Ti-NAMITE®

Tool Coatings
are specifically
engineered for SGS®
solid carbide rotary
tools. This proprietary
multi-layering
process results in
maximized tool life
and increased speed
and feed rates in
any application.

Hardness: 3300HV0.05
Recommended For Your Applications In... Oxidation Temperature:
800°C - 1472°F
• Cast Iron
• High-temperature Alloys Coefficient Of Friction:
• Hardened Steels .45
• Stainless Steels
Thickness: 1 - 4 Microns
Ti-NAMITE-A (AlTiN) is Preferred for High-speed and (based on tool diameter)
Dry Cutting

Drilling Hardened Tool Steel

Series 106M 6mm Series 106M 6mm HOLES PRODUCED BY UNCOATED AND Ti-NAMITE-A
Tool Type SERIES 106M DRILLS
.2362 .2362
20
Condition UNCOATED Ti-NAMITE-A 18
ISO 4957S5H5653 ISO 4957S5H5653
NUMBER OF HOLES

16
Material Type M4 @ 64 HRc M4 @ 64 HRc 14

15 mm 15 mm 12
Depth of Cut .519” .519” 10
8
6 mm 6 mm
Width of Cut 6
.2362” .2362”
4
9 m/min. 9m/min. 2
Spindle Speed 477 rpm 477 rpm 0
25.4 mm/min. 25.4 mm/min. UNCOATED Ti-NAMITE-A COATED
Feed
1 IPM 1 IPM (TOOL FAILURE)

50 SGS HIGH PERFORMANCE

 Recommended For Your Applications In...
• High Silicon • Low Carbon Steel
• Aluminum Alloys • Alloyed Steels
• Titanium Alloys
Milling Application Data
Series 1 1/2” Series 1 1/2” WEAR COMPARSION UNCOATED VERSUS Ti-NAMITE-C
Tool Type
12.7 mm 12.7mm Hardness: 3000HV0.05
0.006
UNCOATED Ti-NAMITE-C .152 mm
Condition
0.005
1018 STEEL 1018 STEEL .127 mm Oxidation Temperature:
Material Type DIN 1.0453 DIN 1.0453 0.004 400°C - 752°F

EDGE WEAR
.102 mm
.500” .500”
Depth of Cut 12.7 mm 12.7 mm
0.003
.076 mm
Coefficient Of Friction:
.125” .125” 0.002 .3 - .45
Width of Cut .05 mm
3.2 mm 3.2 mm
0.001
.025 mm
Spindle Speed
2782 rpm 4185 rpm Thickness: 1 - 4 Microns
111 m/min. 167 m/min. 0
(based on tool diameter)
33 IPM 50 IPM UNCOATED AT Ti-NAMITE-C AT
Feed 838 mm/min. 1270 mm/min.
1350 INCHES / 34 METERS 4000 INCHES / 102 METERS

Recommended For General Purpose And Applications In...

• Stainless Steel • Copper Alloys
• Medium Carbon Steel • Brass
• Alloyed Steel • Bronze
Milling Application Data
Series 1 1/2” Series 1 1/2” WEAR COMPARSION UNCOATED VERSUS Ti-NAMITE
Tool Type
12.7 mm 12.7mm 0.006 Hardness: 2200HV0.05
.152 mm
Condition UNCOATED Ti-NAMITE 0.005
4140 STEEL 4140 STEEL .127 mm
Oxidation Temperature:
Material Type DIN 1.7225 DIN 1.7225 0.004
600°C - 1112°F
EDGE WEAR

.102 mm
.500” .500” 0.003
Depth of Cut 12.7 mm 12.7 mm .076 mm
Coefficient Of Friction:
0.002
.125” .125” .05 mm .4 - .65
Width of Cut 3.18 mm 3.18 mm 0.001
.025 mm
1955 rpm 2933 rpm Thickness: 1 - 4 Microns
Spindle Speed 0
78 m/min. 117 m/min.
UNCOATED Ti-NAMITE COATED (based on tool diameter)
23.5 IPM 32.5 IPM
Feed 596.9 mm/m 825.5 mm/m
300 INCHES / 7.6 METERS

Recommended For Your Applications In...

• High Silicon Aluminum Alloys
• Titanium Alloys

Milling Application Data

Series 135L 1/4" Series 135L 1/4"
Tool Type
6.35 mm 6.35 mm HOLES PRODUCED BY Ti-NAMITE AND Ti-NAMITE-B
Hardness: 4000HV
SERIES 135L DRILLS
Condition Ti-NAMITE Ti-NAMITE-B 25,000

6061 Aluminum 6061 Aluminum Oxidation Temperature:

Material Type DIN AlMg1SiCu 20,000
DIN AlMg1SiCu 850°C - 1562°F
NUMBER OF HOLES

1.600” 1.600” 15,000

Depth of Cut 40.6 mm 40.6 mm Coefficient Of Friction:
10,000
.2500” .2500” .45
Width of Cut 6.35 mm 6.35 mm
5,000
7500 rpm 7500 rpm Thickness: 1 - 2 Microns
Spindle Speed
150 m/min. 200 m/min. 0

Ti-NAMITE Ti-NAMITE-B
(based on tool diameter)
60 IPM 80 IPM
Feed 1524 mm/m 2032 mm/m

WWW.SGSTOOL.COM 51