Designation: A 139/A 139M 004

Standard Specication for

Electric-Fusion (Arc)-Welded Steel Pipe (NPS 4 and Over)
1
This standard is issued under the xed designation A139/A139M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specication covers ve grades of electric-fusion (arc)-welded straight-seam or helical-seam steel pipe. Pipe of NPS
4 (Note 1) and larger with nominal (average) wall thickness of 1.0 in. ( [25.4 mm)] and less are covered. Listing of standardized
dimensions are for reference (Note 2). The grades of steel are pipe mill grades having mechanical properties which differ from
standard plate grades. The pipe is intended for conveying liquid, gas, or vapor.
NOTE 1The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as nominal diameter,
size, and nominal size.
1
This specication is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel, and Related Alloys , and is the direct responsibility of Subcommittee A01.09
on Carbon Steel Tubular Products.
Current edition approved March 10, 20004. Published June 2000. April 2004. Originally published as A 139 32 T. approved in 1932. Last previous edition A 139 96
e1
. approved in 2000 as A 139 00.
1
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
*A Summary of Changes section appears at the end of this standard.
Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
NOTE 2A comprehensive listing of standardized pipe dimensions is contained in ANSI B 36.10. ASME B36.10M
2
.
NOTE 3The suitability of pipe for various purposes is somewhat dependent on its dimensions, properties, and conditions of service. For example,
for high-temperature service see applicable codes and Specication A 691.
1.2 The values stated in either inch-pound units or in SI units are to be regarded separately as standard. Within the text, the SI
units are shown in brackets. The values ind each system are not exact equivalents; therefore, each system is to be used
independently of the other.
2. Referenced Documents
2.1 ASTM Standards:
3
A 370 Test Methods and Denitions for Mechanical Testing of Steel Products
A 691 Specication for Carbon and Alloy Steel Pipe, Electric Fusion-Welded for High-Pressure Service at High Temperatures
A 751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products
E 59 Practice for Sampling Steel and Iron for Determination of Chemical Composition
4
2.2 American Welding Society Standard:
ANSI/AWS B2.1 Standard for Welding Procedure and Performance Qualications Welding Handbook, Vol 1, 8th ed
2.3 ASME Standard:
5
AWS B2.1 Standard for Welding Procedure and Performance Qualications Welding Handbook, Vol 1, 8th ed
2.3 ASME Standards:
6
ASME B36.10M Welded and Seamless Wrought Steel Pipe
ASME B36.19M Stainless Steel Pipe
ASME Boiler and Pressure Vessel Code: Section IX, Welding Qualications
3. Ordering Information
3.1 Orders for material under this specication should include the following, as required, to describe the desired material
adequately:
3.1.1 Quantity (feet, metres, or number of lengths),
3.1.2 Name of material (electric-fusion-(arc) welded steel pipe),
3.1.3 Grade (Table 1),
3.1.4 Size (NPS, or outside diameter, and nominal wall thickness, or schedule number),
3.1.5 Lengths (specic or random, Section 17),
3.1.6 End nish (Section 18),
3.1.7 Hydrostatic test pressure (Section 16, Note 8, and Note 9),
3.1.8 ASTM specication designation, and
3.1.9 End use of material.
4. Process
4.1 The steel shall be made by one or more of the following processes: open-hearth, basic-oxygen, or electric-furnace.
4.2 Steel may be cast in ingots or may be strand cast. When steels of different grades are sequentially strand cast, identication
of the resultant transition material is required. The producer shall remove the transition material by any established procedure that
positively separates the grades.
NOTE 4The term basic-oxygen steelmaking is used generically to describe processes in which molten iron is rened to steel under a basic slag in
a cylindrical furnace lined with basic refractories, by directing a jet of high-purity gaseous oxygen onto the surface of the hot metal bath.
2
Annual Book of ASTM Standards, Vol 01.01.
3
Discontinued 1996; see
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [email protected]. For 1995 Annual Annual Book of
ASTM Standards , Vol 03.05. volume information, refer to the standards Document Summary page on the ASTM website.
4
Available from American Welding Society, 550 NW LeJeune Rd., Miami, FL 33135.
4
Withdrawn.
