The Bessemer process was the first inexpensive industrial process for the mass-production of steel from molten pig
iron. The process is named after its inventor, Henry Bessemer, who took out a patent on the process in 1855. The key
principle is removal of impurities from the iron by oxidation with air being blown through the molten iron. The oxidation
also raises the temperature of the iron mass and keeps it molten.
The process is carried on in a large ovoid steel container lined with clay or dolomite called the Bessemer converter.
The capacity of a converter was from 8 to 30 tons of molten iron with a usual charge being around 15 tons. At the top
of the converter is an opening, usually tilted to the side relative to the body of the vessel, through which the iron is
introduced and the finished product removed. The bottom is perforated with a number of channels called tuyres
through which air is forced into the converter. The converter is pivoted on trunnions so that it can be rotated to receive
the charge, turned upright during conversion, and then rotated again for pouring out the molten steel at the end.

Oxidation
The oxidation process removes impurities
such as silicon, manganese, and carbon as
oxides. These oxides either escape as gas or
form a solid slag. The refractory lining of the
converter also plays a role in the
conversionthe clay lining is used in the acid
Bessemer, in which there is low phosphorus
in the raw material. Dolomite is used when
the phosphorus content is high in the basic
Bessemer (limestone or magnesite linings are
also sometimes used instead of dolomite).
In order to give the steel the desired
properties, other substances could be added
to the molten steel when conversion was
complete, such as spiegeleisen (an iron-
carbon-manganese alloy).

Managing the process
When the required steel had been formed, it was poured out into ladles and then transferred into moulds and the lighter
slag is left behind. The conversion process called the "blow" was completed in around twenty minutes. During this
period the progress of the oxidation of the impurities was judged by the appearance of the flame issuing from the
mouth of the converter.
After the blow, the liquid metal was recarburized to the desired point and other alloying materials are added, depending
on the desired product.
Before the Bessemer process, Britain had no practical method of reducing the carbon content of pig iron. Steel was
manufactured by the reverse process of adding carbon to carbon-free wrought iron, usually imported from Sweden.
The manufacturing process, called cementation process, consisted of heating bars of wrought iron together with
charcoal for periods of up to a week in a long stone box. This produced blister steel. Up to 3 tons of expensive coke
was burnt for each ton of steel produced. Such steel when rolled into bars was sold at 50 to 60 a long ton. The most
difficult and work-intensive part of the process, however, was the production of wrought iron done in finery forges in
Sweden.

This process was refined in the 1700s with the introduction of Benjamin Huntsman's crucible steel-making technique,
which added an additional three hours firing time and required additional large quantities of coke. In making crucible
The Bessemer process
- 2 -
steel the blister steel bars were broken into pieces and melted in small crucibles each containing 20 kg or so. This
produced higher quality crucible steel but increased the cost. The Bessemer process reduced to about half an hour the
time needed to make steel of this quality while requiring only the coke needed to melt the pig iron initially. The earliest
Bessemer converters produced steel for 7 a long ton, although it initially sold for around 40 a ton.

Sir Henry Bessemer described the origin of his invention in his autobiography. According to this book at the time of the
outbreak of the Crimean War many English industrialists and inventors became interested in military technology and
Bessemer himself developed a method for grooving artillery projectiles so that they could spin without the use of rifling
in the bore of the gun. He patented this method in 1854 and began developing it in conjunction with the government of
France. After a successful day of testing of his method at the Polygon in France he had a conversation with Claude-
Etienne Mini who stated that a key barrier to the use of the larger, heavier spinning projectiles would be the strength
of the gun and in particular "... he [Mini] did not consider it safe in practice to fire a 30-lb. shot from a 12-pounder cast-
iron gun. The real question, he said, was; Could any guns be made to stand such heavy projectiles?". This is what
started Bessemer thinking about steel.
At the time steel was difficult and expensive to make and was consequently used in only small items like cutlery and
tools. Starting in January 1855 he began working on a way to produce steel in the massive quantities required for
artillery and by October he filed his first patent related to the Bessemer process.
Bessemer first started working with an ordinary reverbatory furnace but during a test a couple of pig ingots got off to
the side of ladle and were sitting above it in the hot air of the furnace. When Bessemer went to push them into the ladle
he found that they were steel shells: the hot air alone had converted the outer parts of the ingots to steel. This crucial
discovery led him to completely redesign his furnace so that it would force high-pressure air through the molten iron
using special air pumps. Intuitively this would seem to be folly because it would cool the iron, but due to exothermic
oxidation both the silicon and carbon react with the excess oxygen leaving the surrounding molten iron even hotter,
facilitating the conversion to steel.

