Title:Damage accumulation during high temperature fatigue of Ti/SiC$_f$ metal matrix composites under different stress amplitudes
View PDFAbstract:The damage mechanisms and load redistribution of high strength TC17 titanium alloy/unidirectional SiC fibre composite (fibre diameter = 100 $\mu$m) under high temperature (350 °C) fatigue cycling have been investigated in situ using synchrotron X-ray computed tomography (CT) and X-ray diffraction (XRD) for high cycle fatigue (HCF) under different stress amplitudes. The three-dimensional morphology of the crack and fibre fractures has been mapped by CT. During stable growth, matrix cracking dominates with the crack deflecting (by 50-100 $\mu$m in height) when bypassing bridging fibres. A small number of bridging fibres have fractured close to the matrix crack plane especially under relatively high stress amplitude cycling. Loading to the peak stress led to rapid crack growth accompanied by a burst of fibre fractures. Many of the fibre fractures occurred 50-300 $\mu$m from the matrix crack plane during rapid growth, in contrast to that in the stable growth stage, leading to extensive fibre pull-out on the fracture surface. The changes in fibre loading, interfacial stress, and the extent of fibre-matrix debonding in the vicinity of the crack have been mapped for the fatigue cycle and after the rapid growth by high spatial resolution XRD. The fibre/matrix interfacial sliding extends up to 600 $\mu$m (in the stable growth zone) or 700 $\mu$m (in the rapid growth zone) either side of the crack plane. The direction of interfacial shear stress reverses with the loading cycle, with the maximum frictional sliding stress reaching ~55 MPa in both the stable growth and rapid growth regimes.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.