Chapter 6

API 571
6.1

API 571: Introduction

This chapter covers the contents of API 571: Damage

mechanisms affecting xed equipment in the rening industry:
2003. API 571 has only recently been added to the syllabus
for the API 570 and 510 examinations and replaces what
used to be included in an old group of documents dating
from the 1960s entitled IRE (Inspection of renery equipment).
The rst point to note is that the API 571 sections covered
in the API 570 ICP exam syllabus is only an extract from the
full version of API 571.
6.1.1 The fteen damage mechanisms
Your copy of API 571 contains (among other things)
descriptions of fteen damage mechanisms (we will refer to
them as DMs). Here they are in Fig. 6.1.
Remember that these are all DMs that are found in the
1. Brittle fracture
2. Thermal fatigue
3. Erosioncorrosion
4. Mechanical fatigue
5. Vibration-induced fatigue
6. Atmospheric corrosion
7. Corrosion under insulation (CUI)
8. Boiler condensate corrosion
9. Flue-gas dewpoint corrosion
10. Microbiological-induced corrosion (MIC)
11. Soil corrosion
12. Suldation
13. SCC
14. Caustic embrittlement
15. High-temperature hydrogen attack (HTHA)
Figure 6.1 Fifteen API 571 damage mechanisms

WPASME100609
39
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

petrochemical/rening industry (because that is what API

571 is about), but they may or may not be found in other
industries. Some, such as brittle fracture and fatigue, are
commonly found in non-renery plant whearas others, such
as suldation, are not.
6.1.2 Are these DMs in some kind of precise logical
order?
No, or if they are, it is difcult to see what it is. The list
contains a mixture of high- and low-temperature DMs, some
of which affect plain carbon steels more than alloy or
stainless steels and vice versa. There are also various
subdivisions and a bit of repetition thrown in for good
measure. None of this is worth worrying about, as the order
in which they appear is not important.
In order to make the DMs easier to remember you can
think of them as being separated into three groups. There is
no code signicance in this rearrangement at all; it is simply
to make them easier to remember. Figure 6.2 shows the

Figure 6.2 DMs: a revised order

WPASME100609
40
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Q3. API 571 section 4.2.7.3: brittle fracture: critical

factors
At what temperature is brittle fracture most likely to occur?
(a) Temperatures above 400 8C
(b) Temperatures above the Charpy impact transition
temperature
(c) Temperatures below the Charpy impact transition
temperature
(d) In the range 20110 8C

&
&
&
&

Q4. API 571 section 4.2.7.4: brittle fracture

Which of these activities is unlikely to result in a high risk of
brittle fracture?
(a) Repeated hydrotesting above the Charpy impact
transition temperature
&
(b) Initial hydrotesting at low ambient temperatures
&
(c) Start-up of thick-walled vessels
&
(d) Autorefrigeration events
&

Q5. API 571 section 4.2.7.6: brittle fracture:

prevention/mitigation
What type of material change will reduce the risk of brittle
fracture?
(a) Use a material with lower toughness
&
(b) Use a material with lower impact strength
&
(c) Use a material with a higher ductility
&
(d) Use a thicker material section
&

Q6. API 571 section 4.2.7.5: brittle fracture:

appearance
Cracks resulting from brittle fracture will most likely
predominantly:
(a) Branched
(b) Straight and non-branching
(c) Intergranular
(d) Accompanied by localized necking around the crack

be
&
&
&
&

Q7. API 571 section 4.2.9: thermal fatigue: description

What is thermal fatigue?
(a) The result of excessive temperatures
(b) The result of temperature-induced corrosion

&
&

WPASME100609
45
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

a test of your understanding and short-term memory of the

DMs. The questions could come from any of the six
subsections shown in Fig. 6.3.

6.2

The rst group of DMs

The following Figs 6.4 to 6.7 relate to the rst group of DMs
in API 571. When looking through these gures, try to crossreference them to the content of the relevant sections of API
571. Then read the full sections of API 571 covering the four
DMs in this rst group.

Figure 6.4 Brittle facture

WPASME100609
42
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Figure 6.5 Thermal fatigue

Figure 6.6 Mechanical fatigue

WPASME100609
43
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

Figure 6.7 Vibration-induced fatigue

6.3

API 571 familiarization questions (set 1)

Attempt this rst set of self-test questions covering the rst

group of API 571 DMs.
Q1. API 571 section 4.2.7.1: brittle fracture
Which of these is a description of brittle fracture?
(a) Sudden rapid fracture of a material with plastic
deformation
(b) Sudden rapid fracture of a material without plastic
deformation
(c) Unexpected failure as a result of cyclic stress
(d) Fracture caused by reaction with sulfur compounds

&
&
&
&

Q2. API 571 section 4.2.7.2: brittle fracture: affected

materials
Which of these materials are particularly susceptible to brittle
fracture?
(a) Plain carbon and high alloy steels
&
(b) Plain carbon, low alloy and 300 series stainless steels
&
(c) Plain carbon, low alloy and 400 series stainless steels
&
(d) High-temperature resistant steels
&

