Loctite 603: Technical Data Sheet

Technical Data Sheet
LOCTITE 603
TYPICAL CURING PERFORMANCE
100
Steel
50
A
25
0
1min
nu
i
lum
5min10min 30min 1h
3h 6h
Cure Time
24h
72h
Cure Speed vs. Bond Gap

The rate of cure will depend on the bondline gap. The following
graph shows shear strength developed with time on steel pins
and collars at different controlled gaps and tested according to
ISO 10123.
0
1min
m
m
0.2
5m
m
0.
15
0.0
5m
m
5min10min 30min 1h
3h 6h
24h
Cure Time
72h
5C
75
100
50
25
0
1min
5min10min 30min 1h
3h 6h
Cure Time
24h
72h
Cure Speed vs. Activator

Where cure speed is unacceptably long, or large gaps are
present, applying activator to the surface will improve cure
speed. The graph below shows shear strength developed with
time using Activator 7471 and 7649 on Zinc Dichromate steel
pins and collars and tested according to ISO 10123.
75
Zinc Dichromate
25
Cure Speed vs. Temperature

The rate of cure will depend on the temperature. The graph
below shows the shear strength developed with time at
different temperatures on steel pins and collars and tested
according to ISO 10123.
% of Full Strength on Steel
Cure Speed vs. Substrate

The rate of cure will depend on the substrate used. The graph
below shows the shear strength developed with time on steel
pins and collars compared to different materials and tested
according to ISO 10123.
50
22
Specific Gravity @ 25 C
1.10
Flash Point - See MSDS
Viscosity, Brookfield - RVT, 25 C, mPas (cP):
Spindle 1, speed 20 rpm
100 to 150LMS
Viscosity, EN 12092 - MV, 25 C, after 180 s, mPas (cP):
Shear rate 277 s-1
90 to 180
75
TYPICAL PROPERTIES OF UNCURED MATERIAL
100
40
LOCTITE 603 is designed for the bonding of cylindrical fitting

parts, particularly where consistently clean surfaces cannot be
assured. The product cures when confined in the absence of
air between close fitting metal surfaces and prevents loosening
and leakage from shock and vibration. Typical applications
include retaining roller bearings or oil impregnated bushings
into housings.
PRODUCT DESCRIPTION
LOCTITE 603 provides the following product characteristics:
Technology
Acrylic
Chemical Type
Urethane methacrylate
Appearance (uncured) Green liquidLMS
Fluorescence
Positive under UV lightLMS
Components
One component - requires no mixing
Viscosity
Low
Cure
Anaerobic
Secondary Cure
Activator
Application
Retaining
Strength
High
May-2004
100
75
No Activator
50
Activator 7471
25
0
1min
Activator 7649
5min10min 30min 1h
3h 6h
Cure Time
24h
72h
TDS LOCTITE 603, May-2004

TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties:
Coefficient of Thermal Expansion, ASTM D 696, K-1
Coefficient of Thermal Conductivity, ASTM C 177,
W/(mK)
Specific Heat, kJ/(kgK)
Chemical/Solvent Resistance
Aged under conditions indicated and tested @ 22 C.
8010-6
0.10
0.30
TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties
After 24 hours @ 22 C
Compressive Shear Strength, ISO 10123:
Steel pins and collars
N/mm
(psi)
22.50LMS
(3,260)
After 30 minutes @ 22 C
N/mm
(psi)
13.50LMS
(1,960)
TYPICAL ENVIRONMENTAL RESISTANCE

Cured for 1 week @ 22 C
% RT Strength
100
75
50
25
50
100
150
Temperature, C
Heat Aging
Aged at temperature indicated and tested @ 22 C
% Initial Strength at RT
125
120C
100
100 hr
500 hr
1000 hr
Motor Oil
125
100
100
100
Unleaded Petrol
22
100
90
85
Brake fluid
22
100
90
80
Water Glycol 50/50
87
100
90
80
Ethanol
22
100
100
75
Acetone
22
90
90
90
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Material Safety Data Sheet (MSDS).
Where aqueous washing systems are used to clean the
surfaces before bonding, it is important to check for
compatibility of the washing solution with the adhesive. In
some cases these aqueous washes can affect the cure and
performance of the adhesive.
Directions for use

For Assembly
1. For best results, clean all surfaces (external and internal)
with a Loctite cleaning solvent and allow to dry.
2. If the material is an inactive metal or the cure speed is to
slow, spray with Activator 7471 or 7649 and allow to dry.
3. For Slip Fitted Assemblies, apply adhesive around the
leading edge of the pin and the inside of the collar and
use a rotating motion during assembly to ensure good
coverage.
4. For Press Fitted Assemblies, apply adhesive thoroughly
to both bond surfaces and assemble at high press on
rates.
5. For Shrink Fitted Assemblies the adhesive should be
coated onto the pin, the collar should then be heated to
create sufficient clearance for free assembly.
6. Parts should not be disturbed until sufficient handling
strength is achieved.
For Disassembly
1. Apply localized heat to the assembly to approximately 250
C. Disassemble while hot.
75
50
150C
25
0
This product is not normally recommended for use on plastics

