ADOPTION NOTICE ASTM-A516/A516M, "PRESSURE VESSEL PLATES, CARBON STEEL, FOR MODERATE - AND LOWER - TEMPERATURE SERVICE", was adopted on 06-JUN-91 for use by the Department of Defense (DoD). Proposed changes by DoD activities must be submitted to the DoD Adopting Activity: Commander, Defense Supply Center Philadelphia, ATTN: DSCP-ILEA, 700 Robbins Avenue, Philadelphia, PA 19111-5096. Copies of this document may be purchased from the American Society for Testing and Materials 100 Barr Harbor Drive West Conshohocken, Pennsylvania, United States, 19428-2959. ____________________ http://www.astm.org/
Custodians: Army - MR Navy - SH DLA - IS
Adopting Activity: DLA - IS
Reviewer Activities: Navy - YD
FSC 9515 DISTRIBUTION STATEMENT A: Approved for public release; distribution is unlimited.
COPYRIGHT ASTM International
Licensed by Information Handling Services
Designation: A 516/A 516M 01
Used in USDOE-NE Standards
Standard Specification for
Pressure Vessel Plates, Carbon Steel, for Moderate- and
Lower-Temperature Service1 This standard is issued under the fixed designation A 516/A 516M; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval. This standard has been approved for use by agencies of the Department of Defense.
2. Referenced Documents 2.1 ASTM Standards: A 20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels3 A 435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates3 A 577/A577M Specification for Ultrasonic Angle-Beam Examination of Steel Plates3 A 578/A578M Specification for Straight-Beam Ultrasonic Examination of Plain and Clad Steel Plates for Special Applications3
1. Scope 1.1 This specification2 covers carbon steel plates intended primarily for service in welded pressure vessels where improved notch toughness is important. 1.2 Plates under this specification are available in four grades having different strength levels as follows: Grade U.S. [SI] 55 60 65 70
[380] [415] [450] [485]
Tensile Strength, ksi [MPa] 5575 6080 6585 7090
[380515] [415550] [450585] [485620]
3. General Requirements and Ordering Information
3.1 Material supplied to this material specification shall conform to Specification A 20/A 20M. These requirements outline the testing and retesting methods and procedures, permissible variations in dimensions, and mass, quality and repair of defects, marking, loading, etc. 3.2 Specification A 20/A20M also establishes the rules for the ordering information that should be complied with when purchasing material to this specification. 3.3 In addition to the basic requirements of this specification, certain supplementary requirements are available when additional control, testing, or examination is required to meet end use requirements. These include: 3.3.1 Vacuum treatment, 3.3.2 Additional or special tension testing, 3.3.3 Impact testing, and 3.3.4 Nondestructive examination. 3.4 The purchaser is referred to the listed supplementary requirements in this specification and to the detailed requirements in Specification A 20/A20M. 3.5 Coiled product is excluded from qualification to this specification until it is decoiled, leveled, and cut to length. Plate produced from coil means plate that has been cut to individual lengths from a coiled product and is furnished without heat treatment. The processor decoils, levels, cuts to length, and marks the product. Except as allowed by Section 6 in Specification A 20/A 20M, the processor is responsible for performing and certifying all tests, examinations, repairs,
1.3 The maximum thickness of plates is limited only by the
capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the maximum thickness of plates furnished under this specification as follows: Grade U.S. [SI] 55 60 65 70
[380] [415] [450] [485]
Maximum Thickness, in. [mm] 12 8 8 8
[305] [205] [205] [205]
1.4 For plates produced from coil, the additional requirements, including additional testing requirements and the reporting of additional test results of Specification A 20/A 20M apply. 1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee A01.11 on Steel Plates for Boilers and Pressure Vessels. Current edition approved Sept. 10, 2001. Published Sept. 2001. Originally published as A 516 64. Last previous edition A 516/A 516M 90 (2001). 2 For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-516/SA-516M in Section II of that Code.
Copyright ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959, United States.
1 COPYRIGHT ASTM International Licensed by Information Handling Services
Annual Book of ASTM Standards, Vol 01.04.
A 516/A 516M inspections, and operations not intended to affect the properties of the material. For plate produced from coils, the results of the tests performed shall be reported for each qualifying coil. See Note 1.
5.3 When notch-toughness tests are required on plates
112 in. [40 mm] and under in thickness, the plates shall be normalized unless otherwise specified by the purchaser. 5.4 If approved by the purchaser, cooling rates faster than those obtained by cooling in air are permissible for improvement of the toughness, provided the plates are subsequently tempered in the temperature range 1100 to 1300F [595 to 705C].
