, PbFe12O19, Ba Fe12O19, YIG yttrium iron garnet Y3Fe5O12.
The table 16.1 compares different magnetism.

Table 16-1: Various types of magnetisms.

Magnetism

Magnetic susceptibility
sign
magnitude

Dia

Small, Constant

Para

Small, Constant

Ferro

Large, Function of H

Anti-Ferro

Small, Constant

Ferri

Large, Function of H

Examples
Organic materials, superconducting
materials, metals like Bi
Alkali and transition metals, rare
earth elements
Transition metals (Fe, Ni, Co), rare
earth elements (Gd)
Salts of transition elements (MnO)
Ferrites (MnFe2O4, ZnFe2O4) and
chromites

16.2 Influence of temperature on magnetic behavior

Temperature does influence the magnetic characteristics of materials, as it influences
electrical properties. With rising temperature, magnitude of the atom thermal vibrations
increases. This may lead to more randomization of atomic magnetic moments as they are
free to rotate. Usually, atomic thermal vibrations counteract forces between the adjacent
atomic dipole moments, resulting in dipole misalignment up to some extent both in
presence and absence of external field. As a consequence of it, saturation magnetization
initially decreases gradually, then suddenly drops to zero at a temperature called Curie
temperature, Tc. The magnitude of the Curie temperatue is dependent on the material. For
example: for cobalt 1120 C, for nickel 335 C, for iron 768 C, and for Fe3O4 585
C.
16.3 Domains and Hysteresis
In addition to susceptibility differences, the different types of magnetism can be
distinguished by the structure of the magnetic dipoles in regions called domains. Each
domain consists of magnetic moments that are aligned, giving rise to a permanent net
magnetic moment per domain. Each of these domains is separated from the rest by

domain boundaries / domain walls. Boundaries, also called Bolch walls, are narrow zones
in which the direction of the magnetic moment gradually and continuously changes from
that of one domain to that of the next. The domains are typically very small about 50 m
or less, while the Bloch walls are about 100 nm thick. For a polycrystalline specimen,
each grain may have more than one microscopic sized domain.
Domains exist even in the absence of an external field. In a material that has never been
exposed to a magnetic field, the individual domains have a random orientation. This type
of arrangement represents the lowest free energy. The domain structure of material is
determined by many types of energies, with most stable structure being attained when the
overall potential energy of the material is a minimum. Total magnetic energy of a
material is the sum of the contributions of the following: exchange energy, magnetostatic energy, magneto-crystalline anisotropy energy, domain wall energy and magnetostrictive energy. When the bulk material is un-magnetized, the net magnetization of these
domains is zero, because adjacent domains may be orientated randomly in any number of
directions, effectively canceling each other out.
The average magnetic induction of a ferro-magnetic material is intimately related to the
domain structure. When a magnetic field is imposed on the material, domains that are
nearly lined up with the field grow at the expense of unaligned domains. This process
continues until only the most favorably oriented domains remain. In order for the
domains to grow, the Bloch walls must move, the external field provides the force
required for this moment. When the domain growth is completed, a further increase in the
magnetic field causes the domains to rotate and align parallel to the applied field. At this
instant material reaches saturation magnetization and no further increase will take place
on increasing the strength of the external field. Saturation magnetization is the greatest
amount of magnetization tat the material can obtain. Under these conditions the
permeability of these materials becomes quite small. Figure 16-1 in the following
presents the relation between the applied field strength and magnetization of the material.

Figure 16-1: Magnetization saturation of a material with applied field.

As shown in figure 16-1, magnetization increases with applied filed, and reaches a
saturation value in a sufficiently stronger filed. Once magnetic saturation has been
achieved, a decrease in the applied field back to zero results in a macroscopically
permanent or residual magnetization, known as remanance, Mr. The corresponding
induction, Br, is called retentivity or remanent induction of the magnetic material. This
effect of retardation by material is called hysteresis. The material acts as a permanent
magnet, even at zero applied field. At this point, spin orientations within domains have
readily rotated back to their favorable position, but the original random domain
arrangement is not achieved. This is because the resistance offered by the domain walls
prevents re-growth of the domains i.e. domain growth process is not entirely reversible,
and domain wall motion is limited. The magnetic field strength needed to bring the
induced magnetization to zero is termed as coercivity, Hc. This must be applied antiparallel to the original field.
A further increase in the field in the opposite direction results in a maximum induction
i.e. saturation magnetization, but in the opposite direction. The field can once again be
reversed, and the field-magnetization loop can be closed, and so the corresponding fieldinduction loop. This loop is known as hysteresis loop or B-H plot or M- H plot. The area
within the hysteresis loop represents the energy loss per unit volume of material for one
cycle. The B-vs-H curve in figure 16-2 represents a hysteresis loop taken to saturation.
However, it is not necessary to increase the field strength to saturation to generate the
loop.

