Hetron Fabrication Process PDF

A Guide To
Fabricating
Composites With
HETRON and
AROPOL Resins
!
a
t
a
D
AT
C
F
h
t
i
W
w
o
N
TM
Ashland Specialty Chemical Company is the leading supplier of resins

for corrosion resistant and flame retardant composites
Next
Previous | Contents | Next
Table of Contents
SECTION 1
SECTION 6
Product Description
Description of HETRON and
AROPOL Resins . . . . . . . . . . . . . . . . . . . . . . . . . .3
Fabrication Methods
Fabrication Standards . . . . . . . . . . . . . . . . . . . . 24
Hand Lay-Up . . . . . . . . . . . . . . . . . . . . . . . . . . . . 26
Spray-Up . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 27
Filament Winding . . . . . . . . . . . . . . . . . . . . . . . 28
Pultrusion . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 28
Centrifugal Casting . . . . . . . . . . . . . . . . . . . . . . 29
Resin Transfer Molding . . . . . . . . . . . . . . . . . . . 29
Linings . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 30
Fabricating Thick Sections . . . . . . . . . . . . . . . . 31
Finishing Processes . . . . . . . . . . . . . . . . . . . . . . 31
SECTION 2
Catalysts, Promoters and Inhibitors
Methyl Ethyl Ketone Peroxide . . . . . . . . . . . . . 6
Benzoyl Peroxide . . . . . . . . . . . . . . . . . . . . . . . . . 6
Cumene Hydroperoxide . . . . . . . . . . . . . . . . . . . 7
t-Butyl Perbenzoate . . . . . . . . . . . . . . . . . . . . . . . 7
Cobalt Naphthenate . . . . . . . . . . . . . . . . . . . . . . 7
Dimethylaniline . . . . . . . . . . . . . . . . . . . . . . . . . . 8
Copper Naphthenate . . . . . . . . . . . . . . . . . . . . . 8
Inhibitors . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8
Safety . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9
SECTION 3
Thixotropes, Antimony Oxides and
Other Additives
Thixotropes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 10
Antimony Oxides . . . . . . . . . . . . . . . . . . . . . . . . 10
Alumina Trihydrate . . . . . . . . . . . . . . . . . . . . . . 11
Other Fillers . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12
Intumescent Coatings . . . . . . . . . . . . . . . . . . . 12
Ultraviolet Stabilizers . . . . . . . . . . . . . . . . . . . . 12
Air Release Agents . . . . . . . . . . . . . . . . . . . . . . . 12
Wax Topcoats . . . . . . . . . . . . . . . . . . . . . . . . . . . 12
Abrasion Resistant Additives . . . . . . . . . . . . . 13
SECTION 4
Inspecting a Laminate
Visual Inspection . . . . . . . . . . . . . . . . . . . . . . . . 32
Barcol Hardness . . . . . . . . . . . . . . . . . . . . . . . . . 33
Acetone Sensitivity . . . . . . . . . . . . . . . . . . . . . . 33
SECTION 8
Health, Safety and Regulatory Information
Material Safety Data Sheet . . . . . . . . . . . . . . . 34
Styrene . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 34
Flammability . . . . . . . . . . . . . . . . . . . . . . . . . . . . 34
Health Concerns . . . . . . . . . . . . . . . . . . . . . . . . . 35
Resin Spills . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 36
Storage . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 36
Disposal . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 36
SECTION 9
Appendices
Reinforcements
Standard Reinforcement Sequence . . . . . . . 14
Surfacing Veil . . . . . . . . . . . . . . . . . . . . . . . . . . . . 15
Chopped Strand Mat . . . . . . . . . . . . . . . . . . . . 16
Woven Roving . . . . . . . . . . . . . . . . . . . . . . . . . . . 17
Continuous Strand Roving . . . . . . . . . . . . . . . 17
SECTION 5
Resin Preparation
FDA Compliance . . . . . . . . . . . . . . . . . . . . . . . . 18
Adjusting Promoter/Catalyst Levels for
Practical Applications . . . . . . . . . . . . . . . . . . 19
Preparing the Resin . . . . . . . . . . . . . . . . . . . . . 19
Making a Test Laminate . . . . . . . . . . . . . . . . . . 21
Post Curing the Laminate . . . . . . . . . . . . . . . . 23
2
SECTION 7
Appendix A Promoter and Catalyst

Addition Tables . . . . . . . . . . . . . . . . . . . . . . . . 37
Appendix B Ashland Chemical
Technical Service Contacts . . . . . . . . . . . . . 49
Appendix C North American Suppliers 50
Appendix D Equipment Suppliers . . . . . 51
Appendix E Trouble Shooting Guide
for Curing Resins . . . . . . . . . . . . . . . . . . . . . . . 52
Appendix F Weight to Volume
Conversion Tables . . . . . . . . . . . . . . . . . . . . . . 53
Appendix G Visual Acceptance
Criteria for Cured Laminates . . . . . . . . . . . . 54

S
Product Description
The development and manufacture of HETRON and AROPOL polyester and vinyl ester
resins have been a continuing process since 1954.They have been used to fabricate
thousands of different types of corrosion resistant FRP equipment. Many versions of
HETRON and AROPOL resins have been developed for ease of handling during hand
lay-up, spray-up, filament winding, pultrusion, centrifugal casting and most other methods of commercial fabrication. Ashland Specialty Chemical Company provides a variety
of thermoset resins for corrosion resistant applications.Table 1 summarizes the different
types of resins.
TABLE 1
Liquid /
Fume Fume
Service Service
Resin Type
Resin Number
Fabrication Applications
Chlorendic
Polyester
HETRON 72
High viscosity base resin,bulk molding compound (BMC),

sheet molding compound (SMC),coating formulations
HETRON 92
Pultrusion,BMC,SMC,molded electrical sheet,

vacuum bagging,Mil Specification
HETRON 92FR
HETRON 92AT
Hand lay-up,spray-up
Hand lay-up,spray-up
X
X
HETRON 197
Hand lay-up,spray-up,press molding,

pultrusion,vacuum bagging
HETRON
197-3
Hand lay-up,spray-up,filament winding
HETRON 197P
HETRON 700
Hand lay-up,spray-up,filament winding,

press molding,pultrusion,coating formulations,
FDA applications
fire retardant
Flame Retardance
(based on the
ASTM E-84 Tunnel Test)
Class I
Bisphenol A
Fumarate
Polyester
Isophthalic
Polyester
HETRON 99P
Furan
AROPOL
7241T-15* series
AROPOL
7334T-15* series
HETRON 800
Vinyl Ester
HETRON 922
HETRON 922L
HETRON 942/35
HETRON 970/35
HETRON 980
HETRON 980/35
HETRON FR992
HETRON FR998/35
Miscellaneous
Fire Retardant
HETRON
604T-20
HETRON
FR620T20
HETRON 625P
HETRON
692TP-25
MODAR 814**
MODAR 816**
*
**
P
T-XX
Class II
X with 5%
antimony
trioxide
X
X with 3%
antimony
trioxide
X
X
X with 3%
antimony
trioxide
X with 5%
antimony
trioxide
X with 5%
antimony
trioxide
X with 5%
antimony
trioxide
X with 3%
antimony
trioxide
X
X
X
X

FDA applications
FDA applications
flake glass coating
flake glass coatings,FDA applications
Hand lay-up,spray-up,filament winding,flake glass coatings,
applications requiring lower viscosity than Hetron 922,
FDA applications
less than 35% styrene,FDA applications
applications requiring maximum solvent resistance,less
than 35% styrene
higher temperature resistance than Hetron 922
Hand lay-up,spray-up,filament winding,flake glass coating,
less than 35% styrene
flake glass coatings

flake glass coatings,less than 35% styrene
X
X
X
X
X
X
X
X

X
X
X
X
X
X
X
X
X with 3%
antimony
trioxide
X
X
X with 3%
antimony
trioxide
X
X
X
X
X
RTM,hand lay-up,spray lay-up,filament winding

RTM,hand lay-up,spray lay-up,filament winding
Corrosion Resistant isophthalic based products

Please contact Ashland Technical Service for more information on MODAR products
promoted system
thixed system with a room temperature gel (RTG) of XX minutes using 1.25% of an MEKP catalyst
Thixed Promoted
X with ATH X with ATH