WPASME100609
44
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Q3. API 571 section 4.2.7.3: brittle fracture: critical

factors
At what temperature is brittle fracture most likely to occur?
(a) Temperatures above 400 8C
(b) Temperatures above the Charpy impact transition
temperature
(c) Temperatures below the Charpy impact transition
temperature
(d) In the range 20110 8C

&
&
&
&

Q4. API 571 section 4.2.7.4: brittle fracture

Which of these activities is unlikely to result in a high risk of
brittle fracture?
(a) Repeated hydrotesting above the Charpy impact
transition temperature
&
(b) Initial hydrotesting at low ambient temperatures
&
(c) Start-up of thick-walled vessels
&
(d) Autorefrigeration events
&

Q5. API 571 section 4.2.7.6: brittle fracture:

prevention/mitigation
What type of material change will reduce the risk of brittle
fracture?
(a) Use a material with lower toughness
&
(b) Use a material with lower impact strength
&
(c) Use a material with a higher ductility
&
(d) Use a thicker material section
&

Q6. API 571 section 4.2.7.5: brittle fracture:

appearance
Cracks resulting from brittle fracture will most likely
predominantly:
(a) Branched
(b) Straight and non-branching
(c) Intergranular
(d) Accompanied by localized necking around the crack

be
&
&
&
&

Q7. API 571 section 4.2.9: thermal fatigue: description

What is thermal fatigue?
(a) The result of excessive temperatures
(b) The result of temperature-induced corrosion

&
&

WPASME100609
45
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

(c) The result of cyclic stresses caused by temperature

variations
&
(d) The result of cyclic stresses caused by dynamic loadings &

Q8. API 571 section 4.2.9.3: thermal fatigue: critical

factors
As a practical rule, thermal cracking may be caused by
temperature swings of approximately:
(a) 200 8C
&
(b) 200 8F
&
(c) 100 8C
&
(d) 100 8F
&

Q9. API 571 section 4.2.9.5: thermal fatigue:

appearance
Cracks resulting from thermal fatigue will most likely be
predominantly:
(a) Straight and non-branching
&
(b) Dagger-shaped
&
(c) Intergranular
&
(d) Straight and narrow
&

Q10.

API 571 section 4.2.9.6: prevention/mitigation

Thermal fatigue cracking is best avoided by:

(a) Better material selection
(b) Control of design and operation
(c) Better post-weld heat treatment (PWHT)
(d) Reducing mechanical vibrations

6.4

&
&
&
&

The second group of DMs

Figures 6.8 to 6.10 relate to the second group of DMs. Note

how these DMs tend to be environment-related. Remember
to identify the six separate subsections in the text for each
DM.

WPASME100609
46
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Figure 6.8 Erosion/corrosion

Figure 6.9 Corrosion under insulation (CUI)

WPASME100609
47
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

Figure 6.10 Soil corrosion

6.5

API 571 familiarization questions (set 2)

Q1. API 571 section 4.2.14

A damage mechanism that is strongly inuenced by uid velocity
and the corrosivity of the process uid is known as:
(a) Mechanical fatigue
&
(b) Erosioncorrosion
&
(c) Dewpoint corrosion
&
(d) Boiler condensate corrosion
&

Q2. API 571 section 4.3.2: atmospheric corrosion

As a practical rule, atmospheric corrosion:
(a) Only occurs under insulation
(b) May be localized or general (widespread)
(c) Is generally localized
(d) Is generally widespread

&
&
&
&

Q3. API 571 section 4.3.2.3: atmospheric corrosion:

critical factors
A typical atmospheric corrosion rate in mils (1 mil = 0.001 in)
per year (mpy) of steel in an inland location with moderate
precipitation and humidity is:
(a) 13 mpy
&
(b) 510 mpy
&
(c) 1020 mpy
&
(d) 50100 mpy
&

WPASME100609
48
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Q4. API 571 section 4.3.3.3: CUI critical factors

Which of these metal temperature ranges will result in the most
severe CUI?
(a) 051 8C
&
(b) 100121 8C
&
(c) 0 to 10 8C
&
(d) 250+ 8C
&

Q5. API 571 section 4.3.3.6: CUI appearance

Which other corrosion mechanism often accompanies CUI in
300 series stainless steels?
(a) HTHA
&
(b) Erosioncorrosion
&
(c) Dewpoint corrosion
&
(d) SCC
&

Q6. API 571 section 4.3.3.6: CUI prevention/mitigation

Which of these would signicantly reduce the risk of the
occurrence of CUI on a 316 stainless steel pipework system
tted with standard mineral wool lagging?
(a) Change the pipe material to a 304 stainless steel
&
(b) Change to a calcium silicate lagging material
&
(c) Shotblast the pipe surface and re-lag
&
(d) Change to low-chloride lagging material
&

Q7. API 571 section 4.3.9: soil corrosion

What is the main parameter measured to assess the corrosivity of
a soil?
(a) Acidity
&
(b) Alkalinity
&
(c) Density
&
(d) Resistivity
&