Figure 16-2: Schematic presentation of a typical hysteresis loop.

The coercivity of the material is a micro-structure sensitive property. This dependence is
known as magnetic shape anisotropy. The coercivity of recording materials needs to be
smaller than that for others since data written onto a data storage medium should be
erasable. On the other hand, the coercivity values should be higher since the data need to
be retained. Thus such materials are called magnetically semi-hard. Examples: Hard
ferrites based on Ba, CrO2, -Fe2O3; alloys based on Co-Pt-Ta-Cr, Fe-Pt and Fe-Pd, etc.

Soft magnets are characterized by low coercive forces and high magnetic permeabilities;
and are easily magnetized and de-magnetized. They generally exhibit small hysteresis
losses. Application of soft magnets include: cores for electro-magnets, electric motors,
transformers, generators, and other electrical equipment. Examples: ingot iron, lowcarbon steel, Silicon iron, superalloy (80% Ni-5% Mo-Fe), 45 Permalloy (55%Fe45%Ni), 2-79 Permalloy (79% Ni-4% Mo-Fe), MnZn ferrite / Ferroxcube A (48%
MnFe2O4-52%ZnFe2O4), NiZn ferrite / Ferroxcube B (36% NiFe2O4-64% ZnFe2O4), etc.
Hard magnets are characterized by high remanent inductions and high coercivities. These
are also called permanent magnets or hard magnets. They generally exhibit large
hysteresis losses. Examples: Co-steel, Tungsten steel, SmCo5, Nd2Fe14B, ferrite
Bao.6Fe2O3, Cunife (60% Cu 20% Ni-20% Fe), Alnico (alloy of Al, Ni, Co and Fe), etc.
Applications include fractional horse-power motors, automobiles, audio- and videorecorders, earphones, computer peripherals, and clocks.
References
1. William D. Callister, Jr, Materials Science and Engineering An introduction,
sixth edition, John Wiley & Sons, Inc. 2004.
2. V. Raghavan, Materials Science and Engineering, third edition, Prentice Hall of
India Private Limited, New Delhi, 1990.
3. D. Jiles, Introduction to Magnetism and Magnetic Materials, Nelson Thornes,
Cheltenham, UK 1998.

Material Science
Prof. Satish V. Kailas
Associate Professor
Dept. of Mechanical Engineering,
Indian Institute of Science,
Bangalore 560012
India

Chapter 16. Magnetic properties

Magnetism

Magnetism is a phenomenon by which a material exerts either attractive or repulsive

force on another.
Basic source of magnetic force is movement of electrically charged particles. Thus
magnetic behavior of a material can be traced to the structure of atoms.
Electrons in atoms have a planetary motion in that they go around the nucleus. This
orbital motion and its own spin cause separate magnetic moments, which contribute
to the magnetic behavior of materials. Thus every material can respond to a magnetic
field.
However, the manner in which a material responds depend much on its atomic
structure, and determines whether a material will be strongly or weakly magnetic.

Bohr magneton

Magnetic moment due to spin of an electron is known as Bohr magneton, MB.

MB =

qh
= 9.274 X 10 24 A.m 2
4me

where q is the charge on the electron, h Plancks constant, me mass of electron.

Bohr magneton is the most fundamental magnetic moment.

Why not all materials are magnets?

As every material consists spinning electrons, each of them could be a magnet.

Fortunately, not so!
There are two reasons for it.
First: according to Pauli exclusion rule, two electrons with same energy level must
have opposite spins thus so are their magnetic moments, which cancel out each
other.
Second: orbital moments of electrons also cancel out each other thus no net
magnetic moments if there is no unpaired electron(s).

Some elements such as transition elements, lanthanides, and actinides have a net
magnetic moment since some of their energy levels have an unpaired electron.

Magnetic dipoles

Magnetic dipoles are found to exist in magnetic materials, analogous to electric

dipoles.
A magnetic dipole is a small magnet composed of north and south poles instead of
positive and negative charges.
Within a magnetic field, the force of field exerts a torque that tends to orient the
dipoles with the filed.
Magnetic forces are generated by moving electrically charged particles. These forces
are in addition to any electrostatic forces that may already exist.
It is convenient to think magnetic forces in terms of distributed field, which is
represented by imaginary lines. These lines also indicate the direction of the force.

