Nitocote NT550

Nitocote NT550
Flexible protecting coating, based on a hybrid resin system

Uses Provides chemical and abrasion resistance to prevent corrosion of concrete surfaces for applications such as : Wall and floor coating for concrete protection Manhole and pipe linings Secondary containments Lining for sewage and effluent plants Sea water tanks, channels and intakes Foundation waterproofing Reservoirs, water treatment plants Advantages Flexible - Can bridge 0.2mm cracks Environment friendly - Totally free of carcinogenic materials like coal tar, pitch and aromatic hydrocarbons. Cost saving - primerless system, easy brush roller or spray application. Added value system - acts as an impermeable waterproof coating and excellent resistance to underground environment Description Nitocote NT550 is based on graft polymerisation of epoxy resins. It is supplied as a two pack material in pre-weighed quantities ready for on-site mixing and use. Nitocote NT550 is applied as a two coat application. It is generally applied at a wet film thickness of 200 micron per coat. Nitocote NT550 is available in a standard Grey colour, other colours are available subject to minimum order quantities. Specification The corrosion resistant coating shall be Nitocote NT550, a tar-free, a flexible epoxy resin coating. It shall posess excellent bond to the concrete substrate. The coating shall be resistant to underground conditions, alkalis, salt solutions and acidic solutions. Full cure (ASTM D1640) Adhesion Strength (ASTM D4541) Water Absorption (ASTM C570) Tensile Strength (BS2782) Elongation at break (BS2782) Chemical resistance : Min.Overcoating time (ASTM D1640) Properties Solids content (ASTM D1644) Specific gravity (ASTM D1475) Pot life (ASTM D2471) at 23oC at 35oC Tack free time (ASTM D1640)
constructive solutions
92% 1.35 g/cm2 at 23oC
4 hours 2 hours 6-8 hours @ 23oC 2-4 hours @ 35oC 1-2 hours @ 45oC 8 hours @ 23oC 4 hours @ 35oC 2 hours @ 45oC 7 days at 23oC 4 days @ 35oC 1.5 N/mm2 0.2% 5N/mm 2 30-35%
Tests were carried out in accordance with ASTM D1308, at room temperature of 23o C and speciments were soaked in the solution for a period of 7 days. Acids (m/v) Hydrochloric acid 10% Sulphuric acid 25% Nitric acid 10% Phosphoric acid 15% Aqueous solutions Tap water Sea water Ground water Sewage : Resistant : Resistant : Resistant : Resistant : Resistant : Resistant : Resistant : Resistant
Nitocote NT550
Consult the local Fosroc office for specific recommendations to meet each operating condition.
page 1 of 4
Nitocote NT550
Instructions for use