Q8. API 571 section 4.3.9.5: soil corrosion:

appearance
What would you expect the result of soil corrosion to look like?
(a) Branched and dagger-shaped cracks
&
(b) Isolated, large and deep individual pits
&
(c) Straight cracks
&
(d) External corrosion with wall thinning and pitting
&

WPASME100609
49
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

Q9. API 571 section 4.3.9.6: soil corrosion protection

Which of these would be used to reduce the amount of soil
corrosion?
(a) Caustic protection
&
(b) Cathodic protection
&
(c) Anodic protection
&
(d) More post-weld heat treatment
&

Q10. API 571 section 4.3.9.3: soil corrosion critical

factors
What effect does metal temperature have on the rate of soil
corrosion?
(a) None
&
(b) The corrosion rate increases with temperature
&
(c) The corrosion rate decreases with temperature
&
(d) There will be minimum soil corrosion below 0 8C
&

6.6

The third group of DMs

Now look through Figs 6.11 to 6.16 covering the nal group
of seven DMs. These DMs tend to be either more common at
higher temperatures or a little more specic to renery
equipment than those in the previous two groups.
Again, remember to identify the six separate subsections in
the text for each DM, trying to anticipate the type of
examination questions that could result from the content.

Figure 6.11 Oxygen pitting

WPASME100609
50
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Figure 6.12 Microbial-induced corrosion (MIC)

WPASME100609
51
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

Figure 6.13 Suldation corrosion

WPASME100609
52
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Figure 6.14 Stress corrosion cracking (SCC)

WPASME100609
53
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

Figure 6.15 Caustic embrittlement

Figure 6.16 High-temperature hydrogen attack (HTHA)

WPASME100609
54
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

6.7

API 571 familiarization questions (set 3)

Now try the nal set of API 571 self-test questions, covering
the third group of DMs.
Q1. API 571 section 4.3.5: boiler water condensate
corrosion
Which substance is the main cause of corrosion (common to
several corrosion mechanisms) in a boiler water condensate
system?
(a) Hydrogen
&
(b) Chlorine
&
(c) Hydrazine
&
(d) Oxygen
&

Q2. API 571 section 4.3.5.5: boiler water condensate

corrosion: appearance
What does CO2 corrosion of pipe internals look like?
(a) Smooth grooving of the pipe wall
(b) Blisters (tubercles) on the pipe wall
(c) Branched cracks in the pipe wall
(d) Cup-shaped pits and a slimy surface on the pipe wall

&
&
&
&

Q3. API 571 section 4.3.7: dew-point corrosion

Dew-point corrosion in ue gas systems in caused by:
(a) The presence of living organisms
(b) High temperatures
(c) Sulfur and chlorine compounds
(d) Ash, particulates and other non-combustibles

&
&
&
&

Q4. API 571 section 4.3.7.3: dew-point corrosion:

critical factors
Dew-point corrosion in a system where the ue gas contains SO2
and SO3 occurs at what metal temperatures?
(a) Below 138 8C
&
(b) Any temperature above 138 8C
&
(c) 138280 8C
&
(d) Only below 54 8C
&

WPASME100609
55
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

Quick Guide to API 570

Q5. API 571 section 4.3.8: microbiologically induced

corrosion (MIC)
What does MIC typically look like?
(a) Uniform wall thinning with a sparkling corroded
surface
(b) Localized pitting under deposits
(c) Smooth longitudinal grooving
(d) A dry aky appearance

&
&
&
&

Q6. API 571 section 4.4.2: suldation: critical factors

Suldation is the reaction of steels with sulfur compounds at
what temperatures?
(a) Any temperature
&
(b) 54260 8C
&
(c) Above 260 8C
&
(d) Above 380 8C
&

Q7. API 571 section 4.4.2.4: suldation: affected

equipment
Which of these items of equipment would be most likely to suffer
from suldation?
(a) Natural gas-red power boilers
&
(b) Residual oil-red boilers
&
(c) High-pressure compressed air systems
&
(d) Sea water cooling systems
&

Q8. API 571 section 4.4.2: suldation

Which curves document the effect of temperature on suldation
rates in steels?
(a) The NACE economy curves
&
(b) The McConomy curves
&
(c) The LarsenMiller curves
&
(d) The morphology curves
&

Q9. API 571 section 4.4.2: suldation

Which of these materials has the highest resistance to suldation?
(a) Low carbon steel
&
&
(b) 214 % Cr alloy steel
(c) 9 % Cr alloy steel
&
(d) 18/8 stainless steel
&

WPASME100609
56
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

API 571

Q10. API 571 section 4.5: environment-assisted

cracking
According to API, what are the two main types of environmentassisted cracking?
(a) Chloride SCC and CUI
&
(b) Chloride SCC and sulfur SCC
&
(c) Chloride SCC and hydrogen attack
&
(d) Chloride SCC and caustic embrittlement
&

WPASME100609
57
Downloaded From: http://ebooks.asmedigitalcollection.asme.org/ on 04/16/2015 Te

WPASME100609