Tensile Testing
Tensile Testing
Tests are performed as per the ASTM, ISIRI, BS, DIN and EN Standards. A tensile test measures the resistance of a material to a static or slowly applied force. A machined specimen is placed in the testing machine and load is applied. A strain gage or extensometer is used to measure elongation. The stress obtained at the highest applied force is the Tensile Strength. The Yield Strength is the stress at which a prescribed amount of plastic deformation (commonly 0.2%) is produced. Elongation describes the extent to which the specimen stretched before fracture. Information concerning the strength, stiffness, and ductility of a material can be obtained from a tensile test. Variations of the tensile testing include; Room Temperature, Low Temperature, Elevated Temperature (ASTM E21), Shear, Temperature and Humidity, Combined Tension and Compression, Through Thickness, True Strain, Notched Tensile, and r (ASTM E646) & n (ASTM E517) values.
http://me.aut.ac.ir/staff/solidmechanics/alizadeh/Tensile%20Testing.htm
1/9
1/23/2014
Tensile Testing
Principle
The tensile test consists of subjecting a test piece to a continually increasing tensile strain, generally to fracture, for the purpose of determining one or more of the following tensile properties ( figs. 1 and 2): Tensile strength, proof strength, upper and lower yield strength, elongation and percentage reduction of area.
2/9
1/23/2014
Tensile Testing
3/9
1/23/2014
Tensile Testing
Fig.1: Typical stress/extension diagram for a ductile metallic material not exhibiting yield phenomenon
Fig.2: Typical stress/extension diagram for a ductile metallic material exhibiting yield phenomenon
Tensile Properties
Tensile properties indicate how the material will react to forces being
http://me.aut.ac.ir/staff/solidmechanics/alizadeh/Tensile%20Testing.htm 4/9
1/23/2014
Tensile Testing
applied in tension. A tensile test is a fundamental mechanical test where a carefully prepared specimen is loaded in a very controlled manner while measuring the applied load and the elongation of the specimen over some distance. Tensile tests are used to determine the modulus of elasticity, elastic limit, elongation, proportional limit, and reduction in area, tensile strength, yield point, yield strength and other tensile properties. The main product of a tensile test is a load versus elongation curve which is then converted into a stress versus strain curve. Since both the engineering stress and the engineering strain are obtained by dividing the load and elongation by constant values (specimen geometry information), the load-elongation curve will have the same shape as the engineering stress-strain curve. The stress-strain curve relates the applied stress to the resulting strain and each material has its own unique stress-strain curve. A typical engineering stress-strain curve is shown below. If the true stress, based on the actual crosssectional area of the specimen, is used, it is found that the stressstrain curve increases continuously up to fracture.
Yield Point In ductile materials, at some point, the stress-strain curve deviates from the straight-line relationship and Law no longer applies as the
1/23/2014
Tensile Testing
strain increases faster than the stress. From this point on in the tensile test, some permanent deformation occurs in the specimen and the material is said to react plastically to any further increase in load or stress. The material will not return to its original, unstressed condition when the load is removed. In brittle materials, little or no plastic deformation occurs and the material fractures near the end of the linear-elastic portion of the curve. With most materials there is a gradual transition from elastic to plastic behavior, and the exact point at which plastic deformation begins to occur is hard to determine. Therefore, various criteria for the initiation of yielding are used depending on the sensitivity of the strain measurements and the intended use of the data. (See Table) For most engineering design and specification applications, the yield strength is used. The yield strength is defined as the stress required producing a small, amount of plastic deformation. The offset yield strength is the stress corresponding to the intersection of the stressstrain curve and a line parallel to the elastic part of the curve offset by a specified strain (in the US the offset is typically 0.2% for metals and 2% for plastics). To determine the yield strength using this offset, the point is found on the strain axis (x-axis) of 0.002, and then a line parallel to the stress-strain line is drawn. This line will intersect the stress-strain line slightly after it begins to curve, and that intersection is defined as the yield strength with a 0.2% offset. A good way of looking at offset yield strength is that after a specimen has been loaded to its 0.2 percent offset yield strength and then unloaded it will be 0.2 percent longer than before the test. Even though the yield strength is meant to represent the exact point at which the material becomes permanently deformed, 0.2% elongation is considered to be a tolerable amount of sacrifice for the ease it creates in defining the yield strength. Some materials such as gray cast iron or soft copper exhibit essentially no linear-elastic behavior. For these materials the usual practice is to define the yield strength as the stress required to produce some total amount of strain. True elastic limit is a very low value and is related to the motion of a few hundred dislocations. Micro strain measurements are required to detect strain on order of 2 x 10 -6 in/in. Proportional limit is the highest stress at which stress is