Magnetic field

If a magnetic field is generated by passing current I through a coil of length l and

number of turns n, then the magnetic field strength, H (units A/m), is given by

H=

nI
l

Magnetic flux density (induction) is the measure of lines within a medium. It has units as
weber (Wb) /m2 or tesla and is defined as

B = H

where permeability. It is a specific property of the medium, and has units as

Wb/A.m or henry (H) /m.

Relative magnetic permeability, is defined as

r =

r is a measure of the degree to which the material can be magnetized.

where 0 magnetic permeability of vacuum.

If M- magnetization defined as M, is defined as M = m H then

B = 0 H + 0 M = 0 r H

m is called the magnetic susceptibility and is given as

m = r 1
Types of Magnetism

A material is magnetically characterized based on the way it can be magnetized.

This depends on the materials magnetic susceptibility its magnitude and sign.

Three basic magnetisms are:

Dia-magnetism
Para-magnetism
Ferro-magnetism. Anti-ferro-magnetism and ferri-magnetisms are considered as
subclasses of ferro-magnetism.

Dia-magnetism

Very weak; exists ONLY in presence of an external field, non-permanent.

Applied external field acts on atoms of a material, slightly unbalancing their orbiting
electrons, and creates small magnetic dipoles within atoms which oppose the applied
field. This action produces a negative magnetic effect known as diamagnetism.
The induced magnetic moment is small, and the magnetization (M) direction is
opposite to the direction of applied field (H).
Thus the relative permeability is less than unity i.e. magnetic susceptibility is
negative, and is in order of -10-5.
Materials such as Cu, Ag, Si, Ag and alumina are diamagnetic at room temperature.

Para-magnetism

Slightly stronger; when an external field is applied dipoles line-up with the field,
resulting in a positive magnetization. However, the dipoles do not interact.
Materials which exhibit a small positive magnetic susceptibility in the presence of a
magnetic field are called para-magnetic, and the effect is termed as para-magnetism.
In the absence of an external field, the orientations of atomic magnetic moments are
random leading to no net magnetization.
When an external field is applied dipoles line-up with the field, resulting in a positive
magnetization.
However, because the dipoles do not interact, extremely large magnetic fields are
required to align all of the dipoles.
In addition, the effect is lost as soon as the magnetic field is removed.
Since thermal agitation randomizes the directions of the magnetic dipoles, an increase
in temperature decreases the paramagnetic effect.
Para-magnetism is produced in many materials like aluminium, calcium, titanium,
alloys of copper.

Magnetic susceptibility of these materials is slightly positive, and lies in the range
+10-5 to +10-2.

Ferro-magnetism

Both dia- and para- magnetic materials are considered as non-magnetic because they
exhibit magnetization only in presence of an external field.
Certain materials possess permanent magnetic moments even in the absence of an
external field.
This is result of permanent unpaired dipoles formed from unfilled energy levels.
These dipoles can easily line-up with the imposed magnetic field due to the exchange
interaction or mutual reinforcement of the dipoles. These are chrematistics of ferromagnetism.
Materials with ferro-magnetism (Examples: Fe, Co, Ni, Gd) possess magnetic
susceptibilities approaching 106.
Above the Curie temperature, ferro-magnetic materials behave as para-magnetic
materials and their susceptibility is given by the Curie-Weiss law, defined as

m =

C
T Tc

where C material constant, T temperature, Tc Curie temperature.

Ferro Magnets are very strong; dipoles line-up permanently upon application of
external field. Has two sub-classes:o Anti-ferro-magnetism:
o Ferri-magnetism:

Anti-ferro-magnetism

Dipoles line-up, but in opposite directions, resulting in zero magnetization.

Eg: Mn, Cr, MnO, NiO, CoO, MnCl2
Exchange interaction which is responsible for parallel alignment of spins is extremely
sensitive to inter-atomic spacing and to the atomic positions. This sensitivity causes
anti-parallel alignment of spins.
When the strength of anti-parallel spin magnetic moments is equal, no net spin
moment exists, and resulting susceptibilities are quite small.
One noticeable characteristic of anti-ferro-magnets is they attain maximum
susceptibility at a critical temperature called Neel temperature. At temperatures above
this, anti-ferro-magnets become para-magnetic.

Ferri-magnetism

Some ceramic materials exhibit net magnetization.