X with ATH X with ATH
F-Cat

S
Catalysts,Promoters
and Inhibitors
Catalysts, also referred to as initiators, are organic peroxides that work together with
promoters to initiate the chemical reaction that causes a resin to gel and harden.The
amount of time from which the catalyst is added until the resin begins to gel is referred
to as the gel time. Catalyst and promoter levels can be adjusted, to a certain extent, to
shorten or lengthen the gel time and accommodate both high and low temperatures.
For example, Figure 1 shows how the gel time of a prepromoted resin system shortens
with increasing temperature.
If a longer gel time is required, inhibitors can be added to a resin system to lengthen the
gel time. However, care should be taken not to decrease or increase promoter / catalyst
levels beyond what is recommended for that particular resin. If the level of catalyst is
too low, incomplete cure may occur which could result in decreased physical properties
and chemical resistance. On the other hand, levels that are too high could cause the
laminate, particularly thick laminates, to delaminate, burn, or discolor during curing. In
addition, if promoter or catalyst levels are too high, the result can be undercure.
Promoter, catalyst and inhibitor levels for specific resins are listed in Appendix A.
Figure 1.
Gel Time vs.
Temperature
80
70
Gel Time (min.)
60
50
40
30
20
10
0
65
70
1.00%MEKP
1.25%MEKP
1.50%MEKP
75
Temperature (oF)
80
85
CATALYSTS1
There are two primary types of catalysts recommended for curing HETRON and
AROPOL resins at room temperature: methyl ethyl ketone peroxide (MEKP) and benzoyl
peroxide (BPO). A third, less common, catalyst type is cumene hydroperoxide (CHP)
which is often recommended for blending with MEKP. In other processes, such as pultrusion, different types of catalysts are used. Catalysts for the pultrusion process are heat
activated and are not used with promoters.
The proper choice of a catalyst is critical to achieving expected chemical resistance. Care
must be taken not to select catalysts that are too fast or slow in curing. Unusually fast or
slow cure times could result in reduced corrosion resistance in the final cured product.
Methyl Ethyl Ketone Peroxide (MEKP)
MEKP is the most widely used catalyst system. MEKP is used with promoters, usually 6%
cobalt naphthenate or 6% or 12% cobalt octoate and dimethylaniline (DMA) or diethylaniline (DEA)1.The MEKP used most often is supplied at 9% active oxygen.
Many resin producers require the use of special MEKPs that contain very low levels of
hydrogen peroxide.This is because the vinyl ester resins they produce can foam when
they come in contact with hydrogen peroxide. Ashlands Flexible-Catalyzation (F-Cat),
High Performance epoxy vinyl ester resins (EVERs) do not foam when catalyzed with
standard MEKPs.The use of standard MEKPs allows for much greater control of the
exotherm during cure. Ashland Technical Service should be contacted for information
on alternative catalysts for use with HETRON and AROPOL resins and appropriate
exotherm control. See Appendix B for the contact in your area.
Benzoyl Peroxide (BPO)
BPO requires the addition of DMA or DEA for room temperature curing. For curing at
elevated temperatures, greater than 160F, BPO is used without DMA or DEA. BPO is not
as widely used as MEKP primarily because it is more difficult to mix into the resin system
than MEKP, it may cause higher exotherm temperatures, and it is more difficult to fully
post cure. However, the following is an application where a BPO system is definitely recommended over a MEKP cure system.
In sodium hypochlorite environments improved corrosion resistance is observed with
DMA/BPO cure system. HETRON FR992 cured with BPO/DMA will turn a bright yellow
when exposed to the sun.This does not effect chemical resistance.
BPO is available as a powder, a paste or an aqueous dispersion.The aqueous dispersion
is not recommended for corrosion applications. Our tests show that aqueous BPO solutions compromise corrosion resistance in selected environments.The paste form is the
most widely used type with polyesters and vinyl esters. BPO crystals are also available,
however they are used less frequently.The paste is generally supplied in a 50% active
6
form and the crystals in 98% active form.To achieve the same gel time with paste and
crystals, half the amount of crystals should be used as paste. For example, 2.0 grams of
paste will react to give the same gel time as 1.0 gram of the crystals. BPO crystals are
shock sensitive and must be predissolved in styrene prior to addition to the resin.
Cumene Hydroperoxide (CHP)
CHP is used less frequently than MEKP or BPO but can be helpful in lowering laminate
exotherm temperatures, such as those seen in thick parts. CHP should be used with
HETRON 970/35 vinyl ester resin. When using CHP with other resins beside HETRON
970/35 resin, care must be taken to ensure that a thorough cure is obtained, particularly
at ambient temperatures. A post cure is recommended to insure a thorough cure. CHP
can also be used with MEKP in ratios such as a 50/50 mixture. Whenever CHP is used as
the only catalyst (except with HETRON 970/35), it is recommended that Ashland
Technical Service be contacted for specific instructions.
T-butyl Peroxybenzoate
TBPB is a secondary catalyst that can be used in addition to MEKP, BPO, or CHP. The
addition of TBPB assists in achieving a higher degree of cure. We recommend TBPB at
0.2%, based on resin.The addition of TBPB to resin will shorten the pot life. Please
consult Ashland Technical Service for more information on TBPB.
PROMOTERS1
In addition to a catalyst, at least one promoter is required to make a resin cure at room
temperature. Generally, the promoter is mixed in thoroughly before adding the catalyst.
The catalyst then reacts with the promoter to
cause the resin to gel. Promoter levels can also be
adjusted to shorten or lengthen a gel time as
needed.
Cobalt Naphthenate or Octoate2
Cobalt solutions are blue or purple liquids that
are used with MEKP and CHP catalyst systems.
When used at temperatures below 70F (24C),
it is recommended that cobalt be cut in styrene
monomer prior to addition to the resin. Dilution
in styrene will prevent small particles of cobalt
from forming and will facilitate uniform mixing.
Please note that selected grades of Cobalt
Naphthenate are acceptable according to FDA
regulations.
7
Cobalt naphthenate
Dimethylaniline (DMA)
Dimethylaniline is a yellow amine liquid with a
strong odor. DMA can be used with MEKP, BPO
(ambient cure), and CHP catalyst systems.The
addition of DMA is not required with MEKP and
CHP systems. However, small amounts of DMA
may be used in conjunction with cobalt to
improve Barcol development and/or shorten the
cure time at cool temperatures.With ambient
temperature BPO systems, the addition of DMA
is required.
Diethylaniline (DEA) is another amine that can
also be used. DEA is approximately half as reactive as DMA, therefore, if 0.1% DMA is called for,
0.2% of DEA should be added to achieve
the same reactivity.
Dimethylaniline
Copper Naphthenate
Copper naphthenate is available as a green paste that typically contains 6 - 8% elemental copper. It is included in a formulation to control the exotherm of blends intended for
MEKP catalyzation. If low hydrogen peroxide containing MEKPs are used, the impact on
the peak exotherm is marginal. However, if standard MEKPs are used, copper naphthenate will lower the exotherm and lengthen the time from gel to peak, without effecting
the gel time.Typical levels of copper recommended for exotherm control are 0 400
ppm. Copper naphthenate should be added to the formulation the same day the resin
is catalyzed. Please review the suggested amounts for Copper Naphthenate in
Appendix A.
INHIBITORS
Inhibitors are used to lengthen the gel time of vinyl ester and polyester resins. Inhibitors
are useful when very long gel times (1-2 hours) are required or when resin is curing
quickly due to high temperatures. Some common inhibitors include tertiary butyl catechol (TBC), hydroquinone (HQ), and toluhydroquinone (THQ).
TBC is typically sold as an 85% solution but should be further diluted in styrene to a
10% solution before addition to the resin. HQ and THQ are sold as solids and should be
dissolved in methanol to a 10% solution to be added to the resin. Inhibitors can also be
dissolved in propylene glycol, which greatly reduces the flammability of the solution. It
is recommended that inhibitor solutions be used as soon as possible to insure their full
effectiveness.
8
TBC, HQ, and THQ can be used with MEKP, BPO, and CHP catalyst systems. However, care
should be taken not to add too much inhibitor, which could result in permanent undercure, low Barcol, or reduced corrosion resistance. Recommended inhibitor levels vary
from inhibitor to inhibitor and from resin to resin. A general guide for addition levels is
up to 0.30% of a 10% solution, however, Ashland Technical Service should be contacted
for instructions on adding inhibitors to specific resin systems.
Special attention to additives is necessary when fabricating for FDA applications.Title 21
CFR 177.2420 contains a list of FDA approved additives and should be referred to before
adding promoters, inhibitors, catalysts or other additives to resins to be used in FDA
applications.
Included in Appendix C and D are lists of suppliers for many of the products described
in this section.These are not the only suppliers of these products. Check with a local
distributor for suppliers in your area.
Safety
Ashland Specialty Chemical Company does not manufacture cobalt, DMA, DEA,
inhibitors or catalysts. Care should be taken to insure that each product is handled
safely.The material safety data sheet and safety instructions on each product should
be obtained from the manufacturer and read and understood before working with
the products.
WARNING Promoters should always be mixed thoroughly into the resin before adding the
catalyst. If promoters and catalysts are mixed directly together, an explosion could result.
6% Cobalt octoate can be substituted for 6% cobalt naphthenate to obtain comparable gel
times with HETRON and AROPOL resins.

S
Thixotropes,Antimony
Oxides and Other Additives
Thixotropes
Thixotropes, usually fumed silica, are used to thicken resin and reduce drainage, especially on vertical surfaces. Resins with these additives are generally used in hand lay-up
and spray-up applications.
Polyester resins can be purchased with fumed silica already in the resin or the customer
may add it. Ashland Technical Service should be contacted before adding thixotropes to
vinyl esters or other resins that are to be used in corrosion applications.The use of
fumed silica in hydrofluoric acid, sodium hypochlorite, and sodium hydroxide environments is not recommended and could result in a decrease in corrosion resistance.
To insure uniform dispersion, fumed silica should be mixed into the resin using a high
shear dissolver or equivalent.
Antimony Oxides
Cured polyester and vinyl ester resins will burn if provided with a sufficient amount of
heat and oxygen. However, certain resins are flame retardant due to the incorporation
of halogens in the backbone of the polymer.This improves the flame-retardant properties of the laminate. With
most flame-retardant
resins, adding antimony
HETRON FR 992
HETRON FR 992
HETRON FR 992
3%
Sb
O
3%
NYACOL
2 3
trioxide or antimony pentoxide can increase the
degree of flame retardancy of the resin. Antimony
acts as a synergist and
reacts with the halogens
to improve the resins
flame retardant properties.
The addition of antimony
to non-halogenated resins
does not make the resin
flame retardant, but
Laminates containing antimony trioxide, antimony pentoxide,
instead acts only as filler.
and no antimony oxide..
10
In the U.S. composites industry, the flame and smoke properties of polyester and vinyl
ester resins are most often rated according to the ASTM E-84 tunnel test as performed
under strictly controlled conditions. In this test, industry code officials, fire marshals, and
resin suppliers have categorized red oak as a flame spread of 100 and asbestos cement
board a flame spread of zero. A flame spread of less than or equal to 25 is considered a
Class I and less than 75 but greater than 25 is a Class II. Some resin systems can obtain a
Class I flame spread without the addition of antimony, others require the addition of
3-5% antimony trioxide or pentoxide to achieve a Class I rating. Laminates made from
HETRON 197 require 3-5% antimony trioxide or pentoxide to achieve a Class II rating.
Flame spread values of specific resins with and without antimony are listed in Table 1
or refer to the specific data sheet of the resin in question.
The use of some grades of antimony pentoxide have been shown to increase the gel
time of flame-retardant vinyl ester resins over time. Because of this, when antimony
pentoxide is added to the resin, it should be used within 8 hours to minimize gel drift.
Ashland Technical Service should be contacted for specific recommendations regarding
antimony pentoxide. Please note that antimony trioxide and pentoxide do not lower
smoke emissions.
FILLERS
Alumina Trihydrate
Alumina trihydrate is used to improve flame retardancy and reduce smoke emissions of
specific resin systems.
Alumina trihydrate is a fine, white powdered filler which, when added in the proper
amount, can improve flame retardancy of both halogenated and non-halogenated resin
systems. When a properly filled laminate is exposed to fire, the alumina trihydrate
decomposes into water vapor and anhydrous alumina.The water vapor cools the laminate thus slowing the rate of decomposition or burning.
Alumina trihydrate differs from antimony trioxide in several ways. As mentioned earlier,
antimony trioxide is effective only with halogenated resin systems and is used in small
percentages. Alumina trihydrate can be effective with both halogenated and non-halogenated resin systems but much higher filler loadings are required to achieve the
desired flame retardance. Consequently, alumina trihydrate can not be used directly in
place of antimony trioxide.The addition of high levels of alumina trihydrate can produce a higher viscosity system and reduce the physical properties of the laminate. It can
also reduce smoke emissions, especially in non-halogenated systems.
The addition of alumina trihydrate to the corrosion barrier can result in a significant
reduction in corrosion resistance. Before using alumina trihydrate in corrosion applications, contact Ashland Technical Service for specific recommendations.
11
Other Fillers
Calcium carbonate and kaolin clays may also be used as fillers or extenders for polyester
and vinyl ester resins.These materials increase the stiffness of the FRP while reducing
the overall cost of the part.These fillers are not, however, recommended in applications
requiring corrosion resistance. Contact HETRON Techincal Service for specific recommendations.
Intumescent Coatings
Intumescent coatings are also used to improve flame retardancy and reduce smoke
emissions of specific resin systems.
Ultraviolet Stabilizers
FRP structures that are placed outdoors may experience surface chalking and/or discoloration.This chalking and/or discoloration is a surface phenomenon only and should
not be detrimental to properly fabricated equipment. Polyester resins are inherently
more ultraviolet (UV) stable than vinyl ester resins and the addition of UV stabilizers to
the outermost resin layer may reduce UV degradation.The recommended level of UV
stabilizers for use with polyester and vinyl ester resins is 0.25-0.5%. For halogenated
resin systems, the recommended level of UV stabilizer is 0.5%
Another option for decreasing UV degradation is HETROLAC 105 protective lacquer.
HETROLAC 105 is a very low viscosity lacquer containing UV absorber. HETROLAC 105
lacquer improves weather resistance of new FRP, restores gloss and luster to weathered
FRP. For more information on HETROLAC 105 lacquer, consult the technical data sheet or
contact Ashland Technical Service.
Air Release Agents
Air release agents can be added to the resin (0.05-0.5%) to decrease foaming. Excessive
levels of air release agents can cause a laminate to be cloudy, therefore recommended
levels should not be exceeded. Contact Ashland Technical Service for additional
information.
Wax Topcoats
Some resins are subject to surface inhibition when cured in the presence of air. Air
inhibition affects the cure and corrosion resistance of the outermost resin layer, which
results in an acetone sensitive, potentially tacky surface. A wax-containing topcoat
approximately 2.0-3.5 mil (51-89 m) thick applied to the outermost resin surface can
help prevent air inhibition. As the resin cures, the wax migrates to the surface of the
laminate, hardens and prevents air from reaching the laminate. In conditions under hot
sunlight, the wax topcoat may be ineffective. A resin/wax solution should never be
applied between laminate layers, this could result in poor secondary bonding and
premature failure.
12
The wax/styrene solution is made by dissolving 20 g of a fully refined paraffin wax

(melting point = 130-140F (54-60C)) in 180 g of warm styrene (110F (43C)).The solution is then added at the rate of 2% to the resin and mixed thoroughly.The resin solution should then be promoted and catalyzed as normal. Predissolved wax solutions are
also available from FRP distributors.
Abrasion Resistant Additives
An abrasion resistant corrosion liner is necessary when operating conditions involve
slurries or other applications with abrasive particles that can abrade the corrosion liner.
When used correctly, silicon carbide and aluminum oxide have been effective in reducing liner deterioration caused by abrasion.
A mixture of resin and silicon carbide or aluminum oxide should be made and catalyzed
based on resin weight.
The use of carbon veil in place of C glass veil or synthetic veil has also been shown to
improve abrasion resistance. Ashland Technical Service can be contacted for additional
information on improving abrasion resistance.
Included in Appendix C and D are lists of suppliers for many of the additives described
in this section.These are not the only suppliers of these products, check with a local distributor for suppliers in your area.
13