5
Available from American Society of Mechanical Engineers, Three Park Ave., New York, NY 10016-5990. Welding Society, 550 NW LeJeune Rd., Miami, FL 33135.
6
Available from American Society of Mechanical Engineers, Three Park Ave., New York, NY 10016-5990.
TABLE 1 Chemical Requirements
Element Composition, max, %
Grade A Grade B Grade C Grade D Grade E
Carbon 0.25 0.26 0.28 0.30 0.30
Manganese 1.00 1.00 1.20 1.30 1.40
Phosphorus 0.035 0.035 0.035 0.035 0.035
Sulfur 0.035 0.035 0.035 0.035 0.035
A 139/A 139M 004
2
5. Manufacture
5.1 The longitudinal edges of the steel shall be shaped to give the most satisfactory results by the particular welding process
employed. The weld shall be made by automatic (Note 5) means (except tack welds if used) and shall be of reasonably uniform
width and height for the entire length of the pipe.
NOTE 5Upon agreement between the purchaser and the manufacturer, manual welding by qualied procedure and welders may be used as an equal
alternative under these specications.
5.2 All weld seams made in manufacturing pipe shall be made using complete joint penetration groove welds.
6. Chemical Composition
6.1 The steel shall conform to the chemical requirements prescribed in Table 1 and the chemical analysis shall be in accordance
with Test Methods, Practices, and Terminology A 751.
7. Tensile Requirements for the Steel
7.1 Longitudinal tension test specimens taken from the steel shall conform to the requirements as to tensile properties prescribed
in Table 2. At the manufacturers option, the tension test specimen for sizes 8
5
8 in. ( [219.1 mm)] in outside diameter and larger
may be taken transversely as described in 19.4.
7.2 The yield point shall be determined by the drop of the beam, by the halt in the gage of the testing machine, by the use of
dividers, or by other approved methods. The yield strength corresponding to a permanent offset of 0.2 % of the gage length of the
specimen, or to a total extension of 0.5 % of the gage length under load shall be determined.
8. Tensile Requirements of Production Welds
8.1 Reduced-section tension test specimens taken perpendicularly across the weld in the pipe, with the weld reinforcement
removed, shall show a tensile strength not less than 95 % of the minimum specied in Section 7. At the manufacturers option,
the test may be made without removing the weld reinforcement, in which case the tensile strength shall be not less than that
specied in Section 7.
9. Heat Analysis
9.1 An analysis of each heat of steel shall be made by the manufacturer to determine the percentages of the elements specied
in Section 6. This analysis shall be made from a test ingot taken during the pouring of the heat. When requested by the purchaser,
the chemical composition thus determined shall be reported to the purchaser or his representative, and shall conform to the
requirements specied in Section 6.
10. Product Analysis
10.1 An analysis may be made by the purchaser on samples of pipe selected at random and shall conform to the requirements
specied in Section 6. Samples for chemical analysis, except for spectrochemical analysis, shall be taken in accordance with
Method E 59. The number of samples shall be determined as follows:
NPS Number of Samples Selected
Under 14 2 for each lot of 200 pipes or fraction thereof
14 to 36, incl 2 for each lot of 100 pipes or fraction thereof
Over 36 2 for each 3000 ft or fraction thereof
10.2 RetestsIf the analysis of either length of pipe or length of skelp does not conform to the requirements specied in Section
6, analyses of two additional lengths from the same lot shall be made, each of which shall conform to the requirements specied.
11. Dimensions, Weight, Mass, and Permissible Variations
11.1 WeightMassThe specied weight mass per unit length shall be calculated using the following equation:
W 5 C~D 2 t!t (1)
M 5 C~D 2 t!t (1)
M
where:
C = 10.69 ( [0.02466)],
WM = weightmass per unit length, lb/ft (kg/m), [kg/m],
D = outside diameter, in. (mm), [mm], specied or calculated (from inside diameter and wall thickness), and
t = specied wall thickness, in. (to 3 decimal places) (mm) [mm] (to 2 decimal places)
NOTE 6The weights mass per unit length given in the American National Standards ASME B36.10M and ASME B36.19M and the calculated weights
mass given by the equation of 11.1 are based on the weights for carbon steel pipe. The weight mass per unit length of pipe made of ferritic stainless steels
may be about 5 % less, and that made of austenitic stainless steel about 2 % greater than the values given. The specied weight mass of an individual
pipe length shall be calculated as its specied weight mass per unit length times its length.