Preparation All surface to be treated with Nitocote NT550 must be clean and free from dust or loose material. Concrete surfaces All laitance must be removed by grit blasting or other suitable removal methods. Following the preparation of a concrete surface, care should be taken to ensure that any surface irregularities are filled with Nitomortar FC* or Nitomortar FC(B)*. Metal surfaces All metal surfaces should be coated immediately after preparation. If this is not possible and to eliminate formation of rust, prime the metal surfaces using Nitoprime 25*. Mixing The contents of the resin can should be thoroughly stirred to disperse any possible settlement. The entire contents of both the hardener and resin cans should be poured into a suitable sized mixing vessel. It is recommended that the two components are mixed together mechanically using a slow speed electric drill fitted with a Fosroc Mixing Paddle (MR3). Mixing should be carried out continuously for 3 to 4 minutes, until a uniform consistency is achieved. Although Nitocote NT550 is a non-solvented product, it is still recommended that mixing should take place in an open, well ventilated area. Application A minimum 2 coat application is generally recommended to ensure a full, unbroken coating is achieved. Brush/Roller application Once mixed, the material should be immediately applied. ensuring that a continuous coating is obtained. The first coat is applied to achieve a uniform coating with a wet film thickness not less than 200 microns, and should be allowed to dry for at least 2 hours at 35 oC before the application of the second coat. The second coat should be applied after 4 hours (at 35 o C) from the application of the first coat. The second coat should be applied as above again achieving a wet film thickness not less than 200 microns.
Spray application Where large areas are to be coated, it is advisable to consider spray application. Consult the local Fosroc office for further details and recommendations. Cleaning Tools and equipment should be cleaned with Fosroc Solvent 102* immediately after use. Hot weather working practices W hilst the performance properties of Nitocote NT550 at elevated temperatures are assured, application under such conditions can sometimes be difficult. It is therefore suggested that, for temperatures above 35oC, the following guidelines are adopted as a prudent working regime : (i) Store unmixed materials in a cool (preferably temperature controlled) environment, avoiding exposure to direct sunlight. (ii) Keep mixing and placing equipment cool, arranging shade protection if necessary. It is especially important to keep cool those surfaces of the equipment which will come into direct contact with the material itself. (iii) Try to eliminate application in the middle of the day, and certainly avoid application in direct sunlight. (iv) For hand application, ensure that there are sufficient operatives available to complete application within the potlife of the material (v) Have a ready supply of Fosroc Solvent 102 available for immediate cleaning of tools after use. Repairing and overcoating Any applications of Nitocote NT550 which have become damaged can be readily overcoated. The existing surface should be well abraded, using a stiff wire brush, or similar, to ensure that a good mechanical bond will be achieved between the two layers. Any loose material should be removed. Overcoating works can then proceed as for new work, always ensuring that the prepared substrate is free from any moisture
page 2 of 4
Nitocote NT550
Limitations Nitocote NT550 is formulated for application to clean sound substrates of steel or concrete; and where it can be protected from contact with water for the first 24 hours after application as discolouration could occur. Nitocote NT550 should not be applied over other existing coatings, but can be applied on top of itself (see above). For cold weather working (down to 5oC), it is recommended that materials are stored in a heated building and only removed immediately before use. Accelerated heating methods are not to be utilised under any circumstances.
Estimating Supply Nitocote NT550 Nitoprime 25 Fosroc Solvent 102 : 10 litre packs : 1 and 4 litre packs : 5 litre packs
Coverage Nitocote NT550 : 5.0 m2/litre @ 200 microns wft (per coat) : 5.0 m2/litre
Technical support Fosroc offers a comprehensive technical support service to specifiers, end users and contractors. It is also able to offer on-site technical assistance, an AutoCAD facility and dedicated specifiction assistance in locations all over the world
Nitoprime 25 Note :
Coverage figures quoted are theoretical, and based upon application to a properly prepared substrate of nominal C30 concrete. Since application conditions vary greatly due to substrate porosity, quality of surface preparation, application thickness and wastage factors, the onsite figures may vary from those shown above.
Storage Nitocote NT550 supplied in 10 litre packs have a shelf life of 12 months, when stored in warehouse conditions below 35oC
page 3 of 4
Nitocote NT550
Fosroc Chemicals (India) Pvt. Ltd.

Head Office Sapthagiri Palace, No.38, II & III Floor, 12th Cross, CBI Road, Ganganagar North, Bangalore 560 032
Important note : Fosroc products are guaranteed against defective materials and manufacture and are sold subject to its standard terms and conditions of sale, copies of which may be obtained on request. Whilst Fosroc endeavours to ensure that any advice, recommendation specification or information it may give is accurate and correct, it cannot, because it has no direct or continuous control over where or how its products are applied, accept any liability either directly or indirectly arising from the use of its products whether or not in accordance with any advice, specification, recommendation or information given by it.
telephone ++91 80-23551500 fax ++91 80-23551510 e-mail [email protected]
Regional Offices
Bangalore
Sapthagiri Palace, No. 38 II & III Floor, 12th Cross, CBI Road, Ganganagar North, Bangalore 560 032. Ph:080-23551500 Fax : 080-23551510
Mumbai
1401/1402, 14 Floor, A-WingThe Great Eastern Summit Sector-15, CBD, Belapur Navi Mumbai 400 614 Ph: 022 -43406800-04
Noida
D-166 Sector 10 Noida, UP 201 301 Ph:0120-4270620
Kolkata
304, Jodhpur Park Kolkata 700 068 Ph:033-65343188 Fax: 033-2499-0280
www.fosroc.com
page 4 of 4
INDIA/2011/0808/A

Nitocote NT550

Uploaded by

Copyright:

Available Formats

Nitocote NT550

Uploaded by

Document Information

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Nitocote NT550

Uploaded by

Copyright:

Available Formats

Nitocote NT550

Flexible protecting coating, based on a hybrid resin system

92% 1.35 g/cm2 at 23oC

Instructions for use

Fosroc Chemicals (India) Pvt. Ltd.

You might also like