S
Reinforcements
Standard Reinforcement Sequence for Corrosion Resistant Equipment
Laminate sequence for standard corrosion resistant equipment is based on the ASTM
C581/582 Standard Practice for Determining Chemical Resistance of Thermosetting
Resins used in Glass Fiber Reinforced Structures Intended for Liquid Service.This
sequence is illustrated in Figure 2.
g
Figure 2. Laminate
Corrosion Barrier and Structural Layer
primary
corrosion
barrier
alternating layers of
chopped mat and woven
roving to achieve
desired thickness
optional
veil
layer
typical
resin/wax
topcoat
chemical
environment
serfacing veil, 0.010 - 0.020" (0.025 - 0.050mm) thick

chopped strand mat, 0.100 - 0.125" (2.54 - 3.18mm) thick
woven roving
Generally, fabrication begins at the surface that will be exposed to the corrosive environment. A resin rich layer consisting of 95% resin and 5% reinforcement is applied first.
The reinforcement is in the form of a surfacing veil comprised of C-glass, a synthetic fabric, or carbon fiber.Two plies of surfacing veil can be used for more severely corrosive
environments.The veil is followed by two or more layers of chopped strand mat, or the
equivalent chopped spray.This layer should be at least 100 125 mil (2.5 3.1 mm)
thick and should consist of 20 30% glass.Together, the resin, veil, and chopped glass
form the primary corrosion barrier that minimizes permeation of the corrosive media
into the structural portion of the laminate.
The remainder of the laminate, commonly referred to as the structural portion, provides
strength and consists of alternating layers of chopped strand mat and/or chopped
strand, and woven roving.This portion of the laminate should be 40-50% glass.The
14
structural portion of the laminate can also be filament wound where this layer typically
has a minimum of 60% glass.The thickness of this layer will vary depending on the
equipment being fabricated. A final wax topcoat or gelcoat is then applied to the exterior of the equipment to prevent air inhibition.
Types of Reinforcements
The following discussion provides general guidelines for fiberglass selection, however,
the glass manufacturer should be contacted for specific recommendations. Regardless
of glass type, each should be thoroughly evaluated in a test laminate before beginning
actual fabrication. In the test laminate, the glass should wet readily and no glass fibers
should be visible in the final cured laminate.
There are four basic forms of fiberglass commonly used with HETRON and AROPOL
resins.They are:
Surfacing veil
Chopped strand mat
Woven roving
Continuous strand roving
Fiberglass begins as a molten glass and is formed into filaments by pulling it through
bushings. A strand of glass roving is then formed by simultaneously gathering a large
number of filaments together.
The surface of the glass is treated with sizings and binders to facilitate further processing, maintain fiber integrity, and provide compatibility with various resin systems. After
this treatment, the fibers are further processed into the specific glass types that are
described below.
Surfacing Veil
The purpose of surfacing veil, also referred to as surfacing mat or tissue, is to provide
reinforcement for the resin rich inner liner of a corrosion barrier that prevents cracking
and crazing. A second, is to prevent protrusion of the
chopped strand mat fibers to the surface which could
allow wicking of the environment into the laminate to
occur.
The primary type of surfacing veil used in corrosion
applications is C glass veil. However, in applications
where C-glass veil is not suitable, other veil types
made from thermoplastic polyester or carbon fibers
may be used.
C-glass veil
15
C-glass veil is typically recommended for most

corrosion environments. However, synthetic veil is
preferred in some environments such as those containing fluoride compounds. Synthetic veil is preferred in other environments, which are noted in the
resin selection guide. When using synthetic veil with
less flexible resins such as chlorendic polyesters, a
non-apertured synthetic veil type is recommended
to minimize stress in the system. Both non-apertured
and apertured synthetic veils can be used with more
flexible resin systems such as vinyl esters.
NEXUS synthetic surfacing veil
In severe environments, multiple plies of veil may be

recommended, however caution is advised. In applications requiring synthetic veil next to the chemical
environment, a ply of C-glass veil may be placed
behind the synthetic veil to minimize air entrapment
and to assist in making lay-up easier.
Carbon veil is often used in abrasive environments.
When used properly, carbon veil has been shown to
provide better abrasion resistance than either Cveil or synthetic veil. Carbon veil is also used to provide a conductive liner for static electricity control.
For applications where conductivity is not desirable,
the use of carbon veil should be reevaluated. Veils
made with other types of glasses, such as A and
ECR, are used less often in the corrosion industry
but may be acceptable in certain applications.
Thorough testing should be conducted in the specific environment before using A and ECR veil.
Chopped Strand Mat
Two primary types of chopped strand mat are used
in the corrosion industry,E and ECR glass.
Chopped strand fibers are generally 1/2 2 (12.5
50mm) long and, after being chemically treated, are
held together by a binder.Together, the glass fiber
bundles form the chopped strand mat. Chopped
strand mat is available in a variety of thicknesses:
0.75 oz., 1.5 oz. and 2.0 oz. (225 g/m2, 450 g/m2, 600
g/m2) are used most often in corrosion applications.
16
Carbon veil
Chopped strand mat
Woven Roving
Woven roving consists of continuous glass fiber
rovings that are woven together to form a heavy
mat which is available in a variety of thicknesses
and weights. Alternating layers of woven roving
and chopped strand mat are used in the structural
portion of hand lay-up laminates.
Continuous Strand Roving
Most continuous strand roving comes as unwoven
strands of glass wound into a cylindrical package
for additional processing. Continuous strand
roving is used in filament winding and pultrusion or can be chopped into fibers for
spray-up applications to replace chopped
strand mat.
Woven roving
Continuous strand roving
17

S
Resin Preparation
FDA Compliance
Several HETRON and AROPOL resins are manufactured with raw materials that are listed
as acceptable in FDA regulation Title 21 CFR 177.2420 for repeated use in contact with
food subject to users compliance with the prescribed limitations of that regulation.The
raw materials used in the manufacture of the following resins are listed as acceptable in
FDA regulation Title 21 CFR 177.2420 for repeated use in contact with food subject to
users compliance with the prescribed limitations of that regulation:
HETRON 700, 922, 922L, 922L-25, and 942/35 resins
AROPOL 7241T-15, 7334T-15 resins
When fabricating equipment for FDA compliance, contact Ashland Technical Service for
additional resins that meet these requirements.
When fabricating such equipment, there are several steps that should be followed in
order to reduce residual styrene. Prior to exposure, all fabricated equipment should be
post cured at 180F (82C) for 4 hours.The surface of the equipment should then be
washed with a mild detergent and water and rinsed thoroughly with water.
Promoter and Catalyst Addition
When fabricating with HETRON and AROPOL resins, it is important to promote and catalyze the resin correctly in order to insure an appropriate working time. Promoter and
catalyst addition tables for many HETRON and AROPOL resins are shown in Appendix A.
These tables indicate levels to be added at different temperatures to achieve desired
working times.These tables serve only as guidelines and the values should not be considered specifications. One of the most effective ways to control the exotherm without
effecting the gel time is to add up to 400 ppm of copper naphthenate to the solution.
This should be done as close to the time of catalyzation as possible. Over time copper
naphthenate and cobalt will react with one another. If a low hydrogen peroxide catalyst
is used (BPO, CHP, or any of the non foaming MEKPs), the gel time will be affected substantially. HETRON FCat epoxy VERs will not foam with standard MEKPs.
18
Adjusting Promoter / Catalyst Levels for Practical Applications

The levels given in Appendix A represent laboratory conditions and will most often
have to be adjusted to accommodate actual working conditions in a fabricating shop or
in the field. Many things can influence the working time of a resin. High resin and shop
temperatures, direct sunlight, and thick laminates can cause the gel time of a resin to
shorten. Low resin and shop temperatures, heat sinks (metal molds), and fillers can
cause the gel time to lengthen.
When the gel time is too short due to working conditions, promoter levels can be adjusted
in order to lengthen the gel time. An inhibitor should be in accordance with those recommended in the appropriate table.
A summary of some of the most common problems encountered with room temperature cure systems and suggestions for minimizing these problems is shown in Appendix
E. Also, Ashland Technical Service can be contacted for assistance in adjusting gel times.
Preparing the Resin
In order to fabricate equipment correctly, the resin must be prepared properly and in a
safe manner. Below are several steps that should be followed when preparing the resin.
1.
Estimate the amount of time required for fabrication. Remember to take into
account resin and air temperature warmer temperature faster cure, cooler
temperature slower cure.The viscosity of the resin can also be affected by
temperature.
2.
If utilizing a neat resin and adding a thixotrope, the thixotrope should be added to
the resin and agitated using a high shear mixer until the desired thixotrope index
has been achieved. High shear agitation generates heat, therefore, this step should
be done before adding any promoters.
3.
Using the promoter / catalyst addition tables as guidelines, choose the appropriate additive levels to achieve a suitable working time.
4.
Weigh the required amount of resin, cobalt,

DMA, and if applicable, inhibitors (predissolved in styrene or other appropriate
solvent) into separate containers. A conversion table is shown in Appendix F that may
be helpful when measuring materials
volumetrically.
Adding 6% cobalt naphthenate
19
5.
Add the cobalt to the resin and mix thoroughly using an air driven mixer under
slow to moderate agitation. During all mixing, care should be taken to minimize
air entrapment in the resin. Excessive air bubbles in a laminate can cause a reduction of physical and corrosion properties.
6.
Add the DMA or DEA and mix thoroughly.
7.
Add any additional liquid materials such as inhibitors and mix thoroughly.
8.
Add any pigments or fillers such as antimony trioxide, alumina trihydrate, etc. and
mix thoroughly.
9.
After all ingredients have been added, the drum should be mixed thoroughly.
10.
After mixing in required promoters and fillers, a sample of

resin should be removed and a gel time test performed.
Again, refer to the designated promoter / catalyst table for
recommended catalyst level.
11.
The gel time can be lengthened by adding an inhibitor or

shortened by adding additional cobalt or DMA, however,
do not exceed the recommended levels for that resin.
12.
Catalyze the resin as needed.
13.
If the exotherm of cure is too hot, copper naphthenate can

be added to control this.The gel time will not be effected if
using a standard MEKP. If more than a combined 400 ppm
copper naphthenate and inhibitor is added to the resin, a
full cure may not be possible. Contact Ashland Technical
Service for further guide-lines.
20
Typical gel timer
Making a Test Laminate

Below is a step-by-step procedure for making a standard test laminate. Materials that
will be needed include release film, a spreading devise, a serrated roller, resin, glass surfacing veil, chopped fiberglass mat, woven roving, and a cleaning solvent. Before beginning the laminating process, the fiberglass should be cut to the required size and the
required amount of resin should be properly formulated. Do not catalyze the resin until
you are ready to begin laminating.
1. The surface should be prepared by spreading
a release film on the bench top for protection.
2. At this time, catalyze the amount of resin to

achieve the desired resin-to-glass ratio and pour
some onto the release film and spread with the
spreading device (tongue depressor, paint
brush, etc.). When laminating, veil and glass
should be applied to a resin rich mold surface.
Air bubbles form readily when glass is applied
to a dry surface.
3. Carefully position the surfacing veil over the
resin and roll with the roller until the veil is
entirely wet out. When rolling out a laminate,
roll firmly but not too hard and roll from the
center out to the edges.This helps push the
air bubbles out of the laminate.
4. Apply additional resin and spread with the

spreading device. Make sure that all air bubbles
are removed from the current glass layer
before applying another layer of glass.
21
5. Place one ply of chopped fiberglass mat on the

resin and roll with the roller. If necessary, apply
additional resin to thoroughly wet the mat.
6. Apply a second ply of chopped fiberglass and

roll thoroughly. Again, additional resin can be
added if necessary.
7. When the mat is wet out completely, apply

additional resin, spread with the spreading
devise and apply a layer of woven roving.
Woven roving is more difficult to wet out than
veil and mat, therefore, additional resin and
rolling may be required to thoroughly wet the
roving.
8. Repeat steps six and seven as necessary to
make the laminate the required thickness.
9. After all woven roving has been applied, apply
a final layer of resin and chopped strand mat
and roll thoroughly. When rolling is completed,
place the roller in a cleaning solvent and allow
the laminate to cure thoroughly. When the
laminate is thoroughly cured at room temperature, post cure as indicated in the following
section.
22
Post Curing the Laminate

After fabricating FRP equipment, it is important to post cure the equipment in order to
insure that optimum cure has been achieved. Figure 3 illustrates how the post cure temperature affects the ultimate glass transition temperature (Tg) of a resin.
Ideally, a laminate should be post cured for two hours at a temperature above the heat
deflection temperature (HDT) of the resin.The HDT of most HETRON and AROPOL resins
is between 200 and 300F; therefore, a post cure of two hours at 280F is suitable for
most systems. Laminates made with HETRON 970/35 should be post cured at 300F for
two hours since it has an HDT of 297F. Ashland Technical Service can be contacted for
additional information on post curing.
Figure 3. Glass Transition Temperature (Tg) vs. Post Cure Temperature
300
250
Tg (oF)
200
150
100
50
0
0
50
HETRON 922
HETRON 970/35
23
100
150
200
o
Post Cure Temperature ( F)
250
300