1/23/2014
Tensile Testing
directly proportional to strain. It is obtained by observing the deviation from the straight-line portion of the stress-strain curve. Elastic limit is the greatest stress the material can withstand without any measurable permanent strain remaining on the complete release of load. It is determined using a tedious incremental loading-unloading test procedure. With the sensitivity of strain measurements usually employed in engineering studies (10 -4in/in), the elastic limit is greater than the proportional limit. With increasing sensitivity of strain measurement, the value of the elastic limit decreases until it eventually equals the true elastic limit determined from micro strain measurements. Yield strength is the stress required to produce a smallspecified amount of plastic deformation. The yield strength obtained by an offset method is commonly used for engineering purposes because it avoids the practical difficulties of measuring the elastic limit or proportional limit. Ultimate Tensile Strength The ultimate tensile strength (UTS) or, more simply, the tensile strength, is the maximum engineering stress level reached in a tension test. The strength of a material is its ability to withstand external forces without breaking. In brittle materials, the UTS will at the end of the linear-elastic portion of the stress-strain curve or close to the elastic limit. In ductile materials, the UTS will be well outside of the elastic portion into the plastic portion of the stress-strain curve. On the stress-strain curve above, the UTS is the highest point where the line is momentarily flat. Since the UTS is based on the engineering stress, it is often not the same as the breaking strength. In ductile materials strain hardening occurs and the stress will continue to increase until fracture occurs, but the engineering stressstrain curve may show a decline in the stress level before fracture occurs. This is the result of engineering stress being based on the original cross-section area and not accounting for the necking that commonly occurs in the test specimen. The UTS may not be completely representative of the highest level of stress that a material can support, but the value is not typically used in the design of components anyway. For ductile metals the current design practice is to use the yield strength for sizing static components. However, since
1/23/2014
Tensile Testing
the UTS is easy to determine and quite reproducible, it is useful for the purposes of specifying a material and for quality control purposes. On the other hand, for brittle materials the design of a component may be based on the tensile strength of the material. Measures of Ductility (Elongation and Reduction of Area) The ductility of a material is a measure of the extent to which a material will deform before fracture. The amount of ductility is an important factor when considering forming operations such as rolling and extrusion. It also provides an indication of how visible overload damage to a component might become before the component fractures. Ductility is also used a quality control measure to assess the level of impurities and proper processing of a material. The conventional measures of ductility are the engineering strain at fracture (usually called the elongation) and the reduction of area at fracture. Both of these properties are obtained by fitting the specimen back together after fracture and measuring the change in length and cross-sectional area. Elongation is the change in axial length divided by the original length of the specimen or portion of the specimen. It is expressed as a percentage. Because an appreciable fraction of the plastic deformation will be concentrated in the necked region of the tensile specimen, the value of elongation will depend on the gage length over which the measurement is taken. The smaller the gage length the greater the large localized strain in the necked region will factor into the calculation. Therefore, when reporting values of elongation, the gage length should be given. One way to avoid the complication from necking is to base the elongation measurement on the uniform strain out to the point at which necking begins. This works well at times but some engineering stress-strain curve are often quite flat in the vicinity of maximum loading and it is difficult to precisely establish the strain when necking starts to occur. Reduction of area is the change in cross-sectional area divided by the original cross-sectional area. This change is measured in the necked down region of the specimen. Like elongation, it is usually expressed
1/23/2014
Tensile Testing
as a percentage.
STANDARDS
ASTM A370 ASTM E8 DIN EN 10002-1 DIN EN 10002-2 DIN EN 10002-5 ISO 783 ISO 6892 ISO 15579
9/9

Tensile Testing

Uploaded by

Copyright:

Available Formats

Tensile Testing

Uploaded by

Document Information

Original Description:

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Tensile Testing

Uploaded by

Copyright:

Available Formats

1/23/2014

You might also like