Designation: B775 08

Standard Specication for

General Requirements for Nickel and Nickel Alloy Welded Pipe1

This standard is issued under the xed designation B775; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.

1. Scope 1.1 This specication contains various requirements that, with the exception of Section 5 and Section 10, are mandatory requirements to the following ASTM nickel and nickel alloy, longitudinally welded piping specications:2
Title of Specication Welded UNS N08020, N08024, and N08026 Alloy Pipe Welded Nickel-Iron-Chromium Alloy Pipe Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS N06603, UNS N06025 and UNS N06045) Pipe Welded Nickel and Nickel-Cobalt Alloy Pipe UNS N08904, UNS N08925, and UNS N08926 Welded Pipe UNS N08367 Welded Pipe Nickel-Alloy (UNS N06625, N06219, and N08825) Welded Pipe Ni-Cr-Mo-Co-W-Fe-Si Alloy (UNS N06333) Welded Pipe Welded Nickel (UNS N02200/UNS N02201) and Nickel Copper Alloy (UNS N04400) Pipe ASTM Designation2 B464 B514 B517 B619 B673 B675 B705 B723 B725

Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use. 2. Referenced Documents 2.1 ASTM Standards:2 B464 Specication for Welded UNS N08020 Alloy Pipe B514 Specication for Welded Nickel-Iron-Chromium Alloy Pipe B517 Specication for Welded Nickel-Chromium-IronAlloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Pipe B619 Specication for Welded Nickel and Nickel-Cobalt Alloy Pipe B673 Specication for UNS N08925, UNS N08354, and UNS N08926 Welded Pipe B675 Specication for UNS N08367 Welded Pipe B705 Specication for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe B723 Specication for Nickel-Chromium-MolybdenumCobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Welded Pipe B725 Specication for Welded Nickel (UNS N02200/UNS N02201) and Nickel Copper Alloy (UNS N04400) Pipe B880 Specication for General Requirements for Chemical Check Analysis Limits for Nickel, Nickel Alloys and Cobalt Alloys E8 Test Methods for Tension Testing of Metallic Materials E18 Test Methods for Rockwell Hardness of Metallic Materials E29 Practice for Using Signicant Digits in Test Data to Determine Conformance with Specications E39 Methods for Chemical Analysis of Nickel (Withdrawn 1995)3 E76 Test Methods for Chemical Analysis of Nickel-Copper Alloys (Withdrawn 2003)3 E112 Test Methods for Determining Average Grain Size E213 Practice for Ultrasonic Testing of Metal Pipe and Tubing
3 The last approved version of this historical standard is referenced on www.astm.org.

1.2 One or more of the test requirements of Section 5 apply only if specically stated in the product specication or in the purchase order. 1.3 In case of conict between a requirement of the product specication and a requirement of this general specication, only the requirement of the product specication needs to be satised. 1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identied in the appropriate
1 This specication is under the jurisdiction of ASTM Committee B02 on Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee B02.07 on Rened Nickel and Cobalt and Their Alloys. Current edition approved April 1, 2008. Published April 2008. Originally approved in 1987. Last previous edition approved in 2002 as B775 02. DOI: 10.1520/B0775-08. 2 For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [email protected]. For Annual Book of ASTM Standards volume information, refer to the standards Document Summary page on the ASTM website.

Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States

Copyright by ASTM Int'l (all rights reserved); Sat Dec 8 03:45:20 EST 2012 1 Downloaded/printed by Borovkov Roman (Austenit+Import) pursuant to License Agreement. No further reproductions authorized.

B775 08
E426 Practice for Electromagnetic (Eddy-Current) Examination of Seamless and Welded Tubular Products, Austenitic Stainless Steel and Similar Alloys E571 Practice for Electromagnetic (Eddy-Current) Examination of Nickel and Nickel Alloy Tubular Products E1473 Test Methods for Chemical Analysis of Nickel, Cobalt, and High-Temperature Alloys 2.2 ANSI Standards:4 B1.20.1 Pipe Threads B36.10 Welded and Seamless Wrought Steel Pipe B36.19 Stainless Steel Pipe 2.3 Other Documents:5 ASME Boiler and Pressure Vessel Code Section IX Welding and Brazing Qualications 3. Terminology 3.1 Denitions: 3.1.1 average diameter, nthe average of the maximum and minimum outside diameters, as determined at any one cross section of the pipe. 3.1.2 nominal wall, na specied wall thickness with a plus or minus tolerance from the specied thickness. 3.1.3 welded pipe, na round hollow produced by forming at stock and joining the single longitudinal seam by welding, and produced to the particular dimensions commercially known as pipe sizes (NPS). 4. Chemical Composition 4.1 In case of disagreement, the chemical composition shall be determined in accordance with the following methods:
UNS No. Prexes N02 N04 N06, N08 ASTM Method E39 E76 E1473

