DATA SHEET

B-60

22%Cr DUPLEX STAINLESS STEELS

Alloy type 22%Cr standard duplex ferritic-austenitic stainless steels. Materials to be welded
ASTM BS EN & DIN

METRODE PRODUCTS LTD HANWORTH LANE, CHERTSEY SURREY, KT16 9LL Tel: +44(0)1932 566721 Fax: +44(0)1932 566168 Sales Fax: +44(0)1932 569449 Technical Fax: +44(0)1932 566199 Export Email: [email protected] Internet: http//www.metrode.com

Microstructure Multipass welds in the as-welded condition contain about 2550% ferrite depending on dilution and heat input/cooling rate conditions. Welding guidelines Preheat not generally required. Interpass temperature 150C max. Heat input in the range 1.02.5 kJ/min (depending on material thickness) should be acceptable but some codes restrict the max to 1.75 or 2.0kJ/mm. PWHT Although welds in wrought duplex stainless steels are almost always left in the as-welded condition, major repairs to castings are generally specified in the solution treated condition. Experience has indicated good properties following 1120C/3-6h + water quench with or without a cooling step to 1060C before quenching. Additional information A Technical Profile covering duplex and superduplex stainless steels is available. Related alloy groups Superduplex (data sheets B-61, B-62 and B-63) and duplex matching consumables for casting repairs. Products available
Process MMA

A182 Gr F51 A890 Gr 4A (cast)

BS

1.4462 X2CrNiMoN22-5-3
UNS

318S13
Proprietary alloys include:

S31803, S32205 J92205 (cast) SAF2205 2205 UR 45N A903 Cronifer 2205LCN Maresist F51 (cast) SM22Cr

Sandvik Avesta Polarit Creusot Ind Bhler VDM S+C Sumitomo

Lean and Mo-free duplex including:

(UNS S32304 / DIN 1.4362 / X2CrNiN23L) Sandvik SAF 2304 Creusot Ind UR35N LDX 2101 Avesta Polarit Applications Duplex stainless steel pipe, plate, fittings and forgings have an approximate 50:50 microstructure of austenite with a ferrite matrix. This, coupled with general alloying level, confers: - high strength compared with standard austenitic steels, eg type 316L. - good general corrosion resistance in a range of environments. - high resistance to chloride induced stress corrosion cracking (CSCC). - high resistance to pitting attack in chloride environments, eg seawater. These alloys are finding widening application in the offshore oil/gas, chemical and petrochemical process industries, eg pipework systems, flowlines, risers, manifolds etc.

Product Supermet 2205 Ultramet 2205 2205XKS

Specification AWS E2209-16 AWS E2209-15 AWS ER2209 AWS ER2209

BS EN SA AF2 DC

TIG/SAW MIG SAW flux FCW

ER329N ER329N / 2205 MIG SSB Supercore 2205 Supercore 2205P

AWS E2209T0-4 AWS E2209T1-4

Rev 07

09/04

DS: B-60 (pg 1 of 6)

General Data for all 22%Cr Duplex MMA Electrodes

Storage 3 hermetically sealed ring-pull metal tins per carton, with unlimited shelf life. Direct use from tin is satisfactory for longer than a working shift of 8h. Excessive exposure of electrodes to humid conditions will cause some moisture pick-up and increase the risk of porosity. For electrodes that have been exposed: Redry 200 300C/1-2h to restore to as-packed condition. Maximum 380 C, 3 cycles, 10h total. Storage of redried electrodes at 50 200C in holding oven or heated quiver: no limit, but maximum 6 weeks recommended. Recommended ambient storage conditions for opened tins (using plastic lid): < 60% RH, > 18C. Fume composition, wt % typical:
Fe Mn Cr Ni Mo Cu F* OES (mg/m )
3

Fume data

0.2

<0.2

16

0.8

* F = 28% for basic coated 2205XKS but this does not affect OES.

