A study on mechanical, thermal and flame retardant properties of epoxy/expandable graphite composites

The purpose of this paper is to investigate the effect of expandable graphite (EG) plates’ incorporation on the mechanical, thermal and fire-retardant properties of an epoxy–aliphatic amine system. In addition, the optimum amount of EG in epoxy/EG composites is determined to achieve the best thermal and mechanical properties at the same time.

The epoxy/EG composites were prepared by using (1-4) phr of EG. The morphological structure of epoxy/EG composites was studied by using scanning electron microscopy. The thermal, flame-retardant and mechanical properties of epoxy/EG composites were evaluated by using thermogravimetric analysis (TGA), oxygen index test and dynamic mechanical analysis and tensile and impact test, respectively.

TGA results showed that the incorporation of EG to the epoxy resin increased the initial decomposition temperature and residue weight of the composites. It was found that, with increasing EG concentration up to 4 phr, the oxygen index, glass transition temperature and Young’s modulus of epoxy/EG composites increased up to 60 per cent, 4.1°C and 50 per cent, respectively. On the other hand, the sample with 2 phr EG provided the maximum values of tensile strength, storage modulus, cross-linking density, ultimate tensile strain and impact strength.

Prepared epoxy/EG composites can be used as halogen-free flame-retardant composites. The proposed process for the preparation of the composites is simple and can easily be implicated in the industry.

To the best of the authors’ knowledge, there is no other publication that considers mechanical, thermal and fire-retardant properties of epoxy/EG composites in one paper. In this work, the optimum concentration of EG in epoxy/EG composites was determined, considering all these properties.