A 139/A 139M 004
3
11.1.1 The weight mass of any length of pipe shall not vary more than 10 % over the its specied weight. mass.
11.1.2 The weight mass of any length of pipe shall not vary more than 5 % under the specied weight when mass if the specied
wall thickness is 0.188 in. ( [4.78 mm)] or less or more than 5.5 % under when if the specied wall thickness is greater than 0.188
in. ( [4.78 mm)].
11.1.3 The weight mass of a carload lot shall not vary more than 1.75 % under the specied weight. mass. A carload lot is
considered to be a minimum of 40 000 lb (18 144 kg) [18 Mg] shipped on a conveyance.
11.2 ThicknessThe minimum wall thickness at any point shall be not more than 12.5 % under the nominal wall thickness
specied.
TABLE 2 Tensile Requirements
Grade A Grade B Grade C Grade D Grade E
Tensile strength, min, ksi (MPa) 48 (330) 60 (415) 60 (415) 60 (415) 66 (455)
Tensile strength, min, ksi [MPa] 48 [330] 60 [415] 60 [415] 60 [415] 66 [455]
Yield strength, min, ksi (MPa) 30 (205) 35 (240) 42 (290) 46 (315) 52 (360)
Yield strength, min, ksi [MPa] 30 [205] 35 [240] 42 [290] 46 [315] 52 [360]
Elongation in 2 in. or 50 mm, min, %:
Basic minimum elongation for walls
5
16 in. (7.9 mm) and over in 35 30 25 23 22
Basic minimum elongation for walls
5
16 in. [7.9 mm] and over in 35 30 25 23 22
thickness, longitudinal strip tests
For longitudinal strips tests, a deduction for each
1
32-in. (0.8-mm) 1.75
A
1.50
A
1.25 1.50 2.0
For longitudinal strips tests, a deduction for each
1
32-in. [0.8-mm] 1.75
A
1.50
A
1.25 1.50 2.0
decrease in wall thickness below
5
16 in. (7.9 mm) from the
basic minimum elongation of the following percentage
A
decrease in wall thickness below
5
16 in. [7.9 mm] from the
basic minimum elongation of the following percentage
A
Elongation in 8 in. ( 203.2 mm), in min, %
B,C
1 500 000specied tensile strength (psi)
Elongation in 8 in. or 200 mm, min, %
B,C
Inch Pound Units, 1500/specied minimum tensile strength (ksi)
SI Units, 10 300/specied minimum tensile strength [MPa]
A
The table below gives the computed minimum values.
B
For wall thicknesses
1
2 in. ( [12.7 mm)] and greater, the elongation may be taken in 8 in. ( or 203.20 mm).
C
The elongation in 8 in. (203.2 mm) need not exceed 30 %.
Wall Thickness Elongation in 2 in. or 50 mm, min, %
in. mm Grade A Grade B
5
16 (0.312) 7.94 35.00 30.00
5
16 (0.312) 7.9 35.00 30.00
9
32 (0.281) 7.14 33.25 28.50
9
32 (0.281) 7.1 33.25 28.50
1
4 (0.250) 6.35 31.50 27.00
1
4 (0.250) 6.4 31.50 27.00
7
32 (0.219) 5.56 29.75 25.50
7
32 (0.219) 5.6 29.75 25.50
3
16 (0.188) 4.76 28.00 24.00
3
16 (0.188) 4.8 28.00 24.00
5
32 (0.156) 3.97 26.25 22.50
5
32 (0.156) 4.0 26.25 22.50
1
8 (0.125) 3.68 24.50 21.00
1
8 (0.125) 3.7 24.50 21.00
3
32 (0.094) 2.38 22.75 19.50
3
32 (0.094) 2.4 22.75 19.50
1
16 (0.062) 1.59 21.00 18.00
1
16 (0.062) 1.6 21.00 18.00
NoteThe above table gives the computed minimum elongation values for each
1
32-in. ( [0.798-mm)] decrease in wall thickness. Where the wall thickness lies between
two values shown above, the minimum elongation value shall be determined by the following equation:
Grade Equation
Inch-Pound Units
Equation
SI Units
A E = 56t + 17.50
A E = 56t + 17.50 E = 2.20t + 17.50
B E = 48t + 15.00
B E = 48t + 15.00 E = 1.89t + 15.00
C E = 40t + 12.50
C E = 40t + 12.50 E = 1.57t + 12.50
D E = 48t + 8
D E = 48t + 8 E = 1.89t + 8
E E = 64t + 2 E = 2.52t + 2
where:
E = elongation in 2 in. or 50 mm, %, and
t = actual thickness of specimen, in. [mm]
A 139/A 139M 004
4
11.3 CircumferenceThe pipe shall be substantially round. The outside circumference of the pipe shall not vary more than
61.0 %, but not exceeding 6
3
4 in. ( [19.0 mm)], from the nominal outside circumference based upon the diameter specied,
except that the circumference at ends shall be sized, if necessary, to meet the requirements of Section 18.