SUPERMET 2205
Product description

Rutile electrode for 22%Cr duplex

MMA electrode with enhanced Cr, Mo and N levels, giving higher weld pitting resistance than the nearest AWS specification A5.4 E2209-16. See Ultramet 2205 for rutile type conforming to AWS. Supermet 2205 is made on high quality stainless steel core wire with a rutile flux system designed to give minimum carbon content coupled with optimum operating characteristics. Supermet 2205 is designed for welding wrought, forged or cast "standard" duplex stainless steels for service in the as-welded condition. Good properties are also obtained when solution treated, as frequently required for casting repairs. The electrode has a rutile flux system and is used primarily for downhand and H-V welding applications. Smaller sizes offer excellent all-positional operability. Recovery is about 120% with respect to core wire, 65% with respect to whole electrode.

Specifications ASME IX Qualification Composition (weld metal wt %)

NONE

Nearest is AWS A5.4 E2209-16.

QW432 F-No -, QW442 A-No 8

C min max typ Mn Si S P Cr Ni Mo Cu N PREN

-0.5 0.3 0.03 2.0 1.0 0.02 1 0.7 PREN = Cr + 3.3Mo + 16N
As welded Tensile strength 0.2% Proof stress Elongation on 4d Reduction of area Impact energy

-0.02 0.01

-0.03 0.02

24.0 26.0 25

8.5 10.0 9.5

3.0 4.0 3.4

-0.5 0.1
Pipe butt weld

0.14 0.25 0.17

1120C/ 3h + WQ

36 43 38

All-weld mechanical properties

min

typical

+20C - 20C - 30C - 40C - 50C

MPa MPa % % J J J J J

690 480 20 -------

850 650 30 40 60-73 45-55 40-52 35-47 30-40

867 752 25 35 -45-50 42-46 38-43 35-40

800 480 32 ---> 90 > 70 > 35

Operating parameters

DC +ve or AC (OCV 55V min)

mm min A max A 2.5 3.2 4.0 5.0

50 90
2.5

65 120
3.2

100 160
4.0

130 190
5.0

Packaging data

mm length mm kg/carton pieces/carton

300 12.0 630

350 13.2 354

350 13.8 255

450 18.6 165

Rev 07

09/04

DS: B-60 (pg 2 of 6)

ULTRAMET 2205
Product description

Rutile all-positional electrode for 22%Cr duplex

MMA electrode made on high quality stainless steel core wire with a rutile flux system designed to give minimum carbon content coupled with optimum operating characteristics. The electrode has a rutile flux system optimised for all welding positions except vertical down and provides excellent operability. Recovery is about 120% with respect to core wire, 65% with respect to whole electrode.

Specifications ASME IX Qualification Composition (weld metal wt %)

AWS A5.4 BS EN 1600

E2209-16 E 22 9 3 N L R 3 2

QW432 F-No 5, QW442 A-No 8

C min max typ Mn Si S P Cr Ni Mo Cu N PREN

-0.03 0.02

0.5 2.0 1

0.3 0.90 0.7

-0.02 0.01

-0.03 0.02

22.0 23.5 23.2

min

8.5 10.0 9 690 480 20 20 ------

2.8 3.5 3.2

-0.5 0.1
typical

0.14 0.2 0.17

34 38 36

All-weld mechanical properties

As welded Tensile strength 0.2% Proof stress Elongation on 4d Elongation on 5d Reduction of area Hardness Impact energy

MPa MPa % % % HV10 (HRC) + 20C J (mm) - 20C J (mm) - 50C J (mm)

850 675 27 25 40 < 305 (< 24) > 54 (> 0.8) 43-48 (> 0.5) 32-41 (>0.38)

Operating parameters

DC +ve or AC (OCV: 50V min).

mm min A max A 2.5 3.2 4.0 5.0

60 90
2.5

75 120
3.2

100 155
4.0

130 190
5.0

Packaging data

mm length mm kg/carton pieces/carton

300 12.0 654

350 13.5 372

350 13.5 243

450 18.3 177

2205XKS
Product description

Basic pipe-welding electrode for 22%Cr duplex

MMA electrode made on duplex stainless core wire with a special basic flux to give optimum all-positional operability. Recovery is about 105% with respect to core wire, 65% with respect to whole electrode. The electrode has a basic flux system and is recommended where the highest sub-zero toughness is required, and for the most demanding positional welding applications such as fixed pipework qualified in the ASME 6G position.