5.2.1 For welded pipe made with weld ller and at the option of the manufacturer, the transverse guided bend weld test may be substituted in lieu of the attening test. Two bend test specimens shall be taken transversely from pipe or the test specimens may be taken from a test plate of the same material and heat as the pipe, which is attached to the end of the cylinder and welded as a prolongation of the pipe longitudinal seam. Except as provided in 5.2.2, one shall be subject to a face guided bend test and a second to a root guided bend test. One specimen shall be bent with the inside surface of the pipe against the plunger and the other with the outside surface of the pipe against the plunger. Guided bend test specimens shall be prepared and tested in accordance with Section IX, Part QW, Paragraph QW 160 of the ASME Boiler and Pressure Vessel Code and shall be one of the types shown in QW 463.1 of that code. 5.2.2 For wall thicknesses over 38 in. (9.5 mm) but less than 34 in. (19 mm) side bend tests may be made instead of the face and root bend tests. For specied wall thicknesses 34 in. and over, both specimens shall be subjected to the side bend tests. Side bend specimens shall be bent so that one of the side surfaces becomes the convex surface of the bend specimen. 5.2.3 The bend test shall be acceptable if no cracks or other defects exceeding 18 in. (3 mm) in any direction be present in the weld metal or between the weld and the pipe or plate metal after bending. Cracks which originate along the edges of the specimen during testing, and that are less than 14 in. (6.5 mm) measured in any direction shall not be considered. 5.3 Pressure (Leak Test): 5.3.1 HydrostaticEach pipe shall be tested by the manufacturer to a minimum internal hydrostatic pressure of 1000 psi (6.9 MPa) provided that the ber stress, calculated from the following equation, does not exceed the allowable ber stress for the material:
P 5 2 St/ D (1)

4.2 The ladle analysis of the material shall conform to the chemical requirements prescribed by the individual product specication. 4.3 The product (check) analysis of the material shall meet the requirements for the ladle analysis within the tolerance limits prescribed in Specication B880. 5. Test Requirements 5.1 Flattening Test: 5.1.1 A length of pipe not less than 4 in. (102 mm), shall be attened under a load applied gradually at room temperature until the distance between the platens is ve times the wall thickness. The weld shall be positioned 90 from the direction of the applied attening force. 5.1.2 The attened specimen shall not exhibit cracks. 5.1.3 Supercial ruptures resulting from surface imperfections shall not be a cause for rejection. 5.2 Transverse Guided-Bend Weld Test:
4 Available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http://www.ansi.org. 5 Available from American Society of Mechanical Engineers (ASME), ASME International Headquarters, Three Park Ave., New York, NY 10016-5990, http:// www.asme.org.

where: P = hydrostatic test pressure, psi (MPa), S = allowable ber stress, for material in the condition (temper) furnished as specied in the product specication (S is calculated as the lower of 23 of the specied minimum 0.2 % offset yield strength or 14 of the specied minimum ultimate strength for the material), t = minimum wall thickness permitted, in. (mm), including minus tolerance, if any, and D = nominal outside diameter of the pipe, in. (mm). 5.3.1.1 The test pressure shall be held for a sufficient time to permit the entire length of the welded seam to be inspected. 5.3.2 Pneumatic (Air Underwater Test)Each pipe shall be tested at a pressure of 150 psi (1.05 MPa). The test pressure shall be held for a minimum of 5 s. Visual examination is to be made when the material is submerged and under pressure. The full length of pipe must be examined for leaks. 5.3.3 If any pipe shows leaks during hydrostatic or pneumatic testing, it shall be rejected. 5.4 Nondestructive Electric Test: 5.4.1 Eddy Current TestingTesting shall be conducted in accordance with Practices E426 or E571. The eddy current

Copyright by ASTM Int'l (all rights reserved); Sat Dec 8 03:45:20 EST 2012 2 Downloaded/printed by Borovkov Roman (Austenit+Import) pursuant to License Agreement. No further reproductions authorized.