S
Fabrication Methods
Fabrication Standards
The fabrication of FRP equipment is governed by various standards that provide guidelines and requirements for composition, performance, construction, design and testing
methods of such equipment.The American Society of Testing Materials (ASTM), the
National Bureau of Standards (NBS), and the American Society of Mechanical Engineers
(ASME) publish numerous standards for the fabrication of various types of FRP structures. Some common standards are listed below.
1.
ASTM C 581 - Standard Test Method for Chemical Resistance of Thermosetting

Resins Used in Glass Fiber Reinforced Structures
2.
ASTM C 582 Standard Specification for Reinforced Plastic Laminates for SelfSupporting Structures for Use in a Chemical Environment.
3.
ASTM D 2105 Standard Test Method for Longitudinal Tensile Properties of

Reinforced Thermosetting Plastic Pipe and Tube.
4.
ASTM D 2143 Standard Test Method for Cyclic Pressure Strength of Reinforced
Thermosetting Plastic Pipe
5.
ASTM D 2310 Standard Classification for Machine-Made Reinforced

Thermosetting Resin Pipe
6.
ASTM D 2517 Standard Specification for Reinforced Epoxy Resin Gas Pressure
Pipe and Fittings
7.
ASTM D 2562 Standard Practice for Classifying Visual Defects in Parts Molded
from Reinforced Thermosetting Plastics.
8.
ASTM D 2563 Standard Practice for Classifying Visual Defects in Glass-Reinforced

Plastic Laminate Parts.
9.
ASTM D 2924 Standard Test Method for External Pressure Resistance of

10.
ASTM D 2925 Standard Test Method for Beam Deflection of Reinforced

Thermosetting Plastic Pipe Under Full Bore Flow
11.
ASTM D 2992 Standard Method for Obtaining Hydrostatic Design Basis for
Reinforced Thermosetting Resin Pipe and Fittings
24
12.
ASTM D 2996 Standard Specification for Filament-Wound Reinforced

13.
ASTM D 2997 Standard Specification for Centrifugally Cast Reinforced

14.
ASTM D 3262 Standard Specification for Reinforced Plastic Mortar Sewer Pipe
15.
ASTM D 3299 Standard Specification for Filament Wound Glass-Fiber Reinforced

Thermoset Resin Chemical Resistant Tanks
16.
ASTM D 3647 Standard Practice for Classifying Reinforced Plastic Pultruded

Shapes According to Composition
17.
ASTM D 3917 Standard Specification for Dimensional Tolerance of

Thermosetting Glass Reinforced Plastic Pultruded Shapes
18.
ASTM D 3918 Standard Definitions Terms Relating to Reinforced Pultruded

Products
19.
ASTM D 3982 Standard Specification for Custom Contact-Pressure-Molded

Glass-Fiber Reinforced Thermosetting Resin Hoods
20.
ASTM D 4021 Standard Specification for Glass Fiber-Reinforced Polyester

Underground Petroleum Storage Tanks
21.
ASTM D 4350 Standard Test Method for Corrosivity Index of Plastics and Fillers
22.
ASTM D 4385 Standard Practice for Classifying Visual Defects in Thermosetting

Reinforced Plastic Pultruded Products
23.
ASTM D 5364 Standard Guide for Design, Fabrication, and Erection of Fiberglass
Reinforced Plastic Chimney Liners with Coal-Fired Units
24.
NBS PS 15-69 Voluntary Product Standard for Custom Contact-Molded

Reinforced-Polyester Chemical-Resistant Process Equipment (out of print)
25.
ASME/ANSI RTP-1 An American National Standard for Reinforced Thermoset

Plastic Corrosion Resistant Equipment
Standards are also used for classifying smoke and flame retardant properties of FRP
equipment.The most frequently referred to fire standards are listed below.
1.
ASTM D 635 Standard Test Method for Rate of Burning and/or Extent and Time
of Burning of Self Supporting Plastics in a Horizontal Position
2.
ASTM D 2863 Standard Test Method for Measuring the Minimum Oxygen
Concentration to Support Candle-Like Combustion of Plastic (Oxygen Index)
25
3.
ASTM E 84 Standard Test Method for Surfacing Burning Characteristics of

Building Materials
4.
ASTM E 162 Standard Test Method for Surface Flammability of Materials Using a
Radiant Heat Energy Source
5.
ASTM E 662 Standard Test Method for Specific Optical Density of Smoke
Generated by Solid Materials
6.
ASTM E 906 Standard Test Method for Heat and Visible Smoke Release Rates for
Materials and Products
7.
UL 94 Standard for Tests for Flammability of Plastic Materials for Parts in Devices
and Appliances
FABRICATION PROCESSES
Hand Lay-Up
The hand lay-up process requires little capital investment and is the oldest, simplest,
and most labor intensive fabrication method. Hand lay-up is well suited for low volume
production of equipment and can be used for both the corrosion barrier and the
structural portion.
This process uses a room temperature cure system where catalyzed resin is applied to
the surface of a mold and fiberglass, usually veil, chopped mat or roving, is placed on
top of the resin.The fiberglass is then saturated with the resin by rolling the surface with
a roller.This rolling action also
Hand Lay-Up
assists in removing air bubbles
that can detrimentally affect
laminate performance. Following
Resin
rolling, more resin and fiberglass
Reinforcement
are applied to build up the corrosion barrier and the structural
Laminate
portion of the laminate. Each
consecutive layer is applied in
the same manner as the first.
Contact Mold
26
Spray-Up
Spray-up is a faster process
and is less labor intensive
than hand lay-up. Several
drawbacks to spray-up
include the possibility of
more air entrapment and a
difficulty in controlling variables such as thickness and
resin-to-glass ratios. As with
hand lay-up, spray-up can be
used for the corrosion barrier and the structural portion
of equipment.The spray-up
process is a room temperature cure process where continuous strand roving is fed
through a chopper gun,
combined with catalyzed
resin, and sprayed onto a
mold surface.The surface is
then rolled to remove air
bubbles. Additional layers of
resin/glass are applied and
rolled to reach the desired
thickness.
A typical spray gun
Spray Up
SPRAY-UP
Corrosion Barrier
Chopper/
Spray Gun
Chopped
Roving
Laminate
A two-pot system can also

Resin
Catalyst
be used. In this method, two
containers are used, one conContinuous Strand Roving
Mold
tains resin with twice the
required amount of promoters and no catalyst and the other contains resin with twice
the required amount of catalyst and no promoters. Resin is then drawn from both containers and mixed during the spraying process. Resin used with the two pot system
must be stable when promoted and catalyzed with high levels of additives.
27
Filament Winding
Filament winding is an excelFilament Winding
lent process for fabricating
Laminate
round equipment such as
Mandrel
tanks, pipes, ducts, etc.
Filament winding is less labor
intensive than both hand layup and spray-up and produces very uniform strucResin Applicator
Continuous Strand Roving
tures as far as thickness, resin
to glass ratio, etc. Filament
winding is recommended only for the structural portion of FRP equipment.The corrosion barrier should be fabricated using either hand lay-up or spray-up.
Filament winding typically uses a room temperature cure system but generally with
very long gel times. A resin rich corrosion barrier is applied to a mandrel and allowed to
cure. Continuous strand glass or roving is then pulled through guides, impregnated with
resin and guided onto a rotating mandrel in a helical pattern.This produces the structural portion of the equipment that is typically 60% glass.The wind angle formed by
this pattern has a direct bearing on the physical strength of the part. Chopped mat
and/or roving may also be applied to accelerate the build-up of the structural portion.
Pultrusion
Pultrusion is a continuous
process that produces parts
with a constant cross-section
such as I-beams, channels,
solid rods, and rails.The
process utilizes glass, resin,
filler, peroxides, pigments, and
release agent.The glass reinforcement is fed from spools
into a resin bath where the
glass substrate is thoroughly
impregnated with the resin
mixture.The wet fibrous
material then proceeds
through forming guides
Examples of pultruded profiles
where excess resin is removed
from the glass. If the substrate is thin, it proceeds to a heated die where the resin mixture
gels and cures into its final shape. A thick substrate proceeds through an R.F. preheating
28
chamber where the temperature of the resin is brought close to the gelation point of the
system. From here, the material proceeds through a heated metal die where the resinous
mass begins to cure.The
Pulling Device
glass/resin matrix solidifies
Continuous Pultrusion
into the exact shape of the
Die
cavity of the die being used.
Grippers or caterpillar pads
Finished
then pull the cured material
Stock
to a cut off station where it is
Heat Source
cut to the desired length.
Pultrusion can produce
unfilled parts with glass conContinuous Strand Roving,
Resin Applicator
Mat, or Cloth
tents as high as 75% and with
very high strengths.
Centrifugal Casting
Centrifugal casting is used in fabricating cylinders with a constant thickness. Molds used
in centrifugal casting are often buffed and polished to a mirror finish. Glass and catalyzed resin are applied to the inside of a rotating mold.This rotation evenly distributes
the glass and resin against the mold surface.
Resin Transfer Molding
Resin transfer molding (RTM)
is a mechanical process using
a closed mold system.
Catalyst and resin are
pumped in under pressure
from two separate containers
into a closed mold containing
glass reinforcement, usually
continuous strand mat.The
resin is pumped into the
mold until excess resin
escapes through vent tubes
placed at the far end of the
flow pattern.The system is
then allowed to cure for a
specific period of time after
which the mold is opened and
the part is removed.
29
A part made by RTM
RTM requires low viscosity

Resin Transfer Molding
resin, typically less than 250
cps, which can be pumped
easily and readily fills the
mold and wets the glass.
Fillers may also be incorporated into the resin mix for
certain applications. RTM
uses either room temperature or elevated temperature catalyst systems. RTM is
suitable for medium volume
production and provides a
process that is less expensive than compression molding and faster than spray-up.
Linings
In some cases, the lining of an FRP structure may be eroded away but the structural portion of the equipment may be in acceptable condition. In these cases, the existing
equipment can be relined to extend its life span. An FRP lining can also be put in existing steel equipment or applied over concrete. Whether lining an existing structure or
putting in a new lining, the surface must be properly prepared in order to insure good
bonding between the fiberglass lining and the existing structure.
The eroded or damaged FRP lining should first be washed to remove large amounts of
dirt, etc. and then ground out back to the structural layer. In lining a steel tank, the surface should be sandblasted to white metal. The blasted metal surface should conform
to SSPC-SP-5 or NACE No.1 white metal blast profiles. In the case of concrete, the portland cement lattice should be removed to expose stone. Several sanding methods are
acceptable, however, grit blasting and sand blasting are the preferred methods. When
lining a concrete structure, the concrete should be at least 28 days old and completely
dry. Sandblasting should be performed the same as with metal. After blasting, any
cracks, pits, etc. should be filled in with putty, allowed to cure, and then sanded smooth.
After all sanding is complete, the surface should be thoroughly vacuumed to remove all
dust and dirt.
The surface of the equipment to be relined should not exceed 100F (38C). A uniform
primer coat of resin, 1-3 mil (25-76 m) thick, is then applied using a paintbrush or other
suitable equipment.The primer coat prevents surface corrosion prior to the application
of the laminating resin and also provides a bonding surface for the laminating resin.The
primer coat should be allowed to cure under ambient conditions, 60-100F (15-38C) to
a tack free state before applying the laminating resin.The laminating procedure should
follow the primer application as soon as possible. No condensation should be allowed
30
to form over the primer coat. If the primer coat is allowed to develop a hard cure, the
surface should be lightly sanded and another primer coat applied prior to applying the
laminating resin.
Fabricating Thick Sections
HETRON epoxy vinyl ester resin systems are designed to work successfully in the fabrication of thick parts where exotherm temperatures are a concern. When laminating a
thick section, first formulate the promoter package to achieve the desired gel time
needed for the application (see appendix D for specific formulations). Second, fabricate
a test laminate to see if the exotherm of the resin is going to be too high, resulting in
burnt sections of the part. If this is the case, add copper naphthenate to the formulation
up to, but no more than 400 ppm (see appendix D for formulation examples and copper naphthenate charge levels). As a result, the resin system will maintain the same gel
time characteristics, but the peak exotherm temperature will be much lower, eliminating
the concern for burning.The resin should be used within a day of charging the copper.
Copper causes the gel characteristics to drift over time.
Finishing Processes
There are a variety of methods available to finish the exterior surface of FRP equipment.
In many cases a topcoat of resin containing a dissolved wax is sprayed, rolled, or
brushed onto the surface of the FRP equipment.This wax forms a film preventing air
inhibition of the resin. Air inhibition can lead to a tacky surface. However, care must be
taken if there is any future laminating to be done such as the addition of manways or
nozzles as the wax will interfere with secondary bonding. It must be removed prior to
subsequent laminations.This is typically accomplished by surface grinding.
If the equipment needs to be of a certain color it may be gel-coated or painted.These
coatings have the added advantages of providing opacity for light sensitive contents
and protection from the weather for FRP equipment used outdoors.
31