Specifications

AWS A5.4 BS EN 1600 STATOIL

E2209-15 E 22 9 3 N L B 4 2 R-SF-163

ASME IX Qualification

QW432 F-No 5, QW442 A-No 8

Rev 07

09/04

DS: B-60 (pg 3 of 6)

2205XKS (continued)
Composition (weld metal wt %)
C min max typ Mn Si S P Cr Ni Mo Cu N PREN

-0.04 0.03

0.5 2.0 1

-0.90 0.6

-0.02 0.01

-0.03 0.02

22.0 23.5 23

8.5 10.0 9

3.0 3.5 3.2

-0.75 0.1

0.15 0.20 0.17

35 38 36

PREN = Cr + 3.3Mo + 16N All-weld mechanical properties

As welded Tensile strength 0.2% Proof stress Elongation on 4d Elongation on 5d Reduction of area Impact energy min typical 1120 1135C +WQ

+ 20C - 50C - 75C

Hardness

MPa MPa % % % J J J HV

690 450 20 20 --47 ---

750-870 630-700 28 26 45 > 85 > 60 > 30 260-290

790 480 41 37 64 -> 75 -240

Operating parameters

DC +ve only.
mm min A max A 2.5 3.2 4.0 5.0

50 75
2.5

70 95
3.2

100 155
4.0

130 190
5.0

Packaging data

mm length mm kg/carton pieces/carton

300 12.0 720

350 13.5 402

350 13.5 273

350 13.5 171

ER329N / 2205 MIG

Product description Specifications AWS A5.9 BS EN 12072 BS 2901: Pt2 STATOIL ER2209 22 9 3 N L 22.8.3S92 R-SF-163 (TIG)

Solid welding wire for 22%Cr duplex

Solid duplex stainless wire for welding 2205 type duplex stainless steels.

ASME IX Qualification Composition (wire wt %)

QW432 F-No 6, QW442 A-No 8

C min max typ Mn Si S P Cr Ni Mo Cu N

-0.03 0.015

1.0 2.0 1.6

0.25 0.65 0.5

-0.020 0.001

-0.030 0.015

22.5 23.5 23

8.0 9.5 8.2

3.0 3.5 3.2

-0.3 0.1

0.14 0.20 0.17*

Duplex weld metal microstructure with austenite + 30-50% ferrite. Pitting resistance equivalent PREN = Cr + 3.3Mo + 16N is > 35. * ER329N MIG and 2205 MIG spooled wire is selected for suitability for both MIG and auto-TIG, with typically 0.15%N to control porosity. All-weld mechanical properties
Typical values as welded Tensile strength 0.2% Proof stress Elongation on 4d Elongation on 5d Hardness Impact energy min TIG typical MIG SAW + SSB

- 30C - 50C

MPa MPa % % HV HRC J J

690 450 20 20 -----

820 660 32 29 270 (< 310) 23 (< 28) > 140 > 120

800-835 560-620 28-35 30 270 (< 310) 23 (< 28) > 70 > 60

800-835 560-620 28-35 30 270 (< 310) 23 (< 28) 80 (>55) 55 (>35)

Rev 07

09/04

DS: B-60 (pg 4 of 6)

ER329N / 2205 MIG (continued)

Typical operating parameters
TIG Shielding Current Diameter Parameters MIG SAW

Argon DC 1.6 / 2.4mm 100A, 12V

Ar / He / CO2 pulsed 1.2mm 180A, 28V

SSB flux * DC + 1.6mm 350A, 30V

* LA491 flux also suitable. Packaging data

mm 0.8 1.0 1.2 1.6 2.0 2.4 3.2 TIG MIG SAW

--2.5kg tube 2.5kg tube 2.5kg tube 2.5kg tube 2.5kg tube

15kg spool 15kg spool 15kg spool -----

---25kg coil to order 25kg coil --

Fume data

MIG fume composition (wt %) (TIG and SAW fume negligible)

Fe Mn Cr
3

Ni

Mo

Cu

OES (mg/m )

28

10

20

1.5

< 0.5

2.5

SUPERCORE 2205, 2205P

Product description

Flat and positional FCAW for 22%Cr duplex

High performance rutile flux cored wires produced in the most versatile size of 1.2mm. Supercore 2205 is suited to welding in the flat and horizontal-vertical positions (material > 6mm). Supercore 2205P is optimised for positional welding, both vertical up and for fixed pipework qualified in the ASME 5G or 6G welding positions (pipe typically > 150mm diameter, > 15mm wall). Made with an austenitic stainless steel sheath and rutile flux system. Weld metal carbon content is typically <0.03% when using the recommended 80%Ar-20%CO2 shielding gas. Metal recovery about 90% with respect to the wire.