Bessemer licenced the patent for his process to five ironmasters, for a total of 27,000, but the licences failed to
produce the quality of steel he had promised and he later bought them back for 32,500. He realised the problem was
due to impurities in the iron and concluded that the solution lay in knowing when to turn off the flow of air in his
process; so that the impurities had been burnt off, but just the right amount of carbon remained. However, despite
spending tens of thousands of pounds on experiments, he could not find the answer

The simple, but elegant, solution was first discovered by
English metallurgist Robert Forester Mushet, who had
carried out thousands of scientifically valid experiments in
the Forest of Dean. His method was to first burn off, as far
as possible, all the impurities and carbon, then reintroduce
carbon and manganese by adding an exact amount of
spiegeleisen. This had the effect of improving the quality of
the finished product, increasing its malleability - its ability to
withstand rolling and forging at high temperatures and
making it more suitable for a vast array of uses.

The Dowlais Iron Company was the first licensee of the
Bessemer process, constructing the worlds most powerful
rolling mill in 1857, and producing its first Bessemer steel in
1865.

The Bessemer process revolutionized steel manufacture by
decreasing its cost, from 40 per long ton to 6-7 per long
ton during its introduction, along with greatly increasing the
scale and speed of production of this vital raw material. The
process also decreased the labour requirements for steel-
making.
Prior to its introduction, steel was far too expensive to make
bridges or the framework for buildings and thus wrought iron
had been used throughout the Industrial Revolution. After
the introduction of the Bessemer process, steel and wrought
iron became similarly priced, and most manufacturers turned
to steel. The availability of cheap steel allowed large bridges
to be built and enabled the construction of railways,
skyscrapers, and large ships.


Workington No 1 Bessemer Converter at Kelham Island Industrial Museum in Sheffield




- 3 -
Other important steel products were steel cable, steel rod and sheet steel which enabled large, high-pressure boilers
and high-tensile strength steel for machinery which enabled much more powerful engines, gears and axles than were
possible previously. With large amounts of steel it became possible to build much more powerful guns and carriages,
tanks, armored fighting vehicles and naval ships. Industrial steel also made possible the building of giant turbines and
generators thus making the harnessing of water and steam power possible. The introduction of the large scale steel
production process perfected by the Englishman Henry Bessemer paved the way to mass industrialisation as observed
in the 19th-20th centuries.

Obsolescence
Commercial steel production using this method stopped in Workington in 1974. It was replaced by processes such as
the basic oxygen (Linz-Donawitz) process, which offered better control of final chemistry.
The Bessemer process was so fast (1020 minutes for a heat) that it allowed little time for chemical analysis or
adjustment of the alloying elements in the steel. Bessemer converters did not remove phosphorus efficiently from the
molten steel; as low-phosphorus ores became more expensive, conversion costs increased. The process permitted
only limited amount of scrap steel to be charged, further increasing costs, especially when scrap was inexpensive. Use
of electric arc furnace technology competed favourably with the Bessemer process resulting in its obsolescence.

A slag ladel outside Workington Steel Works in 1986.
Up until the 1960s slag from blast furnaces was taken to the shore and dumped into the sea. Photo: Alan Banks