Product Data
Description:
Recommended use:
Service temperature:
Certificates/Approvals:
Availability:
HEMPADUR 15130 is a two-component, polyamide cured coal tar epoxy which provides a very
hardwearing coating, highly resistant to seawater and mineral oils. Limited resistance to a number of
solvents. Aliphatic hydrocarbons may be discoloured.
As a self-priming coating system for long-term protection of steel and concrete in severely corrosive
environment. It provides excellent protection as a lining in crude and fuel oil tanks.
If the exposure is acidic or a temperature gradient is developed, it is recommended to use
HEMPADUR 15100. For application at lower temperatures, ie in the interval from - 10C/14F to
+10C/50F, it is recommended to use HEMPADUR LTC 15030.
Maximum, dry exposure only: 90C/194F
Ballast water service. Resists normal ambient temperatures at sea (Avoid long-term exposure to
negative temperature gradients).
Other water service: 45C/113F. (no temperature gradient)
Other liquids: Contact HEMPEL
Not included in Group Assortment. Availability subject to special agreement.
HEMPADUR 15130
15130: BASE 15139: CURING AGENT 95140
Accepted as a corrosion control coating by Maritime Register of Shipping, Russia. Approved by
Bureau Veritas as a corrosion control coating. Approved by Lloyd's Register of Shipping as a corrosion
control coating.
Approved as a ballast tank coating by Germanischer Lloyd, Germany.
Product Data
PHYSICAL CONSTANTS:
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas.
Shade nos/Colours:
Finish:
Volume solids, %:
Theoretical spreading rate:
VOC content:
Fully cured:
Dry to touch:
Specific gravity:
Flash point:
-
19990*/ Black.
Semi-gloss
70 1
5.6 m
2
/l [224.6 sq.ft./US gallon] to 125 micron/5 mils
7 to 8 approx. hour(s) 20C/68F
7 day(s) , 20C/68F
-
*other shades according to assortment list.
25 C [77 F]
1.3 kg/litre [10.7 lbs/US gallon]
299 g/l [2.5 lbs/US gallon]
Surface dry: 6 approx. hour(s) 20C/68F
Shelf life: 1 year (25C/77F) from time of production. Depending on storage conditions, mechanical stirring may
be necessary before usage.
APPLICATION DETAILS:
Version, mixed product:
Mixing ratio:
Application method:
Thinner (max.vol.):
15130
4:1 by volume
Airless spray / Brush (touch up)
08450 (5%) / 08450 (5%)
Nozzle orifice: 0.023 "
Nozzle pressure: 200 bar [2900 psi]
(Airless spray data are indicative and subject to adjustment)
Indicated film thickness, dry: 125 micron [5 mils] see REMARKS overleaf
Indicated film thickness, wet: 175 micron [7 mils]
Overcoat interval, min: see REMARKS overleaf
Overcoat interval, max: see REMARKS overleaf
BASE 15139: CURING AGENT 95140
2 approx. hour(s) 20C/68F Pot life (Airless spray):
6 approx. hour(s) 20C/68F Pot life (Brush):
Safety: Handle with care. Before and during use, observe all safety labels on packaging and paint containers,
consult HEMPEL Safety Data Sheets and follow all local or national safety regulations.
HEMPEL'S TOOL CLEANER 99610 Cleaning of tools:
Not available.
Page: 1/3
-
Product Data Sheet
Date of issue: October 2014
HEMPADUR 15130
SURFACE PREPARATION: New steel: Abrasive blasting to Sa 2 (ISO 8501-1:2007) is recommended. For temporary protection, if
required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and
fabrication should be thoroughly cleaned prior to final painting. For repair and touch-up use:
HEMPADUR 15130.
Concrete: Remove slip agent and other possible contaminants by emulsion washing followed by high
pressure hosing with fresh water. Remove scum layer and loose matter to a hard, rough and uniform
surface, preferably by abrasive blasting, possibly by other mechanical treatment or acid etching. Seal
surface with suitable sealer, as per relevant painting specification.