B775 08
examination reference in this specication has the capability of detecting signicant discontinuities, especially of the short, abrupt type. 5.4.1.1 Unless otherwise specied by the purchaser, the calibration standard shall contain, at the option of the manufacturer, any one of the following discontinuities to establish a minimum sensitivity level for rejection. The discontinuity shall be placed in the weld if visible. 5.4.1.2 Drill HoleA hole not larger than 0.031 in. (0.79 mm) diameter shall be drilled radially and completely through the wall, care being taken to avoid distortion of the material while drilling. 5.4.1.3 Transverse Tangential NotchUsing a round le or tool with a 14 in. (6 mm) diameter, a notch shall be led or milled on the pipe outside diameter tangential to the surface and transverse to the longitudinal axis of the material. Said notch shall have a depth not exceeding 12.5 % of the specied wall thickness of the material, or 0.004 in. (0.10 mm), whichever is greater. 5.4.2 Ultrasonic TestingTesting shall be conducted in accordance with Practice E213. The ultrasonic examination referred to in this specication is intended to detect longitudinal discontinuities having a reective area similar to or larger than the calibration reference notches specied in 5.4.2.1. The examination may not detect circumferentially oriented imperfections or short, deep defects. 5.4.2.1 For ultrasonic testing, longitudinal calibration notches shall be machined on the outside and inside diameter surfaces. The depth of the notches shall not exceed 12.5 % of the specied wall thickness or 0.004 in. (0.10 mm), whichever is greater. The notch shall be placed in the weld, if visible. 5.4.3 Calibration FrequencyThe frequency of calibration checks shall be as follows: 5.4.3.1 At the beginning of each production run. 5.4.3.2 At least every four hours during testing. 5.4.3.3 At the end of each production run. 5.4.3.4 After any suspected equipment malfunction or work stoppage. 5.4.3.5 If, during any check, the equipment fails to detect the calibration defects, the instrument must be recalibrated and all material tested since the last satisfactory check shall be retested. 5.4.4 Acceptance and RejectionMaterial producing a signal equal to or greater than the calibration defect shall be subject to rejection. 5.4.4.1 Test signals that are produced by imperfections that cannot be identied or that are produced by cracks or cracklike imperfections shall result in rejection of the pipe, subject to rework and retest. 5.4.4.2 If the imperfection is judged as not t for use, the tube shall be rejected, but may be reconditioned and retested providing the wall thickness requirements are met. To be accepted, retested material shall meet the original electric test requirements. 5.4.4.3 If the imperfection is explored to the extent that it can be identied, and the pipe is determined to be t for use, the material may be accepted without further testing providing the imperfection does not encroach on minimum wall thickness requirements. 5.5 Tension TestTension testing shall be conducted in accordance with Test Methods E8. 5.5.1 The material shall conform to the tensile properties prescribed in the individual product specication. 5.6 Hardness TestHardness testing shall be conducted in accordance with Test Methods E18. 5.7 Grain SizeThe measurement of average grain size may be carried out by the planimetric method, the comparison method, or the intercept method described in Test Methods E112. In case of dispute, the referee method for determining average grain size shall be the intercept method. 5.8 For purposes of determining compliance with the specied limits for requirements of the properties listed in the following table, an observed value or a calculated value shall be rounded in accordance with the rounding method of Practice E29:
Requirements Chemical composition and tolerances Tensile strength and yield strength Elongation Rounded Unit for Observed or Calculated Value nearest unit in the last right-hand place of gures of the specied limit nearest 1000 psi (7 MPa) nearest 1 %

6. Dimensions and Permissible Variations 6.1 Dimensions of pipe are shown in Table 1. 6.1.1 Permissible variations in outside diameter and wall thickness are shown in Table 2. 6.2 LengthWhen material is ordered as cut-to-length, the length shall conform to the permissible variations prescribed in Table 3. When material is ordered to random lengths, the lengths and variations shall be agreed upon between the manufacturer and purchaser. 6.3 StraightnessMaterial shall be reasonably straight and free of bends and kinks. 6.4 EndsEnds shall be reasonably square and free from burrs. 7. Workmanship, Finish, and Appearance 7.1 The material shall be uniform in quality and temper, smooth, and free from imperfections that would render it unt for use. 8. Sampling 8.1 Lot Denition: 8.1.1 A lot for chemical analysis shall consist of one heat. 8.1.2 A lot for all other testing shall consist of all material from the same heat, nominal size (excepting length), and condition (temper). When nal heat treatment is in a batch-type furnace, a lot shall include only those pipes of the same size and the same heat that are heat-treated in the same furnace charge. When heat treatment is in a continuous furnace, a lot

Copyright by ASTM Int'l (all rights reserved); Sat Dec 8 03:45:20 EST 2012 3 Downloaded/printed by Borovkov Roman (Austenit+Import) pursuant to License Agreement. No further reproductions authorized.