11.4 StraightnessFinished pipe shall be commercially straight. When specic straightness requirements are desired, the order
should so state, and the tolerance shall be a matter of agreement between the purchaser and the manufacturer.
11.5 Ovality (Out-of-Roundness) The pipe diameter, within 4.0 in. (100 mm) [100 mm] of ends, shall not vary more than 1 %
from the specied diameter as measured across any single plane with a bar gage, caliper, or other instrument capable of measuring
actual diameter.
12. Finish
12.1 Repair by WeldingThe manual, or automatic arc, welding of injurious defects in the pipe wall, provided their depth does
not exceed one third the specied wall thickness, will be permitted. Defects in the welds, such as sweats or leaks, shall be repaired
or the piece rejected at the option of the manufacturer. Repairs of this nature shall be made by completely removing the defect,
cleaning the cavity, and then welding.
12.2 All repaired pipe shall be tested hydrostatically in accordance with Section 16.
13. Retests
13.1 If any specimen tested under Sections 8 or 15 fails to meet the requirements, retests of two additional specimens from the
same lot of pipe shall be made, all of which shall meet the specied requirements. If any of the retests fail to conform to the
requirements, test specimens may be taken from each untested pipe length, at the manufacturers option, and each specimen shall
meet the requirements specied, or that pipe shall be rejected.
14. Number of Production Test Specimens
14.1 One longitudinal tension test specimen specied in 19.2 shall be made from the steel of each heat, or fraction thereof, used
in the manufacture of the pipe.
14.2 One reduced-section production weld test specimen specied in 19.5 shall be taken from a length of pipe from each lot
of 3000 ft (914 m) of pipe, or fraction thereof, of each size and wall thickness.
14.3 If any test specimen shows defective machining or develops aws not associated with the quality of the steel or the
welding, it may be discarded and another specimen substituted.
14.4 Each length of pipe shall be subjected to the hydrostatic test specied in Section 16.
15. Qualication of Welding Procedure
15.1 Welding procedures shall be qualied in accordance with the requirements of ANSI/AWS AWS B2.1; ASME Boiler and
Pressure Vessel Code, Section IX; or other qualication procedures as noted in the American Welding Society Welding Handbook.
Tests and test values shall be as specied in 15.2 and 15.3.
15.2 Two reduced-section tension specimens made in accordance with Fig. 1, with the weld reinforcement removed, shall show
a tensile strength not less than 100 % of the minimum specied tensile strength of the grade of steel used.
15.3 Bend test specimens (two face-bend and two root-bend or four side-bend as designated by the welding procedure according
to thickness) shall be prepared in accordance with Fig. 2 and shall withstand being bent 180 in a jig substantially in accordance
with Fig. 3. The bend test shall be acceptable if no cracks or other defects exceeding
1
8 in. (3.2 mm) [3.2 mm] in any direction
are present in the weld metal or between the weld and the pipe metal after bending. Cracks that originate along the edges of the
specimens during testing, and that are less than
1
4 in. (6.3 mm) [6.4 mm] in any direction shall not be considered. (If necessary,
the specimen shall be broken apart to permit examination of the fracture.)