Eg: Fe3O4, NiFe2O4, (Mn.Mg)Fe2O4, PbFe12O19, Ba Fe12O19, YIG yttrium iron

garnet Y3Fe5O12.
In a magnetic field, the dipoles of a cation may line up with the field, while dipoles of
other cation may not. These ceramics are called ferrites, and the effect is known as
ferri-magnetism.
Ferri-magnetism is similar to anti-ferro-magnetism in that the spins of different atoms
or ions line up anti-parallel. However, the spins do not cancel each other out, and a
net spin moment exists.
Below the Neel temperature, therefore, ferromagnetic materials behave very much
like ferromagnetic materials and are paramagnetic above the Neel temperature.
These materials exhibit a large but field dependent magnetic susceptibility similar to
ferro-magnets.
They also show Curie-Weiss behavior. As these ceramics are good insulators,
electrical losses are minimal, and hence ferrites have lot of applications in devices
such as high frequency transformers.

Magnetism

Magnetic susceptibility
sign
magnitude

Dia

Small, Constant

Para

Small, Constant

Ferro

Large, Function of H

Anti-Ferro

Small, Constant

Ferri

Large, Function of H

Examples
Organic materials, superconducting
materials, metals like Bi
Alkali and transition metals, rare
earth elements
Transition metals (Fe, Ni, Co), rare
earth elements (Gd)
Salts of transition elements (MnO)
Ferrites (MnFe2O4, ZnFe2O4) and
chromites

Temperature effect

Temperature does have a definite effect on a materials magnetic behavior.

With rising temperature, magnitude of the atom thermal vibrations increases. This
may lead to more randomization of atomic magnetic moments as they are free to
rotate.
Usually, atomic thermal vibrations counteract forces between the adjacent atomic
dipole moments, resulting in dipole misalignment up to some extent both in presence
and absence of external field.
As a consequence of it, saturation magnetization initially decreases gradually, then
suddenly drops to zero at a temperature called Curie temperature, Tc.
The magnitude of the Curie temperatue is dependent on the material. For example: for
cobalt 1120 C, for nickel 335 C, for iron 768 C, and for Fe3O4 585 C.

Magnetic domains

In addition to susceptibility differences, the different types of magnetism can be

distinguished by the structure of the magnetic dipoles in regions called domains.
Each domain consists of magnetic moments that are aligned, giving rise to a
permanent net magnetic moment per domain.
Each of these domains is separated from the rest by domain boundaries / domain
walls. Boundaries, also called Bolch walls, are narrow zones in which the direction of
the magnetic moment gradually and continuously changes from that of one domain to
that of the next.
The domains are typically very small about 50 m or less, while the Bloch walls are
about 100 nm thick. For a polycrystalline specimen, each grain may have more than
one microscopic sized domain.
Domains exist even in absence of external field.
In a material that has never been exposed to a magnetic field, the individual domains
have a random orientation. This type of arrangement represents the lowest free
energy.
When the bulk material is un-magnetized, the net magnetization of these domains is
zero, because adjacent domains may be orientated randomly in any number of
directions, effectively canceling each other out.
The average magnetic induction of a ferro-magnetic material is intimately related to
the domain structure.
When a magnetic field is imposed on the material, domains that are nearly lined up
with the field grow at the expense of unaligned domains. This process continues until
only the most favorably oriented domains remain.
In order for the domains to grow, the Bloch walls must move, the external field
provides the force required for this moment.
When the domain growth is completed, a further increase in the magnetic field causes
the domains to rotate and align parallel to the applied field. At this instant material
reaches saturation magnetization and no further increase will take place on increasing
the strength of the external field.
Under these conditions the permeability of these materials becomes quite small.

Magnetic hysteresis

1. Once magnetic saturation has been achieved, a decrease in the applied field back to
zero results in a macroscopically permanent or residual magnetization, known as
remanance, Mr. The corresponding induction, Br, is called retentivity or remanent
induction of the magnetic material. This effect of retardation by material is called
hysteresis.
2. The magnetic field strength needed to bring the induced magnetization to zero is
termed as coercivity, Hc. This must be applied anti-parallel to the original field.
3. A further increase in the field in the opposite direction results in a maximum
induction in the opposite direction. The field can once again be reversed, and the
field-magnetization loop can be closed, this loop is known as hysteresis loop or B-H
plot or M- H plot.