NOTE 1Additional requirements regarding plate produced from coil
are described in Specification A 20/A 20M.
3.6 If the requirements of this specification are in conflict
with the requirements of Specification A 20/A20M, the requirements of this specification shall prevail.
6. Chemical Requirements
4. Manufacture 4.1 Steelmaking PracticeThe steel shall be killed and shall conform to the fine austenitic grain size requirement of Specification A 20/A 20M.
6.1 The steel shall conform to the chemical requirements
shown in Table 1 unless otherwise modified in accordance with Supplementary Requirement S17, Vacuum Carbon-Deoxidized Steel, in Specification A 20/A20M.
5. Heat Treatment 5.1 Plates 1.50 in. [40 mm] and under in thickness are normally supplied in the as-rolled condition. The plates may be ordered normalized or stress relieved, or both. 5.2 Plates over 1.50 in. [40 mm] in thickness shall be normalized.
7. Mechanical Requirements 7.1 Tension Test RequirementsThe material as represented by the tension-test specimens shall conform to the requirements shown in Table 2.
TABLE 1 Chemical Requirements
Elements
Carbon, maxA: 1 / 2 in. [12.5 mm] and under Over 1 / 2 in. to 2 in. [12.5 to 50 mm], incl Over 2 in. to 4 in. [50 to 100 mm], incl Over 4 to 8 in. [100 to 200 mm], incl Over 8 in. [200 mm] Manganese: 1 / 2 in. [12.5 mm] and under: Heat analysisB Product analysisB Over 1 / 2 in. [12.5 mm]: Heat analysis Product analysis Phosphorus,maxA Sulfur, maxA Silicon: Heat analysis Product analysis A B
Composition, % Grade 55 [Grade 380]
Grade 60 [Grade 415]
Grade 65 [Grade 450]
Grade 70 [Grade 485]
0.18 0.20 0.22 0.24 0.26
0.21 0.23 0.25 0.27 0.27
0.24 0.26 0.28 0.29 0.29
0.27 0.28 0.30 0.31 0.31
0.600.90 0.550.98
0.600.90 0.550.98
0.851.20 0.791.30
0.851.20 0.791.30
0.601.20 0.551.30 0.035 0.035
0.851.20 0.791.30 0.035 0.035
0.851.20 0.791.30 0.035 0.035
0.851.20 0.791.30 0.035 0.035
0.150.40 0.130.45
0.150.40 0.130.45
0.150.40 0.130.45
0.150.40 0.130.45
Applies to both heat and product analyses.
Grade 60 plates 1 / 2 in. [12.5 mm] and under in thickness may have 0.851.20 % manganese on heat analysis, and 0.791.30 % manganese on product analysis.
2 COPYRIGHT ASTM International Licensed by Information Handling Services
A 516/A 516M TABLE 2 Tensile Requirements Grade
Tensile strength, ksi [MPa]
Yield strength, min,A ksi [MPa] Elongation in 8 in. [200 mm], min, %B Elongation in 2 in. [50 mm], min, %B A B
55 [380]
60 [415]
65 [450]
70 [485]
5575 [380515] 30 [205] 23 27
6080 [415550] 32 [220] 21 25
6585 [450585] 35 [240] 19 23
7090 [485620] 38 [260] 17 21
Determined by either the 0.2 % offset method or the 0.5 % extension-under-load method. See Specification A 20/A20M for elongation adjustment.
SUPPLEMENTARY REQUIREMENTS Supplementary requirements shall not apply unless specified in the order. A list of standardized supplementary requirements for use at the option of the purchaser are included in ASTM Specification A 20/A 20M. Several of those considered suitable for use with this specification are listed below by title. Other tests may be performed by agreement between the supplier and the purchaser. S8. Ultrasonic Examination in accordance with Specification A 435/A 435M, S9. Magnetic Particle Examination, S11. Ultrasonic Examination in accordance with Specification A 577/A 577M, S12. Ultrasonic Examination in accordance with Specification A 578/A 578M, S14. Bend Test, and S17. Vacuum Carbon-Deoxidized Steel.
S1. Vacuum Treatment,
S2. Product Analysis, S3. Simulated Post-Weld Heat Treatment of Mechanical Test Coupons, S4.1 Additional Tension Test, S5. Charpy V-Notch Impact Test, S6. Drop Weight Test, S7. High-Temperature Tension Test,
The American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM Headquarters. Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below. This standard is copyrighted by ASTM, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above address or at 610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website (www.astm.org).