16. Hydrostatic Test (Note 7)
16.1 Each length of pipe shall be tested by the manufacturer to a hydrostatic pressure that will produce in the pipe wall a stress
Metric Equivalents
in. 0.01
1
4 1
1
2 10
mm 0.3 6.4 38.1 254
mm 0.3 6.4 38 250
FIG. 1 Reduced-Section Tension Test Specimen
A 139/A 139M 004
5
of not less than 60 % of the minimum specied minimum yield point strength at room temperature. The pressure shall be
determined by the following equation:
P 5 2St/D (2)
where:
P = hydrostatic test pressure, psi [MPa] (not to exceed 2800 psi ( [19.3 MPa)] in any case) (Note 8),
S = 0.60 to 0.85 times the minimum specied minimum yield point strength of the grade of steel used in pounds per square
inch, psi [MPa],
t = specied wall thickness, in. [mm], and
D = specied outside diameter, in.[mm]
NOTE 7A hydrostatic sizing operation is not to be considered a hydrostatic test or a substitute for it.
NOTE 8When the diameter and wall thickness of pipe are such that the capacity limits of testing equipment are exceeded by these requirements, the
test pressures may be reduced by agreement between the purchaser and the manufacturer.
16.2 Test pressure shall be held for not less than 5 s, or for a longer time as agreed upon between the purchaser and the
manufacturer.
NOTE 9When agreed upon by 9Where specied in the purchaser and the manufacturer and so stated on the purchase order, the pipe may be tested:
(1) To 1
1
2 times tested: (1) to 1.5 times the specied working pressure, except that provided the maximum test pressure shall
does not exceed 2800 psi (19.31 MPa) nor shall the maximum [19.3 MPa] or produce a ber stress exceed in excess of 85 % of
the specied minimum yield point of strength for the grade of steel used.
(2) To applicable pipe grade, or (2) to a ber stress which does not exceed of 85 % or less of the specied minimum yield point
Metric Equivalents
in.
1
16 1
1
2 6
in.
1
16 1
1
2 6
mm 1.6 38.1 152.4
mm 1.6 38 150
NOTE 1Weld reinforcement may or may not be removed ush with
the surface of the specimen.
NOTE 2Shown in Fig. 2 is a root- or face-bend specimen. Side-bend
specimens shall have a thickness (T) of
3
8 in. (9.5 mm) and a width equal
to the pipe wall thickness.
FIG. 2 Guided-Bend Test Specimen
A 139/A 139M 004
6
of strength for the grade of steel used or exceed 2800-psi applicable pipe grade, provided that the test pressure does not exceed
2800 psi [19.3 MPa].
16.2 Test pressure shall be held for not less than 5 s, or for a longer time as agreed upon between the purchaser and the
manufacturer.
17. Lengths
17.1 Pipe lengths shall be supplied in accordance with the following regular practice:
17.1.1 Specic lengths shall be as specied on the order with a tolerance of 6
1
2 in. ( [12.7 mm)], except that the shorter lengths
from which test coupons have been cut shall also be shipped.
17.1.2 Unless otherwise specied random lengths shall be furnished in lengths averaging 29 ft (8.9 m) [8.9 m] or over, with a
minimum length of 20 ft (6.1 m), [6.1 m], but not more than 5 % may be under 25 ft (7.6 m). [7.6 m].
17.1.3 Pipe lengths containing circumferentially welded joints (Note 6) shall be permitted by agreement between the purchaser
and the manufacturer. Tests of these welded joints shall be made in accordance with the production weld tests described in Section
8. The number of production weld tests shall be one for each lot of 100 joints or fraction thereof, but not less than one for each
welder or welding operator.
NOTE 10Circumferentially welded joints are dened for the purpose of these specications as a welded seam lying in one plane, used to join lengths
of straight pipe.
18. Ends
18.1 Pipe shall be furnished with plain right-angle cut or beveled ends as specied. All burrs at the ends of pipe shall be
removed.
18.2 When pipe is specied to have the ends prepared for eld welding of circumferential joints, the ends shall be beveled on
the outside to an angle of 35, measured from a line drawn perpendicular to the axis of the pipe, with a tolerance of 62
1
2 and
with a width of root face (or at at the end of the pipe) of
1
16 6
1
32 in. ( [1.6 6 0.8 mm)]. Unless otherwise specied, the outside
circumference of pipe ends for a distance of not less than 4 in. ( [101.6 mm)] shall not vary more than 660 % of the nominal wall
thickness of the pipe from the nominal outside circumference based on the diameter specied, except that the tolerance shall be
not less than 6
3
16 in. (9.5 mm). [4.8 mm].