Semi-hard magnets

The area within the hysteresis loop represents the energy loss per unit volume of
material for one cycle.
The coercivity of the material is a micro-structure sensitive property. This
dependence is known as magnetic shape anisotropy.
The coercivity of recording materials needs to be smaller than that for others since
data written onto a data storage medium should be erasable. On the other hand, the
coercivity values should be higher since the data need to be retained. Thus such
materials are called magnetically semi-hard.
Ex.: Hard ferrites based on Ba, CrO2, -Fe2O3; alloys based on Co-Pt-Ta-Cr, Fe-Pt
and Fe-Pd, etc.

Soft magnets

1. Soft magnets are characterized by low coercive forces and high magnetic
permeabilities; and are easily magnetized and de-magnetized.
2. They generally exhibit small hysteresis losses.
3. Application of soft magnets include: cores for electro-magnets, electric motors,
transformers, generators, and other electrical equipment.
4. Ex.: ingot iron, low-carbon steel, Silicon iron, superalloy (80% Ni-5% Mo-Fe), 45
Permalloy (55%Fe-45%Ni), 2-79 Permalloy (79% Ni-4% Mo-Fe), MnZn ferrite /
Ferroxcube A (48% MnFe2O4-52%ZnFe2O4), NiZn ferrite / Ferroxcube B (36%
NiFe2O4-64% ZnFe2O4), etc.
Hard magnets

Hard magnets are characterized by high remanent inductions and high coercivities.
These are also called permanent magnets or hard magnets.
These are found useful in many applications including fractional horse-power motors,
automobiles, audio- and video- recorders, earphones, computer peripherals, and
clocks.
They generally exhibit large hysteresis losses.
Ex.: Co-steel, Tungsten steel, SmCo5, Nd2Fe14B, ferrite Bao.6Fe2O3, Cunife (60% Cu
20% Ni-20% Fe), Alnico (alloy of Al, Ni, Co and Fe), etc.

Multiple Choice Questions Bank:

1. Basic source of magnetism ______________.
(a) Charged particles alone
(c) Magnetic dipoles
2. Units for magnetic flux density

(b) Movement of charged particles

(d) Magnetic domains

(a) Wb / m2

(b) Wb / A.m

(c) A / m

(d) Tesla / m

(c) A / m

(d) Tesla / m

(c) Tesla / m

(d) Henry / m

(c) A / m

(d) Tesla / m

(c) transition metals

(d) Ferrites

(c) transition metals

(d) Ferrites

(c) transition metals

(d) Ferrites

3. Magnetic permeability has units as

(a) Wb / m2

(b) Wb / A.m

4. Magnetic permeability has units as

(a) Tesla

(b) Henry

5. Magnetic field strengths units are

(a) Wb / m2

(b) Wb / A.m

6. Example for dia-magnetic materials

(a) super conductors (b) alkali metals
7. Example for para-magnetic materials
(a) super conductors (b) alkali metals
8. Example for ferro-magnetic materials
(a) super conductors (b) alkali metals
9. Example for anti-ferro-magnetic materials
(a) salts of transition elements
(d) Ferrites

(b) rare earth elements

(c) transition metals

10. Example for ferri-magnetic materials

(a) salts of transition elements
(d) Ferrites

(b) rare earth elements

11. Magnetic susceptibility para-magnetic materials is

(c) transition metals

(a) +10-5

(b) -10-5

(c) 105

(d) 10-5 to 10-2

12. Magnetic susceptibility dia--magnetic materials is

(a) +10-5

(b) -10-5

(c) 105

(d) 10-5 to 10-2

13. Magnetic susceptibility ferro-magnetic materials is

(a) +10-5

(b) -10-5

(c) 105

(d) 10-5 to 10-2

14. Typical size of magnetic domains ______ (mm).

(a) 1-10

(b) 0.1-1

(c) 0.05

(d) 0.001

15. Typical thickness of Bloch walls ______ (nm).

(a) 0.1-1

(b) 1-10

(c) 10-50

(d) 100

(c) Fe-Pd

(d) Alnico

(c) Fe-Pd

(d) Alnico

16. Example for soft magnet

(a) 45 Permalloy

(b) CrO2

17. Example for hard magnet

(a) 45 Permalloy

(b) CrO2

18. Example for magnetic material used in data storage devices

(a) 45 Permalloy

Answers:
1.
2.
3.
4.

b
a
b
d

(b) CrO2

(c) Cunife

(d) Alnico

5. c
6. a
7. b
8. c
9. a
10. d
11. d
12. b
13. c
14. c
15. d
16. a
17. d
18. b