Plastic waste reduction and recycling through circular use has been critical nowadays, since there is an increasing demand for the production of plastic components based on different polymeric matrices in various applications. The most commonly used recycling procedure, especially for thermoplastic materials, is based on thermomechanical process protocols that could significantly alter the polymers' macromolecular structure and physicochemical properties. The study at hand focuses on recycling of polyamide 12 (PA12) filament, through extrusion melting over multiple recycling courses, giving insight for its effect on the mechanical and thermal properties of Fused Filament Fabrication (FFF) manufactured specimens throughout the recycling courses. Three-dimensional (3D) FFF printed specimens were produced from virgin as well as recycled PA12 filament, while they have been experimentally tested further for their tensile, flexural, impact and micro-hardness mechanical properties. A thorough thermal and morphological analysis was also performed on all the 3D printed samples. The results of this study demonstrate that PA12 can be successfully recycled for a certain number of courses and could be utilized in 3D printing, while exhibiting improved mechanical properties when compared to virgin material for a certain number of recycling repetitions. From this work, it can be deduced that PA12 can be a viable option for circular use and 3D printing, offering an overall positive impact on recycling, while realizing 3D printed components using recycled filaments with enhanced mechanical and thermal stability.
Keywords: Charpy’s impact test; Vicker’s micro-hardness; additive manufacturing (AM); flexural test; polyamide 12 (PA12); recycling; scanning electron microscopy (SEM); tensile test; three-dimensional (3D) printing.