S
Inspecting a Laminate
FRP composite equipment should be inspected after all fabrication is completed and
prior to putting the equipment into service. If possible, the inspection should be done
at the fabricators shop where, if any problems are found, they can easily be repaired. An
additional inspection should be done immediately after installing the equipment to
insure that there has been no mechanical damage as a result of transportation and
installation. After installation, periodic inspections should be performed in order to
monitor the integrity of the equipment and determine if and when the equipment
needs to be repaired or replaced.
It is also recommended that the resin type, veil and glass type, method of fabrication,
service conditions and date and place of installation be recorded when the equipment
is installed. Keeping a record of this information is essential when the time comes to
repair or reline the equipment.
Visual Inspection
One of the simplest and most effective types of inspection is visual. Many imperfections
in a laminate can be detected by simply holding a light behind the laminate and looking at the laminate. Air bubbles, laminate uniformity, cracks, and wet out are just a few of
the things that can be detected by looking at a laminate.The table in Appendix G
describes some common defects that can be detected visually and steps that can be
taken to minimize these defects. For additional information on inspecting FRP parts and
common laminate defects, refer to ASTM C 582 Standard Specification for ContactMolded Reinforced Thermosetting Plastic (RTP) Laminates for Corrosion Resistant
Equipment or ASTM D 2563 Standard Recommended Practice for Classifying Visual
Defects in Glass-Reinforced Plastic Laminate Parts.
The surface of the laminate should also be carefully examined. A surface that is smooth
and uniform in color is usually an indication of a well-fabricated laminate.There should
be no dry spots or glass fibers protruding from the laminate surface.
Occasionally, a specification will require a section of the structure to be cut out and
examined for liner and structural thickness, voids, interlaminar bonding, and overall uniformity of the laminate. Areas of high stress can also be detected and usually appear as
minute cracks in the cross section.
32
Barcol Hardness
Barcol hardness values serve as an indication of degree of cure with high values indicating thorough cure and low values indicating incomplete cure. Barcol values will vary
from one resin system to another and will depend on the type and number of veil layers. Generally, a well fabricated, well-cured laminate will have a minimum Barcol reading
of 30. Please contact Ashland Technical Service for additional information.
According to ASTM C 581, the recorded Barcol value must be at least 90% of the published Barcol value for that resin system in order for the equipment to be accepted.
Barcol values for HETRON and AROPOL resins are indicated on the individual product
data sheets or can be obtained from an Ashland Technical Service Representative.
To check Barcol hardness of FRP equipment, refer to ASTM D 2583 Standard Test
Method for Indentation Hardness of Rigid Plastics by Means of a Barcol Impressor.
Usually high or low Barcol values can be attributed to several factors:
High Barcol Values
1. Laminate surface with high glass content, Barcol tester may be measuring glass.
Low Barcol Values
1. Laminate surface with
resin/wax topcoat, sand off
small area of wax coat and
measure Barcol again.
2. Laminate fabricated with synthetic veil.
3. Undercured laminate possibly
due to incomplete catalyst mixing or incorrect catalyst ratios.
4. Testing a curved surface.
Barcol hardness impressor
Acetone Sensitivity
An acetone-sensitivity test can be used in conjunction with the Barcol hardness test to
determine the extent of cure of a laminate.This test consists of rubbing four to five
drops of acetone with a finger on the laminate surface until the acetone evaporates.The
laminate surface should be free of mold release, wax, dust, and dirt. After evaporation, if
the surface of the laminate remains tacky or soft, the laminate is air inhibited and is not
thoroughly cured. In some instances, post curing the FRP part can further cure a laminate and improve Barcol hardness and acetone-sensitivity test results.
33

S
Health,Safety,and
Regulatory Information
Material Safety Data Sheets
Material safety data sheets (MSDS) are available from Ashland Specialty Chemical
Company on all HETRON and AROPOL resins.The MSDS contains health and safety
information to assist handlers in developing appropriate product handling procedures
to protect employees and customers.The MSDS should be read and understood by
all personnel before handling
Ashland Specialty Chemical
Company products in their facility.
HETRON and AROPOL resins are
polymers that are diluted with
styrene, or other monomers, to
obtain a workable viscosity.The
most common hazardous ingredient in the resins is styrene or
other monomers.The polymer
contained in the resin is typically
non-hazardous.
Material safety data sheet
Styrene has a pungent odor that is easily detected due to the very low odor detection
level of less than 1 ppm.
This is why even thoroughly cured parts may have a residual styrene odor.
Styrene is subject to a number of federal and state regulations that have the potential
to impact facilities using HETRON and AROPOL resins. Current regulations should be
reviewed for each facility before using HETRON or AROPOL resins.
For the most current and comprehensive information on styrene health affects see the
following web sites: www. styrene.org or www.styreneforum.org. Other monomers used
in HETRON and AROPOL resins pose different hazards. As always, consult the product
MSDS for details.
Flammability
HETRON and AROPOL liquid resins are flammable due to the
presence of styrene or other monomers. Liquid resin should be stored away from heat
34
sources such as space heaters, open flames, and spark producing equipment.
Smoking in the fabrication area should be strictly prohibited.
Sparks from static electricity can also cause fires. One of the most effective ways to
prevent electrostatic sparking is to properly ground and bond in-plant equipment
and containers. Do not use cutting or welding torches in empty resin drums. They
may contain flammable vapors which could be ignited.
In the event of a fire involving HETRON or AROPOL resins, the fire should be extinguished using foam, dry powder, or carbon dioxide.
When HETRON and AROPOL resins burn, toxic gases such as carbon monoxide and
hydrogen bromide (brominated resins only) may be given off. For this reason, caution
should be used to avoid inhalation of the fumes. If necessary, a self-contained breathing
apparatus should be worn while extinguishing the fire. Consult the MSDS and your site
safety plan for more details.
HEALTH CONCERNS
Skin Contact
Protective gloves and clothing should be worn at all times
while handling HETRON and AROPOL resins. Prolonged or
repeated skin contact causes skin irritation and may damage
the skin. If resin comes in contact with skin, it should be
washed off immediately with large amounts of water and
soap. If the skin is damaged, seek immediate medical attention. If irritation symptoms persist, seek medical attention.
Eye Contact
Eye protection should be worn at all times while handling
HETRON and AROPOL resins. Exposure to liquid or vapor may
cause eye irritation. If symptoms such as stinging, tearing, redness, and swelling develop and persist, seek medical attention.
Inhalation
Inhalation of styrene vapors from HETRON and AROPOL resins
should be minimized with ventilation or other engineering
controls. Exposure over the recommended limits may cause
respiratory irritation and central nervous system (CNS) effects.
Symptoms of CNS depression include headaches, nausea,
drowsiness, etc. If inhalation symptoms develop, immediately
move the individual away form exposure and into fresh air.
Seek immediate medical attention.
35
Protective clothing,
such as safety glasses,
safety shoes, and gloves
should be worn when
handling HETRON and
AROPOL resins.
Ingestion
Swallowing any amount of HETRON or AROPOL resin may be harmful. Seek medical
attention and, if possible, do not leave the person unattended.
Chronic Health Effects
In 1987, the International Agency for Research and Cancer (IRAC) classified styrene as a
group 2B (possibly carcinogenic to humans).This classification was not based on
styrene itself, but upon that of styrene oxide, a metabolite of styrene.The potential for
styrene exposure to cause cancer in humans has been questioned by many orginizations. Current information on this topic is available on the websites previously mentioned in this section.
Resin Spills
Very small resin spills of less than 100 grams can be wiped up with a paper towel or
cloth. Spills greater that 100 grams and less than 10 gallons should be cleaned up by
applying sand or another appropriate absorbent material on the spilled resin. After the
resin is absorbed, the material can be shoveled into a container and properly disposed
of.The sticky residue should be removed using hot, soapy water. Large resin spills,
greater than 10 gallons, should be contained using a dike.The spilled resin should be
removed using containers and properly disposed of.
Storage
Resin in drums should be stored below 80F (27C) and away from direct heat sources
such as sunlight and steam pipes. If stored at temperatures above 80F (27C), storage
life will decrease. Bulk quantities of resin should be stored in stainless steel tanks or
tanks lined with epoxy or phenolic coatings. When stroring resins, bubbling dry air or a
mix of 5% oxygen and 95% nitrogen into the bottom of the tank may be desirable to
keep inhibitors activated and maximize shelf life. Containers should be sealed to prevent moisture pickup and monomer loss.
Disposal
Local, state and federal regulations should be carefully followed when disposing of any
hazardous material. Do not discharge effluent containing this product into lakes,
streams, ponds, estuaries, oceans, or other waters. In some states, completely cured resin
parts may be considered non-hazardous, however, it is recommended that the proper
local or state agency be contacted to confirm the proper method of disposal for cured
resin parts. For assistance with your waste management needsincluding disposal,
recycling and waste stream reduction, contact Ashland Distribution Company, IC&S
Enviromental Services Group at 800-637-7922
36
APPENDIX A
Promoter and Catalyst Addition Tables
Table 1A Typical Gel Times for HETRON 922 Resin with MEKP1
Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Catalyst
Gel Time
(minutes)
Delta X-9
Gel Time
(minutes)
DDM-9
Gel Time
(minutes)
HiPoint 90
65 (18)
0.3
0.3
0.3
0.15
0.075
0.05
1.25
1.25
1.25
14.3
23.8
38.3
21.3
30.7
39.3
21.9
29.4
39.4
75 (24)
0.3
0.3
0.3
0.075
0.05
0.025
1.25
1.25
1.25
14.8
21.3
33.0
17.4
23.3
34.4
16.8
22.5
35.7
85 (29)
0.2
0.2
0.2
0.075
0.05
0.025
1.25
1.25
1.25
15.3
22.2
36.7
17.9
23.7
37.7
18.3
24.2
40.8
Table 2A Typical Gel Times for HETRON 922 Resin with BPO3
Temperature
F (C)
DMA4
Catalyst
(50% BPO Paste)
Gel Time
(minutes)
65 (18)
0.70
0.50
0.30
2.0
2.0
2.0
17.3
23.5
37.6
75 (24)
0.50
0.30
0.15
2.0
2.0
2.0
15.5
25.0
49.0
85 (29)
0.30
0.20
0.10
0.30
2.0
2.0
2.0
2.0
17.7
24.8
36.2
17.9
Table 3A HETRON 922 Resin and Different Levels of Copper at 77F

Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Copper
(PPM)
Catalyst
(Delta X-9)
Gel Time
(minutes)
Gel to Peak
(minutes)
Peak
Exotherm
77 (25)
0.30
0.30
0.30
0.30
0.075
0.075
0.075
0.075
0
100
200
300
1.25
1.25
1.25
1.25
15.6
16.0
15.8
16.6
9.4
8.0
11.2
10.9
322F
284F
248F
228F
37
Table 4A Typical Gel Times for HETRON 942/35 Resin with MEKP1
Gel Time
(minutes)
HiPoint 90/CHP5
(50/50)
Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Catalyst
Gel Time
(minutes)
Delta X-9
Gel Time
(minutes)
DDM-9
Gel Time
(minutes)
HiPoint 90
65 (18)
0.35
0.3
0.3
0.3
0.2
0.2
0.1
0.05
1.25
1.25
1.25
1.25
9.3
13.2
19.2
28.1
17.9
21.0
26.3
39.0
18.0
21.5
26.3
39.4
75 (24)
0.3
0.3
0.2
0.05
0.02
0.02
1.25
1.25
1.25
15.4
28.2
52.4
17.7
32.1
55.4
16.4
30.4
55.9
45.6
53.2
61.1
69.7
34.5
69.4
111.6
85 (29)
0.4
0.3
0.2
0.1
0.04
0.03
0.03
0.03
1.25
1.25
1.25
1.25
9.2
18.1
29.1
53.3
11.1
19.6
32.0
58.1
11.0
18.8
29.6
49.5
21.3
40.5
55.5
80.9
Table 5A Typical Gel Times for HETRON 942/35 Resin with BPO3
Temperature
F (C)
65 (18)
75 (24)
85 (29)
DMA4
Catalyst
(50% BPO Paste)
Gel Time
(minutes)
0.50
0.40
0.30
0.20
0.40
0.30
0.20
0.10
0.30
0.20
0.10
0.05
2.0
2.0
2.0
2.0
2.0
2.0
2.0
2.0
2.0
2.0
2.0
2.0
16.9
19.3
23.1
35.2
11.7
15.1
21.0
44.8
11.4
18.5
41.2
176.1
Table 6A HETRON 942/35 Resin and Different Levels of Copper at 77F

Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Copper
(PPM)
Catalyst
(Delta X-9)
Gel Time
(minutes)
Gel to Peak
(minutes)
Peak
Exotherm
77 (25)
0.30
0.30
0.30
0.30
0.05
0.05
0.05
0.05
0
100
200
300
1.25
1.25
1.25
1.25
13.4
11.5
12.4
11.1
6.3
7.1
10.0
10.3
335F
304F
277F
259F
38
Table 7A Typical Gel Times for HETRON 980/35 Resin with MEKP1
Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Catalyst
Gel Time
(minutes)
Delta X-9
Gel Time
(minutes)
DDM-9
Gel Time
(minutes)
HiPoint 90
65 (18)
0.55
0.4
0.4
0.05
0.05
0.025
1.25
1.25
1.25
16.2
24.9
39.1
18.0
27.5
40.2
18.0
30.6
42.0
75 (24)
0.4
0.3
0.2
0.025
0.025
0.025
1.25
1.25
1.25
20.0
24.9
34.5
20.6
26.7
35.9
20.5
26.4
35.4
85 (29)
0.3
0.25
0.2
0.025
0.025
0.015
1.25
1.25
1.25
19.7
22.1
34.6
20.7
23.5
35.9
21.4
26.5
40.5
Temperature
F (C)
DMA4
Catalyst
(50% BPO Paste)
Gel Time
(minutes)
65 (18)
0.40
0.30
0.20
2.0
2.0
2.0
12.8
24.9
35.7
75 (24)
0.30
0.20
0.10
2.0
2.0
2.0
13.6
24.7
52.1
85 (29)
0.30
0.20
0.10
2.0
2.0
2.0
11.6
17.5
37.9
Table 9A HETRON 980/35 Resin and Different Levels of Copper at 77F

Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Copper
(PPM)
Catalyst
(Delta X-9)
Gel Time
(minutes)
Gel to Peak
(minutes)
Peak
Exotherm
77 (25)
0.30
0.30
0.30
0.30
0.02
0.02
0.02
0.02
0
100
200
300
1.25
1.25
1.25
1.25
28.2
24.0
24.5
24.6
14.0
13.8
16.5
22.0
328F
312F
284F
254F
Table 10A Typical Gel Times for HETRON FR 992 Resin with MEKP1
Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Catalyst
Gel Time
(minutes)
Delta X-9
Gel Time
(minutes)
DDM-9
Gel Time
(minutes)
HiPoint 90
Gel Time
(minutes)
HiPoint 90/CHP5
(50/50)
65 (18)
0.2
0.2
0.2
0.15
0.1
0.075
0.05
0.05
1.25
1.25
1.25
1.25
16.2
19.5
26.9
35.7
27.1
30.6
40.0
50.9
26.0
30.9
33.4
47.9
60.8
68.8
76.1
112.4
75 (24)
0.3
0.2
0.15
0.1
0.04
0.04
0.04
0.04
1.25
1.25
1.25
1.25
10.7
16.2
21.6
29.6
12.4
20.5
27.3
37.1
12.7
19.1
25.7
35.8
26.9
39.8
53.5
73.7
85 (29)
0.3
0.2
0.1
0.1
0.05
0.05
0.05
0.05
1.25
1.25
1.25
1.25
7.7
10.7
20.0
29.1
7.9
11.5
25.1
34.6
8.3
12.1
23.5
30.1
18.4
23.7
47.8
62.4
39
Table 11A Typical Gel Times for HETRON FR 992 Resin with BPO3
Temperature
F (C)
DMA4
Catalyst
(50% BPO Paste)
Gel Time
(minutes)
0.50
0.30
0.20
0.10
2.0
2.0
2.0
20.6
26.0
36.2
70.1
75 (24)
0.30
0.20
0.10
2.0
2.0
2.0
16.3
23.6
47.7
85 (29)
0.30
0.20
0.10
0.05
2.0
2.0
2.0
2.0
11.3
15.9
27.3
59.4
65 (18)
Table 12A HETRON FR 992 Resin and Different Levels of Copper at 77F
Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Copper
(PPM)
Catalyst
(Delta X-9)
Gel Time
(minutes)
Gel to Peak
(minutes)
Peak
Exotherm
77 (25)
0.10
0.10
0.10
0.10
0.04
0.04
0.04
0.04
0
100
200
300
1.25
1.25
1.25
1.25
22.6
20.2
20.2
20.6
10.5
10.2
14.2
15.9
341F
317F
310F
288F
Table 13A Typical Gel Times for HETRON FR 998/35 Resin with MEKP1
Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Catalyst
Gel Time
(minutes)
Delta X-9
Gel Time
(minutes)
DDM-9
Gel Time
(minutes)
HiPoint 90
Gel Time
(minutes)
HiPoint 90/CHP5
(50/50)
65 (18)
0.25
0.35
0.25
0.35
0.025
0.01
0.01
1.25
1.25
1.25
1.25
11.6
15.8
24.5
34.8
15.2
16.4
27.3
36.7
14.6
16.1
26.8
38.3
36.7
42.9
66.1
86.0
75 (24)
0.15
0.3
0.15
0.1
0.05
1.25
1.25
1.25
1.25
6.6
20.5
31.4
51.8
10.1
21.5
35.0
57.6
9.3
22.4
35.2
56.9
21.4
46.8
76.1
115.0
85 (29)
0.3
0.2
0.1
1.25
1.25
1.25
18.0
22.0
37.5
18.7
22.3
41.3
18.7
23.1
41.0
40.8
49.2
84.6
40
Table 14A Typical Gel Times for HETRON FR 998/35 Resin with BPO3
Temperature
F (C)
DMA4
Catalyst
(50% BPO Paste)
Gel Time
(minutes)
65 (18)
0.20
0.20
0.15
0.10
2.0
2.0
2.0
2.0
14.1
20.0
27.0
43.0
75 (24)
0.20
0.15
0.10
0.05
2.0
2.0
2.0
2.0
14.1
20.1
31.4
76.5
85 (29)
0.20
0.15
0.10
0.05
2.0
2.0
2.0
2.0
10.3
12.3
17.7
46.0
Table 15A HETRON FR 998/35 Resin and Different Levels of Copper at 77F
Temperature
F (C)
6% Cobalt2
Naphthenate
DMA4
Copper
(PPM)
Catalyst
(Delta X-9)
Gel Time
(minutes)
Gel to Peak
(minutes)
Peak
Exotherm
77 (25)
0.10
0.10
0.10
0.10
0
100
200
300
1.25
1.25
1.25
1.25
28.3
31.5
32.8
33.1
13.5
15.2
17.4
21.9
320F
307F
286F
279F
Table 16A Typical Gel Times for HETRON 922L Resin with MEKP1
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
Dimethylaniline4
(phr)
MEKP1
(phr)
65 (18)
10 - 20
20 - 30
30 - 40
0.30
0.30
0.30
0.075
0.025
0.010
1.25
1.25
1.25
75 (24)
10 - 20
20 - 30
30 - 40
0.30
0.10
0.05
0.025
1.25
1.25
1.25
85 (29)
10 - 20
20 - 30
30 - 40
0.30
0.05
0.025
0.010
1.25
1.25
1.25
Table 17A Typical Gel Times for HETRON 922L Resin with BPO3
Temperature
F (C)
Gel Time
(minutes)
Dimenthylaniline4
(phr)
BPO3
(phr)
75 (24)
10 - 15
20 - 25
30 - 35
0.25
0.15
0.10
2.00
2.00
2.00
41
Table 18A Typical Gel Times for HETRON 992L-25 Resin with MEKP1
Temperature
F (C)
Gel Time
(minutes)
MEKP1
(phr)
65 (18)
40 - 50
50 - 60
65 - 75
1.50
1.25
1.00
75 (24)
15 - 25
25 - 35
1.50
1.00
85 (29)
10 - 20
20 - 30
1.50
1.00
Table 19A Typical Gel Times for HETRON 970/35 Resin with CHP5 and TBC-856
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
(phr)
Dimethylaniline4
(phr)
TBC-856
(phr)
CHP5
(phr)
65 (18)
10 - 20
20 - 30
30 - 40
0.50
0.40
0.20
0.40
0.10
0.05
2.50
2.00
1.50
75 (24)
10 - 20
20 - 30
30 - 40
0.20
0.10
0.10
0.15
0.05
0.05
0.02
1.50
1.00
1.00
85 (29)
10 - 20
20 - 30
30 - 40
0.15
0.10
0.10
0.05
0.025
0.02
0.02
0.03
1.50
1.00
1.00
Temperature
F (C)
Gel Time
(minutes)
Dimethylaniline4
(phr)
BPO3
(phr)
65 (18)
10 - 20
20 - 30
30 - 40
0.20
0.15
0.10
2.00
1.75
1.25
75 (24)
10 - 20
20 - 30
30 - 40
0.15
0.10
0.07
2.00
2.00
2.00
85 (29)
10 - 20
20 - 30
30 - 40
0.10
0.10
0.05
2.00
1.25
2.00
42
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
(phr)
Dimethylaniline4
(phr)
MEKP1
(phr)
65 (18)
10 - 20
20 - 30
30 - 40
0.30
0.30
0.20
0.10
0.05
0.05
1.25
1.25
1.25
75 (24)
10 - 20
20 - 30
30 - 40
0.30
0.20
0.20
0.05
0.05
0.025
1.25
1.25
1.25
85 (29)
10 - 20
20 - 30
30 - 40
0.20
0.30
0.30
0.05
1.25
1.25
1.25
Table 22A Typical Gel Times for HETRON 980 Resin with BPO3 and HQ7 as an Inhibitor
Temperature
F (C)
Gel Time
(minutes)
Dimethylaniline4
(phr)
HQ7
(phr)
BPO3
(phr)
65 (18)
30 - 40
40 - 50
50 - 60
70 - 80
0.30
0.25
0.20
0.15
2.00
2.00
2.00
2.00
75 (24)
15 - 25
20 - 25
25 - 35
35 - 45
0.30
0.25
0.20
0.15
2.00
2.00
2.00
2.00
85 (29)
15 - 25
20 - 25
25 - 35
45 - 55
0.25
0.20
0.15
0.10
1.50
1.50
1.50
1.50
95 (35)
15 - 25
25 - 30
30 - 40
40 - 50
50 - 60
70 - 80
0.25
0.20
0.15
0.25
0.20
0.10
0.005
0.005
0.005
1.00
1.00
1.00
1.00
1.00
1.00
Table 23A Typical Gel Times for HETRON FR990 ZX Resin with MEKP1
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
(phr)
Dimethylaniline4
(phr)
MEKP1
(phr)
77 (25)
5 - 15
10 - 20
15 - 25
20 - 30
25 - 35
0.30
0.20
0.30
0.10
0.10
0.10
0.10
0.10
1.50
1.50
1.50
1.50
1.50
43
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
(phr)
MEKP1
(phr)
75 (24)
10 - 15
15 - 25
25 - 35
40 - 50
0.50
0.30
0.20
0.10
1.00
1.00
0.90
1.00
85 (29)
10 - 15
15 - 20
20 - 25
25 - 35
0.30
0.20
0.10
0.20
1.00
0.90
1.00
0.50
95 (35)
10 - 15
15 - 20
20 - 25
0.20
0.10
0.20
0.90
1.00
0.70
Table 25A Typical Gel Times for HETRON 92FR Resin with MEKP1
Temperature
F (C)
Gel Time
(minutes)
MEKP1
(phr)
65 (18)
30 - 35
35 - 40
1.25
1.00
75 (24)
15 - 20
20 - 25
1.50
1.00
85 (29)
5 - 10
10 - 15
1.50
1.00
Table 26A Typical Gel Times for HETRON 197 and 197-3 Resin with MEKP1
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
(phr)
Dimethylaniline4
(phr)
MEKP1
(phr)
55 (13)
3-6
15 - 25
35 - 45
0.70
0.70
0.40
0.20
1.90
1.50
15.0
65 (18)
3-6
15 - 25
35 - 45
0.60
0.60
0.40
0.10
1.25
1.25
1.25
75 (24)
10 - 15
20 - 25
30 - 40
55 -65
0.60
0.40
0.20
0.15
1.25
1.25
0.90
0.90
85 (29)
10 - 20
30 - 40
40 - 50
0.40
0.20
0.19
1.25
0.90
0.65
95 (35)
10 -15
15 - 25
25 - 35
0.40
0.20
0.20
1.25
0.90
0.65
44
Table 27A Typical Gel Times for HETRON 197 and 197-3 Resins with BPO3
Temperature
F (C)
Gel Time
(minutes)
Dimethylaniline4
(phr)
BPO3
(phr)
65 (18)
40 - 50
50 - 60
75 - 85
0.25
0.20
0.15
2.00
2.00
2.00
75 (24)
25 -30
30 - 35
35 - 45
50 - 60
0.25
0.20
0.15
0.10
2.00
2.00
2.00
2.00
85 (29)
20 - 25
30 - 35
70 - 80
0.15
0.10
0.05
1.50
1.50
1.50
95 (35)
20 - 25
25 - 30
30 - 40
40 - 50
55 - 65
0.15
0.15
0.10
0.05
0.05
1.50
1.00
1.00
1.50
1.00
Table 28A Typical Gel Times for HETRON 197P Resin with MEKP1 and HQ7 as an Inhibitor
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
(phr)
MEKP1
(phr)
65 (18)
25 - 35
35 - 40
40 - 50
1.50
1.25
1.00
75 (24)
10 - 15
15 - 20
20 - 25
30 - 40
45 - 55
0.010
0.006
0.008
1.25
1.25
1.00
1.25
1.25
85 (29)
5 - 10
15 - 20
1.50
1.00
Table 29A Typical Gel Times for HETRON 604T20 Resin with MEKP1
45
Temperature
F (C)
Gel Time
(minutes)
MEKP1
(phr)
65 (18)
25 - 35
40 - 50
1.75
1.25
75 (24)
10 - 20
25 - 35
1.75
1.00
85 (29)
5 - 15
15 - 25
1.75
1.00
Temperature
F (C)
Gel Time
(minutes)
6% Cobalt2
Naphthenate
(phr)
Dimethylaniline4
(phr)
MEKP1
(phr)
65 (18)
30 - 40
40 - 50
60 - 65
0.50
0.40
0.30
0.10
0.10
0.10
1.25
1.25
1.25
75 (24)
20 - 30
30 - 35
40 - 45
50 - 55
0.50
0.40
0.30
0.20
0.10
0.10
0.10
0.10
1.25
1.25
1.25
1.25
85 (29)
15 - 20
20 - 25
25 - 30
45 - 50
0.40
0.30
0.20
0.10
0.10
0.10
0.10
0.10
1.25
1.25
1.25
1.25
95 (35)
15 - 20
25 - 30
35 - 40
45 - 50
0.30
0.20
0.10
0.10
0.10
0.10
0.10
0.10
1.25
1.25
1.25
1.00
Table 31A Typical Gel Times for HETRON 700 Resin with BPO3
Temperature
F (C)
Gel Time
(minutes)
Dimethylaniline4
(phr)
BPO3
(phr)
65 (18)
25 - 35
35 - 45
50 - 60
0.50
0.40
0.30
2.00
2.00
2.00
75 (24)
15 - 20
20 - 30
30 - 40
40 - 50
50 - 60
0.60
0.50
0.40
0.30
0.20
2.00
2.00
2.00
2.00
85 (29)
25 - 35
35 - 45
50 - 60
65 - 75
0.40
0.30
0.20
0.10
2.00
2.00
2.00
2.00
95 (35)
15 - 20
20 - 30
35 - 45
60 - 70
0.40
0.30
0.20
0.10
2.00
2.00
2.00
2.00
46
Table 32A Typical Gel Times for HETRON 800 Resin with HETRON 803L-1 Catalyst
Temperature
F (C)
Gel Time
(minutes)
HETRON 803L-1
(phr)
65 (18)
15 - 20
25 - 30
30 - 35
5.0
3.0
2.5
75 (24)
10 - 15
15 - 20
4.0
2.5
85 (29)
5 - 10
10 - 15
4.0
2.5
Table 33A Typical Gel Times for AROPOL 7241T-15 Resin with MEKP1
Temperature
F (C)
Gel Time
(minutes)
MEKP1
(phr)
60 (15)
10 - 15
25 - 30
50 - 60
1.90
1.25
0.65
70 (21)
10 - 15
15 - 20
45 - 50
1.90
1.25
0.65
80 (27)
5 - 10
10 - 15
20 - 30
1.90
1.25
0.65
90 (32)
5 - 10
10 - 15
1.25
0.65
Table 34A Typical Gel Times for AROPOL 7334T-15 Resin with MEKP1
47
Temperature
F (C)
Gel Time
(minutes)
MEKP1
(phr)
65 (18)
30 - 35
1.25
75 (24)
15 - 20
1.25
85 (29)
10 - 15
1.25
Table 40D Typical Gel Times for AROPOL 7334T-15 Resin with MEKP1
Temperature
F (C)
Gel Time
(minutes)
MEKP1
(phr)
65 (18)
30 - 35
1.25
75 (24)
15 - 20
1.25
85 (29)
10 - 15
1.25
ppm
55 gallon drum (450 lbs)