18.3 Pipe ends for use with mechanical couplings shall have tolerances within the limits required by the manufacturer of the
type of coupling to be used.
18.4 Upon agreement between the purchaser and the manufacturer, the ends of the pipe may be sized within agreed-upon
tolerances, if necessary to meet the requirements of special installations.
19. Production Test Specimens and Methods of Testing
19.1 The test specimens and the tests required by these specications shall conform to those described in Test Methods and
Denitions A 370.
19.2 The longitudinal tension tests specimen of the steel shall be taken from the end of the pipe in accordance with Fig. 4, or
by agreement between the purchaser and the manufacturer, or may be taken from the skelp or plate, at a point which will be
approximately 90 of arc from the weld in the nished pipe.
19.3 If the tension test specimen is taken transversely, the specimen shall be taken in accordance with Fig. 5.
19.4 The specimens for the reduced-section tension test of production welds shall be taken perpendicularly across the weld at
the end of the pipe. The test specimens shall have the weld approximately in the middle of the specimen. The specimens shall be
straightened and tested at room temperature.
19.5 Reduced-section tension test specimens shall be prepared in accordance with Fig. 1.
20. Inspection
20.1 The inspector representing the purchaser shall have entry, at all times while work on the contract of the purchaser is being
performed, to all parts of the manufacturers works that concern the manufacture of the material ordered. The manufacturer shall
afford the inspector all reasonable facilities to satisfy him that the material is being furnished in accordance with this specication.
All tests and inspection shall be made at the place of manufacture prior to shipment and, unless otherwise specied, shall be so
conducted as not to interfere unnecessarily with the operation of the works. If agreed upon, the manufacturer shall notify the
purchaser in time so that he may have his inspector present to witness any part of the manufacture or tests that may be desired.
FIG. 4 Location from Which Longitudinal Tension Test
Specimens Are To Be Cut from Large Diameter Tubing
A 139/A 139M 004
7
20.2 CerticationUpon request of the purchaser in the contract or order, a manufacturers certication that the material was
manufactured and tested in accordance with this specication together with a report of the chemical and tensile tests shall be
furnished.
21. Rejection
21.1 Each length of pipe received from the manufacturer may be inspected by the purchaser and, if it does not meet the
requirements of this specication based on the inspection and test method as outlined in the specication, the length may be
rejected and the manufacturer shall be notied. Disposition of rejected pipe shall be a matter of agreement between the
manufacturer and the purchaser.
21.2 Pipe found in fabrication or in installation to be unsuitable for the intended use, under the scope and requirements of this
specication, may be set aside and the manufacturer notied. Such pipe shall be subject to mutual investigation as to the nature
and severity of the deciency and the forming or installation, or both, conditions involved. Disposition shall be a matter for
agreement.
22. Protective Coating
22.1 If agreed upon between the purchaser and the manufacturer, the pipe shall be given a protective coating of the kind and
in the manner specied by the purchaser.
23. Product Marking
23.1 Each section of pipe shall be marked with the manufacturers distinguishing marking, the specication number, the grade
of pipe, and other marking if required and agreed upon between the purchaser and the manufacturer.
23.2 Bar CodingIn addition to the requirements in 23.1, bar coding is acceptable as a supplemental identication method. The
purchaser may specify in the order a specic bar coding system to be used.
24. Keywords
24.1 arc welded steel pipe; fusion welded steel pipe; steel pipe; welded steel pipe
SUMMARY OF CHANGES
Committee A01 has identied the location of selected changes to this specication since the last issue,
A 139 00, that may impact the use of this specication. (Approved March 1, 2004)
(1) Revised Sections 1, 3, 7, 11, 16, 17, and 18, Table 2, and Figures 1 and 2 to include rationalized SI units, creating a combined
standard.
FIG. 5 Location of Transverse Tension Test Specimen in Ring Cut
from Tubular Steel Products
A 139/A 139M 004
8
ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every ve years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.
This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website
(www.astm.org).