(particularly thermoplastic materials where stress cracking of
the plastic could result). Users are recommended to confirm
compatibility of the product with such substrates.
Hot Strength
Tested at temperature
% of initial strength
Environment
1000
Henkel Loctite Americas

+860.571.5100
2000
3000
Hours
4000
5000
For Cleanup
1. Cured product can be removed with a combination of
soaking in a Loctite solvent and mechanical abrasion
such as a wire brush.
Henkel Loctite Europe

+49.89.9268.0
Henkel Loctite Asia Pacific

+81.45.758.1810
For the most direct access to local sales and technical support visit: www.loctite.com
TDS LOCTITE 603, May-2004

Loctite Material SpecificationLMS
LMS dated September-1, 1995. Test reports for each batch
are available for the indicated properties. LMS test reports
include selected QC test parameters considered appropriate to
specifications for customer use. Additionally, comprehensive
controls are in place to assure product quality and
consistency. Special customer specification requirements may
be coordinated through Henkel Loctite Quality.
Storage
Store product in the unopened container in a dry location.
Storage information may be indicated on the product container
labeling.
Optimal Storage: 8 C to 21 C. Storage below 8 C or
greater than 28 C can adversely affect product properties.
Material removed from containers may be contaminated during
use. Do not return product to the original container. Henkel
Corporation cannot assume responsibility for product which
has been contaminated or stored under conditions other than
those previously indicated. If additional information is required,
please contact your local Technical Service Center or
Customer Service Representative.
Conversions
(C x 1.8) + 32 = F
kV/mm x 25.4 = V/mil
mm / 25.4 = inches
N x 0.225 = lb
N/mm x 5.71 = lb/in
N/mm x 145 = psi
MPa x 145 = psi
Nm x 8.851 = lb.in
Nmm x 0.142 = oz.in
mPas = cP
Note
The data contained herein are furnished for information only
and are believed to be reliable. We cannot assume
responsibility for the results obtained by others over whose
methods we have no control. It is the user's responsibility to
determine suitability for the user's purpose of any production
methods mentioned herein and to adopt such precautions as
may be advisable for the protection of property and of persons
against any hazards that may be involved in the handling and
use thereof. In light of the foregoing, Henkel Corporation
specifically disclaims all warranties expressed or implied,
including warranties of merchantability or fitness for a
particular purpose, arising from sale or use of Henkel
Corporations products. Henkel Corporation specifically
disclaims any liability for consequential or incidental
damages of any kind, including lost profits. The discussion
herein of various processes or compositions is not to be
interpreted as representation that they are free from
domination of patents owned by others or as a license under
any Henkel Corporation patents that may cover such
processes or compositions. We recommend that each
prospective user test his proposed application before repetitive
use, using this data as a guide. This product may be covered
by one or more United States or foreign patents or patent
applications.
Trademark usage
LOCTITE is a trademark of Henkel Corporation
Reference 0.2
Henkel Loctite Americas

+860.571.5100
Henkel Loctite Europe

+49.89.9268.0
Henkel Loctite Asia Pacific

+81.45.758.1810
For the most direct access to local sales and technical support visit: www.loctite.com

Loctite 603: Technical Data Sheet

Uploaded by

Copyright:

Available Formats

Loctite 603: Technical Data Sheet

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Loctite 603: Technical Data Sheet

Uploaded by

Copyright:

Available Formats

Technical Data Sheet

TYPICAL CURING PERFORMANCE

Cure Speed vs. Bond Gap

Cure Speed vs. Activator

Cure Speed vs. Temperature

% of Full Strength on Steel

% of Full Strength on Steel

Cure Speed vs. Substrate

TYPICAL PROPERTIES OF UNCURED MATERIAL

LOCTITE 603 is designed for the bonding of cylindrical fitting

% of Full Strength on Steel

% of Full Strength on Steel

TDS LOCTITE 603, May-2004

TYPICAL PERFORMANCE OF CURED MATERIAL

TYPICAL ENVIRONMENTAL RESISTANCE

Water Glycol 50/50

Directions for use

This product is not normally recommended for use on plastics

Henkel Loctite Americas

Henkel Loctite Europe

Henkel Loctite Asia Pacific

TDS LOCTITE 603, May-2004

Henkel Loctite Americas

Henkel Loctite Europe

Henkel Loctite Asia Pacific

You might also like