fl. oz. / ccs or grams
5 gallon pail (40 lbs)

ccs or grams
50
0.35 / 10
0.9
100
0.7 / 20
1.8
150
1.0 / 31
2.7
200
1.4 / 41
3.6
250
1.7 / 51
4.5
300
2.1 / 61
5.4
Copper Conversion Table
Notes:
1 Methyl Ethyl Ketone Peroxide, 9.0% active oxygen
2 In Europe, 6% cobalt octoate can be substituted for 6% cobalt naphthenate to obtain comparable gel
times. If 12% cobalt octoate is used, half as much 12% cobalt octoate as 6% cobalt naphthenate should
be used to obtain comparable gel times.
3 Benzyl Peroxide Paste, 50% active
4 Dimethyl Aniline
5 Cumene Hydroperoxide
6 TBC-85 is tertiary butyl catechol, 85% solution
7 Hydroquinone
48
APPENDIX B
Ashland Specialty Chemical Technical Service Contacts
Country/Region
Company/Contact
Address/Phone/Fax
UNITED STATES
Ashland Specialty Chemical Company

HETRON Technical Service
5200 Blazer Pkwy
Dublin, Ohio 43017
phone: 800.327.8720
fax: 614.790.6157
e-mail: [email protected]
AUSTRALIA
Huntsman Chemical Company Australia

Sommerville Road
P.O. Box 62
West Footscray VIC 3012
phone: 61.3.316.3172
fax: 61.3.316.3579
BRAZIL
ARA Quimica, S.A.

Alameda Rio Negro, 1084
Salas M3/M5
Barueri, Sa Paulo
CEP 06454-000, BRAZIL
phone: 55.11.4195.6777
fax: 55.11.4195.1317
e-mail: www.araquimica.com.br
CHINA
Ashland Chemical
Holiday Inn Office Building
45 North Zhongshan Road
Room 1205
Nanjing, CHINA 210008
phone: 86.25.331.8982
fax: 86.25.331.8760
e-mail: [email protected]
EUROPE
Ashland Composite Polymers Division

Via delle Groane, 126
20024 Garbagnate (MI) ITALY
phone: 39.02.3978.8446/8447
fax: 39.02.3978.8413
SAUDI ARABIA
Saudi Industrial Resins, Ltd.

Manufacturing Facility
P.O. Box 7764
Al Farsi Center, 9th Floor
Jeddah, SAUDI ARABIA 21472
phone: 966.2.651.8920
fax: 966.2.651.7072
SPAIN
Ashland Chemical Hispania, S.A.

Manufacturing Facility
Partida Povet 37
APDO Correo 26
12580 Benicarl, SPAIN
phone: 34.964.471.316
fax: 34.964.473.697
49
APPENDIX C
North American Suppliers
Reinforcements
C-Glass Veil
NEXUS Veil
Chopped Mat / Woven Roving
Owens Corning
Precision Fabrics Group Inc.
Vetrotex (CertainTeed)
Owens Corning
PPG Industries, Inc.
419.248.8000
800.284.8071
800.433.0922
419.248.8000
412.434.3131
www.owenscorning.com
www.precisionfabrics.com
www.vetrotexcertainteed.com
www.owenscorning.com
www.ppg.com
Witco Corporation
Elf-Atochem North American Inc.
Akzo Nobel
The Norac Company, Inc.
Akzo Nobel
800.494.8737
800.558.5575
800.227.7070
626.334.2908
800.227.7070
www.witco.com
www.atofina.com
www.akzo-nobel.com
www.norac.com
www.akzo-nobel.com
800.558.5575
www.atofina.com
800.558.5575
www.atofina.com
Promoters
6% Cobalt / 12% Cobalt
Dimethyl Aniline / Diethyl Aniline
OMG Americas, Inc.

Buffalo Color Corporation
216.781.0083
800.631.0171
www.omgi.com
www.buffalocolor.com
Inhibitors
Tertiary Butyl Catechol (TBC)
Hydroquinone (HQ)
Toluhydroquinone (THQ)
Union Carbide Chemicals

Eastman Chemical Products, Inc.
Eastman Chemical Products, Inc.
800.447.4369
615.240.4111
615.240.4111
www.dow.com
www.eastman.com
www.eastman.com
Antimony Oxides
Antimony Trioxide
Antimony Pentoxide
Hoechst Celanese Corporation

PQ Corporation
704.554.3148
610.651.4200
www.vectran.com
www.pqcorp.com
PPG Industries, Inc.
412.434.3131
www.ppg.com
Fumed Silica
CAB-O-SIL TS-720 or M-5
AEROSIL R200 or R202
Cabot Corporation
Degussa Corporation
217.253.3370
201.641.6100
www.cabot-corp.com
www.degussa.com
Cytec Industries
Cytec Industries
800.486.5525
800.486.5525
www.cytec.com
www.cytec.com
Cytec Industries
Ciba Geigy Corporation
BASF Corporation
800.486.5525
800.431.1900
800.669.2273
www.cytec.com
www.ciba.com
www.basf.com
Air Release Agents

BYK A515
SAG 47
BYK Chemie
OSi Specialties
203.265.2086
800.523.5862
www.byk.com
www.osispecialties.com
Abrasion Resistant Additives

Silicon Carbide
Aluminum Oxide
Exolon ESK Company

Degussa Corporation
800 962-1100
201.641.6100
www.exolon.com
www.degussa.com
Air Inhibitors/ Suppressants

Fully Refined Paraffin Wax
Fully Refined Paraffin Wax
BYK S750
H M Royal
Moore & Munger
BYK Chemie
800.257.9452
800.423.7071
203.265.2086
www.hmroyal.com
www.mooremunger.com
www.byk.com
Exotherm Suppressant
Copper Naphthenate
OMG Americas, Inc.
216.781.0083
www.omgi.com
Wetting Agents
Tween 20
BYK R605
ICI Chemicals
BYK Chemie
302.887.3000
203.265.2086
www.ici.com
www.byk.com
Catalysts
MEK Peroxide
HIPOINT 90
LUPERSOL DDM-9
BUTANOX M-50
NOROX MEKP-9
CADOX M-50
Benzyl Peroxide
LUPERCO ATC paste
Cumene Hydroperoxide
Cumene Hydroperoxide
UV Stabilizers
For Polyester Resins
CYASORB 5411
CYASORB UV-9
For Vinyl Esters
CYASORB UV-9
TINUVIN 328
UNIVINUL M-40
Check out suppliers on-line for international contacts!
50
APPENDIX D
Equipment Suppliers
Chopper Guns/RTM Supplies
Magnum Venus Products
Glas-Craft
Binks
800.448.6035
317.875.5592
888.992.4657
www.venus-gusmer.com
www.glascraft.com
www.binks.com
Barcol Hardness Testers

Barber Colman Company
815.637.3222
www.barber-colman.com
Viscometers
Brookfield
800.628.8139
www.brookfieldengineering.com
Gel Timers
Techne
800.225.9243
www.techneusa.com
800.446.1446
www.masterheaters.com
www.vogelzang.com
Pumps & Mixers