B775 08
TABLE 1 Dimensions of Pipe

NOTE 1The following table is a reprint of Table 1 of ANSI B36.19. NOTE 2The decimal thicknesses listed for the respective pipe sizes represent their nominal wall dimensions.
Outside Diameter NPS Designator 1 4 3 8 1 2 3 4 1.0 1 1 4 1 1 2 2 2 1 2 3 3 1 2 4 5 6 8 10 12 14 16 18 20 22 24 30
18

Nominal Wall Thickness Schedule 5SA in. ... ... ... 0.065 0.065 0.065 0.065 0.065 0.065 0.083 0.083 0.083 0.083 0.109 0.109 0.109 0.134 0.156 0.156 0.165 0.165 0.188 0.188 0.218 0.250 mm ... ... ... 1.65 1.65 1.65 1.65 1.65 1.65 2.11 2.11 2.11 2.11 2.77 2.77 2.77 3.40 3.96 3.96 4.19 4.19 4.78 4.78 5.54 6.35 Schedule 10SA in. 0.049 0.065 0.065 0.083 0.083 0.109 0.109 0.109 0.109 0.120 0.120 0.120 0.120 0.134 0.134 0.148 0.165 0.180 0.188B 0.188B 0.188B 0.218B 0.218B 0.250 0.312 mm 1.24 1.65 1.65 2.11 2.11 2.77 2.77 2.77 2.77 3.05 3.05 3.05 3.05 3.40 3.40 3.76 4.19 4.57 4.78B 4.78B 4.78B 5.54B 5.54B 6.35 7.92 Schedule 40S in. 0.068 0.088 0.091 0.109 0.113 0.133 0.140 0.145 0.154 0.203 0.216 0.226 0.237 0.258 0.280 0.322 0.365 0.375B ... ... ... ... ... ... ... mm 1.73 2.24 2.31 2.77 2.87 3.38 3.56 3.68 3.91 5.16 5.49 5.74 6.02 6.55 7.11 8.18 9.27 9.52B ... ... ... ... ... ... ... Schedule 80S in. 0.095 0.119 0.126 0.147 0.154 0.179 0.191 0.200 0.218 0.276 0.300 0.318 0.337 0.375 0.432 0.500 0.500B 0.500B ... ... ... ... ... ... ... mm 2.41 3.02 3.20 3.73 3.91 4.55 4.85 5.08 5.54 7.01 7.62 8.08 8.56 9.52 10.97 12.70 12.70B 12.70B ... ... ... ... ... ... ...

in. 0.405 0.540 0.675 0.840 1.050 1.315 1.660 1.900 2.375 2.875 3.500 4.000 4.500 5.563 6.625 8.625 10.750 12.750 14.000 16.000 18.000 20.000 22.000 24.000 30.000

mm 10.29 13.72 17.15 21.34 26.67 33.40 42.16 48.26 60.33 73.03 88.90 101.60 114.30 141.30 168.28 219.08 273.05 323.85 355.60 406.40 457.20 508.00 558.80 609.60 762.00

A B

Schedules 5S and 10S wall thicknesses do not permit threading in accordance with ANSI B1.20.1. These do not conform to ANSI B36.10.

TABLE 2 Permissible Variations in Outside DiameterA,B and Wall ThicknessC For Welded Pipe
Permissible Variations in Outside Diameter NPS Designator in. to 1 , incl Over 112 to 4, incl Over 4 to 8, incl Over 8 to 18, incl Over 18 to 26, incl Over 26 to 34, incl Over 34 to 48, incl
18 12

TABLE 3 Permissible Variations in Cut LengthA

Outside Diameter, in. (mm) Cold nished: all sizes Hot nished: all sizes
A

Length Tolerance, in. (mm) Over

14

Under 0 0

Over mm 0.4 0.8 1.6 2.4 3.2 4.0 4.8 132 132 132 132 132 132
1 32

Under in. (0.031) (0.031) (0.031) (0.031) (0.031) (0.031) (0.031) mm 0.8 0.8 0.8 0.8 0.8 0.8 0.8

(6.4) (6.4)

132 116 332 1 8 532 316

1 64

(0.015) (0.031) (0.062) (0.093) (0.125) (0.156) (0.187)

14

These permissible variations in length apply to pipe in straight lengths. They apply to cut lengths up to and including 24 ft (7.3 m). For lengths over 24 ft, an additional over-tolerance of 18 in. (3.2 mm) for each 10 ft (3.0 m) or fraction thereof shall be permitted up to a maximum additional over-tolerance of 12 in. (12.7 mm).