Specifications AWS A5.22 BS EN 12073 ASME IX Qualification Composition (weld metal wt %)

Supercore 2205 E2209T0-4 T 22 9 3 N L R M 3

Supercore 2205P E2209T1-4 T 22 9 3 N L P M 2

QW432 F-No 6, QW442 A-No 8

C min max typ Mn Si S P Cr Ni Mo Cu N PRE*

-0.04 0.03

0.5 2.0 1.2

-1.00 0.7

-0.02 <0.01

-0.030 0.02

21.5 24.0 23

8.5 10.0 9.2

2.8 4.0 3.1

-0.5 0.1

0.08 0.20 0.12

34 38 35

* PRE (pitting resistance equivalent) = Cr + 3.3Mo + 16N All-weld mechanical properties

As welded Tensile strength 0.2% Proof stress Elongation on 4d Elongation on 5d Reduction of area Impact energy min typical

- 20C - 50C - 75C

Hardness

MPa MPa % % % J J J HV

690 480 20 18 ------

800 630 32 29 45 65 * 55 * 30 * 270

* These values are for Supercore 2205P. Impact energy values for Supercore 2205 are typically 40J at 20C, 30J at 50C.

Rev 07

09/04

DS: B-60 (pg 5 of 6)

SUPERCORE 2205, 2205P (continued)

Operating parameters
Shielding gas: 80%Ar-20%CO2 at 20-25l/min. Proprietary gases may be used but argon should not exceed 80%.

Gas mixtures without oxygen additions can be helpful for optimum weld metal toughness. Supercore 2205 is also suitable for use with 100% CO2. Current: DC+ve ranges as below for Ar-20%CO2 (Supercore 2205 with 100% CO2 requires approx 3V higher):
mm 1.2 1.2 P amp-volt range typical stickout

150A-25V to 280A-34V 130A-20V to 250A-34V

200A-30V 140A-23V

15-20mm 15-20mm

Packaging data

Spools vacuum-sealed in barrier foil with cardboard carton: 15kg The as-packed shelf life is virtually indefinite. Resistance to moisture absorption is high, but to maintain the high integrity of the wire surface and prevent any possibility of porosity, it is advised that part-used spools are returned to polythene wrappers. Where possible, preferred storage conditions are 60% RH max, 18C min. Fume composition (wt %)
Fe Mn Ni Cr
3

Fume data

Cr

Cu

OES (mg/m )

10

12

5.5

<0.5

0.9

SSB FLUX
Product description Specifications ASME IX Qualification Composition (typical) All-weld mechanical properties with ER329N wire Agglomerated basic non-alloying flux for submerged arc welding. DIN 32522 BS EN 760 BFB6 63353 DC8M SA AF2 DC

Sub-arc flux

QW432 F-No -, QW442 A-No C ER329N wire deposit As welded Tensile strength 0.2% Proof stress Elongation on 4d Hardness Impact energy Mn Si S P Cr Ni Mo Cu N

0.015 0.02

1.6 1.3

0.5 0.5

0.001 --

0.015 --

23 22.5

8.5 8.5

3.2 3.1

0.1 0.1

0.17 0.15

- 30C - 50C

MPa MPa % HV HRC J J

800-835 560-620 28-35 270 (< 310) 23 (< 28) 80 (>55) 55 (>35)

Operating parameters

Current: DC +ve ranges as below: mm 1.6 2.4 amp-volt range typical stickout

200-350A, 27-31V 250-450A, 28-32V

300A, 28V 350A, 29V

20-25mm 20-25mm

Packaging data

Metrode SSB Flux is supplied in sealed moisture resistant 20kg metal drums. Preferred storage conditions for opened drums: < 60%RH, > 18C. If the flux has become damp or has been stored for a long period, it should be redried in the range 250-400C/1-3h.

Rev 07

09/04

DS: B-60 (pg 6 of 6)