Repair and maintenance: Remove oil and grease etc. thoroughly with suitable detergent. Remove
salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly
by power tool cleaning (minor areas) or by abrasive blasting. As an alternative to dry cleaning, water
jetting to sound, well adhering coat and/or to steel. Intact coat must appear with roughened surface
after the water jetting. By water jetting to steel, cleanliness shall be: (minimum) WJ-2 Acceptable flash-
rust degree before application: FR-2, preferably FR-1. Feather edges to sound and intact areas. Dust
off residues. Touch up to full film thickness.
APPLICATION CONDITIONS: Use only where application and drying can proceed at temperatures above: 5C/41F. The
temperature of paint itself should be 15C/59F or above. Apply only on a dry and clean surface with a
temperature above the dew point to avoid condensation. In confined spaces provide adequate
ventilation during application and drying.
SUBSEQUENT COAT: None, or as per specification.
REMARKS:
Weathering/service temperatures: The natural tendency of epoxy coatings to chalk in outdoor exposure and to become more sensitive to
mechanical damage and chemical exposure at elevated temperatures is also reflected in this product.
Film thicknesses/thinning: May be specified in another film thickness than indicated depending on purpose and area of use. This
will alter spreading rate and may influence drying time and overcoating interval. Normal range dry is:
125-200 micron/5-8 mils
HEMPADUR 15130 Bleeding may occur into subsequent coat. This effect is cosmetic only and
has no influence on the protective properties.
For professional use only.
Note:
Overcoating: Overcoating intervals related to later conditions of exposure: If the maximum overcoating interval is
exceeded, roughening of the surface is necessary to ensure intercoat adhesion.
Before overcoating after exposure in contaminated environment, clean the surface thoroughly with
high pressure fresh water hosing and allow drying.
A specification supersedes any guideline overcoat intervals indicated in the table.
X Move PDS Disclaimer to Second page
The maximum overcoating intervals between layers of the product can be doubled on the condition
that the coating has not been exposed to sunlight, to water/condensation, or to (other) contamination
before overcoating. Furthermore the surface of the first layer of the product must be free of any
exudations. This is secured by keeping the conditions of application,
drying and curing, i.e. such as ventilation, temperature, film thickness and thinning within the above
described limits. Note that excessive temperatures also must be avoided. If the maximum overcoating
interval is exceeded, roughening of the surface is necessary to ensure intercoat adhesion.
Overcoating intervals:
ISSUED BY: HEMPEL A/S
1513019990
Environment Immersion
HEMPADUR 14 h 4 d 6 h 48 h 4 h 32 h
HEMPADUR 14 h 4 d 6 h 48 h 4 h 32 h
HEMPATEX 14 h 36 h 16 h 6 h 11 h 4 h
Environment
Min Max Min Max Min Max
Atmospheric, medium
HEMPATEX 14 h 36 h 16 h 6 h 11 h 4 h
10C (50F) 20C (68F) 30C (86F)
NR = Not Recommended, Ext. = Extended, m = minute(s), h = hour(s), d = day(s)
Surface temperature:
Page: 2/3
-
Product Data Sheet
Date of issue: October 2014
HEMPADUR 15130
This Product Data Sheet supersedes those previously issued.
For explanations, definitions and scope, see Explanatory Notes available on www.hempel.com. Data, specifications, directions and recommendations
given in this data sheet represent only test results or experience obtained under controlled or specially defined circumstances. Their accuracy,
completeness or appropriateness under the actual conditions of any intended use of the Products herein must be determined exclusively by the Buyer
and/or User.
The Products are supplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unless
otherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, any liability, including but
not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct or consequential losses or damages arising
from the use of the Products as recommended above, on the overleaf or otherwise. Product data are subject to change without notice and become void
five years from the date of issue.
Page: 3/3
-
Product Data Sheet
Date of issue: October 2014