800.448.6035
Rollers, Laminating Accessories

800.448.6035
Portable Heaters
Master Heaters
Vogelzang International Corporation
51
APPENDIX E
Trouble Shooting Guide for Curing Resins at Room Temperature
Check Points
Defect
MEKP or CHP
BPO
Reduce DMA and/or BPO levels but not below those
recommended for that resin system.
Add inhibitor.
Check resin, shop and mold temperature; warm temperatures cause resin to gel faster.
Resin
gelling
too quickly
Reduce cobalt, DMA, or catalyst levels but not below

those recommended for that resin system.
Add inhibitor.
Check resin, shop and mold temperature; warm temperatures cause resin to gel faster.
Resin
exotherm
too high
during
curing
Reduce DMA and/or catalyst levels but not below

those recommended for that resin system.
Lay up fewer plies at one time to reduce amount of
heat generated during exotherm and allow to
exotherm before adding additional plies.
Use a 50/50 blend of MEKP/CHP.
Reduce DMA level but not below that recommended

for that resin system.
DMA/BPO is a hot system. Lay-up fewer plies at one
time and allow to exotherm before adding additional
plies.
Resin
gelling
too slowly
or will not
gel at all
Increase promoter/catalyst levels, not above those

Reduce or eliminate inhibitor.
Check resin, shop and mold temperature; cool temperatures cause resin to gel slower.
Check other additives. Antimony trioxides, fillers, and
pigments may retard gel time. M ix fillers in just before
adding catalyst.
Check mixing. Cobalt may be difficult to mix into resin,
especially if resin is cool. Dissolve cobalt in a small
amount of styrene before adding to resin.
Check fittings on equipment. Bronze, copper and zinc
may inhibit cure.
Increase promoter/catalyst levels, not above those

Check resin, shop and mold temperature; cool temperatures cause resin to gel slower.
Check other additives. Antimony trioxides, fillers and
pigments may retard gel time. Mix fillers in just before
adding catalyst.
Check active level of BPO. Some BPO is not 100%
active. Levels may have to be adjusted to five required
level of BPO.
Insure proper mixing of all additives.
Resin not
getting
hard after
gelation or
spotty cure.
Increase promoter/catalyst levels but not above those

If surface is tacky or acetone sensitive, a wax topcoat
may be necessary.
Insure proper mixing or all additives.
Check fittings on equipment. Bronze, copper and zinc
may inhibit cure.
Increase promoter/catalyst levels but not above those

If surface is tacky or acetone sensitive, a wax topcoat
may be necessary.
Insure proper mixing of all additives.
52
APPENDIX F
Weight to Volume Conversion Tables
Resin Quantity
Additive
(phf)
6% Cobalt
Naphthenate1
0.10
0.20
0.30
0.40
0.50
Conversion
1 Gallon
(8.8 lbs, 4 kg)
5 Gallons
(44 lbs, 20 kg)
55 Gallons
(450 lbs, 200 kg)
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
0.15
4
0.3
8
0.4
12
0.6
17
0.7
21
0.7
21
1.4
41
2.1
62
2.8
83
3.5
104
7.2
212
14
423
22
634
29
849
36
1.1L
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
0.03
0.9
0.07
2.1
0.1
3.0
0.15
4.1
0.15
4.5
0.35
10
0.5
15
0.7
21
1.5
46
3.6
106
5.1
151
7.0
212
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
1.2
36
1.5
44
1.8
53
2.1
62
2.4
71
6.0
178
7.5
222
9.0
266
11
311
13
355
61
1.8L
77
2.3L
92
2.7L
107
3.2L
122
3.7L
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
fl. oz.
cc
1.2
36
1.7
49
2.3
65
2.9
82
3.5
98
5.8
164
8.6
245
11.5
327
14
409
17
491
59
1.7L
88
2.5L
118
3.3L
147
4.2L
176
5.0L
Dimethylaniline
0.025
0.05
0.075
0.10
Methyl Ethyl Ketone
Peroxide
1.00
1.25
1.50
1.75
2.00
Benzyl Peroxide
Paste (50% active)
1.00
1.50
2.00
2.50
3.00
1
In Europe, 6% cobalt octoate can be substituted for 6% cobalt naphthenate to obtain comparable gel times. If 12% cobalt octoate is used,
half as much 12% cobalt octoate as 6% cobalt naphthenate should be used to obtain comparable gel times.
53
APPENDIX G
Visual Acceptance Criteria for Cured Laminates
Defect
Air bubbles,
Voids
Description
Entrapped air in and
between glass plies
Possible Causes
Possible Solutions
Application of too many

plies of glass at one time
Apply fewer plies at one

time and roll thoroughly
Inadequate rolling between

applications
Reduce mixing speed
Vigorous mixing causing

incorporation of air into
resin
Resin viscosity can be

reduced by adding 3 - 5%
styrene
High viscosity resin used in

combination with thick glass
Round, elevated areas of

varying sizes on laminate
surface, may occur individually or in a group
Blisters
Too rapid cure with high

exotherm may cause separation at mat surfaces
Reduce exotherm of resin

system by laying up fewer
plies at one time
Presence of moisture in
glass, resin, or filler
Reduce exotherm by lowering DMA or catalyst level

Insure proper storage of
resin, glass, and filler, away
from sources of moisture
Cracks running along laminate either on or just below

the surface
Crack
Overly resin-rich areas
Reduce resin content
Cracks may result from dramatic changes in the temperature conditions of the
equipment (thermal shock
cracking)
Monitor and minimize

temperature fluctuations
during equipment operation
Resin shrinkage during cure
Delamination
Separation of glass layers,

occurs particularly in areas
of high stress; i.e., smalldiameter pipe, knuckle
joints, etc.
Inadequate saturation of
glass with resin
Application of two layers of
woven roving with no
chopped mat in between
Application of laminate to
an FRP surface that has been
allowed to cure several
weeks
Use of rapid cure systems in
small radii areas
54
Insure glass is completely

saturated with resin and
roll thoroughly
Always use alternating layers of woven roving and
chopped mat
Before applying another
FRP layer, lightly sand areas
that have been cured for
long periods of time
In tight radii areas, use a
low-exotherm system to
reduce resin shrinkage and
stress build-up
Defect
Description
Possible Causes
Possible Solutions
Dry Spots
Areas where dry glass

fibers are protruding from
laminate
Not thoroughly saturating

glass with resin
Thoroughly saturate
glass with resin and roll
thoroughly
Fish-eye
Mass of foreign material on

or near the laminate surface;
mass is not blended into
surrounding material
Dirty glass
Insure fabricating area

is clean
Initially, laminate appears

clear, but as curing occurs,
white blemishes appear in
the laminate, individual glass
fibers become prominent
and turn white
Incompatibility between
resin and glass binder; as
resin cures, binder phases
out, causing white cloudy
appearance of laminate
Thoroughly evaluate
compatibility of resin
and glass binder before
beginning fabrication
Small, raised area on

laminate surface
Dripping resin onto a

laminate surface that has
already begun to cure
Thoroughly roll out

laminate before resin
begins to cure
Rolling a laminate surface

that has begun to cure
Do not continue rolling if

resin is beginning to cure
Jackstrawing
Pimple
55
Contamination of resin with

foreign material
Properly store resin

and glass to eliminate
contamination
Contact Ashland Technical

Service for assistance in
selecting a glass compatible with specific resins
Defect
Scorching/Burning
Spotty Cure
Description
Possible Causes
Discoloration of laminate as
it cures
Generation of very high

exotherm temperatures due
to one or a combination of
the following -
Reduce DMA and/or

catalyst levels particularly
if working temperatures
are high
hot working temperatures, high DMA and/or

catalyst levels, laying up
too many plies at one
time
Reduce number of plies

laid up at one time and
allow to cure before applying additional layers
Laminate surface is soft in

some areas while cured hard
in others
Incomplete or inadequate
mixing of promoters and/or
catalyst
Possible Solutions
Adjust mixing to achieve

a small vortex and good
movement of resin surface
Mix thoroughly after
addition of each additive
Dissolve cobalt in small
amount of styrene before
adding to resin
Tacky Surface
Laminate surface is tacky

to the touch or fails to pass
acetone sensitivity test
(see page 24)
Incomplete cure caused by

air inhibition
Cobalt level too low
Apply a resin/wax topcoat

to tacky surface (see page
12)
Do not use a resin/wax
topcoat if additional bonding is to be done to the
surface
Increase cobalt level
Wrinkle
56
Crease or wrinkle of glass on

or near the laminate surface
Wrinkling of veil (particularly

synthetic veil) or glass can
occur when laminating over
uneven surfaces or when
using stiff, heavy glass in
corners
Use 1 oz. (300 g/m2) or

1 1/2 oz. (450 g/m2) mat
where wrinkling is a
problem
Reduce resin viscosity by
adding 3 - 5% styrene
RESPONSIBLE CARE
Ashland Specialty Chemical has a strong commitment to our customers, our employees,
and to the communities in which we operate and do business. We believe in maintaining our opertions in a totally safe and an environmentally responsible manner. Weve
focused our efforts on conserving resources and minimizing hazardous materials in
both our working environment and at our customers. In addition, we also participate in
the industrys Responsible Care* initiative of the American Chemistry Council.
*Responsible Care is a service mark of the American Chemistry Council.
QUALITY PLUSSM
Batch to batch uniformity of Ashlands HETRON & AROPOL resin systems not only
means easier molding but also consistent performance and quality.
Ashland Specialty Chemical Company adopted a continuous improvement process
called Quality Plus in the early 1980s. Ashland Specialty Chemical became a quality
leader in many industries we serve; continuous improvement has become an important
part of every employees training and thinking. Driven from the top down, this process
still guides all of our operations and activities, and the way we do business.
Notice: All precautionary labels and notices should be fully read and
understood by all supervisors personnel and employees before using.
For additional safety and health information, contact Ashland
Specialty Chemical Company. Purchaser has the responsibility for
determining any applicability of a compliance with federal, state and
local laws and/or regulations involving use, particularly in making
consumer products.
The information contained herein is correct to the best of our knowledge.The recommendations or suggestions contained in this bulletin
are made without guarantee or representation as to results. We suggest that you evaluate these recommendations and suggestions in
your own laboratory prior to use. Our responsibility for claims arising
from breach of warranty, negligence, or otherwise is limited to the
purchase price of the material. Freedom to use any patent owned by
Ashland or others is not to be inferred from any statement contained
herein.
Ashland Specialty Chemical Company

Composite Polymers
Box 2219
Columbus, Ohio 43216
800/327-8720 Technical Service
800/523-6963 Customer Service
Fax 614/790-6157
Technical Service E-mail [email protected]
Printed in U.S.A.
Copyright 2001, Ashland Inc.
TM
Trademark, Ashland Inc.
SM
Service mark Ashland Inc.
57
Registered Trademark, Ashland Inc.

In Canada, Ashland Canada, Inc. A Division of
Ashland Inc. Registered user of Trademark
* Responsible Care is a registered

service mark of the American
Chemistry Council in the United
States and of different
entities in other countries.
Bulletin #2735

Hetron Fabrication Process PDF

Uploaded by

Copyright:

Available Formats

Hetron Fabrication Process PDF

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Hetron Fabrication Process PDF

Uploaded by

Copyright:

Available Formats

A Guide To

Ashland Specialty Chemical Company is the leading supplier of resins

Previous | Contents | Next

Appendix A Promoter and Catalyst

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

High viscosity base resin,bulk molding compound (BMC),

Pultrusion,BMC,SMC,molded electrical sheet,

Hand lay-up,spray-up,press molding,

Hand lay-up,spray-up,filament winding

Hand lay-up,spray-up,filament winding

Hand lay-up,spray-up,filament winding,

Hand lay-up,spray-up,filament winding,

Hand lay-up,spray-up,filament winding,

Hand lay-up,spray-up,filament winding

Hand lay-up,spray-up,filament winding

RTM,hand lay-up,spray lay-up,filament winding

Corrosion Resistant isophthalic based products

Previous | Contents | Next

X with ATH X with ATH

Previous | Contents | Next

Gel Time (min.)

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

The wax/styrene solution is made by dissolving 20 g of a fully refined paraffin wax

Previous | Contents | Next

Previous | Contents | Next

serfacing veil, 0.010 - 0.020" (0.025 - 0.050mm) thick

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

C-glass veil is typically recommended for most

NEXUS synthetic surfacing veil

In severe environments, multiple plies of veil may be

Previous | Contents | Next

Chopped strand mat

Previous | Contents | Next

Continuous strand roving

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next

Previous | Contents | Next