2015-07-23 Typical Properites of ADI Metric Units

Download as pdf or txt
Download as pdf or txt
You are on page 1of 1

AUSTEMPERED DUCTILE IRON

ASTM A897/897M-15 (SI units)

900-650-9

1050-750-7

1200-850-4

1400-1100-2

1600-1300-1

GRADE 900

GRADE 1050

GRADE 1200

GRADE 1400

GRADE 1600

TENSILE STRENGTH (MPa)

900

1050

1200

1400

1600

0.2% OFFSET YIELD STRENGTH (MPa)

650

750

850

1100

1300

302 (3.50)

340 (3.30)

387 (3.10)

418 (3.00)

460 (2.85)

10

**YOUNG'S MODULUS (GPa)

159.3

157.9

156.5

155.1

153.8

COMPRESSIVE STRENGTH (MPa)

1380

1650

1935

2275

2520
1490

TYPICAL PROPERTIES*
MONOTONIC (STATIC) PROPERTIES

ELONGATION (% IN 2 INCH GAGE LENGTH )


HARDNESS BRINELL BHN (B.I.D. mm)
REDUCTION IN AREA (%)

SHEAR STRENGTH (MPa)

870

1025

1180

1370

MODULUS OF RIGIDITY (GPa)

65.1

64.0

63.2

62.4

62.1

POISSON'S RATIO

0.25

0.25

0.25

0.25

0.25

485

415

-REVERSE BENDING AS MACHINED (MPa)

415

380

- AXIAL PUSH-PULL

385

***STRENGTH COEFFICIENT K (MPa)

1503

***STRAIN HARDENING EXPONENT n

0.143

***TRUE FRACTURE STRENGTH s f

1032

***TRUE FRACTURE DUCTILITY e f

0.082

DYNAMIC PROPERTIES
FATIGUE STRENGTH (@10 MILLION CYCLES):
-ROTATING BENDING AS MACHINED (MPa)

450

1155

1260

1365

1560

1750

-G-50 SINGLE TOOTH BENDING AS MACHINED (MPa)

350

365

350

335

320

-G-50 SINGLE TOOTH BENDING AS SHOT PEENED (MPa)

700

770

700

665

630

-UN-NOTCHED CHARPY IMPACT@ 21C (JOULES)

120

120

93

80

53

12

10.6

9.3

8.6

DYNAMIC ELASTIC MODULUS (GPa)

170

168

167

165

164

EST. DUCTILE/BRITTLE TRANSITION TEMP. (C)

-20

-20

-20

-20

-20

109

85

60

52

44

0.1376

0.1465

0.1600

-G-50 MAX. ALLOWABLE CONTACT STRESS (MPa)

-NOTCHED CHARPY IMPACT @ 21C (JOULES)

FRACTURE TOUGHNESS (MPa*SQRT(m))

1538

**STRENGTH COEFFICIENT K' (MPa)

0.1330

**STRAIN HARDENING EXPONENT n'


**FATIGUE STRENGTH COEFFICIENT s f' (Mpa)
**FATIGUE STRENGTH EXPONENT b

1455

2720

3100

5020

-0.1110

-0.1460

-0.1600

-0.2050

**FATIGUE DUCTILITY COEFFICIENT ef'

0.1990

0.1780

0.3960

0.4880

**FATIGUE DUCTILITY EXPONENT C

-0.6770

-0.6280

-0.7520

-0.8480

7.0965

7.0872

7.0779

7.0686

7.0593

14.6

14.3

14.0

13.8

13.5

10.9

10.8

10.6

10.3

9.8

0.12/0.02

0.18/0.08

0.25/0.13

0.27/0.16

0.28/0.17

22.1

21.8

21.5

21.2

20.9

PHYSICAL (INTRINSIC) PROPERTIES


DENSITY (g/cubic cm)
COEFF. OF THERMAL EXPANSION (mm/mm/C) X 10

-6

WEAR RESISTANCE ( AMAX PIN TEST,VOLUME LOSS cu. mm)


LINEAR EXPANSION - % (from Ferritic/from Pearlitic)
THERMAL CONDUCTIVITY (W/M-K)

5.26
5.41
5.69
12.7
19.2
*UTS, YS and %EL are minimums - the remaining properties are not guaranteed minimums. They represent typical properties that one may observe
in commercial ADI components.
** Young's modulus data courtesy of Daimler-Chrysler
*** Grade 900 fatigue coeff. & exponents courtesy of Daimler-Chrysler. All other grades courtesy of John Deere.

INTERNAL DAMPING (log decr.) X .0001