A These permissible variations in outside diameter apply only to material as nished at the mill before subsequent swaging, expanding, bending, polishing, or other fabricating operations. B Ovality is the difference between the maximum and the minimum outside diameter measured at any one cross section. There is no additional tolerance for ovality on material having a nominal wall thickness for more than 3 % of the outside diameter. On this material, the average of the maximum and the minimum outside diameter measurements will fall within the outside diameter tolerance shown in Table 2. An additional ovality allowance of twice the outside diameter tolerance spreads shown in Table 2, applied 12, is allowed for material having a nominal wall thickness of 3 % or less of the nominal outside diameter. C The wall thickness variation shall not exceed 12.5 % of the nominal wall thickness.

8.1.2.1 Where material cannot be identied by heat, a lot shall consist of not more than 500 lb (227 kg) of material of the same alloy in the same condition (temper) and nominal size (excepting length).
NOTE 1For tension, hardness and attening test requirements, the term lot applies to all lengths prior to cutting.

shall include all pipe of the same size and heat, heat-treated in the same furnace at the same temperature, time at temperature, and furnace speed during one production run. At no time shall a lot consist of more than 20 000 lb (9070 kg).

8.2 Test Material Selection: 8.2.1 Chemical AnalysisRepresentative samples from each lot shall be taken during pouring or subsequent processing. 8.2.2 Mechanical and Other PropertiesSamples of the material to provide test specimens for mechanical and other properties shall be taken from such locations in each lot as to be representative of that lot. Test specimens shall be taken from material in the nal condition (temper).

Copyright by ASTM Int'l (all rights reserved); Sat Dec 8 03:45:20 EST 2012 4 Downloaded/printed by Borovkov Roman (Austenit+Import) pursuant to License Agreement. No further reproductions authorized.

B775 08
9. Retests and Retreatment 9.1 RetestsIf the results of the mechanical tests of any group or lot do not conform to the requirements specied in the individual specication, retests may be made on additional pipes of double the original number from the same group or lot, each of which shall conform to the requirements specied. 9.2 RetreatmentIf the individual pipes or the pipes selected to represent any group or lot fail to conform to the test requirements, the individual pipes or the group or lot represented may be reheat treated and resubmitted for test. Not more than two reheat treatments shall be permitted. 10. Specimen Preparation 10.1 Room Temperature Tensile Specimen: 10.1.1 Material shall be tested in the direction of fabrication. Whenever possible, the pipe shall be tested in full cross section. When testing in full section is not possible, longitudinal strip specimens or the largest possible round section shall be used. In the event of disagreement when full section testing is not possible, a longitudinal strip specimen with reduced gage length as contained in Test Methods E8 shall be used. 10.2 Hardness Specimen: 10.2.1 The hardness specimen shall be prepared in accordance with Test Methods E18. The test shall be made on the inside diameter surface of a specimen cut from the end, or on the inside of the pipe near the end, at the option of the manufacturer. 10.3 Grain Size: 10.3.1 If required, the grain size specimen shall be a transverse sample representing full wall thickness. 11. Inspection 11.1 Witnessing of testing or inspection by the purchasers representative shall be agreed upon by the purchaser and the manufacturer as part of the purchase contract. 12. Rejection and Rehearing 12.1 Material tested by the purchaser that fails to conform to the requirements of this specication may be rejected. Rejection should be reported to the supplier promptly and in writing. In case of dissatisfaction with the results of the test, the producer or supplier may make claim for a rehearing. 13. Certication 13.1 When specied in the purchase contract, a manufacturers certication shall be furnished to the purchaser stating that the material has been manufactured, tested and inspected in accordance with this specication, and that the test results on representative samples meet specication requirements. When specied in the purchase contract, a report of the test results shall be furnished. 14. Product Marking 14.1 Material Marking: 14.1.1 The name or brand of the manufacturer, the name of the material or UNS number, the letters ASTM, the product specication number, heat number, class (if applicable) and nominal pipe size shall be legibly marked on each piece 12 NPS and larger and lengths greater than 3 ft (914 mm). The material marking shall be by any method that will not result in harmful contamination. 14.1.2 For material smaller than 12 NPS, or lengths under 3 ft (914 mm), the information specied in 14.1.1 shall be legibly marked on each piece or marked on a tag securely attached to the bundle or box in which the material is shipped, at the option of the manufacturer. 15. Packaging and Package Marking 15.1 The following information shall be marked on the material or included on the package, or on a label or tag attached thereto: name of the material or UNS number, heat number, condition (temper), the letters ASTM, the product specication number, the nominal pipe size, gross, tare, and net weight, consignor and consignee addresses, contract or order number, and such other information as may be dened by the purchase contract. 16. Keywords 16.1 welded pipe

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. This standard is subject to revision at any time by the responsible technical committee and must be reviewed every ve years and if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below. This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above address or at 610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website (www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/ COPYRIGHT/).